CN1121449C - 高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯 - Google Patents

高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯 Download PDF

Info

Publication number
CN1121449C
CN1121449C CN 00124686 CN00124686A CN1121449C CN 1121449 C CN1121449 C CN 1121449C CN 00124686 CN00124686 CN 00124686 CN 00124686 A CN00124686 A CN 00124686A CN 1121449 C CN1121449 C CN 1121449C
Authority
CN
China
Prior art keywords
polybutylene terephthalate
flame retardant
fire
retardant
glass fibre
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN 00124686
Other languages
English (en)
Other versions
CN1310200A (zh
Inventor
吉继亮
苏妤
刘志力
袁志敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kingfa Science and Technology Co Ltd
Original Assignee
Guangzhou Kingfa Science and Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Kingfa Science and Technology Co Ltd filed Critical Guangzhou Kingfa Science and Technology Co Ltd
Priority to CN 00124686 priority Critical patent/CN1121449C/zh
Publication of CN1310200A publication Critical patent/CN1310200A/zh
Application granted granted Critical
Publication of CN1121449C publication Critical patent/CN1121449C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

本发明涉及一种高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯(PBT)的复合物及其制备方法，该复合物包含：聚对苯二甲酸丁二醇酯、主阻燃剂、助阻燃剂、成核剂和玻璃纤维。本发明涉及阻燃剂复配技术和产生高光泽的成核技术，从根本上解决了材料阻燃剂高温析出、玻纤外露、制品表面泛白、无光泽和成型周期长的难题。本发明复合物适用于电器接插件、继电器、汽车零部件、节能灯等产品。

Description

高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯
本发明涉及一种高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物及其制备方法，该复合物及其制备方法属于高分子材料成型加工领域。
目前国内生产阻燃增强聚对苯二甲酸丁二醇酯的厂家较多，但产品在成型加工时容易产生阻燃剂高温析出，制品表面泛白，析出的阻燃剂腐蚀模具；普通阻燃增强聚对苯二甲酸丁二醇酯对玻璃纤维包覆不好，制品表面容易产生浮纤，因而光泽差；普通阻燃增强聚对苯二甲酸丁二醇酯结晶速度慢，制品成型周期长，生产效率低；此外，普通阻燃增强聚对苯二甲酸丁二醇酯采用十溴联苯醚和三氧化二锑阻燃体系，到2003-2004年，欧洲将开始限制十溴联苯醚阻燃的产品进入欧洲。
国外阻燃增强聚对苯二甲酸丁二醇酯的生产厂家较多，对阻燃增强聚对苯二甲酸丁二醇酯研究开发较早，但生产周期长。
本发明的目的就是为了克服现有材料的以上缺点而提供一种新的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物。
依据本发明所设计的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物，其典型组成(重量份数)为：聚对苯二甲酸丁二醇酯100份、苄基苯氧基苯的氟溴化物12-22份、聚醚1-9份、饱和羧酸盐2-8份、玻璃纤维20-65份。
本发明的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物的制备方法为：先将复合物中除阻燃剂外的其它组分经高速搅拌混合，再由精密计量的喂料器送入双螺杆挤出机，随后将复合阻燃剂和玻璃纤维从各自的精密计量喂料器加入挤出机，充分塑化、熔融、复合，再经挤出、拉条、冷却、切粒、烘干和包装。
本发明的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物中的主阻燃剂是先将溴化的苄基苯氧基苯加入到高速混合机中，升温至100-120℃，高速搅拌下缓慢加入一种氟化合物，然后恒温低速搅拌20-45分钟，放料即可得到淡黄色的粉状的苄基苯氧基苯的氟溴化物。
本发明的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物所用的溴化的苄基苯氧基苯和氟化合物均有市售。
本发明的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物的制备工艺流程参见附图。
应用于本发明制备方法中的双螺杆挤出机的长经比至少为32，至少有两套带有精密计量仪器的侧向加料装置；带有精确的温度控制和真空排气设备。
本发明的制备方法中的各段螺杆温度应控制在215-295℃之间，最好控制在225-275℃之间。
本发明的具体实施方案由实施实例给出。
将90份溴化的苄基苯氧基苯加入到高速混合机中，升温至105℃，高速搅拌下缓慢加入10份聚四氟乙烯乳液，然后恒温低速搅拌30分钟，放料得到主阻燃剂苄基苯氧基苯的氟溴化物。
实施实例配方见表1。
                                     表1
名称   聚对苯二甲酸丁二醇酯  苄基苯氧基苯的氟溴化物 聚苯醚 十八烷基苯磺酸钠 固体石蜡 硬脂酸锌            玻璃纤维
 情形1  情形2  情形3
重量份数 100 20 8 7 0.3 0.3 20 40 60
实施实例复合物的性能检测结果见表2。
                                 表2
项目 测试方法 单位               指标
   情形1    情形2    情形3
熔融指数 GB3682 G/10min     24     22     18
拉伸强度 GB1040 MPa     92     100     118
弯曲强度 GB9341 MPa     125     140     160
弯曲模量 GB9341 MPa     3980     4000     6000
缺口冲击强度 GB1843 KJ/m2     7.5     8.5     9.5
热变形温度 GB1634 ℃     195     205     212
阻燃性能 UL94 0.8mm     V-0     V-0     V-0
光泽度 GB8807 ％     96     96     96

Claims (10)

1.一种高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物，该复合物包含：聚对苯二甲酸丁二醇酯、主阻燃剂、助阻燃剂、成核剂和玻璃纤维，其中聚对苯二甲酸丁二醇酯为100份、主阻燃剂为12-22份、助阻燃剂为1-9份、成核剂为2-8份、玻璃纤维为20-65份，其中所述主阻燃剂为苄基苯氧基苯的氟溴化物，助阻燃剂为聚醚，成核剂为饱和羧酸盐。
2.根据权利要求1所述的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物，其特征在于玻璃纤维为20-30份。
3，根据权利要求1所述的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物，其特征在于玻璃纤维为30-40份。
4.根据权利要求1所述的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物，其特征在于玻璃纤维为55-65份。
5.根据权利要求1所述的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物，其特征在所述主阻燃剂通过下述复配技术制得：先将溴化的苄基苯氧基苯加入到高速混合机中，升温至100-120℃，高速搅拌下缓慢加入一种氟化合物乳液，然后恒温低速搅拌一段时间，得到主阻燃剂苄基苯氧基苯的氟溴化物。
6.制备利要求1所述的高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯复合物的方法，该方法包括：将复合物中的聚对苯二甲酸丁二醇酯、聚醚、成核剂及其它组分经高速搅拌机混合后，由精密计量的喂料器送入双螺杆挤出机，同时将苄基苯氧基苯的氟溴化物、玻璃纤维从各自的喂料口加入挤出机，在双螺杆输送和剪切作用下，充分塑化、熔融、复合，再经挤出、拉条、冷却、切粒、烘干和包装。
7.根据权利要求6所述的方法，其特征在于该方法是采用双螺杆挤出工艺及设备。
8.根据权利要求6所述的方法，其特征在于该方法是采用双螺杆挤出设备的长经比至少是32；并配有精确的温度控制和真空排气设备。
9.根据权利要求6所述的方法，其特征在于该方法的各段螺杆温度应控制在215-295℃之间。
10、根据权利要求6所述的方法，其特征在于该方法的各段螺杆温度应控制在225-275℃之间。
CN 00124686 2000-09-28 2000-09-28 高光泽、快速成型阻燃增强聚对苯二甲酸丁二醇酯 Expired - Lifetime CN1121449C (zh)