CN112111806A - 一种医用纤维及其制备方法和应用 - Google Patents
一种医用纤维及其制备方法和应用 Download PDFInfo
- Publication number
- CN112111806A CN112111806A CN202010851644.7A CN202010851644A CN112111806A CN 112111806 A CN112111806 A CN 112111806A CN 202010851644 A CN202010851644 A CN 202010851644A CN 112111806 A CN112111806 A CN 112111806A
- Authority
- CN
- China
- Prior art keywords
- fiber
- parts
- medical
- medical fiber
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种医用纤维及其制备方法和应用，所述医用纤维包括以下重量份的组分：羧甲基纤维素钠15‑28份、壳聚糖化合物纤维48‑136份、纳米级超导电材料22‑30份、抗辐射添加剂2‑9份、分散剂6‑14份。本发明的医用纤维具有较好的柔韧性，且透气性好，吸湿性强，不会起球、起毛，护色效果好；添加无机纳米级超导电材料，起到抗静电的作用；添加有机抗辐射剂，使得医用纤维有一定的抗辐射、抗紫外的效果。
Description
技术领域
本发明涉及纺织纤维技术领域，尤其涉及一种医用纤维及其制备方法和应用。
背景技术
涤纶，学名聚酯纤维之一，是我国合成纤维的重要组成部分，是以对苯二甲酸(PTA)或对苯二甲酸二甲酯(DMT)和乙二醇(EG)原料经过酯化或者酯交换和缩聚反应而制得的成纤高聚物-聚对苯二甲酸乙二醇酯(PET)，经过纺丝和后处理制得纤维，具有良好的机械强度、耐光、耐热，具有良好的加工性和易纺性，在医疗领域被广泛使用。
医用制服是针对医护人员设计的一类特殊的服装，与其他的职业服不同，它面对的是特殊的群体和特定的操作环境，因此有特殊的功能设计要求。目前随着科技的发展，出现了许多具有新功能的医用面料，例如，申请号为201310357613.6的中国发明专利公开了一种医用面料，该医用面料由云母冰凉纤维、纯壳聚糖纤维和长效蓄光纤维混纺而成的织物，所述云母冰凉纤维是由云母矿石为原料，所述云母冰凉纤维占面料主体重量的84-95％，所述纯壳聚糖纤维占面料主体重量的2-10％，所述长效蓄光纤维占面料主体重量的2-9％，该面料具有良好的抑菌、吸湿防湿快、吸附异味及重金属元素等特点。上述专利中的医用面料虽然均具有一定的特殊功用，但医护人员的工作环境较复杂，例如：辐射、静电以及感染性较强的细菌、病毒等，因此急需对现有的医用面料进行改进，提供一种抗菌效果好、透气吸湿性强，不起球不起毛不掉色，同时能够有一定防辐射和抗静电效果的医用布料，以提高医护人员的工作舒适度和安全保障。
发明内容
本发明的目的是针对现有技术中的不足，提供一种医用纤维及其制备方法和应用，制得的医用纤维具有较好的柔韧性，且透气性好，吸湿性强，不会起球、起毛，护色效果好；添加无机纳米级超导电材料，起到抗静电的作用；添加有机抗辐射剂，使得医用纤维有一定的抗辐射、抗紫外的效果。
为实现上述目的，本发明采取的技术方案是：
本发明第一方面提供一种医用纤维，所述医用纤维包括以下重量份的组分：羧甲基纤维素钠15-28份、壳聚糖化合物纤维48-136份、纳米级超导电材料22-30份、抗辐射添加剂2-9份、分散剂6-14份。
优选的，所述医用纤维包括以下重量份的组分：羧甲基纤维素钠20份、壳聚糖化合物纤维96份、纳米级超导电材料28份、抗辐射添加剂7份、分散剂9份。
优选的，所述羧甲基纤维素钠与壳聚糖化合物纤维的重量比为(1-3):(7-9)。
优选的，所述壳聚糖化合物纤维为水溶性壳聚糖纤维。
优选的，所述纳米级超导电材料为镍包石墨粉、镍包碳纤维炭黑、金属粉、金属纤维、碳纤维、白炭黑、石墨、碳纳米管和富勒烯中的一种或者几种。
优选的，所述抗辐射添加剂为碳化铅、碳化硼、二苯基砜、无水硼酸、碳酸锂和氧化锡中的一种或几种。
优选的，所述分散剂为硬脂酸钠和油酸钠的混合液。
本发明第二方面提供医用纤维的制备方法，包括以下步骤：
将羧甲基纤维素钠、壳聚糖化合物纤维、纳米级超导电材料、抗辐射添加剂和分散剂按比例通过湿法纺丝制备得到医用纤维。
优选的，所述湿法纺丝工艺流程为：溶解-过滤-脱泡-纺丝-拉伸-水洗-上油-集束-干燥-切断。
本发明第三方面提供上述医用纤维用于制造医用纤维敷料，所述医用纤维敷料包括依次连接的的无纺布基层、甲壳素纤维网中间层、敷芯层和布料外层；所述无纺布基层为亲水布，所述敷芯层由SAF纤维和PLA纤维分层针刺而成，所述布料外层采用天丝材料织造构成，所述无纺布基层、甲壳素纤维网中间层、敷芯层和布料外层各层之间均采用医用双面胶复合固定连接。
优选的，所述无纺布基层为纺粘无纺布、热风无纺布和热轧无纺布中的一种。
优选的，所述无纺布基层的克重为16-48g/m2。
优选的，所述甲壳素纤维网中间层的表面具有开孔结构。
优选的，所述甲壳素纤维网中间层的克重为21-30g/m2。
优选的，所述敷芯层的克重为18-28g/m2。
优选的，所述布料外层的克重为30-120g/m2。
本发明采用以上技术方案，与现有技术相比，具有如下技术效果：
1、采用本发明的医用纤维制造的针织产品具有较好的柔韧性，且透气性好，吸湿性强，不会起球、起毛，护色效果好；添加无机纳米级超导电材料，起到抗静电的作用；添加有机抗辐射剂，使得医用纤维有一定的抗辐射、抗紫外的效果。
2、本发明的医用纤维还可以用作包括止血剂、防粘连屏障和伤口敷料的各种医用材料，应用范围较广。
附图说明
图1为本发明中医用纤维敷料的示意图；
其中的各附图标记为：
1-无纺布基层；2-甲壳素纤维网中间层；3-敷芯层；4-布料外层。
具体实施方式
下面结合具体实施例对本发明作进一步说明，但不作为本发明的限定。
需要说明的是，在不冲突的情况下，本发明中的实施例及实施例中的特征可以相互组合。
实施例一
一种医用纤维，所述医用纤维包括以下重量份的组分：羧甲基纤维素钠15份、水溶性壳聚糖纤维48份、镍包石墨粉22份、碳化铅2份、硬脂酸钠和油酸钠的混合液6份。
上述医用纤维的制备方法，包括以下步骤：
将羧甲基纤维素钠、壳聚糖化合物纤维、纳米级超导电材料、抗辐射添加剂和分散剂按上述比例通过湿法纺丝制备得到医用纤维。
值得注意的是，本实施例所述湿法纺丝为现有技术中的常规湿法纺丝工艺，流程为：溶解-过滤-脱泡-纺丝-拉伸-水洗-上油-集束-干燥-切断。
实施例二
一种医用纤维，所述医用纤维包括以下重量份的组分：羧甲基纤维素钠20份、水溶性壳聚糖纤维96份、金属粉28份、二苯基砜7份、硬脂酸钠和油酸钠的混合液9份。
上述医用纤维的制备方法，包括以下步骤：
将羧甲基纤维素钠、壳聚糖化合物纤维、纳米级超导电材料、抗辐射添加剂和分散剂按上述比例通过湿法纺丝制备得到医用纤维。
值得注意的是，本实施例所述湿法纺丝为现有技术中的常规湿法纺丝工艺，流程为：溶解-过滤-脱泡-纺丝-拉伸-水洗-上油-集束-干燥-切断。。
实施例三
一种医用纤维，所述医用纤维包括以下重量份的组分：羧甲基纤维素钠28份、水溶性壳聚糖纤维136份、碳纳米管30份、碳酸锂9份、硬脂酸钠和油酸钠的混合液14份。
上述医用纤维的制备方法，包括以下步骤：
将羧甲基纤维素钠、壳聚糖化合物纤维、纳米级超导电材料、抗辐射添加剂和分散剂按上述比例通过湿法纺丝制备得到医用纤维。
值得注意的是，本实施例所述湿法纺丝为现有技术中的常规湿法纺丝工艺，流程为：溶解-过滤-脱泡-纺丝-拉伸-水洗-上油-集束-干燥-切断。
采用上述任一实施例中医用纤维用于制造医用纤维敷料，如图1所示，医用纤维敷料包括依次连接的的无纺布基层1、甲壳素纤维网中间层2、敷芯层3和布料外层4；无纺布基层1为亲水布，敷芯层3由SAF纤维和PLA纤维分层针刺而成，布料外层4采用天丝材料织造构成，无纺布基层1、甲壳素纤维网中间层2、敷芯层3和布料外层4各层之间均采用医用双面胶复合固定连接。
作为一个优选实施例，无纺布基层为纺粘无纺布、热风无纺布和热轧无纺布中的一种，无纺布基层的克重为16-48g/m2。甲壳素纤维网中间层的表面具有开孔结构，甲壳素纤维网中间层的克重为21-30g/m2。敷芯层的克重为18-28g/m2。所述布料外层的克重为30-120g/m2。
应用例
对实施例1-3制得的医用纤维进行各种性能测试，结果如表1所示：
表1
| 毒性试验结果 | 抗菌率(％) | 电导率(S/cm) | |
| 实施例1 | 无毒 | 97 | 0.0086 |
| 实施例2 | 无毒 | 99 | 0.012 |
| 实施例3 | 无毒 | 98 | 0.0092 |
由表1中的数据可知，所制得的医用纤维属于无毒级别，且具有很好的抗菌活性，此外，电导率较高表明医用纤维的抗静电效果好。
以上所述仅为本发明较佳的实施例，并非因此限制本发明的实施方式及保护范围，对于本领域技术人员而言，应当能够意识到凡运用本发明说明书内容所作出的等同替换和显而易见的变化所得到的方案，均应当包含在本发明的保护范围内。
Claims (10)
1.一种医用纤维，其特征在于，所述医用纤维包括以下重量份的组分：羧甲基纤维素钠15-28份、壳聚糖化合物纤维48-136份、纳米级超导电材料22-30份、抗辐射添加剂2-9份、分散剂6-14份。
2.根据权利要求1所述的医用纤维，其特征在于，所述医用纤维包括以下重量份的组分：羧甲基纤维素钠20份、壳聚糖化合物纤维96份、纳米级超导电材料28份、抗辐射添加剂7份、分散剂9份。
3.根据权利要求1所述的医用纤维，其特征在于，所述羧甲基纤维素钠与壳聚糖化合物纤维的重量比为(1-3):(7-9)。
4.根据权利要求1所述的医用纤维，其特征在于，所述壳聚糖化合物纤维为水溶性壳聚糖纤维。
5.根据权利要求1所述的医用纤维，其特征在于，所述纳米级超导电材料为镍包石墨粉、镍包碳纤维炭黑、金属粉、金属纤维、碳纤维、白炭黑、石墨、碳纳米管和富勒烯中的一种或者几种。
6.根据权利要求1所述的医用纤维，其特征在于，所述抗辐射添加剂为碳化铅、碳化硼、二苯基砜、无水硼酸、碳酸锂和氧化锡中的一种或几种。
7.根据权利要求1所述的医用纤维，其特征在于，所述分散剂为硬脂酸钠和油酸钠的混合液。
8.根据权利要求1-7任一项所述医用纤维的制备方法，其特征在于，包括以下步骤：
将羧甲基纤维素钠、壳聚糖化合物纤维、纳米级超导电材料、抗辐射添加剂和分散剂按比例通过湿法纺丝制备得到医用纤维。
9.根据权利要求8所述医用纤维的制备方法，其特征在于，所述湿法纺丝工艺流程为：溶解-过滤-脱泡-纺丝-拉伸-水洗-上油-集束-干燥-切断。
10.采用如权利要求1-7任一项所述的医用纤维，其特征在于，用于制造医用纤维敷料，所述医用纤维敷料包括依次连接的的无纺布基层(1)、甲壳素纤维网中间层(2)、敷芯层(3)和布料外层(4)；所述无纺布基层(1)为亲水布，所述敷芯层(3)由SAF纤维和PLA纤维分层针刺而成，所述布料外层(4)采用天丝材料织造构成，所述无纺布基层(1)、甲壳素纤维网中间层(2)、敷芯层(3)和布料外层(4)各层之间均采用医用双面胶复合固定连接。