CN112094129A - 高温粘结剂及其制备方法 - Google Patents

高温粘结剂及其制备方法 Download PDF

Info

Publication number
CN112094129A
CN112094129A CN202011070597.9A CN202011070597A CN112094129A CN 112094129 A CN112094129 A CN 112094129A CN 202011070597 A CN202011070597 A CN 202011070597A CN 112094129 A CN112094129 A CN 112094129A
Authority
CN
China
Prior art keywords
aggregate
micro powder
liquid material
temperature
mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202011070597.9A
Other languages
English (en)
Inventor
盛玉龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI BAOSTEEL CASTING CO Ltd
Original Assignee
SHANGHAI BAOSTEEL CASTING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI BAOSTEEL CASTING CO Ltd filed Critical SHANGHAI BAOSTEEL CASTING CO Ltd
Priority to CN202011070597.9A priority Critical patent/CN112094129A/zh
Publication of CN112094129A publication Critical patent/CN112094129A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高温粘结剂及其制备方法，分别取液料铝溶胶、水玻璃、硅溶胶、纤维素、三氧化二铝微粉、二氧化硅微粉、特级铝矾土、黏土：液料混制比例为1:1；骨料中的三氧化二铝微粉、二氧化硅微粉、特级铝矾土、黏土混制比例为5:1:0.5:1~5；全液料加入10%~80%的三氧化二铝微粉；液料占骨料的百分含量为3%~15%；将液料搅拌均匀，通过球磨机将骨料充分混碾，然后将液料和骨料混合；高温粘结剂先后形成‑Si‑O‑Si‑网格结构，无定形二氧化硅转变为α‑鳞石英，在高温1200℃~1500℃时进行二次莫来石化反应，在1500℃以上具有高温强度。本发明方法能生产出在高温条件下具有较高强度的粘结剂。

Description

高温粘结剂及其制备方法
技术领域
本发明属于冶金行业，特别涉及一种生产用的高温粘结剂及其制备方法。
背景技术
冶金行业生产用的绝大部分粘结剂需要在高温环境下使用，且在高温条件下应具有相当的高温强度。目前冶金行业生产用的高温粘结剂大多采用日本进口产品，其价格高，交货周期长，当生产中急需增加粘结剂用量而得不到货物时，或者出现贸易不稳定因素时，会影响到生产的正常运行。
有鉴于此，该领域技术人员致力于研发一种高温粘结剂，以满足冶金行业生产厂的生产需要。
发明内容
本发明的任务是提供一种高温粘结剂及其制备方法，能生产出在高温条件下具有较高强度的粘结剂，该粘结剂为无机类粘结剂，尤其是硅酸盐类胶粘剂，具有相当的高温强度，能够在高温环境下使用。
本发明的技术解决方案如下：
一种高温粘结剂及其制备方法，分别取液料铝溶胶、水玻璃、硅溶胶、纤维素、三氧化二铝（Al2O3）微粉、二氧化硅（SiO2）微粉、特级铝矾土、黏土：
其中液料混制比例为1:1；
其中骨料中的三氧化二铝（Al2O3）微粉、二氧化硅（SiO2）微粉、特级铝矾土、黏土混制比例为5:1:0.5:1~5；
全液料加入10%~80%的三氧化二铝（Al2O3）微粉；
液料占骨料的百分含量为3%~15%；
将液料搅拌均匀，通过球磨机将骨料充分混碾，然后将液料和骨料混合；
高温粘结剂先后形成-Si-O-Si-网格结构，无定形二氧化硅（SiO2）转变为α-鳞石英，在高温1200℃~1500℃时进行二次莫来石化反应，在1500℃以上具有高温强度。
水玻璃模数为1.8~3.5。
硅溶胶中的二氧化硅（SiO2）含量为15%~30%。
三氧化二铝（Al2O3）微粉目数为100~1000目。
二氧化硅（SiO2）微粉目数为80~2000目。
由于冶金行业生产用的绝大部分粘结剂需要在高温环境下使用，且在高温条件下应具有相当的高温强度，因此需要使用无机类粘结剂。磷酸盐类和硅酸盐类胶粘剂是反应固化型胶粘剂中最为主要的两大系列。由于磷酸盐类胶粘剂质地太脆，使用温度一般不宜高于900℃，因而在实际生产中广泛应用的是硅酸盐类胶粘剂。
按本发明的制备方法生产出的高温粘结剂是硅酸盐类胶粘剂，具有较高的高温强度，能够在高温环境下使用，且具有较好的经济价值，满足冶金行业生产厂的生产需要。
具体实施方式
下面结合实施例对本发明作详细说明。
本发明提供一种高温粘结剂及其制备方法，制备时分别取液料铝溶胶、水玻璃、硅溶胶、纤维素、三氧化二铝（Al2O3）微粉、二氧化硅（SiO2）微粉、特级铝矾土、黏土。其中纤维素可以是一种纤维素，也可以是若干种纤维素组合。水玻璃模数为1.8~3.5。硅溶胶中的二氧化硅（SiO2）含量为15%~30%。三氧化二铝（Al2O3）微粉目数为100~1000目。二氧化硅（SiO2）微粉目数为80~2000目。
原料中的液料混制比例为1:1。
原料中的骨料包含三氧化二铝（Al2O3）微粉、二氧化硅（SiO2）微粉、特级铝矾土、黏土，这四种原料的混制比例为5:1:0.5:1~5。
在全液料中加入10%~80%的三氧化二铝（Al2O3）微粉。
液料占骨料的百分含量为3%~15%。
制备时将液料搅拌均匀，通过球磨机将骨料充分混碾，然后将液料和骨料混合。
高温粘结剂先后形成-Si-O-Si-网格结构，无定形二氧化硅（SiO2）转变为α-鳞石英，在高温1200℃~1500℃时进行二次莫来石化反应，在1500℃以上具有高温强度。
本发明的高温粘结剂的原料配比根据生产厂的不同工况可以有所不同。
综上所述，按本发明的高温粘结剂及其制备方法，能生产出在高温条件下具有较高强度的粘结剂，该粘结剂是硅酸盐类胶粘剂，具有相当的高温强度，能够在高温环境下使用，且具有较好的经济价值，满足冶金行业生产厂的生产需要。
当然，本技术领域内的一般技术人员应当认识到，上述实施例仅是用来说明本发明，而并非用作对本发明的限定，只要在本发明的实质精神范围内，对上述实施例的变化、变型等都将落在本发明权利要求的范围内。

Claims (5)

1.一种高温粘结剂及其制备方法，其特征在于：分别取液料铝溶胶、水玻璃、硅溶胶、纤维素、三氧化二铝（Al2O3）微粉、二氧化硅（SiO2）微粉、特级铝矾土、黏土：
其中液料混制比例为1:1；
其中骨料中的三氧化二铝（Al2O3）微粉、二氧化硅（SiO2）微粉、特级铝矾土、黏土混制比例为5:1:0.5:1~5；
全液料加入10%~80%的三氧化二铝（Al2O3）微粉；
液料占骨料的百分含量为3%~15%；
将液料搅拌均匀，通过球磨机将骨料充分混碾，然后将液料和骨料混合；
高温粘结剂先后形成-Si-O-Si-网格结构，无定形二氧化硅（SiO2）转变为α-鳞石英，在高温1200℃~1500℃时进行二次莫来石化反应，在1500℃以上具有高温强度。
2.按权利要求1所述的高温粘结剂及其制备方法，其特征在于：水玻璃模数为1.8~3.5。
3.按权利要求1所述的高温粘结剂及其制备方法，其特征在于：硅溶胶中的二氧化硅（SiO2）含量为15%~30%。
4.按权利要求1所述的高温粘结剂及其制备方法，其特征在于：三氧化二铝（Al2O3）微粉目数为100~1000目。
5.按权利要求1所述的高温粘结剂及其制备方法，其特征在于：二氧化硅（SiO2）微粉目数为80~2000目。
CN202011070597.9A 2020-10-10 2020-10-10 高温粘结剂及其制备方法 Pending CN112094129A (zh)