CN111957741A - 户外运动鞋底料的生产方法 - Google Patents

户外运动鞋底料的生产方法 Download PDF

Info

Publication number
CN111957741A
CN111957741A CN202010772559.1A CN202010772559A CN111957741A CN 111957741 A CN111957741 A CN 111957741A CN 202010772559 A CN202010772559 A CN 202010772559A CN 111957741 A CN111957741 A CN 111957741A
Authority
CN
China
Prior art keywords
steel strip
straightening
withdrawal
rolling
sole material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010772559.1A
Other languages
English (en)
Inventor
余叙斌
汤福朋
赵宇
栾久成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUXI HUASHENG PRECISON MATERIAL CO Ltd
Original Assignee
WUXI HUASHENG PRECISON MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI HUASHENG PRECISON MATERIAL CO Ltd filed Critical WUXI HUASHENG PRECISON MATERIAL CO Ltd
Priority to CN202010772559.1A priority Critical patent/CN111957741A/zh
Publication of CN111957741A publication Critical patent/CN111957741A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高强韧性200系列不锈钢带的生产方式，具体是户外运动鞋底料的生产方法。它将201L1不锈钢坯料依次经过轧制、清洗、一次拉矫、去应力退火和二次拉矫制得户外运动鞋底料。采用该方法制得的户外运动鞋底料的稳定性较好，不易生锈，产品疲劳寿命较高。

Description

户外运动鞋底料的生产方法
技术领域
本发明涉及一种高强韧性200系列不锈钢带的生产方式，具体是户外运动鞋底料的生产方法。
背景技术
目前，户外运动鞋底料均是由40Mn冷轧钢经淬回火工艺制得的。淬回火工艺在制备过程中为了成品达到HRC43-47（保证鞋底料既有一定的强度又有韧性），必须严格控制淬火硬度以及回火温度的均匀性，然而，这在实际生产过程中很难控制，会出现成品韧性充足（疲劳次数超过50万次）但防穿刺能力不足或防穿刺能力足够但韧性不足的问题，产品品质的稳定性较差。同时，40Mn材质冷轧钢非不锈钢，耐腐蚀能力较差，野外容易生锈。而且，40Mn材质冷轧钢本身的疲劳寿命较低，导致制得的产品疲劳寿命也较低。
发明内容
本发明要解决的技术问题是提供一种户外运动鞋底料的生产方法，采用该方法制得的户外运动鞋底料的稳定性较好，不易生锈，产品疲劳寿命较高。
为解决上述问题，提供以下技术方案：
本发明的户外运动鞋底料的生产方法的特点是包括如下步骤：
第一步，选材
选取201L1不锈钢坯料作为原材料，待用。
第二步，轧制
采用轧机，经过2~3道次的轧制，将原材料轧制成厚度为0.48~0.52mm的半成品钢带。
第三步，清洗
将轧制后的半成品钢带以80~100m/min的速度通过脱脂清洗机组，脱除轧制时残留在半成品钢带表面的轧制油。
第四步，一次拉矫
采用拉矫机对清洗后的钢带进行板型矫正，板型矫正过程中钢带的硬度控制在HV400~450。
第五步，去应力退火
在500~600℃下，对一次拉矫后的钢带进行高温去应力退火。
第六步，二次拉矫
采用拉矫机对去应力退火后的钢带进行反拉矫以矫正钢带的C型翘曲，即可得到户外运动鞋底料。
其中，所述一次拉矫步骤中使用的拉矫机为二十三辊拉矫机。
采取以上方案，具有以下优点：
由于本发明将201L1不锈钢坯料依次经过轧制、清洗、一次拉矫、去应力退火和二次拉矫制得户外运动鞋底料。这种户外运动鞋底料在制备过程中无需经过淬回火工艺，从而不会出现成品韧性充足（但防穿刺能力不足或防穿刺能力足够但韧性不足的问题，成品的稳定性较好。同时，201L1材料的材质为不锈钢，耐腐蚀能力较好，在野外不易腐蚀。而且，201L1不锈钢本身的疲劳寿命较高，制得的产品在同等条件下比背景技术中户外运动鞋底料的疲劳寿命提高了5倍以上，疲劳寿命较高。
具体实施方式
以下对本发明做进一步详细说明。
实施例1
本发明的户外运动鞋底料的生产方法包括如下步骤：
第一步，选材
选取北海诚德公司的201L1不锈钢坯料作为原材料，待用。
第二步，轧制
采用轧机，经过2道次的轧制，将原材料轧制成厚度为0.48mm的半成品钢带。
第三步，清洗
将轧制后的半成品钢带以80m/min的速度通过脱脂清洗机组，脱除轧制时残留在半成品钢带表面的轧制油。
第四步，一次拉矫
采用二十三辊拉矫机对清洗后的钢带进行板型矫正，板型矫正过程中钢带的硬度控制在HV400。
第五步，去应力退火
在500℃，对一次拉矫后的钢带进行高温去应力退火。
第六步，二次拉矫
采用拉矫机对去应力退火后的钢带进行反拉矫以矫正钢带的C型翘曲，即可得到户外运动鞋底料。
实施例2
本发明的户外运动鞋底料的生产方法的特点是包括如下步骤：
第一步，选材
选取北海诚德公司的201L1不锈钢坯料作为原材料，待用。
第二步，轧制
采用轧机，经过3道次的轧制，将原材料轧制成厚度为0.52mm的半成品钢带。
第三步，清洗
将轧制后的半成品钢带以100m/min的速度通过脱脂清洗机组，脱除轧制时残留在半成品钢带表面的轧制油。
第四步，一次拉矫
采用二十三辊拉矫机对清洗后的钢带进行板型矫正，板型矫正过程中钢带的硬度控制在HV450。
第五步，去应力退火
在600℃，对一次拉矫后的钢带进行高温去应力退火。
第六步，二次拉矫
采用拉矫机对去应力退火后的钢带进行反拉矫以矫正钢带的C型翘曲，即可得到户外运动鞋底料。

Claims (2)

1.户外运动鞋底料的生产方法，其特征在于包括如下步骤：
第一步，选材
选取201L1不锈钢坯料作为原材料，待用；
第二步，轧制
采用轧机，经过2~3道次的轧制，将原材料轧制成厚度为0.48~0.52mm的半成品钢带；
第三步，清洗
将轧制后的半成品钢带以80~100m/min的速度通过脱脂清洗机组，脱除轧制时残留在半成品钢带表面的轧制油；
第四步，一次拉矫
采用拉矫机对清洗后的钢带进行板型矫正，板型矫正过程中钢带的硬度控制在HV400~450；
第五步，去应力退火
在500~600℃下，对一次拉矫后的钢带进行高温去应力退火；
第六步，二次拉矫
采用拉矫机对去应力退火后的钢带进行反拉矫以矫正钢带的C型翘曲，即可得到户外运动鞋底料。
2.如权利要求1所述的户外运动鞋底料的生产方法，其特征在于所述一次拉矫步骤中使用的拉矫机为二十三辊拉矫机。
CN202010772559.1A 2020-08-07 2020-08-07 户外运动鞋底料的生产方法 Pending CN111957741A (zh)