CN113210423B - 一种殷瓦合金热轧钢卷的制造方法 - Google Patents
一种殷瓦合金热轧钢卷的制造方法 Download PDFInfo
- Publication number
- CN113210423B CN113210423B CN202110430111.6A CN202110430111A CN113210423B CN 113210423 B CN113210423 B CN 113210423B CN 202110430111 A CN202110430111 A CN 202110430111A CN 113210423 B CN113210423 B CN 113210423B
- Authority
- CN
- China
- Prior art keywords
- temperature
- rolling
- percent
- hot
- equal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种殷瓦合金热轧钢卷的制造方法，钢卷的生产工艺为：钢坯修磨→加热炉加热→热轧→酸洗；通过对加热炉升温曲线和轧制工艺的控制，降低因钢卷表面裂纹问题导致的一系列品质及成本问题，形成一套特定的殷瓦合金热轧钢卷的生产工艺。采用本发明的加热炉升温曲线和轧制工艺，钢卷表面无裂纹缺陷。
Description
技术领域
本发明属于钢铁材料制备领域；尤其涉及一种殷瓦合金热轧钢卷的制造方法。
背景技术
殷瓦合金4J36为低膨胀合金钢，加热升温过程容易因膨胀系数低、坯料不同部位膨胀不一致产生内应力而产生裂纹，轧制困难。因此，热轧加热炉采用特殊的升温曲线，避免坯料裂纹风险，解决了殷瓦合金4J36加热和轧制难题。
申请号为201310347452.2的专利文件，公开了“一种镍基合金Ni36板的加热和轧制方法”，其采用的升温模式为：先电炉加热后再在煤气加热炉加热，其采用的是两种设备加热，此方法导致坯料需要多次调运，生产工序不够顺畅，影响生产节奏。
发明内容
本发明提供了一种殷瓦合金热轧钢卷的制造方法，通过对加热炉升温曲线和轧制工艺的控制，降低因钢卷表面裂纹问题导致的一系列品质及成本问题，形成一套特定的殷瓦合金热轧钢卷的生产工艺。
为实现上述目的，本发明采用以下技术方案实现：
一种殷瓦合金热轧钢卷的制造方法，所述钢卷的生产工艺为：钢坯修磨→加热炉加热→热轧→酸洗；具体方法包括：
1)加热炉加热：加热炉为法国斯坦因步进梁式加热炉，加热炉采用特殊的升温曲线，利用加热炉息炉定修完再准备点火生产时机，在预热段缓慢升温，升温速率≤40℃/h，并在200±50℃温度时恒温5±1小时，以及600±50℃时恒温8±1小时，当钢坯温度超过850±20℃后，快速升温，升温速率80～150℃/h，直至温度升至出炉温度1140±20℃，相关温度数据都来自于加热炉钢坯温度管控模型数据；
2)热轧工艺：热轧出炉温度1140±20℃，高压水除锈速度1.0～1.5m/s，除锈压力16～20Mpa，热轧粗轧采用5或7道次轧延，中间坯厚度30～40mm，精轧采用7连轧，最后轧制成目标厚度，终轧温度≥900℃；
3)酸洗工艺：利用酸洗工艺将热轧黑皮卷锈皮去除，生产成白皮钢卷。
所述钢卷化学成分按重量百分比计为：C≤0.05％，Si≤0.3％，Mn 0.2％～0.6％，P≤0.02％，Ni 35.0％～37.0％，S含量管控在10ppm以内，余量为Fe和不可避免杂质元素。
成品卷厚度为：3.0～10.0mm。
与现有的技术相比，本发明的有益效果是：
一种殷瓦合金热轧钢卷的制造方法，通过对加热炉升温曲线和轧制工艺的控制，降低因钢卷表面裂纹问题导致的一系列品质及成本问题，形成一套特定的殷瓦合金热轧钢卷的生产工艺。
采用本发明的加热炉升温曲线和轧制工艺，钢卷表面无裂纹缺陷。
附图说明
图1为本发明的加热炉升温曲线。
图2为本发明实施例1成品钢卷表面图像。
具体实施方式
下面结合实施例对本发明方案做进一步详细描述，下述说明仅是为了解释本发明，并不对其内容进行限定。
实施例钢卷化学成分见表1；实施例加热轧制工艺见表2；实施例结果见表3。
表1：实施案例的化学成分(wt％)
| C | Si | Mn | P | S | Ni |
| 0.011 | 0.29 | 0.35 | 0.005 | 0.0004 | 35.87 |
表2：本发明实施案例的轧制工艺
酸洗：将热轧黑皮卷酸洗成白皮卷，去除表面锈皮。
表3：本实施案例的结果
| 实施例 | 试验结果(表面裂纹) |
| 1 | 无 |
| 2 | 无 |
由表1～3及图2可见，采用本发明技术方案生产的殷瓦合金钢卷表面质量良好，表面无裂纹缺陷。
Claims (3)
1.一种殷瓦合金热轧钢卷的制造方法，所述钢卷的生产工艺为：钢坯修磨→加热炉加热→热轧→酸洗；其特征在于，具体方法包括：
1)加热炉加热：利用加热炉息炉定修完再准备点火生产时机，在预热段缓慢升温，升温速率≤40℃/h，并在200±50℃温度时恒温5±1小时，以及600±50℃时恒温8±1小时，当钢坯温度超过850±20℃后，快速升温，升温速率80～150℃/h，直至温度升至出炉温度1140±20℃；
2)热轧工艺：热轧出炉温度1140±20℃，高压水除锈速度1.0～1.5m/s，除锈压力16～20Mpa，热轧粗轧采用5或7道次轧延，中间坯厚度30～40mm，精轧采用7连轧，最后轧制成目标厚度，终轧温度≥900℃；
3)酸洗工艺：利用酸洗工艺将热轧黑皮卷锈皮去除，生产成白皮钢卷。
2.根据权利要求1所述的一种殷瓦合金热轧钢卷的制造方法，其特征在于，所述钢卷化学成分按重量百分比计为：C≤0.05％，Si≤0.3％，Mn 0.2％～0.6％，P≤0.02％，S≤0.02％，Ni 35.0％～37.0％，余量为Fe和不可避免杂质元素。
3.根据权利要求1所述的一种殷瓦合金热轧钢卷的制造方法，其特征在于，成品卷厚度为：3.0～10.0mm。