CN111923274A - 一种透明pet材料的注塑工艺 - Google Patents
一种透明pet材料的注塑工艺 Download PDFInfo
- Publication number
- CN111923274A CN111923274A CN202010815974.0A CN202010815974A CN111923274A CN 111923274 A CN111923274 A CN 111923274A CN 202010815974 A CN202010815974 A CN 202010815974A CN 111923274 A CN111923274 A CN 111923274A
- Authority
- CN
- China
- Prior art keywords
- injection molding
- parts
- pet material
- transparent pet
- injection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种透明PET材料的注塑工艺，对透明PET材料进行除湿处理，然后将除湿处理后的透明PET材料闭环输送至注塑机，通过注塑机对透明PET材料进行注塑成型，注塑成型完成后，通过机械手将注塑机上的注塑产品取下。本发明透明PET材料的注塑工艺，其可缩短成型周期，降低报废率。
Description
技术领域
本发明涉及一种透明PET材料的注塑工艺。
背景技术
PET里面有聚对苯二甲酸乙二醇酯，是热塑性聚酯中最主要的品种，英文名为Polyethylene terephthalate，简称PET，俗称涤纶树脂。它是对苯二甲酸与乙二醇的缩聚物，与PBT一起统称为热塑性聚酯，或饱和聚酯。
PET材料在市场上可以进行可回收处理，但透明PET注塑一直是行业内的难点，成型工艺的窗口相对很小，成型周期长，且报废率高。
发明内容
本发明的目的在于提供一种透明PET材料的注塑工艺，其可缩短成型周期，降低报废率。
为实现上述目的，本发明的技术方案是设计一种透明PET材料的注塑工艺，对透明PET材料进行除湿处理，然后将除湿处理后的透明PET材料闭环输送至注塑机，通过注塑机对透明PET材料进行注塑成型，注塑成型完成后，通过机械手将注塑机上的注塑产品取下。
优选的，利用除湿干燥机对透明PET材料进行除湿处理。
优选的，除湿处理的工艺参数包括：除湿温度为150～155℃，除湿时间为4小时。
优选的，注塑成型的工艺参数包括：注塑速度为3～150mm/s，保压压力是注塑压力的70%，注塑时间控制在10s以内，成型温度在260℃，模温50℃。
优选的，在注塑机的注塑模具中设置冷却水路。
优选的，按重量份计，透明PET材料由以下组分组成：
32.6份PET树脂，
5.7份2,2′-亚基甲-二(4,6-二正丁基苯酚)磷酸钠，
8.4份乙烯基三甲氧基硅烷，
1.2份正丁基萘磺酸钠，
2.5份三聚磷酸钠，
1.7份过氧化苯甲酰，
2.6份2-膦酸基丁烷-1,2,4-三羧酸，
3.4份氟硅酸钠，
6.5份甲醇聚氧乙烯醚磷酸酯，
3.3份二丁基羟基甲苯，
1.9份4-(2-壬酰氧基乙氧基羰基氧基)苯磺酸钠。
本发明的优点和有益效果在于：提供一种透明PET材料的注塑工艺，其可缩短成型周期，降低报废率。
本发明能保证在除湿干燥机与注塑机之间的材料输送为闭环热输送。
本发明对于注塑的速度、压力、温度等进行优化控制，可缩短成型周期，降低报废率。
本发明注塑速度可根据注塑产品的厚薄壁来切换快慢，可从慢到快变换。
本发明在注塑模具中设置冷却水路，冷却效果好，可使注塑工艺更稳定。
本发明透明PET材料具有特别优化的配方，透明PET材料的透光率接近玻璃，仅次于PETG。
本发明透明PET材料还具有优异的抗氧化性能和抗紫外性能。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
本发明提供一种透明PET材料的注塑工艺，对透明PET材料进行除湿处理，然后将除湿处理后的透明PET材料闭环输送至注塑机，通过注塑机对透明PET材料进行注塑成型，注塑成型完成后，通过机械手将注塑机上的注塑产品取下。
具体地的，利用除湿干燥机对透明PET材料进行除湿处理。
具体地的，除湿处理的工艺参数包括：除湿温度为150～155℃，除湿时间为4小时。
具体地的，注塑成型的工艺参数包括：注塑速度为3～150mm/s，保压压力是注塑压力的70%，注塑时间控制在10s以内，成型温度在260℃，模温50℃。
具体地的，在注塑机的注塑模具中设置冷却水路。
具体地的，按重量份计，透明PET材料由以下组分组成：
32.6份PET树脂，
5.7份2,2′-亚基甲-二(4,6-二正丁基苯酚)磷酸钠，
8.4份乙烯基三甲氧基硅烷，
1.2份正丁基萘磺酸钠，
2.5份三聚磷酸钠，
1.7份过氧化苯甲酰，
2.6份2-膦酸基丁烷-1,2,4-三羧酸，
3.4份氟硅酸钠，
6.5份甲醇聚氧乙烯醚磷酸酯，
3.3份二丁基羟基甲苯，
1.9份4-(2-壬酰氧基乙氧基羰基氧基)苯磺酸钠。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (6)
1.一种透明PET材料的注塑工艺，其特征在于，对透明PET材料进行除湿处理，然后将除湿处理后的透明PET材料闭环输送至注塑机，通过注塑机对透明PET材料进行注塑成型，注塑成型完成后，通过机械手将注塑机上的注塑产品取下。
2.根据权利要求1所述的透明PET材料的注塑工艺，其特征在于，利用除湿干燥机对透明PET材料进行除湿处理。
3.根据权利要求2所述的透明PET材料的注塑工艺，其特征在于，除湿处理的工艺参数包括：除湿温度为150～155℃，除湿时间为4小时。
4.根据权利要求3所述的透明PET材料的注塑工艺，其特征在于，注塑成型的工艺参数包括：注塑速度为3～150mm/s，保压压力是注塑压力的70%，注塑时间控制在10s以内，成型温度在260℃，模温50℃。
5.根据权利要求4所述的透明PET材料的注塑工艺，其特征在于，在注塑机的注塑模具中设置冷却水路。
6.根据权利要求5所述的透明PET材料的注塑工艺，其特征在于，按重量份计，透明PET材料由以下组分组成：
32.6份PET树脂，
5.7份2,2′-亚基甲-二(4,6-二正丁基苯酚)磷酸钠，
8.4份乙烯基三甲氧基硅烷，
1.2份正丁基萘磺酸钠，
2.5份三聚磷酸钠，
1.7份过氧化苯甲酰，
2.6份2-膦酸基丁烷-1,2,4-三羧酸，
3.4份氟硅酸钠，
6.5份甲醇聚氧乙烯醚磷酸酯，
3.3份二丁基羟基甲苯，
1.9份4-(2-壬酰氧基乙氧基羰基氧基)苯磺酸钠。