CN1119144A - Method for forming pattern incised board by composite mould pressing of wood and chemical material and producing method - Google Patents
Method for forming pattern incised board by composite mould pressing of wood and chemical material and producing method Download PDFInfo
- Publication number
- CN1119144A CN1119144A CN 94116332 CN94116332A CN1119144A CN 1119144 A CN1119144 A CN 1119144A CN 94116332 CN94116332 CN 94116332 CN 94116332 A CN94116332 A CN 94116332A CN 1119144 A CN1119144 A CN 1119144A
- Authority
- CN
- China
- Prior art keywords
- industrial chemicals
- chloride solution
- mould
- magnesium chloride
- magnesia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The novel board with shallow relief pattern on its surface uses wooden board as substrate, glass fibre cloth as skeleton material, and magnesium oxide, gypsum powder, magnesium chloride solution and saw dust as surficial shaping and compounding material, and features better high temp., ageing and acid-alkali corrosion resistances, superior hardness, toughness and antiwear level, and moderate price.
Description
The invention belongs to ornament materials and production technology, relate generally to the carving plate and the production method of a kind of timber chemical industry composite coining moulding.
Along with the raising of expanding economy and living standards of the people, building industry, home dwelling decoration and furniture especially to fine quality, tend to nature to the requirement trend variation of ornament materials, and moderate ornament materials demand is increasing; The decorative panel of existing wood surface carving is admittedly for people like, but it is owing to be difficult for suitability for industrialized production thereby the cost cost is higher, and the requirement of incompatibility construction material fire protection flame retarding.
Purpose of the present invention promptly is to propose composite and carved plate of a kind of timber industrial chemicals and production method, and it be the moulding of timber industrial chemicals composite coining, and it is luxurious to make it both have an incrustation, and attractive in appearance have the comparatively cheap characteristics with fire protection flame retarding of price again.
The technical scheme that the present invention takes is: it is to be the substrate material with the wood-based planet, with glass fibre as framework material, as surface forming material and compound material, the surface that is composited has the board of basse-taille with magnesia, land plaster, magnesium chloride solution and sawdust.
The colored groove material of plate surface basse-taille pattern of the present invention may be selected to be; Magnesia, land plaster, magnesium chloride solution, sawdust;
The superficial layer molding mass may be selected to be: sawdust, magnesia, magnesium chloride solution;
The compound material of compound employing is between underboarding and the surperficial chemical industry stock chart layer: magnesia, magnesium chloride solution;
Between surface carving groove in low relief material and superficial layer molding mass in addition glass fabric as framework material;
Described wooden boards substrate material can be plank, glued board or fiber moulded board etc.
The production method of basse-taille composite plate of the present invention:
1, handles mould with releasing agent or machine oil;
2, will spend the groove material to pour mould in order in the pattern groove that forms surperficial basse-taille pattern, material is flat with groove;
3, expand glass fabric as framework material;
4, upper surface layer molding mass;
5, compound material on underboarding and in the mould; The two combination also compresses or uses the clip clamping.
The mould that the present invention adopts can be the mould that woodcut, cement making or industrial chemicals are made, and it is to go to the bottom to have pattern groove and the last template groove for the formation superficial layer that forms surperficial basse-taille pattern flower type.
Basse-taille composite plate of the present invention has following characteristics;
1, luxurious, the beautiful and intelligent of outward appearance, high temperature resistant, ageing-resistant, waterproof fireproofing, acid-alkali-corrosive-resisting, its hardness, suppleness, abrasion resistance all are better than wood-based planet.
2, specification variation can make the product of different size, different designs according to different needs.
3, easy to use, with the same usage of wood-based planet.
4, cost is moderate, and industrial chemicals is easily got and be cheap, and cost is significantly less than import carving plate and homemade wooden carving plate thus.
5, of many uses, be applicable to the finishing decoration, external door pasting board, furniture making, technology embossment, mural painting etc. in doing.
The embodiment of the invention:
As the substrate material, as framework material, the colored groove material of surperficial basse-taille pattern flower type is: magnesia, land plaster, magnesium chloride solution, sawdust with glass fabric with wooden glued board; Usage ratio is: magnesia: land plaster: magnesium chloride solution: sawdust=6: 1: 7: 0.1; The superficial layer molding mass is; Sawdust, magnesia, magnesium chloride solution; Usage ratio is: sawdust: magnesia: magnesium chloride solution=1: 7: 8, and the compound material of substrate material and superficial layer is magnesia, magnesium chloride solution; Usage ratio is a magnesia: magnesium chloride solution=5: 1 more than is weight ratio.
Make forming method:
1, releasing agent or machine oil are wiped on mould, cleared up with sponge.
2, will spend the groove material to be poured in the mould flower groove, and make material and groove flat.
3, glass fabric is layered in the mould, makes non-wrinkle.
4, upper surface layer molding mass.
5, compound material in mould and on the underboarding simultaneously, the two is compound.
6, use special clamp.
7, taking-up is existing after 6～18 hours.
Mould of the present invention is made:
1, makes workbench, flat surfaced;
2, adopt common carving plate to make original mould, be fixed on the workbench.
3, fixing batten around the original mould of workbench, make batten and original mould all around apart from being 2.5～3cm.
4, clean cleaning original mould surface and batten with machine oil.
The colored groove material that 5, will prepare is poured on the original mould, and vibration template makes colored groove material consistency of thickness, and bubble is discharged.
6, the glass fabric that shears is layered on the flower material, makes non-wrinkle.
7, filler is poured on the fiber cloth, floating.
8, go up second layer fiber cloth, add 8# or 3.5mm dish circle and make skeleton.
9, mulch is poured on the fiber cloth, pushes down the dish circle, polish with thick film.
10, take out mould after 8～10 hours,, can use after the Exposure to Sunlight through maintenance.
When using, can be processed into different colours according to different needs as ornament materials, as spray paint, plastic-blasting, veneer etc.
The mould batching:
Flower groove material; Magnesia 5: land plaster 1: magnesium chloride solution 6 (furnishing pasty state)
Filler: sawdust 2: land plaster 2: magnesia 6: magnesium chloride solution 9 (furnishing pasty state)
Mulch is identical with flower groove material, rare slightly getting final product.
Claims (6)
1, a kind of timber industrial chemicals composite coining moulding carving plate is characterized in that; With wood-based planet as the substrate material, with glass fabric as framework material, be composited with magnesia, land plaster, magnesium chloride solution and sawdust superficial layer with basse-taille pattern flower type as composition material.
2, timber industrial chemicals composite coining moulding carving plate according to claim 1 is characterized in that: the colored groove material of surperficial basse-taille pattern flower type is: magnesia, land plaster, magnesium chloride solution, sawdust.
3, timber industrial chemicals composite coining moulding carving plate according to claim 1, it is characterized in that: the superficial layer molding mass is: sawdust, magnesia, magnesium chloride solution.
4, timber industrial chemicals composite coining moulding carving plate according to claim 1 is characterized in that; The compound material that adopts between superficial layer and the substrate material can be magnesia, magnesium chloride solution.
5, a kind of production method of timber industrial chemicals composite coining moulding carving plate, it is characterized in that: will spend the groove material to pour in the colored groove of mould bottom in order to the moulding of surperficial basse-taille pattern flower type earlier after mould is handled with releasing agent or machine oil, lining shop glass fabric is as framework material, upper surface layer molding mass and in mould goes up on the underboarding that compound material is compound to be made.
6, the production method of timber industrial chemicals composite coining moulding carving plate according to claim 5 is characterized in that: mould is to go to the bottom to have pattern groove and the last template groove for the formation superficial layer that forms surperficial basse-taille pattern flower type.