CN105904908A - Processing method for decorative bamboo plate charcoal drawing - Google Patents
Processing method for decorative bamboo plate charcoal drawing Download PDFInfo
- Publication number
- CN105904908A CN105904908A CN201610294999.4A CN201610294999A CN105904908A CN 105904908 A CN105904908 A CN 105904908A CN 201610294999 A CN201610294999 A CN 201610294999A CN 105904908 A CN105904908 A CN 105904908A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- bamboo clappers
- monolayer
- plasterboard
- processing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a processing method for a decorative bamboo plate charcoal drawing. The processing method comprises the following steps of firstly, preparing single-layer bamboo plates by utilizing moso bamboos; secondarily, punching holes for a needed pattern in a purchased gypsum plate by using a punching machine, blending asbestos gypsum mud, coating on panels of the single-layer bamboo plates, compounding the single-layer bamboo plates with the gypsum plate, totally removing the gypsum mud which is punched out of the hole parts from the gypsum plate by using a probe or a bamboo stick, exposing the inside single-layer bamboo plate material, arranging the two single-layer bamboo plates with the asbestos gypsum mud totally removed from the holes back to back, sending the combined single-layer bamboo plates into a wood drying kiln to carry out carbonization treatment, and forming basic charcoal drawing pattern contours on the surfaces of the single-layer bamboo plates; and finally, colorizing by using color pens with combination of the concrete condition of the pattern so as to improve the authenticity of the pattern, and preparing the intact decorative bamboo plate charcoal drawing. According to the processing method, the processing technology is simple and feasible, the prepared decorative bamboo plate charcoal drawing is high-end, generous and high-grade, the needs of multiple places including common families, hotels, restaurants, stations and markets for decoration can be met, and the processing method has very high economic value.
Description
Technical field
The invention belongs to bamboo processing field, the processing method being specifically related to a kind of ornamental bamboo clappers charcoal drawing.
Background technology
Decoration painting is a kind of not emphasize the highest artistry, but is particular about very much the special art type works of the coordination with environment and landscaping effect.Its origin can chase after tide to the ornamental grain pattern with Neolithic Age faience, such as animal stricture of vagina, people's stricture of vagina, geometry stricture of vagina, is all the figure refined through exaggerated deformation, height.It is generally divided into tool as subject matter, image subject matter, flowers subject matter, personal portrait subject matter, abstract subject matter and comprehensive subject matter etc..It meets modern trend, is pursued by vast white collar and Zhong Chan consumer, becomes the needs of many places such as average family, hotel, restaurant, station, market decoration, and the market demand is huge.
The present invention utilizes resourceful Phyllostachys pubescens Mazei ex H.de Lebaie, first make monolayer bamboo clappers, then in this, as charcoal drawing base material, process through special process, produce the charcoal drawing product of uniqueness, disclosure satisfy that the needs of many places such as average family, hotel, restaurant, station, market decoration, there is the highest economic worth, therefore there is vast potential for future development.
Summary of the invention
The processing method that it is an object of the invention to provide a kind of ornamental bamboo clappers charcoal drawing.The method utilizes resourceful Phyllostachys pubescens Mazei ex H.de Lebaie, first make monolayer bamboo clappers as charcoal drawing base material, process through special process, produce the charcoal drawing product of uniqueness, disclosure satisfy that the needs of many places such as average family, hotel, restaurant, station, market decoration, there is the highest economic worth, therefore there is vast potential for future development.
In order to realize foregoing invention purpose, the present invention adopts the following technical scheme that
The processing method of a kind of ornamental bamboo clappers charcoal drawing, the method comprises the steps:
Step 1: the Phyllostachys pubescens Mazei ex H.de Lebaie that fresh felling comes is cut into the bamboo section of 2010mm length, cuts open into the circular arc bamboo chip of 25mm width by cuing open bamboo machine；
Step 2: circular arc bamboo chip is processed into specification force plane bamboo chip by bamboo chip force plane machine, sends into lumber kiln and is dried, and dried bamboo chip moisture control is at 8 below wt%；
Step 3: dry bamboo chip is sent into adjustable cast iron planes machine, makes specification adjustable cast iron planes bamboo chip, after artificial separation, standby；
Step 4: by the specification lateral gluing of adjustable cast iron planes bamboo chip after sorting, sends into hot press and makes monolayer bamboo clappers after assembly；
Step 5: the monolayer bamboo clappers after cooling is sent into edging saw, makes specification 2000mm × 1200mm × 6mm(length × width x thickness) monolayer bamboo clappers, then process through the two-sided sanding of sander, make the fixed thick monolayer bamboo clappers of 5mm, standby；
Step 6: outsourcing dimensions is 2000mm × 1200mm × 5mm(length × width x thickness) plasterboard, computer select popular pattern, go out pattern hole on gypsum with punch press；
Step 7: outsourcing asbestos wool product, in red soil powder: asbestos wool: the ratio of water quality ratio=60:40:60 pours blender furnishing cream mud into, is spread upon equably on the panel of monolayer bamboo clappers by cream mud with cement paint spatula, smears layer thickness and control at 3mm；
Step 8: after cream mud layer Stability Analysis of Structures floating on monolayer bamboo clappers, the plasterboard going out picture grass pattern hole is combined with the monolayer bamboo clappers smearing cream mud carefully, beat plasterboard with mallet gently, discharge the air in space between cream mud layer and plasterboard, make cream mud layer with plasterboard bonding closely；
Step 9: monolayer bamboo clappers and plasterboard surrounding clamped with iron clamp, be placed on horizontal table, the cream mud that plasterboard upper punch goes out hole position with probe or bamboo let is all rejected, and exposes the monolayer bamboo clappers material of inside；
Step 10: the monolayer bamboo clappers face back of the body back of the body of the composite plate that just two steps 9 prepare mutually by (punching plasterboard is the most outside), with iron clamp fixing after lift and carry out carbonization process into lumber kiln, be vertically placed on the shelf in lumber kiln；
Step 11: the temperature of lumber kiln rises to 185～215 DEG C, keeps 2～3 hours at such a temperature, completes the carbonization process of monolayer bamboo clappers；
Step 12: close lumber kiln heating system, sprays water-atomization cooling damping to monolayer bamboo clappers, controls the final moisture content of carbonization monolayer bamboo clappers 6～8wt%；
Step 13: taken out the monolayer bamboo clappers that carbonization processes, unclamps the iron clamp that surrounding is fixing, removes punching plasterboard and the asbestos cream mud of surface adhesion, and monolayer bamboo clappers surface open goes out the pattern contour of ornamental bamboo clappers charcoal drawing；
Step 14: the concrete condition coloured pencil combining pattern is painted to pattern, increases the verity of pattern, makes complete ornamental bamboo clappers charcoal drawing.
Dry bamboo chip feeding adjustable cast iron planes machine is made specification adjustable cast iron planes bamboo chip by described step 3, is to select solid colour through the purpose of artificial separation, do not have the adjustable cast iron planes bamboo chip of open defect (rotten, aberration, small holes caused by worms etc.) to use as the base material of ornamental bamboo clappers charcoal drawing.
In described step 6, outsourcing goes out pattern hole at plasterboard, the most penetrating in order to ensure the pattern hole that plasterboard is gone out, occur, before plasterboard punching without sticking and tear phenomenon, should be first in the two sides brushing polyvinyl alcohol glue of plasterboard, glue brushing amount is 150g/m2。
Utilizing punch press to go out the pattern designed on gypsum in described step 6 can be flowers, animal, landscape, character moulding etc..
Being mixed into asbestos wool refractory material in described step 7 in red soil powder and making the purpose that cream mash is put on the panel of monolayer bamboo clappers is to protect unexposed monolayer bamboo clappers in carbonization processing procedure, is allowed to form obvious aberration (charcoal drawing formation mechenism) with the monolayer bamboo clappers position that exposes in carbonization processing procedure.
Described step 8 has to wait for asbestos cream mud layer Stability Analysis of Structures (after having certain structural strength) floating on monolayer bamboo clappers, just can be combined with plasterboard, otherwise it may happen that the accident of conquassation asbestos cream mud layer.
For the air discharged between asbestos cream mud layer and plasterboard in space in described step 8, during beaing plasterboard with mallet, it should be noted that 2 points: first, plasterboard should be beaten gently, prevent conquassation asbestos cream mud layer；Second, it should be noted that mallet beat direction, select from left to right or from top to bottom beat direction, be conducive to discharging the air in space between asbestos cream mud layer and plasterboard, make asbestos cream mud layer with plasterboard bonding closely.
Plasterboard upper punch is gone out, with probe or bamboo let, the process that the asbestos cream mud at hole position all rejects by described step 9 should select to complete before the asbestos unseasoned solidification of cream mud.
Plasterboard upper punch is gone out, with probe or bamboo let, the mode that the monolayer bamboo clappers back of the body back of the body that the asbestos cream mud at hole position all rejects carries out carbonization process by feeding lumber kiln mutually by two by described step 10 most economical rationally; carry out carbonization in like fashion to process and the monolayer bamboo clappers back side can be protected not processed by carbonization affected, and labor efficiency is the highest.
In order to ensure that lumber kiln heats up and the accuracy of temperature control in described step 10, this lumber kiln heating system uses deep fat heat supply.
It is an advantage of the current invention that:
The present invention provides the processing method of a kind of ornamental bamboo clappers charcoal drawing；The method utilizes resourceful Phyllostachys pubescens Mazei ex H.de Lebaie, first make monolayer bamboo clappers as charcoal drawing base material, process through special process, produce the charcoal drawing product of uniqueness, disclosure satisfy that the needs of many places such as average family, hotel, restaurant, station, market decoration, there is the highest economic worth, therefore there is vast potential for future development.
Detailed description of the invention
For the openest rather than restriction present invention, below in conjunction with example, the present invention is described in further detail.
Embodiment
1
Concretely comprising the following steps of the processing method of a kind of ornamental bamboo clappers charcoal drawing:
Step 1: the Phyllostachys pubescens Mazei ex H.de Lebaie that fresh felling comes is cut into the bamboo section of 2010mm length, cuts open into the bamboo chip of 25mm width by cuing open bamboo machine；
Step 2: circular arc bamboo chip is processed into specification force plane bamboo chip by bamboo chip force plane machine, sends into lumber kiln and is dried, and dried bamboo chip moisture control is at 8 below wt%；
Step 3: dry bamboo chip is sent into adjustable cast iron planes machine, makes specification adjustable cast iron planes bamboo chip, after artificial separation, standby；
Step 4: by the specification lateral gluing of adjustable cast iron planes bamboo chip after sorting, sends into hot press and makes monolayer bamboo clappers after assembly；
Step 5: the monolayer bamboo clappers after cooling is sent into edging saw, makes specification 2000mm × 1200mm × 6mm(length × width x thickness) monolayer bamboo clappers, then process through the two-sided sanding of sander, make the fixed thick monolayer bamboo clappers of 5mm, standby；
Step 6: outsourcing dimensions is 2000mm × 1200mm × 5mm(length × width x thickness) plasterboard, computer select popular pattern, go out pattern hole on gypsum with punch press；
Step 7: outsourcing asbestos wool product, in red soil powder: asbestos wool: the ratio of water quality ratio=60:40:60 pours blender furnishing cream mud into, is spread upon equably on the panel of monolayer bamboo clappers by asbestos cream mud with cement paint spatula, smears layer thickness and control at 3mm;
Step 8: after asbestos cream mud layer Stability Analysis of Structures floating on monolayer bamboo clappers, the plasterboard going out picture grass pattern hole is combined with the monolayer bamboo clappers smearing asbestos cream mud carefully, plasterboard is beaten gently with mallet, discharge the air in space between asbestos cream mud layer and plasterboard, make asbestos cream mud layer with plasterboard bonding closely；
Step 9: monolayer bamboo clappers and plasterboard surrounding clamped with iron clamp, be placed on horizontal table, the cream mud that plasterboard upper punch goes out hole position with probe or bamboo let is all rejected, and exposes the monolayer bamboo clappers material of inside；
Step 10: the monolayer bamboo clappers back of the body back of the body completing step 9 by two leans on (punching plasterboard is the most outside) mutually, lifts and carries out carbonization process into lumber kiln, be vertically placed on the shelf in lumber kiln after fixing with iron clamp；
Step 11: the temperature of lumber kiln rises to 200 DEG C, keeps 2.5 hours at such a temperature, completes the carbonization process of monolayer bamboo clappers；
Step 12: close lumber kiln heating system, sprays water-atomization cooling damping to monolayer bamboo clappers, controls the final moisture content of carbonization monolayer bamboo clappers 6～8wt%；
Step 13: taken out the monolayer bamboo clappers that carbonization processes, unclamps the iron clamp that surrounding is fixing, removes punching plasterboard and the asbestos cream mud of surface adhesion, and monolayer bamboo clappers surface open goes out the pattern contour of ornamental bamboo clappers charcoal drawing；
Step 14: the concrete condition coloured pencil combining pattern is painted to pattern, increases the verity of pattern, makes complete ornamental bamboo clappers charcoal drawing.
The ornamental bamboo clappers charcoal drawing prepared by the present invention, there is feature simple to operate, easy to learn, the method utilizes resourceful Phyllostachys pubescens Mazei ex H.de Lebaie, first make monolayer bamboo clappers as charcoal drawing base material, process through special process, produce the charcoal drawing product of uniqueness, it is possible to meet the needs of many places such as average family, hotel, restaurant, station, market decoration, there is the highest economic worth, therefore there is vast potential for future development.
Embodiment 2
Concretely comprising the following steps of the processing method of a kind of ornamental bamboo clappers charcoal drawing:
Step 1: the Phyllostachys pubescens Mazei ex H.de Lebaie that fresh felling comes is cut into the bamboo section of 2010mm length, cuts open into the bamboo chip of 25mm width by cuing open bamboo machine；
Step 2: circular arc bamboo chip is processed into specification force plane bamboo chip by bamboo chip force plane machine, sends into lumber kiln and is dried, and dried bamboo chip moisture control is at 8 below wt%；
Step 3: dry bamboo chip is sent into adjustable cast iron planes machine, makes specification adjustable cast iron planes bamboo chip, after artificial separation, standby；
Step 4: by the specification lateral gluing of adjustable cast iron planes bamboo chip after sorting, sends into hot press and makes monolayer bamboo clappers after assembly；
Step 5: the monolayer bamboo clappers after cooling is sent into edging saw, makes specification 2000mm × 1200mm × 6mm(length × width x thickness) monolayer bamboo clappers, then process through the two-sided sanding of sander, make the fixed thick monolayer bamboo clappers of 5mm, standby；
Step 6: outsourcing dimensions is 2000mm × 1200mm × 5mm(length × width x thickness) plasterboard, computer select popular pattern, go out pattern hole on gypsum with punch press；
Step 7: outsourcing asbestos wool product, in red soil powder: asbestos wool: the ratio of water quality ratio=60:40:60 pours blender furnishing cream mud into, is spread upon equably on the panel of monolayer bamboo clappers by asbestos cream mud with cement paint spatula, smears layer thickness and control at 3mm;
Step 8: after asbestos cream mud layer Stability Analysis of Structures floating on monolayer bamboo clappers, the plasterboard going out picture grass pattern hole is combined with the monolayer bamboo clappers smearing asbestos cream mud carefully, plasterboard is beaten gently with mallet, discharge the air in space between asbestos cream mud layer and plasterboard, make asbestos cream mud layer with plasterboard bonding closely；
Step 9: monolayer bamboo clappers and plasterboard surrounding clamped with iron clamp, be placed on horizontal table, the cream mud that plasterboard upper punch goes out hole position with probe or bamboo let is all rejected, and exposes the monolayer bamboo clappers material of inside；
Step 10: the monolayer bamboo clappers back of the body back of the body completing step 9 by two leans on (punching plasterboard is the most outside) mutually, lifts and carries out carbonization process into lumber kiln, be vertically placed on the shelf in lumber kiln after fixing with iron clamp；
Step 11: the temperature of lumber kiln rises to 185 DEG C, keeps 3 hours at such a temperature, completes the carbonization process of monolayer bamboo clappers；
Step 12: close lumber kiln heating system, sprays water-atomization cooling damping to monolayer bamboo clappers, controls the final moisture content of carbonization monolayer bamboo clappers 6～8wt%；
Step 13: taken out the monolayer bamboo clappers that carbonization processes, unclamps the iron clamp that surrounding is fixing, removes punching plasterboard and the asbestos cream mud of surface adhesion, and monolayer bamboo clappers surface open goes out the pattern contour of ornamental bamboo clappers charcoal drawing；
Step 14: the concrete condition coloured pencil combining pattern is painted to pattern, increases the verity of pattern, makes complete ornamental bamboo clappers charcoal drawing.
Embodiment 3
Concretely comprising the following steps of the processing method of a kind of ornamental bamboo clappers charcoal drawing:
Step 1: the Phyllostachys pubescens Mazei ex H.de Lebaie that fresh felling comes is cut into the bamboo section of 2010mm length, cuts open into the bamboo chip of 25mm width by cuing open bamboo machine；
Step 2: circular arc bamboo chip is processed into specification force plane bamboo chip by bamboo chip force plane machine, sends into lumber kiln and is dried, and dried bamboo chip moisture control is at 8 below wt%；
Step 3: dry bamboo chip is sent into adjustable cast iron planes machine, makes specification adjustable cast iron planes bamboo chip, after artificial separation, standby；
Step 4: by the specification lateral gluing of adjustable cast iron planes bamboo chip after sorting, sends into hot press and makes monolayer bamboo clappers after assembly；
Step 5: the monolayer bamboo clappers after cooling is sent into edging saw, makes specification 2000mm × 1200mm × 6mm(length × width x thickness) monolayer bamboo clappers, then process through the two-sided sanding of sander, make the fixed thick monolayer bamboo clappers of 5mm, standby；
Step 6: outsourcing dimensions is 2000mm × 1200mm × 5mm(length × width x thickness) plasterboard, computer select popular pattern, go out pattern hole on gypsum with punch press；
Step 7: outsourcing asbestos wool product, in red soil powder: asbestos wool: the ratio of water quality ratio=60:40:60 pours blender furnishing cream mud into, is spread upon equably on the panel of monolayer bamboo clappers by asbestos cream mud with cement paint spatula, smears layer thickness and control at 3mm;
Step 8: after asbestos cream mud layer Stability Analysis of Structures floating on monolayer bamboo clappers, the plasterboard going out picture grass pattern hole is combined with the monolayer bamboo clappers smearing asbestos cream mud carefully, plasterboard is beaten gently with mallet, discharge the air in space between asbestos cream mud layer and plasterboard, make asbestos cream mud layer with plasterboard bonding closely；
Step 9: monolayer bamboo clappers and plasterboard surrounding clamped with iron clamp, be placed on horizontal table, the cream mud that plasterboard upper punch goes out hole position with probe or bamboo let is all rejected, and exposes the monolayer bamboo clappers material of inside；
Step 10: the monolayer bamboo clappers back of the body back of the body completing step 9 by two leans on (punching plasterboard is the most outside) mutually, lifts and carries out carbonization process into lumber kiln, be vertically placed on the shelf in lumber kiln after fixing with iron clamp；
Step 11: the temperature of lumber kiln rises to 215 DEG C, keeps 2 hours at such a temperature, completes the carbonization process of monolayer bamboo clappers；
Step 12: close lumber kiln heating system, sprays water-atomization cooling damping to monolayer bamboo clappers, controls the final moisture content of carbonization monolayer bamboo clappers 6～8wt%；
Step 13: taken out the monolayer bamboo clappers that carbonization processes, unclamps the iron clamp that surrounding is fixing, removes punching plasterboard and the asbestos cream mud of surface adhesion, and monolayer bamboo clappers surface open goes out the pattern contour of ornamental bamboo clappers charcoal drawing；
Step 14: the concrete condition coloured pencil combining pattern is painted to pattern, increases the verity of pattern, makes complete ornamental bamboo clappers charcoal drawing.
The foregoing is only presently preferred embodiments of the present invention, all impartial changes done according to scope of the present invention patent and modification, all should belong to the covering scope of the present invention.
Claims (7)
1. the processing method of an ornamental bamboo clappers charcoal drawing, it is characterised in that comprise the steps:
Step 1: the Phyllostachys pubescens Mazei ex H.de Lebaie that fresh felling comes is cut into the bamboo section of 2010mm length, cuts open into the circular arc bamboo chip of 25mm width by cuing open bamboo machine；
Step 2: circular arc bamboo chip is processed into specification force plane bamboo chip, sends into lumber kiln and is dried, and dried bamboo chip moisture control is at 8 below wt%；
Step 3: dried for step 2 bamboo chip is sent into adjustable cast iron planes machine, makes specification adjustable cast iron planes bamboo chip, after artificial separation, standby；
Step 4: by the specification lateral gluing of adjustable cast iron planes bamboo chip after sorting, sends into hot press and makes monolayer bamboo clappers after assembly, cooling；
Step 5: edging saw sent into by the monolayer bamboo clappers after step 4 being cooled down, makes the monolayer bamboo clappers that length × width x thickness is 2000mm × 1200mm × 6mm, the more two-sided sanding process through sander, makes the fixed thick monolayer bamboo clappers of 5mm, standby；
Step 6: outsourcing length × width x thickness is the plasterboard of 2000mm × 1200mm × 5mm, computer selects popular pattern, goes out pattern hole with punch press on gypsum；
Step 7: outsourcing asbestos wool product, in red soil powder: asbestos wool: the ratio of water quality ratio=60:40:60 pours blender furnishing cream mud into, spreads upon cream mud equably on the panel of the monolayer bamboo clappers that step 5 prepares with cement paint spatula, smears layer thickness and control at 3mm；
Step 8: after cream mud layer Stability Analysis of Structures floating on monolayer bamboo clappers, step 6 is gone out the monolayer bamboo clappers that the plasterboard of pattern hole and step 7 smear cream mud layer be combined, plasterboard is beaten gently with mallet, discharge the air in space between cream mud layer and plasterboard, make cream mud layer with plasterboard bonding closely；
Step 9: monolayer bamboo clappers and plasterboard surrounding clamped with iron clamp, be placed on horizontal table, the cream mud that plasterboard upper punch goes out hole position with probe or bamboo let is all rejected, and exposes the monolayer bamboo clappers material of inside；Prepare composite plate；
Step 10: the monolayer bamboo clappers face back of the body back of the body of the composite plate two steps 9 prepared leans on mutually, after fixing with iron clamp, lifts and carries out carbonization process into lumber kiln, be vertically placed on the shelf in lumber kiln；
Step 11: the temperature of lumber kiln rises to 185～215 DEG C, keeps 2～3 hours at such a temperature, completes the carbonization process of monolayer bamboo clappers；
Step 12: close lumber kiln heating system, sprays water-atomization cooling damping to monolayer bamboo clappers, controls the final moisture content of carbonization monolayer bamboo clappers 6～8wt%；
Step 13: taken out the monolayer bamboo clappers that carbonization processes, unclamps the iron clamp that surrounding is fixing, removes punching plasterboard and the cream mud of surface adhesion, and monolayer bamboo clappers surface open goes out the pattern contour of ornamental bamboo clappers charcoal drawing；
Step 14: the concrete condition coloured pencil combining pattern is painted to pattern, increases the verity of pattern, makes complete ornamental bamboo clappers charcoal drawing.
The processing method of a kind of ornamental bamboo clappers charcoal drawing the most according to claim 1, it is characterised in that: the artificial separation described in step 3 is to select solid colour, do not have the adjustable cast iron planes bamboo chip of open defect.
The processing method of a kind of ornamental bamboo clappers charcoal drawing the most according to claim 1, it is characterised in that: before going out pattern hole on gypsum with punch press in step 6, first in the two sides brushing polyvinyl alcohol glue of plasterboard, glue brushing amount is 150g/m2。
The processing method of a kind of ornamental bamboo clappers charcoal drawing the most according to claim 1, it is characterised in that: in step 8 mallet beat the direction of plasterboard be from left to right or from top to bottom beat direction.
The processing method of a kind of ornamental bamboo clappers charcoal drawing the most according to claim 1, it is characterised in that: plasterboard upper punch is gone out, with probe or bamboo let, the process that the cream mud at hole position all rejects by step 9 and should select to complete before the unseasoned solidification of cream mud.
The processing method of a kind of ornamental bamboo clappers charcoal drawing the most according to claim 1, it is characterised in that: in step 10, the heating system of lumber kiln uses deep fat heat supply.
7. the ornamental bamboo clappers charcoal drawing that the processing method as described in any one of claim 1-6 prepares.