CN111904874A - 一种中药海藻纤维面膜及其制备方法 - Google Patents
一种中药海藻纤维面膜及其制备方法 Download PDFInfo
- Publication number
- CN111904874A CN111904874A CN202010768567.9A CN202010768567A CN111904874A CN 111904874 A CN111904874 A CN 111904874A CN 202010768567 A CN202010768567 A CN 202010768567A CN 111904874 A CN111904874 A CN 111904874A
- Authority
- CN
- China
- Prior art keywords
- chinese medicine
- traditional chinese
- alginate
- solution
- alginate fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开的一种中药海藻纤维面膜及其制备方法，属于护肤用品技术领域。含中药提取物溶液的海藻酸钠溶液经湿法纺丝得到中药海藻纤维，再经开松‑梳理成网‑预湿‑水刺‑烘燥‑卷绕得到中药海藻纤维非织造布；中药海藻纤维非织造布经凝胶处理后再经裁剪和灭菌处理，得到中药海藻纤维面膜。不添加任何人工合成，含有中药成分，天然，绿色，环保，安全，作用缓和，无毒害无刺激，抑菌性能好，容易保存，方便使用；无需其他精华液，面膜遇水即可凝胶敷于面部使用，避免精华液变质，滋生微生物，过敏等问题。面膜整体重量轻，携带方便；生产工艺简单，使用后海藻纤维可自然降解，绿色环保。
Description
技术领域
本发明属于护肤用品技术领域，具体涉及一种中药海藻纤维面膜及其制备方法。
背景技术
随着科技的发展和生活品质的提高，人们对外在形象有了更多的追求，化妆品种类也日益增多，面膜逐渐成为人们皮肤保养的必需品。目前市场上面膜产品主要为两类：一类是人工合成化学品为主料的产品，成分里往往添加了各种防腐剂、杀菌剂等各种化学成分，其特点是使用效果明显，但是长期使用易造成过敏，刺激皮肤等副作用，对人体存在潜在的危害。另一类是以天然产物为配方主料的产品，其特点是对人体副作用小甚至无副作用，同时具备一定的功效。因此“天然、绿色、方便、有效”的面膜产品也慢慢成为消费者所追求的目标。天然而又实惠的海藻受到了人们越来越多的青睐。
当前海藻面膜的制备方法一般有两种：一种是将海藻经简单粉碎或水煮与其它营养成分混合而成胶状物质，然后将胶状物涂抹在脸上。这样的方法使海藻提取不完全，造成大量活性成分浪费。同时海藻成膜效果差、防水性能弱，不能有效锁定水分，导致面膜时效性短，营养物质不能被皮肤完全吸收，在清洗时不容易清净面部。另一种是将海藻提取液与其它物质混合，做成海藻营养液，将无纺布浸泡在营养液中一段时间后使用。这种方法制备比较繁琐，营养液不易保存，易滋生微生物，而且面膜容易干，使用时间和效果有限。
发明内容
为了解决上述问题，本发明提供一种中药海藻纤维面膜及其制备方法，原料绿色天然、安全环保，具有一定的保健和治疗作用，作用缓和，无毒害无刺激，抑菌性能好，容易保存，方便使用；重量轻，使用携带方便，用完后可自然降解，对环境友好。
本发明是通过以下技术方案来实现：
本发明公开了一种中药海藻纤维面膜的制备方法，包括以下步骤：
步骤1：向海藻酸钠溶液中加入中药提取物溶液，得到共混纺丝液，充分搅拌均匀后静置消泡，再经湿法纺丝后得到的初生纤维经拉伸、水洗、热处理后得到中药海藻纤维；将所得中药海藻纤维依次经开松-梳理成网-预湿-水刺-烘燥-卷绕，得到中药海藻纤维非织造布；
步骤2：将步骤1得到的中药海藻纤维非织造布经体积浓度为0.05％～0.2％的HCl溶液浸泡处理后，再用乙醇冲洗至pH值不再变化，最后在浓度为3～5mmol/L的NaOH的乙醇溶液中浸泡处理，烘干后得到中药海藻纤维面膜布；
步骤3：将步骤2得到的中药海藻纤维面膜布裁剪成型后装入无菌包装袋进行高压灭菌，得到中药海藻纤维面膜。
优选地，步骤1中，海藻酸钠溶液是采用海藻酸钠溶解于去离子水中制得的，海藻酸钠溶液中海藻酸钠的质量百分比为2.5％～4.5％；中药提取物溶液的质量为共混纺丝液质量的0.6％～1.5％。
进一步优选地，步骤1中，中药提取物溶液为黄连提取物溶液、三七提取物溶液和茯苓提取物溶液。
优选地，步骤1中，湿法纺丝的温度为20～45℃，初生纤维的拉伸倍数为1.5～2倍，水洗的温度为25～50℃，热处理的温度为40～100℃。
优选地，步骤1中，开松的时间为3min；梳理成网前，向中药海藻纤维中加入蒸馏水；梳理成网采用交叉铺网；预湿采用输网帘夹持式预湿；水刺采用三级水刺，一级、二级水刺为转鼓式水刺，三级水刺为平网式水刺；烘燥前经压辊压榨脱水和真空抽吸脱水。
进一步优选地，一级水刺和三级水刺的水压为25～35MPa，二级水刺的水压为35～45MPa；烘燥的温度为90℃，时间为2min。
优选地，步骤2中，HCl溶液浸泡处理的温度为20～30℃，时间为30min；NaOH的乙醇溶液浸泡处理的温度为30～40℃，时间为1h。
优选地，步骤2中，烘干的温度为50℃，时间为30min。
优选地，步骤3中，灭菌的压力为300个大气压，时间为40min。
本发明公开的采用上述制备方法制得的中药海藻纤维面膜，克重为30～50g/m2，厚度为0.2～0.4mm。
与现有技术相比，本发明具有以下有益的技术效果：
本发明公开的一种中药海藻纤维面膜的制备方法，含中药提取物溶液的海藻酸钠溶液经湿法纺丝得到中药海藻纤维，再经开松-梳理成网-预湿-水刺-烘燥-卷绕得到中药海藻纤维非织造布；中药海藻纤维非织造布经凝胶处理后再经裁剪和灭菌处理，得到中药海藻纤维面膜。不添加任何人工合成，可以根据实际需要增加中药成分，达到相应的保健效果，天然，绿色，环保，安全，作用缓和，无毒害无刺激，抑菌性能好，容易保存，方便使用；无需其他精华液，面膜遇水即可凝胶敷于面部使用，避免精华液变质，滋生微生物，过敏等问题。面膜整体重量轻，携带方便；生产工艺简单，使用后海藻纤维可自然降解，绿色环保。
进一步地，海藻酸钠溶液中海藻酸钠的质量百分比为2.5％～4.5％，海藻酸钠浓度过低，形成的纤维容易断裂，难以牵伸，不易成型，纺丝较为困难；浓度过高，影响纺丝的连续性、均匀性，甚至堵塞喷丝孔，纺丝效率降低。
进一步地，中药提取物溶液为黄连提取物溶液、三七提取物溶液或茯苓提取物溶液，根据实际需要进行配比，对皮肤具有保湿、补水、消炎、抗菌、修复、抗皱、祛斑、促进血液循环和吸收的作用。
进一步地，梳理成纤网之前，在纤维中加入一定量的蒸馏水，减少静电产生，使得纤维的梳理性能和成网性能均得到提高，输出较为连续完整的纤维网。采用交叉铺网，这种成网方式能很好的调节纤网的横纵向强力比，保证水刺布的强力，适合面膜基布的生产。采用的输网帘夹持式预湿，通过预湿罗拉给水、压实，使纤网中的纤维紧密接触，排出纤网中的空气，让水针刺透纤维，加强纤维缠结效果。采用平网与转鼓相结合的水刺加固方式，既能保护纤网，提高非织造布性能，又能高速生产。采用三级水刺工艺，一、二级为转鼓式水刺，纤网吸附在转鼓曲面上，不会发生偏移，外层松散，内层受压力收缩，有利于纤维网纠缠，提高无纺布的质量和织造速度。三级为平网式水刺，纤维与水针垂直，增大接触面积，同时不会破坏纤网，易于织造。烘燥前经过压辊压榨脱水和真空抽吸脱水，除去纤网中多余的水，使非织造布水分迅速蒸发，减少烘干时的能耗。
本发明还公开了采用上述制备方法制得的中药海藻纤维面膜，质量轻、保湿和抑菌效果好。
附图说明
图1为本发明制得的中药海藻纤维面膜扫描电镜图。
具体实施方式
下面结合实施例对本发明做进一步详细描述：
实施例1
一种中药海藻纤维面膜的制备方法，包括以下步骤：
(1)中药海藻纤维的制备
将海藻酸钠溶解于去离子水中，制得质量分数为2.5％的海藻酸钠溶液。将配置好的黄连提取物溶液、茯苓提取物溶液和三七提取物溶液加入到海藻酸钠溶液中，添加适量蒸馏水，加速搅拌，使各成分充分分散在海藻酸钠溶液中，待溶液搅拌均匀后，将纺丝原液静置消泡。其中在共混纺丝液中，黄连提取物的质量分数为0.2％，茯苓提取物的质量分数为0.2％，三七提取物的质量分数为0.2％。将配制好的纺丝液加入到氯化钙质量分数为2％的凝固浴和氯化钙质量分数为5％的牵伸浴中，然后在20℃温度下进行常规湿法纺丝，所得初生纤维经1.5倍的后拉伸，随后在25℃温度下水洗，再经40℃热处理，即得中药海藻纤维。
(2)中药海藻纤维非织造布的制备
将制备好的中药海藻纤维送入开松机，开松时间为3min；向开松完成的中药海藻纤维中加入蒸馏水，通过喂棉系统喂入梳理机，采用交叉铺网；然后进行输网帘夹持式预湿；预湿后进行三级水刺，其中一级、二级水刺为转鼓式水刺，水压分别为25MPa和35MPa，三级水刺为平网式水刺，水压为25MPa；水刺完毕后经压辊压榨脱水和真空抽吸脱水，然后在烘干机中进行烘燥，烘干机烘干温度为90℃，烘干时间为2min，制得中药海藻纤维非织造布，克重为30g/m2，厚度为0.2mm。
(3)中药海藻纤维非织造布的凝胶处理
将中药海藻纤维非织造布先在体积浓度为0.05％的HCl溶液中，20℃下浸泡处理30min，再用乙醇冲洗至pH值不再变化，然后在浓度为3mmol/L的NaOH乙醇溶液中浸泡处理1h，温度为30℃，然后在50℃的烘箱中烘干30min。
(4)裁剪及灭菌处理
将面膜布按照脸部特征裁剪成一定形状后，在装入无菌包装袋中密封并在高压下进行灭菌。灭菌的工作压力为300个大气压，灭菌时间为40min。
实施例2
一种中药海藻纤维面膜的制备方法，包括以下步骤：
(1)中药海藻纤维的制备
将海藻酸钠溶解于去离子水中，制得质量分数为3％的海藻酸钠溶液。将配置好的黄连提取物溶液、茯苓提取物溶液、三七提取物溶液加入到海藻酸钠溶液中，添加适量蒸馏水，加速搅拌，使各成分充分分散在海藻酸钠溶液中，待溶液搅拌均匀后，将纺丝原液静置消泡。其中在共混纺丝液中，黄连提取物的质量分数为0.3％，茯苓提取物的质量分数为0.3％，三七提取物的质量分数为0.3％。将配制好的纺丝液加入到氯化钙质量分数为2％的凝固浴和氯化钙质量分数为5％的牵伸浴中，然后在30℃温度下进行常规湿法纺丝，所得初生纤维经1.7倍的后拉伸，随后在30℃温度下水洗，再经50℃热处理，即得中药海藻纤维。
(2)中药海藻纤维非织造布的制备
将制备好的中药海藻纤维送入开松机，开松时间为3min；向开松完成的中药海藻纤维中加入蒸馏水，通过喂棉系统喂入梳理机，采用交叉铺网；然后进行输网帘夹持式预湿；预湿后进行三级水刺，其中一级、二级水刺为转鼓式水刺，水压分别为30MPa和40MPa，三级水刺为平网式水刺，水压为30MPa；水刺完毕后经压辊压榨脱水和真空抽吸脱水，然后在烘干机中进行烘燥，烘干机烘干温度为90℃，烘干时间为2min，制得中药海藻纤维非织造布，克重为35g/㎡，厚度为0.25mm。
(3)中药海藻纤维非织造布的凝胶处理
将中药海藻纤维非织造布先在体积浓度为0.1％的HCl溶液中，20℃下浸泡处理30min，再用乙醇冲洗至pH值不再变化，然后在浓度为3.5mmol/L的NaOH乙醇溶液中浸泡处理1h，温度为30℃，然后在50℃的烘箱中烘干30min。
(4)裁剪及灭菌处理
将面膜布按照脸部特征裁剪成一定形状后，在装入无菌包装袋中密封并在高压下进行灭菌。灭菌的工作压力为300个大气压，灭菌时间为40min。
实施例3
一种中药海藻纤维面膜的制备方法，包括以下步骤：
(1)中药海藻纤维的制备
将海藻酸钠溶解于去离子水中，制得质量分数为3.5％的海藻酸钠溶液。将配置好的黄连提取物溶液、茯苓提取物溶液、三七提取物溶液加入到海藻酸钠溶液中，添加适量蒸馏水，加速搅拌，使各成分充分分散在海藻酸钠溶液中，待溶液搅拌均匀后，将纺丝原液静置消泡。其中在共混纺丝液中，黄连提取物的质量分数为0.4％，茯苓提取物的质量分数为0.4％，三七提取物的质量分数为0.4％。将配制好的纺丝液加入到氯化钙质量分数为2％的凝固浴和氯化钙质量分数为5％的牵伸浴中，然后在35℃温度下进行常规湿法纺丝，所得初生纤维经1.8倍的后拉伸，随后在35℃温度下水洗，再经80℃热处理，即得中药海藻纤维。
(2)中药海藻纤维非织造布的制备
将制备好的中药海藻纤维送入开松机，开松时间为3min；向开松完成的中药海藻纤维中加入蒸馏水，通过喂棉系统喂入梳理机，采用交叉铺网；然后进行输网帘夹持式预湿；预湿后进行三级水刺，其中一级、二级水刺为转鼓式水刺，水压分别为35MPa和40MPa，三级水刺为平网式水刺，水压为35MPa；水刺完毕后经压辊压榨脱水和真空抽吸脱水，然后在烘干机中进行烘燥，烘干机烘干温度为90℃，烘干时间为2min，制得中药海藻纤维非织造布，克重为40g/m2，厚度为0.3mm。
(3)中药海藻纤维非织造布的凝胶处理
将中药海藻纤维非织造布先在体积浓度为0.15％的HCl溶液中，25℃下浸泡处理30min，再用乙醇冲洗至pH值不再变化，然后在浓度为4mmol/L的NaOH乙醇溶液中浸泡处理1h，温度为35℃，然后在50℃的烘箱中烘干30min。
(4)裁剪及灭菌处理
将面膜布按照脸部特征裁剪成一定形状后，在装入无菌包装袋中密封并在高压下进行灭菌。灭菌的工作压力为300个大气压，灭菌时间为40min。
实施例4
一种中药海藻纤维面膜的制备方法，包括以下步骤：
(1)中药海藻纤维的制备
将海藻酸钠溶解于去离子水中，制得质量分数为4％的海藻酸钠溶液。将配置好的黄连提取物溶液、茯苓提取物溶液、三七提取物溶液加入到海藻酸钠溶液中，添加适量蒸馏水，加速搅拌，使各成分充分分散在海藻酸钠溶液中，待溶液搅拌均匀后，将纺丝原液静置消泡。其中在共混纺丝液中，黄连提取物的质量分数为0.5％，茯苓提取物的质量分数为0.5％，三七提取物的质量分数为0.5％。将配制好的纺丝液加入到氯化钙质量分数为2％的凝固浴和氯化钙质量分数为5％的牵伸浴中，然后在45℃温度下进行常规湿法纺丝，所得初生纤维经2倍的后拉伸，随后在50℃温度下水洗，再经100℃热处理，即得中药海藻纤维。
(2)中药海藻纤维非织造布的制备
将制备好的中药海藻纤维送入开松机，开松时间为3min；向开松完成的中药海藻纤维中加入蒸馏水，通过喂棉系统喂入梳理机，采用交叉铺网；然后进行输网帘夹持式预湿；预湿后进行三级水刺，其中一级、二级水刺为转鼓式水刺，水压分别为35MPa和45MPa，三级水刺为平网式水刺，水压为35MPa；水刺完毕后经压辊压榨脱水和真空抽吸脱水，然后在烘干机中进行烘燥，烘干机烘干温度为90℃，烘干时间为2min，制得中药海藻纤维非织造布，克重为50g/m2，厚度为0.4mm。
(3)中药海藻纤维非织造布的凝胶处理
将中药海藻纤维非织造布先在体积浓度为0.2％的HCl溶液中，25℃下浸泡处理30min，再用乙醇冲洗至pH值不再变化，然后在浓度为5mmol/L的NaOH乙醇溶液中浸泡处理1h，温度为40℃，然后在50℃的烘箱中烘干30min。
(4)裁剪及灭菌处理
将面膜布按照脸部特征裁剪成一定形状后，在装入无菌包装袋中密封并在高压下进行灭菌。灭菌的工作压力为300个大气压，灭菌时间为40min。
实施例5
一种中药海藻纤维面膜的制备方法，包括以下步骤：
(1)中药海藻纤维的制备
将海藻酸钠溶解于去离子水中，制得质量分数为3.5％的海藻酸钠溶液。将配置好的黄连提取物溶液、茯苓提取物溶液、三七提取物溶液加入到海藻酸钠溶液中，添加适量蒸馏水，加速搅拌，使各成分充分分散在海藻酸钠溶液中，待溶液搅拌均匀后，将纺丝原液静置消泡。其中在共混纺丝液中，黄连提取物的质量分数为0.2％，茯苓提取物的质量分数为0.3％，三七提取物的质量分数为0.3％。将配制好的纺丝液加入到氯化钙质量分数为2％的凝固浴和氯化钙质量分数为5％的牵伸浴中，然后在30℃温度下进行常规湿法纺丝，所得初生纤维经2倍的后拉伸，随后在40℃温度下水洗，再经60℃热处理，即得中药海藻纤维。
(2)中药海藻纤维非织造布的制备
将制备好的中药海藻纤维送入开松机，开松时间为3min；向开松完成的中药海藻纤维中加入蒸馏水，通过喂棉系统喂入梳理机，采用交叉铺网；然后进行输网帘夹持式预湿；预湿后进行三级水刺，其中一级、二级水刺为转鼓式水刺，水压分别为30MPa和45MPa，三级水刺为平网式水刺，水压为35MPa；水刺完毕后经压辊压榨脱水和真空抽吸脱水，然后在烘干机中进行烘燥，烘干机烘干温度为90℃，烘干时间为2min，制得中药海藻纤维非织造布，克重为40g/m2，厚度为0.3mm。
(3)中药海藻纤维非织造布的凝胶处理
将中药海藻纤维非织造布先在体积浓度为0.15％的HCl溶液中，25℃下浸泡处理30min，再用乙醇冲洗至pH值不再变化，然后在浓度为4.5mmol/L的NaOH乙醇溶液中浸泡处理1h，温度为40℃，然后在50℃的烘箱中烘干30min。
(4)裁剪及灭菌处理
将面膜布按照脸部特征裁剪成一定形状后，在装入无菌包装袋中密封并在高压下进行灭菌。灭菌的工作压力为300个大气压，灭菌时间为40min。
图1为本发明制得的中药海藻纤维面膜扫描电镜图，中药海藻面膜中纤维直径均匀，纤维之间孔隙率较高，纤维之间相互穿插纠缠程度高，面膜上具有较大的孔洞。这表明该发明制得的中药海藻纤维面膜吸湿透气性好，而且由于海藻纤维的遇水的天然凝胶作用，其保湿性也非常优良。
Claims (10)
1.一种中药海藻纤维面膜的制备方法，其特征在于，包括以下步骤：
步骤1：向海藻酸钠溶液中加入中药提取物溶液，得到共混纺丝液，充分搅拌均匀后静置消泡，再经湿法纺丝后得到的初生纤维经拉伸、水洗、热处理后得到中药海藻纤维；将所得中药海藻纤维依次经开松-梳理成网-预湿-水刺-烘燥-卷绕，得到中药海藻纤维非织造布；
步骤2：将步骤1得到的中药海藻纤维非织造布经体积浓度为0.05％～0.2％的HCl溶液浸泡处理后，再用乙醇冲洗至pH值不再变化，最后在浓度为3～5mmol/L的NaOH的乙醇溶液中浸泡处理，烘干后得到中药海藻纤维面膜布；
步骤3：将步骤2得到的中药海藻纤维面膜布裁剪成型后装入无菌包装袋进行高压灭菌，得到中药海藻纤维面膜。
2.根据权利要求1所述的中药海藻纤维面膜，其特征在于，步骤1中，海藻酸钠溶液是采用海藻酸钠溶解于去离子水中制得的，海藻酸钠溶液中海藻酸钠的质量百分比为2.5％～4.5％；中药提取物溶液的质量为共混纺丝液质量的0.6％～1.5％。
3.根据权利要求2所述的中药海藻纤维面膜，其特征在于，步骤1中，中药提取物溶液为黄连提取物溶液、三七提取物溶液和茯苓提取物溶液。
4.根据权利要求1所述的中药海藻纤维面膜，其特征在于，步骤1中，湿法纺丝的温度为20～45℃，初生纤维的拉伸倍数为1.5～2倍，水洗的温度为25～50℃，热处理的温度为40～100℃。
5.根据权利要求1所述的中药海藻纤维面膜，其特征在于，步骤1中，开松的时间为3min；梳理成网前，向中药海藻纤维中加入蒸馏水；梳理成网采用交叉铺网；预湿采用输网帘夹持式预湿；水刺采用三级水刺，一级、二级水刺为转鼓式水刺，三级水刺为平网式水刺；烘燥前经压辊压榨脱水和真空抽吸脱水。
6.根据权利要求5所述的中药海藻纤维面膜，其特征在于，一级水刺和三级水刺的水压为25～35MPa，二级水刺的水压为35～45MPa；烘燥的温度为90℃，时间为2min。
7.根据权利要求1所述的中药海藻纤维面膜，其特征在于，步骤2中，HCl溶液浸泡处理的温度为20～30℃，时间为30min；NaOH的乙醇溶液浸泡处理的温度为30～40℃，时间为1h。
8.根据权利要求1所述的中药海藻纤维面膜，其特征在于，步骤2中，烘干的温度为50℃，时间为30min。
9.根据权利要求1所述的中药海藻纤维面膜，其特征在于，步骤3中，灭菌的压力为300个大气压，时间为40min。
10.采用权利要求1～9任意一项所述制备方法制得的中药海藻纤维面膜，其特征在于，克重为30～50g/m2，厚度为0.2～0.4mm。