CN111843301A - 一种液压支架结构件在线焊接补温方法 - Google Patents
一种液压支架结构件在线焊接补温方法 Download PDFInfo
- Publication number
- CN111843301A CN111843301A CN202010639988.1A CN202010639988A CN111843301A CN 111843301 A CN111843301 A CN 111843301A CN 202010639988 A CN202010639988 A CN 202010639988A CN 111843301 A CN111843301 A CN 111843301A
- Authority
- CN
- China
- Prior art keywords
- welding
- temperature
- crawler
- hydraulic support
- type ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种液压支架结构件在线焊接补温方法,首先用履带式陶瓷远红外加热器覆盖在待预热焊道两侧160mm范围内;然后调节温度调节器仪至设定预热温度,加热达到预热温度,对焊道进行快速、均匀在线补温。履带式陶瓷远红外加热器的长度根据焊道长度进行拼接,两头用永久磁铁固定在母材上,加热时间为10‑20min。可用于液压支架二次顶梁焊接强化,包括对柱窝组件和底板组件的焊接强化。采用履带式陶瓷远红外加热器加热,远红外加热体嵌入陶瓷中,防止加热体过热,延长使用寿命;远红外热辐射效率高,更节能,温度分布均匀。
Description
技术领域
本发明涉及一种煤矿用液压支架结构件在线焊接技术,尤其涉及一种液压支架结构件在线焊接补温方法。
背景技术
随着液压支架工作阻力的增大,支架结构件种调质细晶粒度钢板Q550、Q690的比例越来越高,由于钢中加入Cr、Mo、Ni、Nb、V、Ti等淬透性元素,所以焊接时为防止热影响区淬硬组织和冷裂纹的发生,在结构件焊前入电加热炉预热80℃以上。
而结构件体积大,焊接工作量大,在焊接过程中活件温度极易下降到预热温度以下。为此多采用火焰烤枪补温,而烤枪加热气体流量消耗大,升温速度慢且温度不可控造成母材软化。
发明内容
本发明的目的是提供一种液压支架结构件在线焊接补温方法。
本发明的目的是通过以下技术方案实现的:
本发明的液压支架结构件在线焊接补温方法,包括步骤:
首先,用履带式陶瓷远红外加热器覆盖在待预热焊道两侧;
然后,调节温度调节器仪至设定预热温度,加热达到预热温度,对焊道进行快速、均匀在线补温。
由上述本发明提供的技术方案可以看出,本发明实施例提供的液压支架结构件在线焊接补温方法,由于采用履带式陶瓷远红外加热器加热,远红外加热体嵌入陶瓷中,可防止加热体过热,延长使用寿命;远红外热辐射效率高,更节能,温度分布均匀。
附图说明
图1为本发明实施例采用拼接式陶瓷远红外加热器在线补温示意图。
图中:
1、焊缝,2、拼接式陶瓷远红外加热器,3、永久磁铁。
具体实施方式
下面将对本发明实施例作进一步地详细描述。本发明实施例中未作详细描述的内容属于本领域专业技术人员公知的现有技术。
本发明的液压支架结构件在线焊接补温方法,其较佳的具体实施方式是:
首先,用履带式陶瓷远红外加热器覆盖在待预热焊道两侧;
然后,调节温度调节器仪至设定预热温度,加热达到预热温度,对焊道进行快速、均匀在线补温。
所述履带式陶瓷远红外加热器覆盖在待预热焊道两侧160mm范围内,所述履带式陶瓷远红外加热器的长度根据焊道长度进行拼接,所述履带式陶瓷远红外加热器的两头用永久磁铁固定在母材上。
所述履带式陶瓷远红外加热器的加热时间为10-20min。
用于液压支架二次顶梁焊接强化,包括对柱窝组件和底板组件的焊接强化。
本发明的液压支架结构件在线焊接补温方法,采用履带式陶瓷远红外加热器加热,远红外加热体嵌入陶瓷中,防止加热体过热,延长使用寿命。远红外热辐射效率高,更节能,温度分布均匀。
具体实施例,如图1所示:
首先,用履带式陶瓷远红外加热器覆盖在待预热焊道两侧160mm范围内,加热器长度可以根据焊道长度进行拼接,加热器两头用永久磁铁固定在母材上。
然后,调节温度调节器仪至设定预热温度,只需加热10-20min就能达到预热温度,且受热面均匀。
上述实施例用可拼接履带式陶瓷远红外加热器覆盖在待预热焊道两侧160mm范围内,对焊道进行快速、均匀在线补温。
本发明用于二次顶梁强化方法,包括柱窝组件和底板组件的焊接强化。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明披露的技术范围内,可轻易想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书的保护范围为准。
Claims (4)
1.一种液压支架结构件在线焊接补温方法,其特征在于,包括步骤:
首先,用履带式陶瓷远红外加热器覆盖在待预热焊道两侧;
然后,调节温度调节器仪至设定预热温度,加热达到预热温度,对焊道进行快速、均匀在线补温。
2.根据权利要求1所述的液压支架结构件在线焊接补温方法,其特征在于,所述履带式陶瓷远红外加热器覆盖在待预热焊道两侧160mm范围内,所述履带式陶瓷远红外加热器的长度根据焊道长度进行拼接,所述履带式陶瓷远红外加热器的两头用永久磁铁固定在母材上。
3.根据权利要求2所述的液压支架结构件在线焊接补温方法,其特征在于,所述履带式陶瓷远红外加热器的加热时间为10-20min。
4.根据权利要求1、2或3所述的液压支架结构件在线焊接补温方法,其特征在于,用于液压支架二次顶梁焊接强化,包括对柱窝组件和底板组件的焊接强化。