CN111808487A - 一种冰花漆 - Google Patents
一种冰花漆 Download PDFInfo
- Publication number
- CN111808487A CN111808487A CN202010642445.5A CN202010642445A CN111808487A CN 111808487 A CN111808487 A CN 111808487A CN 202010642445 A CN202010642445 A CN 202010642445A CN 111808487 A CN111808487 A CN 111808487A
- Authority
- CN
- China
- Prior art keywords
- flower
- parts
- paint
- ice
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种冰花漆，包括以下以重量计的组分：成膜树脂50‑80份、成花材料10‑15份、脱浮剂3‑5份、附着力促进剂3‑5份、消泡剂2‑4份；本冰花漆由成膜树脂、成花材料、脱浮剂、附着力促进剂、消泡剂等组成，其构成的成分中特配了成花材料和脱浮剂，在本冰花漆制得之后使用在玻璃上进行烘干时，其能够形成较细密的冰花图案，且冰花漆能够牢靠的粘附在附着物的表面。
Description
技术领域
本发明涉及漆料领域，具体为一种冰花漆。
背景技术
随着经济的发展，人民生活水平逐步提高，对于家具款式、颜色等的要求越来越高，尤其是以玻璃装饰的各种家具表面只是单纯的带有颜色的涂层已经不能满足大众的需要。因而各种造型、各种效果的玻璃漆的需求便越来越多。其中冰花漆就是其中一种比较特殊的漆料，其在涂覆之后采用适当的烘干方式可以在附着物表面形成冰花状的图案，故称为冰花漆。
现有公开号为CN105400337A的中国专利，其公开了一种玻璃冰花漆，由以下原料按质量百分比计制得：环氧改性丙烯酸树脂50～75％；流平剂0.1～0.3％；消泡剂0.2～0.5％；催干剂0.1～0.3％；附着力促进剂1～5％；醋酸丁酯10～20％；丙二醇丁醚醋酸酯4～12％；柠檬酸1～6％；30％透明染料1～6％。
再如现有公开号为CN105400337A的中国专利，其公开了一种硅树脂冰花漆膜及其制备方法，所述冰花漆膜包括底漆和面漆，所述底漆的原料及其重量份为：所述面漆的原料及其重量份为：丙烯酸树脂60-85份、有机溶剂14-38份、助剂0.3-2份。
上述的这两种冰花漆都是以丙烯酸树脂为基料，然而上述的这两种冰花漆都存在着一些不足，如：都缺少特制的成花材料和脱浮剂作为原料。
发明内容
本发明的目的在于提供一种冰花漆，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种冰花漆，包括以下以重量计的组分：成膜树脂50-80份、成花材料10-15份、脱浮剂3-5份、附着力促进剂3-5份、消泡剂2-4份。
优选的，所述成膜树脂为丙烯酸树脂、聚氨酯树脂、聚氯乙烯树脂中的一种或多种混合。
优选的，所述成花材料包括精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油，其中精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油的质量比为10：6：5：1：2。
优选的，所述脱浮剂包括脱浮铝粉、甲苯、二甲苯、松香、松节油，其中脱浮铝粉、甲苯、二甲苯、松香、松节油的质量比为7：5：6：3：5。
优选的，所述附着力促进剂选自TR90附着力促进剂、PET附着力促进剂、TPE附着力促进剂中的一种。
优选的，所述丙烯酸树脂为热塑性丙烯酸树脂。
优选的，所述成花材料还包括EFKA-4010，其中精萘与EFKA-4010的重量比为10：3。
优选的，所述消泡剂为EFKA-2038消泡剂。
优选的，所述成花材料内添加有有色颜料，所述颜料选自钛白为PW-6、锌钡白PW-5、铅铬黄PY-34、喹吖啶酮PR-207、氧化铁红PR-101、酞菁蓝PB-15中的一种。
优选的，所述精萘在使用之前进行二次处理，先将将硫酸加入熔融的精萘中脱水，搅拌后静置分离废酸，再加入98％的硫酸，在85-95℃条件下搅拌40分钟，静置分离废酸，在搅拌下加入37％的甲醛溶液在85-95℃条件下搅拌50分钟，加温水搅拌后静置，分层聚合物及磺化物料，用10％氢氧化钠溶液中和PH到7-8，静置后除去废碱，最后蒸馏冷却得到可利用的精萘。
与现有技术相比，本发明的有益效果是：
本冰花漆由成膜树脂、成花材料、脱浮剂、附着力促进剂、消泡剂等组成，其构成的成分中特配了成花材料和脱浮剂，在本冰花漆制得之后使用在玻璃上进行烘干时，其能够形成较细密的冰花图案，且冰花漆能够牢靠的粘附在附着物的表面。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种冰花漆，包括以下以重量计的组分：成膜树脂50份、成花材料10份、脱浮剂3份、附着力促进剂3份、消泡剂2份。
其中，成膜树脂为丙烯酸树脂和聚氨酯树脂质量比为1：1的混合物。
其中，成花材料包括精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油，其中精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油的质量比为10：6：5：1：2，当成花材料采用以上配比组成时，其分子间键具有微引力，在烘干冰花漆时，成花材料中分子键断裂，在宏观形态上表现为冰棱的出现。
其中，脱浮剂包括脱浮铝粉、甲苯、二甲苯、松香、松节油，其中脱浮铝粉、甲苯、二甲苯、松香、松节油的质量比为7：5：6：3：5。
其中，附着力促进剂为TR90附着力促进剂。
其中，成花材料还包括EFKA-4010，其中精萘与EFKA-4010的重量比为10：3；EFKA-4010是一种高效的分散剂，EFKA4010是主要为稳定无机颜料包括碳黑而开发的高分子分散剂，在很多有机颜料中它也能提供很好的效能，其能够减少分散时间、提高光泽、提高颜料着色力，且其拥有良好的性能价格比，最适合取代传统润湿分散剂。
其中，消泡剂为EFKA-2038消泡剂，EFKA-2038有很好的相容性,非常适应于含义清漆成分的漆料使用，其能够有效防止泡沫和气泡形成。
其中，成花材料内添加有有色颜料，颜料选自钛白为PW-6、锌钡白PW-5、铅铬黄PY-34、喹吖啶酮PR-207、氧化铁红PR-101、酞菁蓝PB-15中的一种，选择某种特定的颜料即能够得到特定的色彩。
其中，为了提高精萘应用时的纯度，将精萘在使用之前进行二次处理，先将将硫酸加入熔融的精萘中脱水，搅拌后静置分离废酸，再加入98％的硫酸，在85℃条件下搅拌40分钟，静置分离废酸，在搅拌下加入37％的甲醛溶液在85℃条件下搅拌50分钟，加温水搅拌后静置，分层聚合物及磺化物料，用10％氢氧化钠溶液中和PH到7，静置后除去废碱，最后蒸馏冷却得到可利用的精萘。
实施例2
一种冰花漆，包括以下以重量计的组分：成膜树脂80份、成花材料15份、脱浮剂5份、附着力促进剂5份、消泡剂4份。
其中，成膜树脂为丙烯酸树脂。
其中，成花材料包括精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油，其中精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油的质量比为10：6：5：1：2。
其中，脱浮剂包括脱浮铝粉、甲苯、二甲苯、松香、松节油，其中脱浮铝粉、甲苯、二甲苯、松香、松节油的质量比为7：5：6：3：5。
其中，附着力促进剂为TR90附着力促进剂。
其中，丙烯酸树脂为热塑性丙烯酸树脂。
其中，成花材料还包括EFKA-4010，其中精萘与EFKA-4010的重量比为10：3；EFKA-4010是一种高效的分散剂，EFKA4010是主要为稳定无机颜料包括碳黑而开发的高分子分散剂，在很多有机颜料中它也能提供很好的效能，其能够减少分散时间、提高光泽、提高颜料着色力，且其拥有良好的性能价格比，最适合取代传统润湿分散剂。
其中，消泡剂为EFKA-2038消泡剂，EFKA-2038有很好的相容性,非常适应于含义清漆成分的漆料使用，其能够有效防止泡沫和气泡形成。
其中，成花材料内添加有有色颜料，颜料选自钛白为PW-6、锌钡白PW-5、铅铬黄PY-34、喹吖啶酮PR-207、氧化铁红PR-101、酞菁蓝PB-15中的一种，选择某种特定的颜料即能够得到特定的色彩。
其中，为了提高精萘应用时的纯度，将精萘在使用之前进行二次处理，先将将硫酸加入熔融的精萘中脱水，搅拌后静置分离废酸，再加入98％的硫酸，在85℃条件下搅拌40分钟，静置分离废酸，在搅拌下加入37％的甲醛溶液在85℃条件下搅拌50分钟，加温水搅拌后静置，分层聚合物及磺化物料，用10％氢氧化钠溶液中和PH到7，静置后除去废碱，最后蒸馏冷却得到可利用的精萘。
实施例3
一种冰花漆，包括以下以重量计的组分：成膜树脂60份、成花材料15份、脱浮剂3份、附着力促进剂4份、消泡剂3份。
其中，成膜树脂为聚氨酯树脂。
其中，成花材料包括精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油，其中精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油的质量比为10：6：5：1：2。
其中，脱浮剂包括脱浮铝粉、甲苯、二甲苯、松香、松节油，其中脱浮铝粉、甲苯、二甲苯、松香、松节油的质量比为7：5：6：3：5。
其中，附着力促进剂为TR90附着力促进剂。
其中，成花材料还包括EFKA-4010，其中精萘与EFKA-4010的重量比为10：3；EFKA-4010是一种高效的分散剂，EFKA4010是主要为稳定无机颜料包括碳黑而开发的高分子分散剂，在很多有机颜料中它也能提供很好的效能，其能够减少分散时间、提高光泽、提高颜料着色力，且其拥有良好的性能价格比，最适合取代传统润湿分散剂。
其中，消泡剂为EFKA-2038消泡剂，EFKA-2038有很好的相容性,非常适应于含义清漆成分的漆料使用，其能够有效防止泡沫和气泡形成。
实施例4
一种冰花漆，包括以下以重量计的组分：成膜树脂55份、成花材料15份、脱浮剂3份、附着力促进剂4份、消泡剂2份。
其中，成膜树脂为聚氨酯树脂。
其中，成花材料包括精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油，其中精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油的质量比为10：6：5：1：2。
其中，脱浮剂包括脱浮铝粉、甲苯、二甲苯、松香、松节油，其中脱浮铝粉、甲苯、二甲苯、松香、松节油的质量比为7：5：6：3：5。
其中，附着力促进剂为TR90附着力促进剂。
实施例5
一种冰花漆，包括以下以重量计的组分：成膜树脂50份、成花材料15份、脱浮剂3份、附着力促进剂4份、消泡剂3份。
其中，成膜树脂为丙烯酸树脂、聚氨酯树脂、聚氯乙烯树脂质量比为1：1：1的混合物。
其中，成花材料包括精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油，其中精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油的质量比为10：6：5：1：2。
其中，脱浮剂包括脱浮铝粉、甲苯、二甲苯、松香、松节油，其中脱浮铝粉、甲苯、二甲苯、松香、松节油的质量比为7：5：6：3：5。
其中，附着力促进剂为TR90附着力促进剂。
其中，消泡剂为EFKA-2038消泡剂，EFKA-2038有很好的相容性,非常适应于含义清漆成分的漆料使用，其能够有效防止泡沫和气泡形成。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (10)
1.一种冰花漆，其特征在于，包括以下以重量计的组分：成膜树脂50-80份、成花材料10-15份、脱浮剂3-5份、附着力促进剂3-5份、消泡剂2-4份。
2.根据权利要求1所述的一种冰花漆，其特征在于：所述成膜树脂为丙烯酸树脂、聚氨酯树脂、聚氯乙烯树脂中的一种或多种混合。
3.根据权利要求1所述的一种冰花漆，其特征在于：所述成花材料包括精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油，其中精萘、清漆、二甲苯、389-8长油醇酸树脂、200#溶剂油的质量比为10：6：5：1：2。
4.根据权利要求1所述的一种冰花漆，其特征在于：所述脱浮剂包括脱浮铝粉、甲苯、二甲苯、松香、松节油，其中脱浮铝粉、甲苯、二甲苯、松香、松节油的质量比为7：5：6：3：5。
5.根据权利要求2所述的一种冰花漆，其特征在于：所述附着力促进剂选自TR90附着力促进剂、PET附着力促进剂、TPE附着力促进剂中的一种。
6.根据权利要求2所述的一种冰花漆，其特征在于：所述丙烯酸树脂为热塑性丙烯酸树脂。
7.根据权利要求3所述的一种冰花漆，其特征在于：所述成花材料还包括EFKA-4010，其中精萘与EFKA-4010的重量比为10：3。
8.根据权利要求1所述的一种冰花漆，其特征在于：所述消泡剂为EFKA-2038消泡剂。
9.根据权利要求3所述的一种冰花漆，其特征在于：所述成花材料内添加有有色颜料，所述颜料选自钛白为PW-6、锌钡白PW-5、铅铬黄PY-34、喹吖啶酮PR-207、氧化铁红PR-101、酞菁蓝PB-15中的一种。
10.根据权利要求1所述的一种冰花漆，其特征在于：所述精萘在使用之前进行二次处理，先将将硫酸加入熔融的精萘中脱水，搅拌后静置分离废酸，再加入98％的硫酸，在85-95℃条件下搅拌40分钟，静置分离废酸，在搅拌下加入37％的甲醛溶液在85-95℃条件下搅拌50分钟，加温水搅拌后静置，分层聚合物及磺化物料，用10％氢氧化钠溶液中和PH到7-8，静置后除去废碱，最后蒸馏冷却得到可利用的精萘。