CN111790278B - 一种双层聚合物分离膜及其制备方法 - Google Patents
一种双层聚合物分离膜及其制备方法 Download PDFInfo
- Publication number
- CN111790278B CN111790278B CN202010264299.7A CN202010264299A CN111790278B CN 111790278 B CN111790278 B CN 111790278B CN 202010264299 A CN202010264299 A CN 202010264299A CN 111790278 B CN111790278 B CN 111790278B
- Authority
- CN
- China
- Prior art keywords
- layer
- membrane
- polymer
- double
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提出一种通过具有特殊官能团的单体改性聚合物制备层间黏结性优良的双层膜的方法。本发明通过在双层膜制备过程中，向铸膜液或纺丝液中添加具有活性基团和特征基团的改性单体，利用单体的活性基团与铸膜液或纺丝液中的聚合物发生接枝反应、利用单体的特征基团增强与其他聚合物的分子间相互作用，以提高聚合物之间的相容性，制备界面黏结性优良的双层膜。该方法同时适用于双层平板膜和双层中空纤维膜的制备，并且可以实现在温和的制备条件下制备界面处具有互相贯穿结构的双层膜。界面处的互相贯穿的结构使得制备的双层膜具有优良的层间黏结性，同时具有更低的传质阻力。
Description
技术领域
本发明属于膜分离技术领域，具体涉及一种通过具有特殊官能团的单体改性聚合物制备 层间黏结性优良的双层膜的方法。
背景技术
过程工业作为国民经济发展的支柱产业为社会发展提供基础物质保障。过程工业中的物 料分离纯化过程占据了巨大的能源消耗，同时伴随着大量的固体、液体、气体废弃物的排放。 膜分离技术作为新兴的分离技术兼具能耗低、分离精度高、环境友好等优势，将其与传统分 离纯化工艺耦合可以实现技术革新与产业升级以淘汰落后产能、降低环境污染。膜分离技术 已经在石化、食品、医药、水处理等诸多领域展现了巨大的应用价值和社会经济效益。
分离膜作为膜分离技术的核心，按照膜构型主要分为整体非对称结构膜和复合膜两种。 整体非对称结构膜通常由相转化法制备，其制备工艺简洁有利于过程放大。但受限于膜的选 择分离层和支撑层由同种聚合物材料整体相转化的制备方法，整体非对称膜的分离性能通常 较低。相比于整体非对称膜，复合膜由于各层结构、性质可以独立设计从而获得更优的分离 性能。然而，传统复合膜通常需要多步骤的制备过程，造成生产周期长，试剂消耗多，生产 设备投资大等问题。
由共刮涂或共挤出技术制备的双层膜结合了整体非对称膜和复合膜的优势，具有简洁的 一步制备的工艺方法同时兼备各层独立设计的复合膜结构形式。例如，在一步共挤出过程中， 通过使用分离性能优异的膜材料作为分离层，而使用价格低廉、机械性能优异的膜材料作为 支撑层，双层膜可以实现以最低的材料成本，获得最优化的性能。双层膜已经在超滤、纳滤、 压力延迟渗透、渗透汽化、气体分离等膜分离领域展现了广阔的应用前景。
两层聚合物的相容性差异、机械性质差异、两层铸膜液(纺丝液)成膜条件匹配问题等 诸多因素或其耦合作用均会造成双层膜的层间结合力弱，从而导致双层膜在制备或应用中发 生分层。由于双层膜的分层现象导致的分离性能降低，使用寿命缩短问题，已经成为阻碍双 层膜发展的技术瓶颈。如何优化层间结构，扩大聚合物选择范围，利用不相容聚合物制备层 间黏附性优良的双层膜已经成为双层膜发展的亟待解决的技术难题。
发明内容
本发明提供了一种通过具有特殊官能团的单体接枝改性聚合物制备黏结性优良的双层 膜，以及提供了这种膜的制备方法和改性剂的用途。
本发明的第一个方面，提供了：
一种双层聚合物分离膜，包括第一聚合物层以及第二聚合物层；在第一聚合物层中还含 有改性剂。
在一个实施方式中，所述的第一聚合物是含有亚胺结构的高分子聚合物；所述的第二聚 合物是含有羰基、羧基或者醚键的高分子聚合物。
在一个实施方式中，所述的第一聚合物是聚酰亚胺、聚醚酰亚胺、聚酰胺酰亚胺等；所 述的第二聚合物是聚醚酰亚胺、聚醚砜、聚砜等。
在一个实施方式中，所述的改性剂是是含有氟或氟甲基和氨基的氟代芳香氨类单体。
在一个实施方式中，所述的改性剂是4-氟-2-(三氟甲基)苄胺。
在一个实施方式中，所述的双层膜是平板式或者中空纤维式。
在一个实施方式中，所述的双层膜是微滤膜、超滤膜、纳滤膜、反渗透膜、渗透汽化膜、 蒸汽渗透膜、气体分离膜或者正渗透膜。
本发明的第二个方面，提供了：
上述的双层膜的制备方法，包括如下步骤：
第1步，将第一聚合物、改性剂、溶剂、添加剂配制成第一溶液；
第2步，将第二聚合物、溶剂、添加剂配制成第二溶液；
第3步，将第一溶液和第二溶液相层叠涂覆，再经过相转化后，得到分离层。
在一个实施方式中，所述的第3步中是制备平板式分离膜，包括以下步骤：采用共刮涂 技术，将第一溶液、第二溶液刮涂在支撑载体上，经过一定时间的相分离处理后使溶剂进入 凝胶浴中，固化成双层平板膜。
在一个实施方式中，所述的第3步中是制备中空纤维式，包括以下步骤：采用共挤出技 术，将第一溶液、第二溶液与芯液从纺丝喷头挤出，经过一定距离的空气间隙进入凝固浴中， 固化成双层中空纤维膜。
在一个实施方式中，第一溶液中第一聚合物、改性剂、添加剂的含量范围是：15-25％、 1-10％、0-5％。
在一个实施方式中，第二溶液中第二聚合物、添加剂的含量范围是：15-25％、0-5％。
在一个实施方式中，凝固浴是水。
在一个实施方式中，所述的溶剂是NMP，添加剂是LiCl。
本发明的第三个方面，提供了：
上述的双层聚合物膜在用于液体分离或者气体分离中的应用。
本发明的第四个方面，提供了：
上述的改性剂在用于制备双层聚合物膜的试剂中的应用。
在一个实施方式方式中，所述的试剂是用于提高第一溶液和第二溶液的高分子间的相互 渗透性，提高两层聚合物之间的结合力。
附图说明
图1是本发明制备得到的双层膜的示意图。
图2是制备得到的FTB结合
膜的ATR-FTIR光谱。
图3是双层膜的形态。顶层分别为：(a)区域是纯
(b)区域是2wt％添加量的FTB-245 
(c)区域是4wt％添加量的
(d)区域是6wt％添加量的
底层 为Ultem。
图4是不同含量的4-氟-2-(三氟甲基)苄胺接枝改性P84聚酰亚胺/Ultem聚醚酰亚胺双层中空 纤维膜的断面形貌图。
图5是上下层铸膜液的浊点线。
图6是相变过程的光学显微镜观察。(a)区域是纯
涂膜溶液；(b)区域是3wt％
涂膜溶液；(c)区域是6wt％
涂膜溶液。
图7是聚合物之间的相容性计算结果。其中，(a)区域显示的是FTB-接枝的
和
之间的溶解度参数差；(b)区域显示的是
膜表面的表面能和极化率。
图8是由(1)
和
共混物、(2)
和
组成的聚合物共混物的红外 光谱。
图9是三种液体在
膜表面上的接触角。
图10是用于说明上层和下层聚合物之间的分子间相互作用，其中，(a)区域是
and 
(b)区域是FTB-接枝的
和
图11是聚合物混合物的相行为，其中，(a)区域是纯
和
混合溶液；(b)区域是 
和
混合溶液。
图12是用于说明聚合物溶液的相行为。其中，(a)纯
and
混合溶液；(b)区域 是纯
和
混合溶液。
图13是双层膜界面区的形貌。
图14是不同FTB掺入量的双层中空纤维NF膜的水分离性能：(a)区域是纯水渗透性；(b) 区域是不同单盐的截留率；4wt％FTB掺入双层中空纤维膜的溶剂分离性能：(c)区域是四环 素溶液的紫外可见吸收光谱；(d)区域是维生素B12溶液的紫外-可见吸收光谱。
图15是交联的原始
双层中空纤维膜在DMF浸泡的SEM照片。
具体实施方式
本发明提出一种通过具有特殊官能团的单体改性聚合物制备层间黏结性优良的双层膜的 方法。本发明通过在双层膜制备过程中，向铸膜液或纺丝液中添加具有活性基团和特征基团 的改性单体，利用单体的活性基团与铸膜液或纺丝液中的聚合物发生接枝反应、利用单体的 特征基团增强与其他聚合物的分子间相互作用，以提高聚合物之间的相容性，制备界面黏结 性优良的双层膜。该方法同时适用于双层平板膜和双层中空纤维膜的制备，并且可以实现在 温和的制备条件下制备界面处具有互相贯穿结构的双层膜。界面处的互相贯穿的结构使得制 备的双层膜具有优良的层间黏结性，同时具有更低的传质阻力。该制备方法具有一定的普适 性，能够拓展制备双层膜的聚合物的选择范围，并拓展双层膜的应用领域。
示意图1说明：
传统制备双层膜的方法，由于聚合物之间相容性差异，或者成膜过程中参数匹配问题， 制备的双层膜的两层界面处结合力弱(界面处高分子不易于互相渗透)，易于分层。
本方法，在一层聚合物层中的高分子(如上层)接枝改性单体，提高了两层聚合物的相 容性、分子间相互作用增强，从而导致两层界面处高分子相互渗透，形成黏附性优良的双层 膜。
本发明中，对于上下层聚合物(其并不是指空间意义的上下关系，也可以定义为第一聚 合物层和第二聚合物层，只是用于定义其相互层叠的空间位置关系)。
对于第一聚合物，基于本发明的技术构思，应当是含有亚胺结构的高分子聚合物，如聚 酰亚胺、聚醚酰亚胺、聚酰胺酰亚胺等；对于第二聚合物，应当是含有羰基、羧基或者醚键 的高分子聚合物，例如：聚醚酰亚胺、聚醚砜、聚砜等。在此基础上，采用的改性剂应当是 含有氟或氟甲基和氨基的氟代芳香氨类单体。另一方面，改性剂的加入后可以改善第一聚合 物和第二聚合物之间的相容性，增强与第二聚合物中含羧基和醚的分子间的相互作用，提高 两种聚合物之间的相容和渗透性，由上述两个原因导致双层膜成膜过程中，界面处高分子相 互扩散增强。界面处高分子相互扩散，贯穿，使得双层膜层间黏附性优良。
在以下的实施例中，如通过4-氟-2-(三氟甲基)苄胺接枝改性聚酰亚胺，可以制备层间黏 附性优良的聚酰亚胺/聚醚酰亚胺双层膜，也可以制备层间黏附性优良的聚酰亚胺/聚醚砜双层 膜。
例如，可以采用如下原料：
聚合物A：
(聚酰亚胺)
聚合物B：
(聚醚酰亚胺)
改性剂：4-氟-2-(三氟甲基)苄胺(FTB)
其分子式如下所示：
4-Fluoro-2-(trifluoromethyl)benzylamine
FTB与P84的交联接枝过程如下所示：
基于以上的过程，本发明中的双层膜，是指通过同步的方式依次将两层聚合物的原料进 行施加，最终形成由第一聚合物和第二聚合物相层叠的双层膜。这里的双层膜的结构，可以 是指平板状的，也可以是指中空纤维状的。当平板状时，是通过两种聚合物的溶液相叠地刮 涂方式在支撑材料上进行涂膜，相转化后获得双层膜；如果采用中空纤维状时，可以采用共 挤出的方式通过纺丝头压出，并且在纺丝头的内部压出芯液，再经过凝固浴固化后，得到双 层的中空纤维膜。
更具体地说，其制备步骤如下：
平板膜的制备过程是：
步骤一，铸膜液(纺丝液)配制：
铸膜液(纺丝液)A：将第一高分子聚合物与改性剂、溶剂、添加剂按一定配比混合均 匀，配制成铸膜液(纺丝液)A。
铸膜液(纺丝液)B：将第二高分子聚合物与溶剂、添加剂按一定比例混合均匀，配制 成铸膜液(纺丝液)B。
步骤二，刮涂(纺制)双层膜：
采用共刮涂技术，将脱泡后的铸膜液A、B刮涂在支撑载体上，经过一定时间的相分离 处理后使溶剂进入凝胶浴中，固化成双层平板膜。
中空纤维膜的制备过程是：
采用共挤出技术，将脱泡后的纺丝液A、B与芯液从纺丝喷头挤出，经过一定距离的空 气间隙进入凝胶浴中，固化成双层中空纤维膜。
以下实验中所采用的材料
采用
聚酰亚胺(HP Polymer GmbH)作为双层膜的选择层材料。采用SABIC提供 的
1000聚醚酰胺作为支撑层的聚合物材料。以N-甲基-2-吡咯烷酮(NMP，99％，Macklin)为溶剂，四氢呋喃(THF，99％，国药化学试剂股份有限公司)为挥发性助溶剂， 在选择性层的溶液中。使用4-氟-2-(三氟甲基)苄胺(FTB，>99％，Leyan)对
聚酰亚 胺进行改性。以氯化锂(LiCl，>99％，阿拉丁)和二氧化硅(SiO2，>99.8％，Maclin)作为 载体层铸膜溶液中的添加剂。采用1,6-己二胺(HDA，99％，国药化学试剂有限公司)交联 双层膜。将从国药化学试剂有限公司购得的硫酸钠(Na2SO4，99％)、氯化钠(NaCl，99％)、 硫酸镁(MgSO4，99％)、氯化镁(MgCl2，99％)溶解于水溶液中，测试纳滤性能。将从阿 拉丁中提取的四环素(Mw:444.435Da)和维生素B12(Mw:1355.37Da)溶于甲醇中，测试其 耐溶剂纳滤性能。
铸膜液配制，测定铸膜液浊点，粘度，相分离行为
在室温下，用滴定法测定了添加FTB的
溶液和
溶液的浊点。在玻璃瓶中制 备了均匀的铸膜溶液，并在滴定实验中保持搅拌一致。将小滴水分批加入均匀的溶液中，直 到溶液变浑浊并在搅拌下保持24小时以上。计算了添加水的总量。用Brookfield粘度计 (DV2T)测定了不同铸膜溶液的粘度。在剪切速率为10s-1时获得粘度。
用偏光显微镜(PLM，Olympus BX53，日本)观察了掺入一定量FTB的
铸膜溶液及其与
铸膜溶液的相转变过程，并用CDD相机进行了记录。详细步骤可以参阅文献(T.Z.Jia,J.P.Lu,X.Y.Cheng,Q.C.Xia,X.L.Cao,Y.Wang,W.Xing,S.P.Sun,Surfaceenriched sulfonated polyarylene ether benzonitrile(SPEB)that enhances heavymetal removal from polyacrylonitrile(PAN)thin-film composite nanofiltrationmembranes,J.Membr.Sci.623 580 (2019)214-223.)。
制备双层平板膜和双层中空纤维膜
加入一定量FTB单体的
铸膜溶液和
铸膜溶液使用耦合刮刀在玻璃板上刮 涂，然后浸入水混凝剂浴中，以相转化。
具体的操作步骤如下：
将高分子聚合物P84聚酰亚胺和Ultem聚醚酰亚胺置于90℃真空干燥箱中12小时，去 除水气。
将P84聚酰亚胺高分子溶解于NMP溶剂中，磁力搅拌24小时至形成均匀溶液。向高分 子溶液中加入4-氟-2-(三氟甲基)苄胺改性剂，室温下，磁力搅拌24小时至形成均匀铸膜液A。
将Ultem聚醚酰亚胺高分子和LiCl添加剂溶解于NMP溶剂中，水浴加热70℃，磁力搅 拌24小时至形成均匀铸膜液B。
将铸膜液A，B静置12小时，进行脱泡。
采用相转化法和共刮涂(co-casting)技术，调整高分子铸膜液B的刮刀高度为150μm, 高分子铸膜液A的刮刀高度为200μm，将高分子铸膜液A，B刮涂于载体(玻璃板或者无纺布)上，将其浸入凝胶浴(纯水)中，铸膜液固化成双层平板膜。
采用干-湿法纺丝和共挤出(co-extrusion)技术，利用注射泵将高分子铸膜液A，B和芯 液分别从三孔喷丝头挤出。初生纤维经过一段空气间隙后，浸入凝胶浴(水)中固化双层中 空纤维膜。固化后的中空纤维膜丝经收丝装置收集后，浸入纯水中2天，置换溶剂。然后将 膜丝浸泡30％甘油水溶液中2天后，空气中晾干。
双层平板膜的详细制备过程也可以参见(Q.C.Xia,J.Wang,X.Wang,B.Z.Chen,J.L.Guo, T.Z.Jia,S.P.Sun,A hydrophilicity 598 gradient control mechanism forfabricating delamination-free dual-layer membranes,J.Membr.599Sci.539(2017)392-402)。
表1总结了详细的涂料成分及其粘度。
表1
利用三孔喷丝头，采用干喷湿纺和共挤出技术制备了双层中空膜。两台ISCO注射泵同 时向喷丝板内和外喷液，液相色谱泵同时向喷丝板内喷液。共挤出的涂料在进入水混凝剂之 前经历了气隙。通过卷取滚筒收集沉淀的中空纤维。用自来水将初生中空纤维漂洗2天，去 除残留溶剂。将部分用于模块制造的中空纤维浸入40wt％甘油水溶液中2天，然后在环境空 气中干燥。另一种中空纤维采用溶剂交换法，包括三次正己烷和三次甲醇，以消除表面张力。
膜表征
采用傅立叶变换红外光谱(FTIR)分析了
顶层与一定量的FTB单体结合后的化学 变化。使用FTIR光谱仪(Thermo Scientific，Nicolet iS50)在400–4000cm-1范围内应用衰 减全反射(ATR)模式，每个样品共64次扫描。为了进一步量化
聚酰亚胺上FTB的含 量，使用X射线光电子能谱(XPS，Escalab250Xi，Thermo Scientific)进行元素分析。
采用场发射扫描电镜(FESEM)、日立S4800对双层平板膜的形貌进行了观察。采用扫描电 镜(SEM)、日立TM3000对双层中空纤维膜的截面形貌进行了观察。在FESEM或SEM分析之前，样品在液氮中破碎并用金溅射。
利用FTIR和XPS研究了FTB单体与
聚酰亚胺在顶层铸膜溶液中的接枝反应。1780、 1718和1360cm-1处的酰亚胺带的信号强度逐渐衰减，而1534cm-1处的酰胺带随着
溶液 中FTB单体含量的逐渐增加而增强(图2)，这表明
中的酰亚胺基与FTB中的胺反应并 形成酰胺基。随着FTB单体添加量的增加，XPS检测到的1317cm-1处的三氟甲基带(图2) 和F/O原子比随之增加(表2)，进一步验证了FTB在P84聚合物链上的成功掺入。FTB单体与
聚酰亚胺之间反应机理如前文所示。FTB接枝改性
表示为FTB-P84。每个 重复单元包含一个FTB单体的
表示为S-FTB-P84，每个重复单元包含两个FTB单 体的
表示为D-FTB-P84。FTB单体的加入在
聚合物链上引入了酰胺和三氟甲基单元，可作为质子给体和受体并形成与含羰基聚合物的分子间相互作用。说明通过4-氟-2-(三氟甲基)苄胺接枝改性，P84聚酰亚胺的亚胺键特征峰减弱，酰胺键特征峰出现并增强， 同时出现了氟甲基特征峰。证明了4-氟-2-(三氟甲基)苄胺改性剂成功接枝到P84聚酰亚胺高 分子链上，并引入了氟甲基，酰胺基团。
表2 制备得到的P84膜的表层XPS元素分析结果
含有一定量FTB的
溶液与
溶液使用耦合浇铸刀在玻璃板上共刮涂。然后在室 温下将膜浸入混凝浴中，进行相转化。图3说明了在顶层铸膜溶液中添加不同FTB制备的双 层膜的形态演变。当使用未添加FTB单体的纯
铸膜溶液作为顶层铸膜溶液时，在共铸 后的水中凝固过程中，顶层
直接从底层
分离(图3的(a)区域)。在顶层溶液 中加入2wt％的FTB单体，可使双层膜在凝固过程中获得宏观粘附。然而，当在液氮中断裂 时，双层膜轻微分层(图3的(b)区域)。进一步增加顶层溶液中的FTB单体含量，可以无分层的界面区域(图3(的c)区域，(d)区域)。说明未添加的4-氟-2-(三氟甲基)苄胺改性 剂的双层膜，上层P84聚酰亚胺层和下层Ultem聚醚酰亚胺层直接剥离分层。随着4-氟-2-(三氟甲基)苄胺改性剂的加入，双层膜界面处黏附性逐渐增强，当添加一定量的的4-氟-2-(三氟 甲基)苄胺接枝改性P84聚酰亚胺后，双层膜上下层实现了优良的黏附性。
可以看出，随着FTB单体在
聚酰亚胺溶液中的掺入量逐渐增加，可以实现从分层 到部分附着的连续形态转变，并进一步实现双层膜的粘附。解决双层膜脱层问题的温和而有 效的方法显示出良好的应用前景。
将所阐述的双层平板膜的制备方法成功地移植到采用干喷湿纺和共挤出技术制备双层中 空纤维纳滤膜上。详细的纺丝条件见表3。
表3
随着FTB添加量的逐渐增加，可以观察到从分层到轻微附着和进一步粘附的类似形态转 变(图4)。外层约为5μm，大部分为海绵结构，而内部
层约为200μm，大部分为长指状大孔隙。说明未添加的4-氟-2-(三氟甲基)苄胺改性剂的双层膜图4的(a)区域所示，外层P84聚酰亚胺层从内层Ultem聚醚酰亚胺层直接剥离。随着4-氟-2-(三氟甲基)苄胺改性 剂的加入，双层膜界面处黏附性逐渐增强，如图4的(b)区域所示。当添加一定量的的4-氟-2-(三氟甲基)苄胺接枝改性P84聚酰亚胺后，双层膜内外层实现了优良的黏附性如图2的 (c)(d)区域。
FTB接枝改性对铸膜液的热力学性质和成膜动力学影响
聚合物分子的互穿可在双层膜的界面区域形成互穿网络结构，从而使双层膜具有坚固的 完整性和较低的转移阻力。铸膜铸膜
测量了
和
铸膜铸膜溶液的浊点曲线，如图5所示。
底层溶液的 浊点曲线非常接近聚合物溶剂轴，表明对水的耐受性非常有限。与
溶液相比，纯
溶液的浊点曲线与聚合物溶剂轴之间的距离要大得多。因此，与
铸膜溶液相比，纯 
铸膜溶液的相转化速度要慢得多。随着
溶液中FTB单体含量的增加，浊点曲线向 聚合物-溶剂轴相反方向移动。因此，上下层溶解液的浊点曲线之间的距离增大，说明上下层 降水速率差异较大。顶层铸膜溶液的逐步延迟沉淀速率可为顶层聚合物与底层聚合物相互渗 透提供更多停留时间，这是促进双层粘合的一个因素。
通过显微镜进一步观察了相转化过程(图6)。将一小滴溶液滴在玻璃载玻片上，并用玻 璃罩盖住。铸膜铸膜溶液与非溶剂(水)接触后，在水-铸膜液界面发生溶剂与非溶剂的交换。 当水的侵入超过液-液分离的临界浓度时，聚合物稀相核形成并聚结。
涂膜溶液中FTB 单体含量的增加不会显著改变指状大孔的生长速度。因此，随着顶层铸膜铸膜溶液中FTB单 体添加量的增加，水从顶层铸膜溶液渗透到界面区域的速度不会减慢。从上述表征可以明显 看出，
铸膜的热力学在为
双层膜界面区域的粘附提供先决条件 方面起着更重要的作用。
FTB接枝改性对双层膜界面处高分子相互渗透的影响
从本质上讲，双层膜的粘附起源于聚合物分子的相互渗透，即聚合物分子或链段的自发 混合，当铸膜铸膜溶液被共铸或共挤出时而在界面处相遇时，聚合物分子的互穿性是由混合 吉布斯自由能(ΔGM/RT)在热力学上决定的，可以用下面的方程来描述：
式(16)中，ФA、Ф(B)和NA(NB)分别表示聚合物A(B)的体积分数和聚合度， 而χ定义为聚合物-聚合物相互作用参数。ΔGH/RT项反映了聚合物之间特定的分子间相互作 用对混合自由能的贡献。上式给出了聚合物分子自发混合的两个主要因素：(1)聚合物之间的相互相对亲和力，可以用相互作用参数或溶解度参数来描述；(2)聚合物之间的特定分子间相互作用，如氢键。
溶解度参数反映了相互作用力的性质和大小，体现了“相似相溶”的原则。聚合物对之 间的溶解度参数差异很小，表明它们之间具有更好的相互亲和力，并且可能具有更好的相容 性。纯
和
的溶解度参数组分根据它们的化学结构进行分组 计算，具体的计算过程如下：
聚合物的溶解度参数可用基团贡献法计算，这取决于组成官能团的内聚能及其在重复单 元中的摩尔体积。聚合物的总溶解度参数δtotal及其分散力分量δd、偶极子分量δp和氢键分 量δh可由下列方程求得：
表4是上式所用参数的数值。
表4
由于缺少氟基团的参数，偶极和氢键组分结合为δa，由δtotal和δd计算如下：
物质1和2混合物的溶解度参数组分i的计算方法如下：
δi，mixture＝φ1·δi，1+φ2·δi，2
式中，
和
表示物质1和2的摩尔分数。因此，可以通过如下描述的溶解度参数差计算 相互相对亲和力(RA)：
得到了不同配比的
和
混合物以及不同配比的
和
混合物的溶解度参数组分。通过溶解度参数(图7的(a)区域)评估顶层和底 层聚合物之间的相对亲和力。导出的纯
和
之间的溶解度参数差为3.34 cal1/ 2cm-3/2，这反映了聚合物对之间有限的相互相对亲和力。通过在
聚合物链上逐步加 入FTB单体，改性
和
之间的溶解度参数差从3.34降到0.27cal1/2cm-3/2，这意味 着
和
之间的亲和力显著提高。进一步提高FTB单体的比例，从
到
聚合物对之间的溶解度差再次变大。换言之，在
聚合物链上加入过量的 FTB单体可提高由大量支化基团和F原子引起的空间位阻，并阻碍改性
分子之间的相 互作用。
由于氟原子的强电负性，氟基团与
聚合物链的结合可以改变聚合物的极化率和表面 性质。接枝反应引入的酰胺基和氟基也可以作为有效的质子给体或受体，与含羧基和醚基的 聚合物形成特定的分子间相互作用。
用Lifshitz-van der Waals/酸碱(LW/AB)法计算了膜表面的表面能和极化率。根据LW/AB 法，由非极性组分γLW和酸碱性组分γAB组成的固体表面γ的表面能如下：
γ＝γLW+γAB
电子供体酸碱组分γAB可根据电子供体γ+和电子受体γ-计算，如下所示：
固液相γSL之间的界面能可计算为：
下标S表示固体，L表示液体。下标SL表示固液相界面。将上述方程与Young方程相结合，可得到如下关系：
通过获取三种不同极性液体(水、甘油和二碘甲烷)的接触角测量仪(KRUSS、DSA30) 测量的接触角数据及其表面张力参数(表5)，可以通过方程式(4)得到γLW、γ+和γ–的值。 膜表面的极化率(Pol)可进一步计算如下：
Pol＝γAB/γ
表5
随着在
上逐渐加入FTB，顶层的表面能不遵循明显的趋势，但加入FTB的
的极化率显著提高(图7的(b)区域)。聚合物分子的极化率与聚合物之间的分子相互作用 (如偶极-偶极相互作用)正相关。
和
之间的特殊分子间相互作用通过聚合 物共混物的红外透射峰的频移进一步得到验证。氟基(1317cm-1)和酰胺基(1534cm-1)的特 征峰出现在
和
的混合物中(图8的(a)(b)区域，表6)。
和 
混合物中的羰基(C＝O)和芳香醚(C-O-C)与纯
和
混合物相比频率更 高(图7的(c)(d)区域，表6)。因此，共混物中的分子间相互作用可归因于酰胺基、氟 基和羰基之间的氢键和偶极-偶极相互作用。
表6
加入和不加入FTB的
和
之间的分子化学特性和可能普遍存在的相互作用如 图10所示。
由于在纯
和
聚合物中不存在有效的质子给体基团，特定的分子间相互作用 包括纯
和
之间的π-π堆积和n-π络合物。在
聚酰亚胺链上加入FTB单体 后，酰胺基的氢可以作为质子供体，并与
的醚和羰基形成氢键。此外，来自FTB-接 枝
的甲基氟化物可能与含有
分子的羰基和醚形成强烈的相互作用。
和
之间增强的相互相对亲和力和建立的特定分子间相互作用有助于促进聚合物分子 在双层膜界面区域的相容性和渗透性。为了验证上述两个因素的作用，即进一步研究了聚合 物之间的亲和力和分子间的特殊相互作用对分子在双层膜界面区的相互渗透、聚合物共混溶 液的相行为以及双层膜界面形态的影响。
界面相的相行为转变反映了聚合物之间的相容性。为了模拟共铸过程中在界面区域遇到 的铸膜混合，将不同FTB添加量的
铸膜溶液和
铸膜铸膜溶液等效地混合。将混 合铸膜溶液搅拌24小时，然后静置24小时，然后用光学显微镜观察。如光学显微镜所观察 到的，所有的混合溶液在宏观上呈现均匀状态，而在微米尺度上有不同程度的相分离(图11)。 纯
和
的混合溶液由高度分散的相组成，如微小的液滴(图11的(a)区域)。这 可能是因为纯
和
的相容性因相互亲和力差和聚合物对之间没有特定的分子间相 互作用而受到热力学阻碍。搅拌后，
和
混合溶液形成分散相，如图12的(a) 区域所示。引入水后，靠近水界面的分散相聚集、沉淀成固体。与纯P84和Ultem混合物不 同，4wt％FTB-P84和Ultem铸膜溶液的大部分混合物由具有部分分散相的连续相组成，如图 11的(b)区域所示。由于FTB结合的P84和Ultem之间具有高度的相互亲和力和特定的分 子间相互作用，FTB-P84聚合物可作为连接P84和Ultem相的相容性，如图12的(b)区域 所示。引入水后，连续相析出，指状大孔隙通过相间生长。可以观察到相转化混合物之间的 连接性和互穿性。
为了进一步证实分子间相互亲和力和分子间相互作用对相互渗透的贡献，用扫描电镜观 察了不同FTB添加量的双层膜界面区域的形貌(图13)。在顶层的底面可以看到大的空洞， 这证明手指状的宏观空洞从顶层的主体延伸到底层。当纯
和
溶液共铸时(图13 的(a)区域)，顶层和底层聚合物之间的不相容性在热力学上阻碍了界面区域聚合物分子的 混合，导致界面相的形成受到限制。在相转变过程中，含有一定量非溶剂的表层扩展的宏观 孔洞进入界面区域。底部
层的疏水性进一步阻碍了非溶剂从顶层渗透到底层。在非溶 剂积累的诱导下，新形成的界面相发生了相转化。如图11的(a)区域所示，由不互溶 
混合物组成的界面相沉淀成具有有限连接的孤立固体。如图13的(a)区域所 示，可在底层的顶面上看到孤立且微小互穿的结构。界面处不能承受凝固过程中上下层的不 同收缩。因此，原始
双层膜之间发生分层。通过在
上加入FTB单体，聚 合物分子在界面区域的混合增强，这归因于提高了相互间的相对亲和力，并在顶层和底层之 间建立了特定的分子间相互作用。在底层的上表面上可以观察到顶层聚合物与底层聚合物的 相互渗透逐渐改善(图13的(b)，(c)，(d)区域)。此外，如图11的(b)区域所示，相转 化后由
组成的界面相显示出互穿结构，形成彼此之间的连接。界面区分子 间的互穿性增强和相转化界面相的互连结构使含FTB的
双层膜具有很强的附着 力。
由以上讨论可知，通过加入特定的官能团，可以形成特定的分子间相互作用，增强相互 亲和力，可以调节甚至跨越聚合物之间的相容性差异。界面区域聚合物分子的混合可在双层 之间形成互穿网络结构，如图1所示。基于本发明提出的理论，可以显著地扩大从固有不相 容聚合物中选择聚合物对制备无分层双层膜的范围。
过滤和截留性能
一步法制备的双层中空纤维纳滤膜在水和有机溶剂体系中进行了过滤试验。
用纯水渗透性的角度评价双层中空纤维膜的分离性能，甲醇渗透性和溶质排出采用实验 室制过滤系统。纯水和甲醇渗透样品作为时间的函数进行收集，并根据下式通过计算溶剂渗 透性(P，Lm-2h-1bar-1)：
式中，ΔV(L)是在跨膜压力Δp(bar)下，在时间段Δt(h)内收集的渗透液体积，a(m2)是有效膜面积。
分别用1000.0mg L-1的Na2SO4、NaCl、MgSO4和MgCl2水溶液进行了水体系中的溶质截 留试验。用维生素B12和四环素的50.0mg L-1甲醇溶液在溶剂体系中进行了溶质截留试验。
截留率由以下方程式计算：
式中，Cp和Cf分别表示渗透液和进料溶液中的溶质浓度。分别用电导仪(Mettler-Toledo) 和紫外可见分光光度计(AOE)测定饲料和渗透液中的盐和药物浓度。
双层中空纤维膜的纯水渗透性随着顶层铸膜铸膜铸膜溶液中FTB添加量的影响(图14 的(a)区域)。铸膜铸膜铸膜四种盐的截留顺序为Na2SO4>NaCl>MgSO4>MgCl2(图14的(b) 区域)，特别是控制FTB的加入量在4％-6％时，可以获得80％以上的对Na2SO4截留率，以及对NaCl 50％以上的截留率。将质量分数为4wt％的FTB复合双层膜进一步应用于有机溶剂 中的药物回收。在纯甲醇渗透性为3.7LMH/bar的甲醇溶液中，膜显示出99％的四环素和维 生素B12的截留率(图13的(c)(d)区域)。
耐溶剂性能测试
为进一步验证双层中空纤维膜在界面区的分子混合性，考察双层中空纤维膜在有机溶剂 中的耐受性，将制备的双层中空纤维膜与1,6-己二胺交联15h，在DMF中浸泡两周。如图15 所示，交联的原始
双层中空纤维膜在DMF浸泡后分层。交联后的4wt％
双层中空纤维膜在DMF溶剂中浸泡两周后仍然没有脱层，这表明FTB在双层界面区域的
和
分子达到了良好的混合状态，因此可以通过HDA进行化学交联。图15说明了可能的反应存在于双层膜的外层、内层和界面区域。成本低廉的双层中空纤维膜能在恶劣的溶剂中保持结构的完整性，在有机溶剂纳滤和反渗透领域具有广阔的应用 前景。
Claims (6)
1.一种双层聚合物分离膜，其特征在于，包括第一聚合物层以及第二聚合物层；在第一聚合物层中还含有改性剂；
所述的双层聚合物分离膜是纳滤膜；
所述的第一聚合物是聚酰亚胺、聚醚酰亚胺或者聚酰胺酰亚胺；所述的第二聚合物是聚醚酰亚胺、聚醚砜或者聚砜；
所述的改性剂是4-氟-2-(三氟甲基)苄胺；
所述的双层聚合物分离膜的制备方法，包括如下步骤：
第1步，将第一聚合物、改性剂、溶剂、添加剂配制成第一溶液；
第2步，将第二聚合物、溶剂、添加剂配制成第二溶液；
第3步，将第一溶液和第二溶液相层叠涂覆，再经过相转化后，得到分离层。
2.根据权利要求1所述的双层聚合物分离膜，其特征在于，所述的双层膜是平板式或者中空纤维式。
3.根据权利要求1所述的双层聚合物分离膜，其特征在于，所述的第3步中是制备平板式分离膜，包括以下步骤：采用共刮涂技术，将第一溶液、第二溶液刮涂在支撑载体上，经过一定时间的相分离处理后使溶剂进入凝胶浴中，固化成双层平板膜。
4.根据权利要求1所述的双层聚合物分离膜，其特征在于，所述的第3步中是制备中空纤维式，包括以下步骤：采用共挤出技术，将第一溶液、第二溶液与芯液从纺丝喷头挤出，经过一定距离的空气间隙进入凝固浴中，固化成双层中空纤维膜。
5.根据权利要求1所述的双层聚合物分离膜，其特征在于，凝固浴是水；所述的溶剂是NMP或者THF中的一种或者两种的混合，添加剂是LiCl。
6.权利要求1所述的双层聚合物分离膜在用于液体分离或者气体分离中的应用。