CN111635625A - 具有耐清洗耐高温湿热灭菌组合物的防护眼罩 - Google Patents
具有耐清洗耐高温湿热灭菌组合物的防护眼罩 Download PDFInfo
- Publication number
- CN111635625A CN111635625A CN202010522710.6A CN202010522710A CN111635625A CN 111635625 A CN111635625 A CN 111635625A CN 202010522710 A CN202010522710 A CN 202010522710A CN 111635625 A CN111635625 A CN 111635625A
- Authority
- CN
- China
- Prior art keywords
- protective
- temperature
- polycarbonate
- resistant
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种具有耐清洗耐高温湿热灭菌组合物的防护眼罩，该防护眼罩包括防护镜片、眼罩框和固定件，防护镜片嵌入眼罩框内，固定件将眼罩框和织带固定在一起，防护镜片由改性的聚碳酸酯组合物组成，改性的聚碳酸酯组合物包括聚碳酸酯、耐高温树脂、相容剂、抗氧剂、阻燃剂和抗菌剂；眼罩框和固定件均由改性的热塑性硫化橡胶组合物组成，改性的热塑性硫化橡胶组合物包括热塑性硫化橡胶、增韧剂、硫化剂和防老化剂；本发明采用改性的聚碳酸酯组合物和改性的热塑性硫化橡胶组合物制备防护眼罩，使得该防护眼罩具有耐高温、耐清洗、耐冲击性能好、高强度、抗菌性能好、阻燃性能好和耐老化性能等特点，具有良好的弹性、耐压缩变形性，可重复使用。
Description
技术领域
本发明属于人体防护用品技术领域，具体涉及一种具有耐清洗耐高温湿热灭菌组合物的防护眼罩。
背景技术
由于制药企业生产环境的特殊性，在洁净区内的工作人员穿戴防护眼罩每次都需要清洗灭菌消毒，这种方式容易对眼罩产生化学反应，导致对眼罩产生变形甚至损坏，给洁净区的生产区域带来安全风险。目前市场上主要防护眼罩多为普通塑料材质无法进行高温清洗灭菌，另外市场上的一些防护眼罩所使用的材质经过高温清洗湿热灭菌后，使用寿命严重缩短，导致频繁的更换报废眼罩，即浪费资源与人力物力，同时也增加了环境污染。
发明内容
针对现有技术中的不足，本发明的目的是提供一种具有耐清洗耐高温湿热灭菌组合物的防护眼罩。
为达到上述目的，本发明的解决方案是：
一种具有耐清洗耐高温湿热灭菌组合物的防护眼罩，该防护眼罩包括防护镜片、眼罩框和固定件，防护镜片嵌入眼罩框内，固定件将眼罩框和织带固定在一起。
其中，防护镜片由改性的聚碳酸酯组合物组成。
改性的聚碳酸酯组合物包括如下组分：
改性的聚碳酸酯组合物制备方法包括如下步骤：
(1)、将聚碳酸酯、耐高温树脂、相容剂、抗氧剂、阻燃剂和抗菌剂依次加入混合机中共混，得到预混物；
(2)、然后将预混物投入双螺杆挤出机中进行熔融混合并挤出造粒，得到改性的聚碳酸酯组合物。
其中，步骤(2)中，螺杆的长径比为(30-40)：1，螺杆的转速为400-500rpm。
实际上，在本发明的一种具体实施例中，聚碳酸酯为双酚A型聚碳酸酯，熔融指数为6-15g/10min。
在本发明的一种具体实施例中，耐高温树脂为ABS树脂。
在本发明的一种具体实施例中，相容剂选自聚丙烯接枝马来酸酐、苯乙烯与马来酸酐的无规共聚物中的一种以上。
在本发明的一种具体实施例中，抗氧剂选自四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯和三[2,4-二叔丁基苯基]亚磷酸酯中的一种以上。
在本发明的一种具体实施例中，阻燃剂选自聚膦酸酯、三氧化二铝和氢氧化镁中的一种以上。
在本发明的一种具体实施例中，抗菌剂选自壳聚糖和纳米二氧化钛中的一种以上。
使用特定的耐高温树脂、相容剂与聚碳酸酯配合使用，其中特定耐高温树脂大大提高了聚碳酸酯的耐热温度，使得聚碳酸酯可以应用于超高耐热领域，且结合相容剂使用，也大幅改善了聚碳酸酯的耐溶剂性能和韧性。
具体地，眼罩框和固定件均由改性的热塑性硫化橡胶组合物组成。
改性的热塑性硫化橡胶组合物包括如下组分：
改性的热塑性硫化橡胶组合物的制备方法包括如下步骤：
(1)、将热塑性硫化橡胶、增韧剂、硫化剂和防老化剂加入密炼机内混合，混合的温度为40-50℃，得到初混料；
(2)、将初混料进行硫化，硫化的温度为80℃，硫化的时间为2min，出料冷却得到改性的热塑性硫化橡胶组合物。
其中，在本发明的一种具体实施例中，增韧剂选自马来酸酐接枝线性低密度聚乙烯、甲基丙烯酸甲酯-丁二烯-苯乙烯三元共聚物中的一种以上。
在本发明的一种具体实施例中，硫化剂选自双马来酰亚胺、辛基酚醛树脂和二叔丁基过氧化异丙基苯的混合物中的一种以上。
在本发明的一种具体实施例中，防老化剂选自防老化剂4020和防老化剂RD中的一种以上。
由于采用上述方案，本发明的有益效果是：
本发明的防护镜片采用改性的聚碳酸酯组合物，眼罩框和固定件采用改性的热塑性硫化橡胶组合物制备防护眼罩，从而使得该防护眼罩具有耐高温、耐清洗、耐冲击性能好、高强度、抗菌性能好、阻燃性能好和耐老化性能等特点，进一步具有良好的弹性、耐压缩变形性，可重复使用，环保性能优良，使用范围广泛，因此可以适用于具有防液体飞溅、防菌、防污、防毒的洁净区生产环境，如制药企业等，另外也可应用于观察室、清洗室和治疗室等场所。
具体实施方式
以下结合实施例对本发明作进一步的说明。
实施例1：
本实施例的具有耐清洗耐高温湿热灭菌组合物的防护眼罩包括防护镜片、眼罩框和固定件，防护镜片嵌入眼罩框内，固定件将眼罩框和织带固定在一起。
其中，防护镜片由改性的聚碳酸酯组合物组成。
改性的聚碳酸酯组合物包括如下组分：
改性的聚碳酸酯组合物制备方法包括如下步骤：
(1)、将聚碳酸酯、耐高温树脂、相容剂、抗氧剂、阻燃剂和抗菌剂依次加入混合机中共混，混合的温度为50℃，混合的时间为6min，得到预混物；
(2)、然后将预混物投入双螺杆挤出机中进行熔融混合并挤出造粒，得到改性的聚碳酸酯组合物。
其中，步骤(2)中，螺杆的长径比为30：1，螺杆的转速为400rpm。
聚碳酸酯为双酚A型聚碳酸酯，熔融指数为6g/10min。
耐高温树脂为ABS树脂。
相容剂为聚丙烯接枝马来酸酐。
抗氧剂为四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯。
阻燃剂为聚膦酸酯。
抗菌剂为壳聚糖。
具体地，眼罩框和固定件均由改性的热塑性硫化橡胶组合物组成。
改性的热塑性硫化橡胶组合物包括如下组分：
改性的热塑性硫化橡胶组合物的制备方法包括如下步骤：
(1)、将热塑性硫化橡胶、增韧剂、硫化剂和防老化剂加入密炼机内混合，混合的温度为40℃，得到初混料；
(2)、将初混料进行硫化，硫化的温度为80℃，硫化的时间为2min，出料冷却得到改性的热塑性硫化橡胶组合物。
其中，增韧剂为马来酸酐接枝线性低密度聚乙烯。
硫化剂为双马来酰亚胺。
防老化剂为防老化剂4020。
实施例2：
本实施例的具有耐清洗耐高温湿热灭菌组合物的防护眼罩包括防护镜片、眼罩框和固定件，防护镜片嵌入眼罩框内，固定件将眼罩框和织带固定在一起。
其中，防护镜片由改性的聚碳酸酯组合物组成。
改性的聚碳酸酯组合物包括如下组分：
改性的聚碳酸酯组合物制备方法包括如下步骤：
(1)、将聚碳酸酯、耐高温树脂、相容剂、抗氧剂、阻燃剂和抗菌剂依次加入混合机中共混，混合的温度为40℃，混合的时间为6min，得到预混物；
(2)、然后将预混物投入双螺杆挤出机中进行熔融混合并挤出造粒，得到改性的聚碳酸酯组合物。
其中，步骤(2)中，螺杆的长径比为40：1，螺杆的转速为500rpm。
聚碳酸酯为双酚A型聚碳酸酯，熔融指数为15g/10min。
耐高温树脂为ABS树脂。
相容剂为苯乙烯与马来酸酐的无规共聚物。
抗氧剂为三[2,4-二叔丁基苯基]亚磷酸酯。
阻燃剂为氢氧化镁。
抗菌剂为纳米二氧化钛。
具体地，眼罩框和固定件均由改性的热塑性硫化橡胶组合物组成。
改性的热塑性硫化橡胶组合物包括如下组分：
改性的热塑性硫化橡胶组合物的制备方法包括如下步骤：
(1)、将热塑性硫化橡胶、增韧剂、硫化剂和防老化剂加入密炼机内混合，混合的温度为50℃，得到初混料；
(2)、将初混料进行硫化，硫化的温度为70℃，硫化的时间为2min，出料冷却得到改性的热塑性硫化橡胶组合物。
其中，增韧剂为甲基丙烯酸甲酯-丁二烯-苯乙烯三元共聚物。
硫化剂为辛基酚醛树脂和二叔丁基过氧化异丙基苯的混合物。
防老化剂为防老化剂RD。
实施例3：
本实施例的具有耐清洗耐高温湿热灭菌组合物的防护眼罩包括防护镜片、眼罩框和固定件，防护镜片嵌入眼罩框内，固定件将眼罩框和织带固定在一起。
其中，防护镜片由改性的聚碳酸酯组合物组成。
改性的聚碳酸酯组合物包括如下组分：
改性的聚碳酸酯组合物制备方法包括如下步骤：
(1)、将聚碳酸酯、耐高温树脂、相容剂、抗氧剂、阻燃剂和抗菌剂依次加入混合机中共混，混合的温度为40℃，混合的时间为6min，得到预混物；
(2)、然后将预混物投入双螺杆挤出机中进行熔融混合并挤出造粒，得到改性的聚碳酸酯组合物。
其中，步骤(2)中，螺杆的长径比为30：1，螺杆的转速为400rpm。
聚碳酸酯为双酚A型聚碳酸酯，熔融指数为9g/10min。
耐高温树脂为ABS树脂。
相容剂为苯乙烯与马来酸酐的无规共聚物。
抗氧剂为四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯。
阻燃剂为三氧化二铝。
抗菌剂为壳聚糖。
具体地，眼罩框和固定件均由改性的热塑性硫化橡胶组合物组成。
改性的热塑性硫化橡胶组合物包括如下组分：
改性的热塑性硫化橡胶组合物的制备方法包括如下步骤：
(1)、将热塑性硫化橡胶、增韧剂、硫化剂和防老化剂加入密炼机内混合，混合的温度为50℃，得到初混料；
(2)、将初混料进行硫化，硫化的温度为80℃，硫化的时间为2min，出料冷却得到改性的热塑性硫化橡胶组合物。
其中，增韧剂为马来酸酐接枝线性低密度聚乙烯。
硫化剂为辛基酚醛树脂和二叔丁基过氧化异丙基苯的混合物。
防老化剂为防老化剂4020。
对比例1：
本对比例的防护眼罩包括防护镜片、眼罩框和固定件，防护镜片嵌入眼罩框内，固定件将眼罩框和织带固定在一起。
其中，防护镜片由聚碳酸酯组合物组成。
聚碳酸酯组合物包括如下组分：
聚碳酸酯 50份，
相容剂 6份，
抗氧剂 0.01份。
聚碳酸酯组合物制备方法包括如下步骤：
(1)、将聚碳酸酯、相容剂和抗氧剂依次加入混合机中共混，混合的温度为50℃，混合的时间为6min，得到预混物；
(2)、然后将预混物投入双螺杆挤出机中进行熔融混合并挤出造粒，得到聚碳酸酯组合物。
其中，步骤(2)中，螺杆的长径比为30：1，螺杆的转速为400rpm。
聚碳酸酯为双酚A型聚碳酸酯，熔融指数为6g/10min。
相容剂为苯乙烯与马来酸酐的无规共聚物。
抗氧剂为三[2,4-二叔丁基苯基]亚磷酸酯。
具体地，眼罩框和固定件均由热塑性硫化橡胶组合物组成。
热塑性硫化橡胶组合物包括如下组分：
热塑性硫化橡胶 45份，
增韧剂 0.3份，
硫化剂 0.1份。
热塑性硫化橡胶组合物的制备方法包括如下步骤：
(1)、将热塑性硫化橡胶、增韧剂和硫化剂加入密炼机内混合，混合的温度为40℃，得到初混料；
(2)、将初混料进行硫化，硫化的温度为80℃，硫化的时间为2min，出料冷却得到热塑性硫化橡胶组合物。
其中，增韧剂为马来酸酐接枝线性低密度聚乙烯。
硫化剂为双马来酰亚胺。
对比例2：
本对比例的防护眼罩包括防护镜片、眼罩框和固定件，防护镜片嵌入眼罩框内，固定件将眼罩框和织带固定在一起。
其中，防护镜片由聚碳酸酯组合物组成。
聚碳酸酯组合物包括如下组分：
聚碳酸酯 65份，
相容剂 10份。
聚碳酸酯组合物制备方法包括如下步骤：
(1)、将聚碳酸酯和相容剂依次加入混合机中共混，混合的温度为50℃，混合的时间为6min，得到预混物；
(2)、然后将预混物投入双螺杆挤出机中进行熔融混合并挤出造粒，得到聚碳酸酯组合物。
其中，步骤(2)中，螺杆的长径比为40：1，螺杆的转速为500rpm。
实际上，聚碳酸酯为双酚A型聚碳酸酯，熔融指数为6g/10min。
相容剂为聚丙烯接枝马来酸酐。
具体地，眼罩框和固定件均由热塑性硫化橡胶组合物组成。
热塑性硫化橡胶组合物包括如下组分：
热塑性硫化橡胶 56份，
增韧剂 0.7份。
热塑性硫化橡胶组合物的制备方法包括如下步骤：
(1)、将热塑性硫化橡胶和增韧剂加入密炼机内混合，混合的温度为50℃，得到初混料；
(2)、将初混料进行硫化，硫化的温度为70℃，硫化的时间为2min，出料冷却得到热塑性硫化橡胶组合物。
其中，增韧剂为甲基丙烯酸甲酯-丁二烯-苯乙烯三元共聚物。
将上述实施例和对比例的防护眼罩进行如下测试：
表1实施例和对比例中防护眼罩的性能数据
从上表可知，本发明的防护镜片采用改性的聚碳酸酯组合物，眼罩框和固定件采用改性的热塑性硫化橡胶组合物制备防护眼罩，从而使得该防护眼罩具有耐高温、耐清洗、耐冲击性能好、高强度、抗菌性能好、阻燃性能好和耐老化性能等特点，进一步具有良好的弹性、耐压缩变形性，可重复使用，环保性能优良，使用范围广泛，因此可以适用于具有防液体飞溅、防菌、防污、防毒的洁净区生产环境，如制药企业等，另外也可应用于观察室、清洗室和治疗室等场所。
将上述实施例的防护眼罩进行测试，得到如下性能：
镜片参数：
球镜度：+0.02D～+0.06D
柱镜度:+0.00D～+0.08D
水平棱镜度:0.12D～0.16D
垂直棱镜度:0.00D～0.01D
可见透光射比:89.0％
湿热灭菌湿度可达121℃
反复高温(121℃、30min)灭菌3次，灭菌后，眼镜不变形，不改变镜片透射比，以及光学参数。
高温(121℃、24h)灭菌10次，灭菌后，眼镜不变形，不改变镜片透射比，以及光学参数。
上述对实施例的描述是为了便于该技术领域的普通技术人员能理解和使用本发明。熟悉本领域技术人员显然可以容易的对这些实施例做出各种修改，并把在此说明的一般原理应用到其他实施例中，而不必经过创造性的劳动。因此，本发明不限于上述实施例。本领域技术人员根据本发明的原理，不脱离本发明的范畴所做出的改进和修改都应该在本发明的保护范围之内。
Claims (10)
1.一种具有耐清洗耐高温湿热灭菌组合物的防护眼罩，其特征在于：该防护眼罩包括防护镜片、眼罩框和固定件，所述防护镜片嵌入所述眼罩框内，所述固定件将所述眼罩框和织带固定在一起；
所述防护镜片由改性的聚碳酸酯组合物组成；
所述改性的聚碳酸酯组合物包括如下组分：
所述眼罩框和固定件均由改性的热塑性硫化橡胶组合物组成；
所述改性的热塑性硫化橡胶组合物包括如下组分：
2.根据权利要求1所述的防护眼罩，其特征在于：所述聚碳酸酯为双酚A型聚碳酸酯，熔融指数为6-15g/10min。
3.根据权利要求1所述的防护眼罩，其特征在于：所述耐高温树脂为ABS树脂。
4.根据权利要求1所述的防护眼罩，其特征在于：所述相容剂选自聚丙烯接枝马来酸酐、苯乙烯与马来酸酐的无规共聚物中的一种以上。
5.根据权利要求1所述的防护眼罩，其特征在于：所述抗氧剂选自四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯和三[2,4-二叔丁基苯基]亚磷酸酯中的一种以上。
6.根据权利要求1所述的防护眼罩，其特征在于：所述阻燃剂选自聚膦酸酯、三氧化二铝和氢氧化镁中的一种以上。
7.根据权利要求1所述的防护眼罩，其特征在于：所述抗菌剂选自壳聚糖和纳米二氧化钛中的一种以上。
8.根据权利要求1所述的防护眼罩，其特征在于：所述增韧剂选自马来酸酐接枝线性低密度聚乙烯、甲基丙烯酸甲酯-丁二烯-苯乙烯三元共聚物中的一种以上。
9.根据权利要求1所述的防护眼罩，其特征在于：所述硫化剂选自双马来酰亚胺、辛基酚醛树脂和二叔丁基过氧化异丙基苯的混合物中的一种以上。
10.根据权利要求1所述的防护眼罩，其特征在于：所述防老化剂选自防老化剂4020和防老化剂RD中的一种以上。