CN111495606A - 一种钛铁矿浮选捕收剂 - Google Patents
一种钛铁矿浮选捕收剂 Download PDFInfo
- Publication number
- CN111495606A CN111495606A CN202010456473.8A CN202010456473A CN111495606A CN 111495606 A CN111495606 A CN 111495606A CN 202010456473 A CN202010456473 A CN 202010456473A CN 111495606 A CN111495606 A CN 111495606A
- Authority
- CN
- China
- Prior art keywords
- component
- ilmenite
- water
- flotation collector
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种浮选捕收剂，尤其是钛铁矿浮选捕收剂及其制备方法，属于矿物浮选捕收技术领域。钛铁矿捕浮选收剂，原料包含二丁基二硫代磷酸铵、油酸钠、乙二胺四乙酸二钠盐、马来酸盐、水玻璃，其他均为水；并经过以下方法配制而成：按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h‑1.5h，此为组分A，在50℃‑60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h‑4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂；所述钛铁矿浮选捕收剂，在有效的保证钛铁矿的选矿效果的同时，成本低廉，安全环保，各组分协同后能有效的提高钛铁矿精品品位。
Description
技术领域
本发明涉及一种浮选捕收剂，尤其是一种钛铁矿浮选捕收剂及其制备方法，本发明属于矿物浮选捕收剂技术领域。
背景技术
浮选是利用矿物表面疏水 - 亲水性的差别，对矿物进行加工的一种方法。利用矿物表面的物理化学性质差异选别矿物颗粒的过程，旧称浮游选矿，是应用最广泛的选矿方法。几乎所有的矿石都可用浮选分选。如金矿、银矿、方铅矿、闪锌矿、黄铜矿、辉铜矿、辉钼矿、镍黄铁矿等硫化矿物，孔雀石、白铅矿、菱锌矿、异极矿和赤铁矿、锡石、黑钨矿、钛铁矿、绿柱石、锂辉石以及稀土金属矿物、铀矿等氧化矿物的选别。石墨、硫磺、金刚石、石英、云母、长石等非金属矿物和硅酸盐矿物及萤石、磷灰石、重晶石等非金属盐类矿物和钾盐、岩盐等可溶性盐类矿物的选别。虽然利用矿物的天然疏水性也可以进行矿石的选别，但通常都使用浮选药剂以增大或减小矿物表面的疏水性，调整控制矿物的浮选行为。
钛铁矿是铁和钛的氧化物矿物，是提炼钛的主要矿石。中国四川攀枝花铁矿中，钛铁矿分布于磁铁矿颗粒之间或裂理中，并形成大型矿床。钛铁矿的化学成分与形成条件有关。高效的选取日益贫细化的钛铁矿是选矿中的主要难题，但现有的捕收剂主要以油酸和脂肪酸为主要原料，例如 MOS 捕收剂，其主要成分是油酸，还含有毒的砷成分，易造成环境污染，同时具有成本高和设备腐蚀等问题。
发明内容
本发明的目的在于针对现有技术中存在的不足，如选择性不高、环境污染和分散性不好等缺陷，寻找一种适合该矿石的矿物浮选捕收剂。在油酸钠中添加二丁基二硫代磷酸铵、乙二胺四乙酸二钠盐、马来酸盐和水玻璃，经过充分混合均匀，有利于油酸钠离子在矿浆中的分散，二丁基二硫代磷酸铵和油酸钠的协同作用，使得在浮选效果更好，乙二胺四乙酸二钠盐的加入，使得该捕收剂的抗硬度能力增强，有利于精选。
本发明的另一个目的在于提供了一种钛铁矿浮选捕收剂的制备方法，该制备方法流程简单，操作易于控制，原料来源广泛，成本低廉，安全环保，产品回收率高且易于实现工业化生产。
本发明为实现上述目的采取如下技术方案，一种钛铁矿浮选捕收剂，其特征在于该钛铁矿浮选捕收剂含有二丁基二硫代磷酸铵、油酸钠、乙二胺四乙酸二钠盐、马来酸盐、水玻璃，其他均为水。
进一步优选，所述的钛铁矿浮选捕收剂是由以下重量百分比的原料制备而成。
1.二丁基二硫代磷酸铵重量百分比为2%-9%。
2.油酸钠的重量百分比为35%-55%。
3.乙二胺四乙酸二钠盐的重量百分比为25%-45%。
4.马来酸盐的重量百分比为13%-20%。
5.水玻璃的添加量的重量百分比为0.5%-2%。
其他均为水。
进一步优选，所述的钛铁矿浮选捕收剂是由以下重量百分比的原料制备而成。
二丁基二硫代磷酸铵重量百分比为3%-4%。
油酸钠的重量百分比为45%-49%。
乙二胺四乙酸二钠盐的重量百分比为19%-23%。
马来酸盐的重量百分比为16%-18%。
水玻璃的添加量的重量百分比为1%-2%。
水的添加量的重量百分比为9%-11%。
本发明所述的钛铁矿浮选捕收剂的制备方法，其特征在于步骤为：按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
本发明的所述的钛铁矿浮选捕收剂原料安全无毒，在油酸钠中添加二丁基二硫代磷酸铵、乙二胺四乙酸二钠盐、马来酸盐和水玻璃，经过充分混合均匀，有利于油酸钠离子在矿浆中的分散，二丁基二硫代磷酸铵和油酸钠的协同作用，使得在浮选效果更好，乙二胺四乙酸二钠盐的加入，使得该捕收剂的抗硬度能力增强，有利于精选，提高精矿品位。
本发明的所述的钛铁矿浮选捕收剂区别于传统的浮选剂，不含有重金属砷等，安全环保。
本发明的所述的钛铁矿浮选捕收剂制备方法简单，操作易于控制，成本低廉且非常适合余工业化生产。
本发明的所述的钛铁矿浮选捕收剂在使用过程中具有极好的水溶性，有利于药剂在矿浆中的溶解，方便使用。
具体实施方式
本说明书中公开的所有特征，或公开的所有方法或过程中的步骤，除了互相排斥的特征或步骤外，均可以以任何方式组合。
本说明书中公开的任一特征，除非特别叙述，均可被其他等效或具有类似的替代特征加以替换。即，除非特别叙述，每个特征只是一系列等效或类似特征中的一个例子而已。
实施例1
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵4%，油酸钠45%，二胺四乙酸二钠盐23%，马来酸盐16%，水玻璃1%，水11%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.21%，回收率为81.91%的良好指标。
实施例2
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵4%，油酸钠47%，二胺四乙酸二钠盐21%，马来酸盐16%，水玻璃1%，水11%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.54%，回收率为82.33%的良好指标。
实施例3
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵4%，油酸钠49%，二胺四乙酸二钠盐19%，马来酸盐16%，水玻璃1%，水11%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.66%，回收率为82.67%的良好指标。
实施例4
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵3%，油酸钠45%，二胺四乙酸二钠盐23%，马来酸盐16%，水玻璃2%，水11%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.82%，回收率为81.57%的良好指标。
实施例5
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵3%，油酸钠47%，二胺四乙酸二钠盐21%，马来酸盐16%，水玻璃2%，水11%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.26%，回收率为81.19%的良好指标。
实施例6
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵3%，油酸钠49%，二胺四乙酸二钠盐19%，马来酸盐16%，水玻璃2%，水11%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.41%，回收率为81.28%的良好指标。
实施例7
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵4%，油酸钠45%，二胺四乙酸二钠盐23%，马来酸盐17%，水玻璃1%，水10%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.84%，回收率为81.42%的良好指标。
实施例8
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵4%，油酸钠45%，二胺四乙酸二钠盐23%，马来酸盐18%，水玻璃1%，水9%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.81%，回收率为81.09%的良好指标。
实施例9
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵4%，油酸钠47%，二胺四乙酸二钠盐21%，马来酸盐17%，水玻璃1%，水10%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.77%，回收率为81.36%的良好指标。
实施例10
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵4%，油酸钠49%，二胺四乙酸二钠盐19%，马来酸盐17%，水玻璃1%，水10%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.49%，回收率为82.28%的良好指标。
实施例11
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵3%，油酸钠45%，二胺四乙酸二钠盐23%，马来酸盐17%，水玻璃2%，水10%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.71%，回收率为81.54%的良好指标。
实施例12
本实施例的钛铁矿浮选捕收剂，是由以下重量百分比的原料制备而成：二丁基二硫代磷酸铵3%，油酸钠45%，二胺四乙酸二钠盐23%，马来酸盐18%，水玻璃2%，水9%，按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
采用制得的钛铁矿浮选捕收剂，浮选品位为20.42%的原矿，获得的钛精矿品位达48.33%，回收率为81.85%的良好指标。
以上实施例描述了本发明的基本原理、主要特征及优点，本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明原理的范围下，本发明还会有各种变化和改进，这些变化和改进均落入本发明保护的范围内。
Claims (3)
1.一种钛铁矿浮选捕收剂，其特征在于：原料包含按重量份计的以下组分：1.二丁基二硫代磷酸铵重量百分比为2%-9%，2.油酸钠的重量百分比为35%-55%，3.乙二胺四乙酸二钠盐的重量百分比为25%-45%，4.马来酸盐的重量百分比为13%-20%，5.水玻璃的添加量的重量百分比为0.5%-2%，6.其他均为水。
2.如权利要求1所述的钛铁矿浮选捕收剂的制备方法，其特征在于具体步骤为：按照配方分别称取原料，加入部分水，混合后加热到60℃到80℃，搅拌0.5h-1.5h，此为组分A，在50℃-60℃将乙二胺四乙酸二钠和马来酸盐添加剩余的水，搅拌2h-4h，此为组分B，将A组分和B组分混合后，加入水玻璃，搅拌均匀后，制得钛铁矿浮选捕收剂。
3.根据权利要求2所述的钛铁矿浮选捕收剂的制备方法，其特征在于：最终搅拌的时间为4小时。