CN111411442A - Roman cloth and manufacturing method thereof - Google Patents
Roman cloth and manufacturing method thereof Download PDFInfo
- Publication number
- CN111411442A CN111411442A CN202010248272.9A CN202010248272A CN111411442A CN 111411442 A CN111411442 A CN 111411442A CN 202010248272 A CN202010248272 A CN 202010248272A CN 111411442 A CN111411442 A CN 111411442A
- Authority
- CN
- China
- Prior art keywords
- yarns
- soaking
- roman cloth
- dyeing
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides Roman cloth and a manufacturing method thereof, and relates to the technical field of fabric production. The Roman cloth is formed by interweaving cotton yarns, terylene, spandex, flame-retardant yarns, tc blended yarns and natural bamboo fibers, wherein the cotton yarns, the terylene, the spandex, the flame-retardant yarns, the tc blended yarns and the natural bamboo fibers are in percentage by weight: 25-35% of cotton yarn, 30-40% of terylene, 10-20% of spandex, 10-15% of flame retardant yarn, 8-15% of tc blended yarn and 5-10% of natural bamboo fiber. The Roman cloth manufactured by the method is good in moisture absorption and high in strength, the Roman cloth is not easy to deform under the action of external force, the heat resistance and the light resistance of the Roman cloth are obviously improved, and meanwhile, the yarns are pretreated before weaving, so that the rigidity of materials is reduced, and the quality of the Roman cloth is greatly improved.
Description
Technical Field
The invention relates to the technical field of fabric production, in particular to Roman cloth and a manufacturing method thereof.
Background
Roman cloth is a knitted fabric woven by a circular knitting machine, is commonly called as chicken cloth, the cloth cover of the Roman cloth is not flat than common double-faced cloth, the fabric has better horizontal and vertical elasticity, but has stronger transverse tensile property than the double-faced cloth, and the Roman cloth has strong hygroscopicity, is breathable and soft and is comfortable to wear when being used for manufacturing underwear.
With the development of economy and the progress of society, people have a certain trend of pursuing healthy, fashionable and natural life style, the requirement on comfort of the clothes is higher and higher except for basic requirements on charming, warm keeping, cold protection and the like, at present, a plurality of Roman cloths are poor in hygroscopicity and low in strength, are easy to deform under the action of external force, are poor in heat resistance and light resistance, and meanwhile, yarns used in weaving are high in rigidity, so that the quality of the Roman cloths is reduced.
Disclosure of Invention
Technical problem to be solved
Aiming at the defects of the prior art, the invention provides a Roman cloth and a manufacturing method thereof, which solve the defects and shortcomings of the prior art.
(II) technical scheme
In order to achieve the purpose, the invention is realized by the following technical scheme: the Roman cloth is formed by interweaving cotton yarns, terylene, spandex, flame-retardant yarns, tc blended yarns and natural bamboo fibers, wherein the cotton yarns, the terylene, the spandex, the flame-retardant yarns, the tc blended yarns and the natural bamboo fibers are in percentage by weight: 25-35% of cotton yarn, 30-40% of terylene, 10-20% of spandex, 10-15% of flame retardant yarn, 8-15% of tc blended yarn and 5-10% of natural bamboo fiber.
Preferably, the gram weight of the Roman cloth is 250-320g/m2The width is 145-185 cm.
A manufacturing method of Roman cloth comprises the following manufacturing steps:
s1, preprocessing: soaking cotton yarn, terylene, spandex, flame-retardant yarn, tc blended yarn and natural bamboo fiber by using warm water, taking out and placing the soaked cotton yarn, the terylene, the spandex, the flame-retardant yarn, the tc blended yarn and the natural bamboo fiber into a pretreatment tank, adding a softening agent into the pretreatment tank to continue soaking for a period of time, taking out materials to cool under natural conditions, cleaning the materials by using cold water after cooling, and drying the materials after cleaning;
s2, weaving into cloth: weaving the yarns into cloth by using a large circular knitting machine;
s3, presetting: presetting the fabric by using a presetting device, and slowly cooling the fabric by using cold air after the presetting is finished, wherein the cooling uniformity is ensured in the cooling process;
s4, dyeing: putting the pre-shaped fabric into a dyeing kettle, adding a dyeing solution into the dyeing kettle, introducing supercritical carbon dioxide fluid into the dyeing kettle for dyeing, keeping the constant temperature and the constant pressure for a period of time, closing the dyeing kettle, and opening a pressure relief device to restore the dyeing kettle to the normal temperature and the normal pressure;
s5, post-processing: and taking out the dyed fabric, dehydrating, drying, then padding the dried fabric in a soaking pool with a softening agent, drying the fabric after padding, and tentering and setting.
Preferably, the warm water soaking time in the step 1 is 30-60min, the adding amount of the softening agent in the pretreatment tank is 5-10 g/L, the soaking temperature in the pretreatment tank is 110-120 ℃, and the soaking time is 10-20 min.
Preferably, the 1F and 2F weaving interlock texture when the circular knitting machine works in the step 2; the needle cylinder needles of the 3F and the 4F do not participate in the work, and the dial needles participate in the knitting respectively by the high-bell needle and the low-bell needle; no. 5F and No. 6F indicate that the dial needles do not work, and the needle cylinder needles are respectively a low-clock needle and a high-clock needle to knit.
Preferably, the presetting temperature in the step 3 is 110-130 ℃, and the presetting time is 3-5 min.
Preferably, the flow rate of the supercritical carbon dioxide in the step 4 is 12-16L/h, the temperature inside the dyeing kettle is 110-130 ℃, the pressure inside the dyeing kettle is 22-30MPa, and the dyeing time is 24-30 min.
Preferably, the adding amount of the softening agent in the soaking pool in the step 5 is 6-15 g/L, the soaking temperature in the soaking pool is 40-50 ℃, and the soaking time is 8-15 min.
(III) advantageous effects
The invention provides a Roman cloth and a manufacturing method thereof. The method has the following beneficial effects:
1. the Roman cloth manufactured by the method is good in moisture absorption and high in strength, the Roman cloth is not easy to deform under the action of external force, the heat resistance and the light resistance of the Roman cloth are obviously improved, and meanwhile, the yarns are pretreated before weaving, so that the rigidity of materials is reduced, and the quality of the Roman cloth is greatly improved.
2. The manufactured roman cloth has a good color fixing effect, the roman cloth is not easy to fade, the wearing comfort of the roman cloth is greatly improved, and the manufactured clothes are cool and breathable when being worn in summer.
Drawings
FIG. 1 is a schematic flow chart of the present invention.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The first embodiment is as follows:
as shown in fig. 1, an embodiment of the present invention provides a roman fabric, which is formed by interweaving cotton yarn, polyester, spandex, flame-retardant yarn, tc blended yarn and natural bamboo fiber, wherein the weight percentages of the cotton yarn, the polyester, the spandex, the flame-retardant yarn, the tc blended yarn and the natural bamboo fiber are: 25% of cotton yarn, 30% of terylene, 15% of spandex, 10% of flame-retardant yarn, 10% of tc blended yarn and 10% of natural bamboo fiber, wherein the gram weight of the Roman cloth is 250-one 320g/m2The width is 145-185 cm.
A manufacturing method of Roman cloth comprises the following manufacturing steps:
s1, preprocessing, namely soaking cotton yarns, terylene, spandex, flame-retardant yarns, tc blended yarns and natural bamboo fibers in warm water, taking out the cotton yarns, the terylene, the spandex, the flame-retardant yarns, the tc blended yarns and the natural bamboo fibers, putting the cotton yarns, the terylene, the flame-retardant yarns and the tc blended yarns into a preprocessing pool, adding a softening agent into the preprocessing pool, continuously soaking for a period of time, taking out the materials, cooling the materials under natural conditions, washing the materials with cold water after cooling, and drying the materials after washing, wherein the warm water soaking time is 30min, the adding amount of the softening agent in the preprocessing pool is 10 g/L, the soaking temperature in the preprocessing pool is 110 ℃, and;
s2, weaving into cloth: weaving the yarns into cloth by using a large circular machine, wherein the 1F and 2F weave a interlock texture when the large circular machine works; the needle cylinder needles of the 3F and the 4F do not participate in the work, and the dial needles participate in the knitting respectively by the high-bell needle and the low-bell needle; 5F and 6F are that the dial knitting needles do not participate in the work, and the needle cylinder knitting needles respectively participate in the knitting by the low-clock knitting needles and the high-clock knitting needles;
s3, presetting: presetting the fabric by using a presetting device, slowly cooling the fabric by using cold air after the presetting is finished, wherein the cooling uniformity is ensured in the cooling process, the presetting temperature is 110 ℃, and the presetting time is 5 min;
s4, dyeing, namely putting the pre-shaped fabric into a dyeing kettle, adding a dyeing solution into the dyeing kettle, introducing supercritical carbon dioxide fluid into the dyeing kettle for dyeing, keeping the temperature and the pressure constant for a period of time, closing the dyeing kettle, opening a pressure relief device, and restoring the dyeing kettle to normal temperature and normal pressure, wherein the flow of the supercritical carbon dioxide is 12L/h, the temperature inside the dyeing kettle is 110 ℃, the pressure inside the dyeing kettle is 22MPa, and the dyeing time is 30 min;
and S5, post-treatment, namely taking out the dyed fabric, dehydrating, drying, then placing the dried fabric into a soaking pool with a softening agent for padding, drying the fabric after padding, tentering and shaping, wherein the adding amount of the softening agent in the soaking pool is 6 g/L, the soaking temperature in the soaking pool is 40 ℃, and the soaking time is 15 min.
Example two:
the embodiment of the invention provides Roman cloth which is formed by interweaving cotton yarns, terylene, spandex, flame-retardant yarns, tc blended yarns and natural bamboo fibers, wherein the weight percentages of the cotton yarns, the terylene, the spandex, the flame-retardant yarns, the tc blended yarns and the natural bamboo fibers are as follows: 30% of cotton yarn, 35% of terylene, 10% of spandex, 10% of flame-retardant yarn, 10% of tc blended yarn and 5% of natural bamboo fiber, wherein the gram weight of the Roman fabric is 250-320g/m2The width is 145-185 cm.
A manufacturing method of Roman cloth comprises the following manufacturing steps:
s1, preprocessing, namely soaking cotton yarns, terylene, spandex, flame-retardant yarns, tc blended yarns and natural bamboo fibers in warm water, taking out the cotton yarns, the terylene, the spandex, the flame-retardant yarns, the tc blended yarns and the natural bamboo fibers, putting the cotton yarns, the terylene, the flame-retardant yarns and the tc blended yarns into a preprocessing pool, adding a softening agent into the preprocessing pool, continuously soaking for a period of time, taking out the materials, cooling the materials under natural conditions, washing the materials with cold water after cooling, and drying the materials after washing, wherein the warm water soaking time is 45min, the adding amount of the softening agent in the preprocessing pool is 7 g/L, the soaking temperature in the preprocessing pool is 115 ℃, and;
s2, weaving into cloth: weaving the yarns into cloth by using a large circular machine, wherein the 1F and 2F weave a interlock texture when the large circular machine works; the needle cylinder needles of the 3F and the 4F do not participate in the work, and the dial needles participate in the knitting respectively by the high-bell needle and the low-bell needle; 5F and 6F are that the dial knitting needles do not participate in the work, and the needle cylinder knitting needles respectively participate in the knitting by the low-clock knitting needles and the high-clock knitting needles;
s3, presetting: presetting the fabric by using a presetting device, slowly cooling the fabric by using cold air after the presetting is finished, wherein the cooling uniformity is ensured in the cooling process, the presetting temperature is 120 ℃, and the presetting time is 4 min;
s4, dyeing, namely putting the pre-shaped fabric into a dyeing kettle, adding a dyeing solution into the dyeing kettle, introducing supercritical carbon dioxide fluid into the dyeing kettle for dyeing, keeping the temperature and the pressure constant for a period of time, closing the dyeing kettle, opening a pressure relief device, and restoring the dyeing kettle to normal temperature and normal pressure, wherein the flow rate of the supercritical carbon dioxide is 14L/h, the temperature inside the dyeing kettle is 120 ℃, the pressure inside the dyeing kettle is 26MPa, and the dyeing time is 26 min;
and S5, post-treatment, namely taking out the dyed fabric, dehydrating, drying, then placing the dried fabric into a soaking pool with a softening agent for padding, drying the fabric after padding, tentering and shaping, wherein the adding amount of the softening agent in the soaking pool is 10 g/L, the soaking temperature in the soaking pool is 45 ℃, and the soaking time is 12 min.
Example three:
the embodiment of the invention provides Roman cloth which is formed by interweaving cotton yarns, terylene, spandex, flame-retardant yarns, tc blended yarns and natural bamboo fibers, wherein the weight percentages of the cotton yarns, the terylene, the spandex, the flame-retardant yarns, the tc blended yarns and the natural bamboo fibers are as follows: 25% of cotton yarn, 40% of terylene, 10% of spandex, 10% of flame-retardant yarn, 10% of tc blended yarn and 5% of natural bamboo fiber, wherein the gram weight of the Roman fabric is 250-320g/m2The width is 145-185 cm.
A manufacturing method of Roman cloth comprises the following manufacturing steps:
s1, preprocessing, namely soaking cotton yarns, terylene, spandex, flame-retardant yarns, tc blended yarns and natural bamboo fibers in warm water, taking out the cotton yarns, the terylene, the spandex, the flame-retardant yarns, the tc blended yarns and the natural bamboo fibers, putting the cotton yarns, the terylene, the flame-retardant yarns and the tc blended yarns into a preprocessing pool, adding a softening agent into the preprocessing pool, continuously soaking for a period of time, taking out the materials, cooling the materials under natural conditions, washing the materials with cold water after cooling, and drying the materials after washing, wherein the warm water soaking time is 60min, the adding amount of the softening agent in the preprocessing pool is 5 g/L, the soaking temperature in the preprocessing pool is 120 ℃, and;
s2, weaving into cloth: weaving the yarns into cloth by using a large circular machine, wherein the 1F and 2F weave a interlock texture when the large circular machine works; the needle cylinder needles of the 3F and the 4F do not participate in the work, and the dial needles participate in the knitting respectively by the high-bell needle and the low-bell needle; 5F and 6F are that the dial knitting needles do not participate in the work, and the needle cylinder knitting needles respectively participate in the knitting by the low-clock knitting needles and the high-clock knitting needles;
s3, presetting: presetting the fabric by using a presetting device, slowly cooling the fabric by using cold air after the presetting is finished, wherein the cooling uniformity is ensured in the cooling process, the presetting temperature is 130 ℃, and the presetting time is 3 min;
s4, dyeing, namely putting the pre-shaped fabric into a dyeing kettle, adding a dyeing solution into the dyeing kettle, introducing a supercritical carbon dioxide fluid into the dyeing kettle for dyeing, keeping the temperature and the pressure constant for a period of time, closing the dyeing kettle, opening a pressure relief device, and restoring the dyeing kettle to the normal temperature and the normal pressure, wherein the flow rate of the supercritical carbon dioxide is 16L/h, the temperature inside the dyeing kettle is 130 ℃, the pressure inside the dyeing kettle is 30MPa, and the dyeing time is 24 min;
and S5, post-treatment, namely taking out the dyed fabric, dehydrating, drying, then placing the dried fabric into a soaking pool with a softening agent for padding, drying the fabric after padding, tentering and shaping, wherein the adding amount of the softening agent in the soaking pool is 15 g/L, the soaking temperature in the soaking pool is 50 ℃, and the soaking time is 8 min.
The Roman cloth manufactured by the method is good in moisture absorption and high in strength, the Roman cloth is not easy to deform under the action of external force, the heat resistance and the light resistance of the Roman cloth are obviously improved, and meanwhile, the yarns are pretreated before being knitted, so that the rigidity of materials is reduced, and the quality of the Roman cloth is greatly improved; the color fixing effect of the manufactured roman cloth is good, the roman cloth is not prone to fading, the wearing comfort level of the roman cloth is greatly improved, and the manufactured clothes are cool and breathable when being worn in summer.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (8)
1. A Roman cloth is characterized in that: the Roman cloth is formed by interweaving cotton yarns, terylene, spandex, flame-retardant yarns, tc blended yarns and natural bamboo fibers, wherein the cotton yarns, the terylene, the spandex, the flame-retardant yarns, the tc blended yarns and the natural bamboo fibers are in percentage by weight: 25-35% of cotton yarn, 30-40% of terylene, 10-20% of spandex, 10-15% of flame retardant yarn, 8-15% of tc blended yarn and 5-10% of natural bamboo fiber.
2. A roman cloth according to claim 1 wherein: the gram weight of the Roman cloth is 250-320g/m2The width is 145-185 cm.
3. A manufacturing method of Roman cloth is characterized in that: the method comprises the following manufacturing steps:
s1, preprocessing: soaking cotton yarn, terylene, spandex, flame-retardant yarn, tc blended yarn and natural bamboo fiber by using warm water, taking out and placing the soaked cotton yarn, the terylene, the spandex, the flame-retardant yarn, the tc blended yarn and the natural bamboo fiber into a pretreatment tank, adding a softening agent into the pretreatment tank to continue soaking for a period of time, taking out materials to cool under natural conditions, cleaning the materials by using cold water after cooling, and drying the materials after cleaning;
s2, weaving into cloth: weaving the yarns into cloth by using a large circular knitting machine;
s3, presetting: presetting the fabric by using a presetting device, and slowly cooling the fabric by using cold air after the presetting is finished, wherein the cooling uniformity is ensured in the cooling process;
s4, dyeing: putting the pre-shaped fabric into a dyeing kettle, adding a dyeing solution into the dyeing kettle, introducing supercritical carbon dioxide fluid into the dyeing kettle for dyeing, keeping the constant temperature and the constant pressure for a period of time, closing the dyeing kettle, and opening a pressure relief device to restore the dyeing kettle to the normal temperature and the normal pressure;
s5, post-processing: and taking out the dyed fabric, dehydrating, drying, then padding the dried fabric in a soaking pool with a softening agent, drying the fabric after padding, and tentering and setting.
4. The manufacturing method of the Roman cloth as claimed in claim 3, wherein the soaking time of the warm water in the step 1 is 30-60min, the adding amount of the softening agent in the pretreatment tank is 5-10 g/L, the soaking temperature in the pretreatment tank is 110-120 ℃, and the soaking time is 10-20 min.
5. A method of making a roman cloth according to claim 3 wherein: the 1F and 2F weave interlock texture when the circular knitting machine in the step 2 works; the needle cylinder needles of the 3F and the 4F do not participate in the work, and the dial needles participate in the knitting respectively by the high-bell needle and the low-bell needle; no. 5F and No. 6F indicate that the dial needles do not work, and the needle cylinder needles are respectively a low-clock needle and a high-clock needle to knit.
6. A method of making a roman cloth according to claim 3 wherein: the presetting temperature in the step 3 is 110-130 ℃, and the presetting time is 3-5 min.
7. The method for manufacturing Roman cloth according to claim 3, wherein the flow rate of supercritical carbon dioxide in step 4 is 12-16L/h, the temperature inside the dyeing kettle is 110-130 ℃, the pressure inside the dyeing kettle is 22-30MPa, and the dyeing time is 24-30 min.
8. The method for manufacturing Roman cloth according to claim 3, wherein the softening agent is added into the soaking pool in the step 5 at a ratio of 6-15 g/L, the soaking temperature in the soaking pool is 40-50 ℃, and the soaking time is 8-15 min.