CN111305510A - 一种建筑地面防裂施工工艺 - Google Patents

一种建筑地面防裂施工工艺 Download PDF

Info

Publication number
CN111305510A
CN111305510A CN202010253474.2A CN202010253474A CN111305510A CN 111305510 A CN111305510 A CN 111305510A CN 202010253474 A CN202010253474 A CN 202010253474A CN 111305510 A CN111305510 A CN 111305510A
Authority
CN
China
Prior art keywords
parts
layer
crack
ground
cracking
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010253474.2A
Other languages
English (en)
Inventor
李欢
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hangzhou Linqi Metal Materials Co Ltd
Original Assignee
Hangzhou Linqi Metal Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hangzhou Linqi Metal Materials Co Ltd filed Critical Hangzhou Linqi Metal Materials Co Ltd
Priority to CN202010253474.2A priority Critical patent/CN111305510A/zh
Publication of CN111305510A publication Critical patent/CN111305510A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种建筑地面防裂施工工艺，包括以下步骤：A、首先打磨地面及阴角处，并清洁地面；B、之后在清洁后的地面上滚刷一层抗裂底漆，待晾干后再次滚刷一层抗裂底漆；C、在抗裂底漆表面铺设一层抗裂纤维布；D、在抗裂纤维布上浇筑一层抗裂砂浆层；E、待砂浆固化后铺设一层钢筋网；F、在钢筋网上再浇筑一层抗裂砂浆层；G、最后在抗裂砂浆层表面滚刷一层面漆层，本发明采用的施工工艺能够提高地面的抗裂、抗冲击、抗压、抗变形性能，确保地面经久耐用。

Description

一种建筑地面防裂施工工艺
技术领域
本发明涉及地面施工技术领域，具体为一种建筑地面防裂施工工艺。
背景技术
现有的地面在施工后容易出现开裂现象，因此，需要对现有的施工工艺进行改进。
发明内容
本发明的目的在于提供一种建筑地面防裂施工工艺，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种建筑地面防裂施工工艺，包括以下步骤：
A、首先打磨地面及阴角处，并清洁地面；
B、之后在清洁后的地面上滚刷一层抗裂底漆，待晾干后再次滚刷一层抗裂底漆；
C、在抗裂底漆表面铺设一层抗裂纤维布；
D、在抗裂纤维布上浇筑一层抗裂砂浆层；
E、待砂浆固化后铺设一层钢筋网；
F、在钢筋网上再浇筑一层抗裂砂浆层；
G、最后在抗裂砂浆层表面滚刷面漆层。
所述步骤B中抗裂底漆由30%蓖麻油类短油醇酸树脂、30%三元氯醋树脂、20%锆酸钙、5%锆酸钡、5%氮化锆、5%聚二甲基硅氧烷、5%纳米二氧化钛组成。
所述步骤D和步骤F中抗裂砂浆层材料组分按重量份数包括普通硅盐水泥40-60份、EVA胶料15-25份、煅烧磷石膏粉10-20份、复合保水稳定剂4-10份、羟乙基纤维素3-9份、苯乙烯-丁二烯共聚物10-20份、埃洛石纳米管4-10份、纳米二氧化铈3-9份、白炭黑2-4份、抗裂纤维4-10份、氟石膏粉6-14份、羟丙基甲基纤维素醚5-15份、萘系高效减水剂4-10份。
所述步骤G中面漆层组分按重量份数包括环氧丙烯酸酯30-50份、苯丙乳液10-20份、芳纶短纤维4-12份、氧化铝3-9份、全甲醚化氨基树脂10-18份、聚硅氧烷7-13份、轻质碳酸钙粉8-20份、纳米氧化锌4-10份、纳米硅微粉3-9份、聚四氟蜡粉4-12份、碱性碳酸铝珠光素3-9份。
所述步骤G中刷完一层后自然晾干，再刷一层，晾干后再刷一层，连续刷三层面漆。
与现有技术相比，本发明的有益效果是：
（1）本发明采用的施工工艺能够提高地面的抗裂、抗冲击、抗压、抗变形性能，确保地面经久耐用。
（2）本发明采用的抗裂底漆具有防潮、防潮、抗裂、抗冻效果，能够对水泥地面和砂浆起到保护作用。
（3）本发明采用的抗裂砂浆层具有抗冲击、抗裂、抗压、耐磨性能，浇筑两层抗裂砂浆层，能够提高地面整体抗裂性能。
（4）本发明采用的面漆层具有耐磨、耐刮性能、抗冻性能，易清洁，不易损坏，使用寿命长。
附图说明
图1为本发明流程图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一：
请参阅图1，本发明提供如下技术方案：一种建筑地面防裂施工工艺，包括以下步骤：
A、首先打磨地面及阴角处，并清洁地面；
B、之后在清洁后的地面上滚刷一层抗裂底漆，待晾干后再次滚刷一层抗裂底漆；
C、在抗裂底漆表面铺设一层抗裂纤维布；
D、在抗裂纤维布上浇筑一层抗裂砂浆层；
E、待砂浆固化后铺设一层钢筋网；
F、在钢筋网上再浇筑一层抗裂砂浆层；
G、最后在抗裂砂浆层表面滚刷面漆层。
本实施例中，步骤B中抗裂底漆由30%蓖麻油类短油醇酸树脂、30%三元氯醋树脂、20%锆酸钙、5%锆酸钡、5%氮化锆、5%聚二甲基硅氧烷、5%纳米二氧化钛组成。
本实施例中，步骤D和步骤F中抗裂砂浆层材料组分按重量份数包括普通硅盐水泥40份、EVA胶料15份、煅烧磷石膏粉10份、复合保水稳定剂4份、羟乙基纤维素3份、苯乙烯-丁二烯共聚物10份、埃洛石纳米管4份、纳米二氧化铈3份、白炭黑2份、抗裂纤维4份、氟石膏粉6份、羟丙基甲基纤维素醚5份、萘系高效减水剂4份。
本实施例中，步骤G中面漆层组分按重量份数包括环氧丙烯酸酯30份、苯丙乳液10份、芳纶短纤维4份、氧化铝3份、全甲醚化氨基树脂10份、聚硅氧烷7份、轻质碳酸钙粉8份、纳米氧化锌4份、纳米硅微粉3份、聚四氟蜡粉4份、碱性碳酸铝珠光素3份。
本实施例中，步骤G中刷完一层后自然晾干，再刷一层，晾干后再刷一层，连续刷三层面漆。
实施例二：
一种建筑地面防裂施工工艺，包括以下步骤：
A、首先打磨地面及阴角处，并清洁地面；
B、之后在清洁后的地面上滚刷一层抗裂底漆，待晾干后再次滚刷一层抗裂底漆；
C、在抗裂底漆表面铺设一层抗裂纤维布；
D、在抗裂纤维布上浇筑一层抗裂砂浆层；
E、待砂浆固化后铺设一层钢筋网；
F、在钢筋网上再浇筑一层抗裂砂浆层；
G、最后在抗裂砂浆层表面滚刷面漆层。
本实施例中，步骤B中抗裂底漆由30%蓖麻油类短油醇酸树脂、30%三元氯醋树脂、20%锆酸钙、5%锆酸钡、5%氮化锆、5%聚二甲基硅氧烷、5%纳米二氧化钛组成。
本实施例中，步骤D和步骤F中抗裂砂浆层材料组分按重量份数包括普通硅盐水泥60份、EVA胶料25份、煅烧磷石膏粉20份、复合保水稳定剂10份、羟乙基纤维素9份、苯乙烯-丁二烯共聚物20份、埃洛石纳米管10份、纳米二氧化铈9份、白炭黑4份、抗裂纤维10份、氟石膏粉14份、羟丙基甲基纤维素醚15份、萘系高效减水剂10份。
本实施例中，步骤G中面漆层组分按重量份数包括环氧丙烯酸酯50份、苯丙乳液20份、芳纶短纤维12份、氧化铝9份、全甲醚化氨基树脂18份、聚硅氧烷13份、轻质碳酸钙粉20份、纳米氧化锌10份、纳米硅微粉9份、聚四氟蜡粉12份、碱性碳酸铝珠光素9份。
本实施例中，步骤G中刷完一层后自然晾干，再刷一层，晾干后再刷一层，连续刷三层面漆。
实施例三：
一种建筑地面防裂施工工艺，包括以下步骤：
A、首先打磨地面及阴角处，并清洁地面；
B、之后在清洁后的地面上滚刷一层抗裂底漆，待晾干后再次滚刷一层抗裂底漆；
C、在抗裂底漆表面铺设一层抗裂纤维布；
D、在抗裂纤维布上浇筑一层抗裂砂浆层；
E、待砂浆固化后铺设一层钢筋网；
F、在钢筋网上再浇筑一层抗裂砂浆层；
G、最后在抗裂砂浆层表面滚刷面漆层。
本实施例中，步骤B中抗裂底漆由30%蓖麻油类短油醇酸树脂、30%三元氯醋树脂、20%锆酸钙、5%锆酸钡、5%氮化锆、5%聚二甲基硅氧烷、5%纳米二氧化钛组成。
本实施例中，步骤D和步骤F中抗裂砂浆层材料组分按重量份数包括普通硅盐水泥45份、EVA胶料16份、煅烧磷石膏粉12份、复合保水稳定剂5份、羟乙基纤维素4份、苯乙烯-丁二烯共聚物12份、埃洛石纳米管5份、纳米二氧化铈4份、白炭黑3份、抗裂纤维5份、氟石膏粉7份、羟丙基甲基纤维素醚8份、萘系高效减水剂5份。
本实施例中，步骤G中面漆层组分按重量份数包括环氧丙烯酸酯35份、苯丙乳液12份、芳纶短纤维5份、氧化铝4份、全甲醚化氨基树脂11份、聚硅氧烷8份、轻质碳酸钙粉10份、纳米氧化锌5份、纳米硅微粉4份、聚四氟蜡粉6份、碱性碳酸铝珠光素4份。
本实施例中，步骤G中刷完一层后自然晾干，再刷一层，晾干后再刷一层，连续刷三层面漆。
实施例四：
一种建筑地面防裂施工工艺，包括以下步骤：
A、首先打磨地面及阴角处，并清洁地面；
B、之后在清洁后的地面上滚刷一层抗裂底漆，待晾干后再次滚刷一层抗裂底漆；
C、在抗裂底漆表面铺设一层抗裂纤维布；
D、在抗裂纤维布上浇筑一层抗裂砂浆层；
E、待砂浆固化后铺设一层钢筋网；
F、在钢筋网上再浇筑一层抗裂砂浆层；
G、最后在抗裂砂浆层表面滚刷面漆层。
本实施例中，步骤B中抗裂底漆由30%蓖麻油类短油醇酸树脂、30%三元氯醋树脂、20%锆酸钙、5%锆酸钡、5%氮化锆、5%聚二甲基硅氧烷、5%纳米二氧化钛组成。
本实施例中，步骤D和步骤F中抗裂砂浆层材料组分按重量份数包括普通硅盐水泥55份、EVA胶料23份、煅烧磷石膏粉18份、复合保水稳定剂9份、羟乙基纤维素8份、苯乙烯-丁二烯共聚物18份、埃洛石纳米管8份、纳米二氧化铈8份、白炭黑4份、抗裂纤维9份、氟石膏粉12份、羟丙基甲基纤维素醚14份、萘系高效减水剂9份。
本实施例中，步骤G中面漆层组分按重量份数包括环氧丙烯酸酯45份、苯丙乳液18份、芳纶短纤维11份、氧化铝8份、全甲醚化氨基树脂17份、聚硅氧烷12份、轻质碳酸钙粉17份、纳米氧化锌9份、纳米硅微粉8份、聚四氟蜡粉10份、碱性碳酸铝珠光素8份。
本实施例中，步骤G中刷完一层后自然晾干，再刷一层，晾干后再刷一层，连续刷三层面漆。
实施例五：
一种建筑地面防裂施工工艺，包括以下步骤：
A、首先打磨地面及阴角处，并清洁地面；
B、之后在清洁后的地面上滚刷一层抗裂底漆，待晾干后再次滚刷一层抗裂底漆；
C、在抗裂底漆表面铺设一层抗裂纤维布；
D、在抗裂纤维布上浇筑一层抗裂砂浆层；
E、待砂浆固化后铺设一层钢筋网；
F、在钢筋网上再浇筑一层抗裂砂浆层；
G、最后在抗裂砂浆层表面滚刷面漆层。
本实施例中，步骤B中抗裂底漆由30%蓖麻油类短油醇酸树脂、30%三元氯醋树脂、20%锆酸钙、5%锆酸钡、5%氮化锆、5%聚二甲基硅氧烷、5%纳米二氧化钛组成。
本实施例中，步骤D和步骤F中抗裂砂浆层材料组分按重量份数包括普通硅盐水泥48份、EVA胶料22份、煅烧磷石膏粉17份、复合保水稳定剂6份、羟乙基纤维素5份、苯乙烯-丁二烯共聚物14份、埃洛石纳米管6份、纳米二氧化铈5份、白炭黑3份、抗裂纤维8份、氟石膏粉8份、羟丙基甲基纤维素醚14份、萘系高效减水剂6份。
本实施例中，步骤G中面漆层组分按重量份数包括环氧丙烯酸酯42份、苯丙乳液16份、芳纶短纤维10份、氧化铝5份、全甲醚化氨基树脂12份、聚硅氧烷12份、轻质碳酸钙粉10份、纳米氧化锌9份、纳米硅微粉4份、聚四氟蜡粉10份、碱性碳酸铝珠光素4份。
本实施例中，步骤G中刷完一层后自然晾干，再刷一层，晾干后再刷一层，连续刷三层面漆。
实施例六：
一种建筑地面防裂施工工艺，包括以下步骤：
A、首先打磨地面及阴角处，并清洁地面；
B、之后在清洁后的地面上滚刷一层抗裂底漆，待晾干后再次滚刷一层抗裂底漆；
C、在抗裂底漆表面铺设一层抗裂纤维布；
D、在抗裂纤维布上浇筑一层抗裂砂浆层；
E、待砂浆固化后铺设一层钢筋网；
F、在钢筋网上再浇筑一层抗裂砂浆层；
G、最后在抗裂砂浆层表面滚刷面漆层。
本实施例中，步骤B中抗裂底漆由30%蓖麻油类短油醇酸树脂、30%三元氯醋树脂、20%锆酸钙、5%锆酸钡、5%氮化锆、5%聚二甲基硅氧烷、5%纳米二氧化钛组成。
本实施例中，步骤D和步骤F中抗裂砂浆层材料组分按重量份数包括普通硅盐水泥50份、EVA胶料20份、煅烧磷石膏15份、复合保水稳定剂7份、羟乙基纤维素6份、苯乙烯-丁二烯共聚物15份、埃洛石纳米管7份、纳米二氧化铈6份、白炭黑3份、抗裂纤维7份、氟石膏粉10份、羟丙基甲基纤维素醚10份、萘系高效减水剂7份。
本实施例中，步骤G中面漆层组分按重量份数包括环氧丙烯酸酯40份、苯丙乳液15份、芳纶短纤维8份、氧化铝6份、全甲醚化氨基树脂14份、聚硅氧烷10份、轻质碳酸钙粉14份、纳米氧化锌7份、纳米硅微粉6份、聚四氟蜡粉8份、碱性碳酸铝珠光素6份。
本实施例中，步骤G中刷完一层后自然晾干，再刷一层，晾干后再刷一层，连续刷三层面漆。
实验例：
对施工后的地面进行性能测试，得到数据如下表：
抗压强度（MPA） 抗冲击强度（MPA）
实施例一 95 50
实施例二 98 52
实施例三 97 51
实施例四 98 51
实施例五 96 50
实施例六 99 53
本发明采用的抗裂底漆具有防潮、防潮、抗裂、抗冻效果，能够对水泥地面和砂浆起到保护作用；本发明采用的抗裂砂浆层具有抗冲击、抗裂、抗压、耐磨性能，浇筑两层抗裂砂浆层，能够提高地面整体抗裂性能；本发明采用的面漆层具有耐磨、耐刮性能、抗冻性能，易清洁，不易损坏，使用寿命长。
综上所述，本发明采用的施工工艺能够提高地面的抗裂、抗冲击、抗压、抗变形性能，确保地面经久耐用。
本发明未详述之处，均为本领域技术人员的公知技术。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。

Claims (5)

1.一种建筑地面防裂施工工艺，其特征在于：包括以下步骤：
A、首先打磨地面及阴角处，并清洁地面；
B、之后在清洁后的地面上滚刷一层抗裂底漆，待晾干后再次滚刷一层抗裂底漆；
C、在抗裂底漆表面铺设一层抗裂纤维布；
D、在抗裂纤维布上浇筑一层抗裂砂浆层；
E、待砂浆固化后铺设一层钢筋网；
F、在钢筋网上再浇筑一层抗裂砂浆层；
G、最后在抗裂砂浆层表面滚刷面漆层。
2.根据权利要求1所述的一种建筑地面防裂施工工艺，其特征在于：所述步骤B中抗裂底漆由30%蓖麻油类短油醇酸树脂、30%三元氯醋树脂、20%锆酸钙、5%锆酸钡、5%氮化锆、5%聚二甲基硅氧烷、5%纳米二氧化钛组成。
3.根据权利要求1所述的一种建筑地面防裂施工工艺，其特征在于：所述步骤D和步骤F中抗裂砂浆层材料组分按重量份数包括普通硅盐水泥40-60份、EVA胶料15-25份、煅烧磷石膏粉10-20份、复合保水稳定剂4-10份、羟乙基纤维素3-9份、苯乙烯-丁二烯共聚物10-20份、埃洛石纳米管4-10份、纳米二氧化铈3-9份、白炭黑2-4份、抗裂纤维4-10份、氟石膏粉6-14份、羟丙基甲基纤维素醚5-15份、萘系高效减水剂4-10份。
4.根据权利要求1所述的一种建筑地面防裂施工工艺，其特征在于：所述步骤G中面漆层组分按重量份数包括环氧丙烯酸酯30-50份、苯丙乳液10-20份、芳纶短纤维4-12份、氧化铝3-9份、全甲醚化氨基树脂10-18份、聚硅氧烷7-13份、轻质碳酸钙粉8-20份、纳米氧化锌4-10份、纳米硅微粉3-9份、聚四氟蜡粉4-12份、碱性碳酸铝珠光素3-9份。
5.根据权利要求1所述的一种建筑地面防裂施工工艺，其特征在于：所述步骤G中刷完一层后自然晾干，再刷一层，晾干后再刷一层，连续刷三层面漆。
CN202010253474.2A 2020-04-02 2020-04-02 一种建筑地面防裂施工工艺 Pending CN111305510A (zh)