CN111206418A - 一种抗菌纱线及其制备方法 - Google Patents

一种抗菌纱线及其制备方法 Download PDF

Info

Publication number
CN111206418A
CN111206418A CN202010204245.1A CN202010204245A CN111206418A CN 111206418 A CN111206418 A CN 111206418A CN 202010204245 A CN202010204245 A CN 202010204245A CN 111206418 A CN111206418 A CN 111206418A
Authority
CN
China
Prior art keywords
yarn
antibacterial
agent
graphene
combination
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN202010204245.1A
Other languages
English (en)
Inventor
魏春光
王静霞
梁燕
洪碧玙
谷星星
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Graduate School Tsinghua University
Original Assignee
Shenzhen Graduate School Tsinghua University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Graduate School Tsinghua University filed Critical Shenzhen Graduate School Tsinghua University
Priority to CN202010204245.1A priority Critical patent/CN111206418A/zh
Publication of CN111206418A publication Critical patent/CN111206418A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提供一种抗菌纱线及其制备方法，本发明的抗菌纱线，在实现纱线色彩可选性和符合纺织品多样性需求的同时，兼具石墨烯安全无毒、高效持久的抗菌性能；本发明抗菌纱线的制备方法，是先超声分散石墨烯，使亲水基团、染色基团通过氢键、共价键等作用力插入到石墨烯基团上，同时通过浸泡染色作用，在普通纱线上均匀原位地植入抗菌石墨烯基团，然后通过皂洗和固色作用，再次增强抗菌石墨烯基团、染色基团与纱线的结合，最后脱水烘干得到抗菌纱线。该制备方法不仅工艺简单、节能高效，可制备出一致性和稳定性好的产品，而且环境友好，充分实现精细化工和绿色环保的可持续发展理念，适合大规模推广和使用。

Description

一种抗菌纱线及其制备方法
技术领域
本发明涉及纺织技术领域，尤其涉及一种抗菌纱线及其制备方法。
背景技术
纱线是用各种纺织纤维加工成一定细度的产品，用于织布、制绳、制线、针织和刺绣等。随着社会的发展、经济水平的提高，人们更加注重自身健康和纺织品的品质，但传统的纱线并具有良好的抗菌性能，从而导致纱线易变质污染。为保护人们的身体健康和减少纱线制品滋生细菌引发疾病的危险，开发出具有抗菌性能的纺织品成为目前研究的重点。
目前，具有抗菌功能的纺织品大多数是纺织品后整理中添加，以获得具有抗菌性能的纺织品。常见的抗菌后整理剂分为无机抗菌整理剂、有机抗菌整理剂和天然生物抗菌整理剂三大类。无机抗菌剂主要以银溶液为主，但纺织品在使用过程中容易脱落影响抗菌性能，而且纳米级别的银通过皮肤接触渗入人体内部，对人体造成伤害；有机抗菌剂主要为有机化学合成物质组成，抗菌剂制备和添加过程中不仅对环境污染大，而且抗菌剂容易在纺织品表面形成覆盖层改变原有纺织品吸湿透气的特点，洗涤过程中抗菌剂又容易与有机清洗剂发生反应失去抗菌性能；天然生物抗菌剂是在天然生物中提取的具有抗菌功能的有机高分子物质组成的抗菌剂，制备成本高，不能广泛推广和使用。
石墨烯是一种由碳原子以Sp2杂化方式形成的蜂窝状平面薄膜，是一种只有一个原子层厚度的准二维材料，所以又叫做单原子层石墨。石墨烯的抗菌性能于 2010年被中国科学院上海应用物理研究所首次证实。国外专家揭示了石墨烯破坏细菌细胞膜的机制，相比于传统的无机、有机抗菌剂，石墨烯基本没有细胞毒性，更适合与人体皮肤直接接触。根据国内外专家研究石墨烯的抗菌机理主要有两种方式，一种是通过破坏细胞膜完整性，引起细菌结构的破坏和功能的紊乱；另外一种是通过与微生物相互作用后进入微生物体内，使微生物自由基代谢平衡失调，导致生物膜和大分子物质发生纸质过氧化损伤，从而达到抑菌效果。
但现有的石墨烯纺织产品，颜色基本都是与石墨烯本身相同的灰黑色，色调单一，使用范围有所局限，无法实现色彩可选性和符合纺织品多样性的需求。
发明内容
本发明的目的在于：针对现有技术的不足，提供一种抗菌纱线及其制备方法，该抗菌纱线在实现纱线色彩可选性和符合纺织品多样性需求的同时，兼具石墨烯安全无毒、高效持久的抗菌性能，该制备方法工艺简单，节能高效。为了达到上述目的，本发明采用如下技术方案：
一种抗菌纱线，所述抗菌纱线由普通纱线和抗菌石墨烯浆料制备获得，所述抗菌石墨烯浆料的各组分按重量百分比的构成为：石墨烯材料0.01%~5%、分散剂0.1%~3%、润湿剂0.01%~1%、染色剂0%~25%，余量为水。
作为本发明抗菌纱线的一种改进，所述石墨烯材料为石墨烯、氧化石墨烯、氧化还原石墨烯、改性石墨烯的一种或两种以上的组合，所述石墨烯材料在所述抗菌纱线上的负载比例为0.1%~5%。
作为本发明抗菌纱线的一种改进，所述分散剂为十二烷基苯磺酸钠、聚乙二醇、三聚磷酸钠、六偏磷酸钠、聚丙烯酰胺、聚乙烯吡咯烷酮、聚山梨酯、微晶纤维素、十二烷基硫酸钠的一种或者两种以上的组合。
作为本发明抗菌纱线的一种改进，所述润湿剂为二辛基磺化琥珀酸钠、炔二醇乙氧基化合物、聚醚改性硅氧烷共聚物的一种或者两种以上的组合。
作为本发明抗菌纱线的一种改进，所述普通纱线的材质为棉、麻、真丝、羊毛、腈纶、涤纶、锦纶、丙纶、氯纶、粘纤的一种或两种以上的组合。
作为本发明抗菌纱线的一种改进，所述染色剂为酸性染料、阳离子染料、偶氮染料、活性染料、分散染料、硫化染料、还原染料的一种或两种以上的组合。
本发明的另一目的是提供一种抗菌纱线的制备方法，包括如下步骤：
S01、按比例称取石墨烯材料、分散剂、润湿剂、染色剂至水中，超声分散均匀，其中浆料中各组分按重量百分比的构成为：石墨烯材料0.01%~5%、分散剂0.1%~3%、润湿剂0.01%~1%、染色剂0%~25%；
S02、将普通纱线与浆料按质量比为1:10~25进行混合，浸泡；
S03、将浸泡好的纱线进行脱水、烘干，得到抗菌纱线。
作为本发明抗菌纱线的制备方法的一种改进，所述步骤S02中，普通纱线使用前先进行松解和除杂处理，除杂处理包括煮练、除油、烧毛、食毛、漂白、丝光一种或两种以上的组合，使纱线表面色度均匀，无黄斑、黑斑、碱斑、锈斑、污渍以及含氯等杂质。
作为本发明抗菌纱线的制备方法的一种改进，所述步骤S02中，普通纱线与浆料浸泡温度为45~120℃，浸泡时间为0.5~8h，浸泡过程中不断进行浆料搅动作用，使得浆料能够完全渗入普通纱线内部。
作为本发明抗菌纱线的制备方法的一种改进，所述步骤S02中，浸泡时加入促染剂，
所述促染剂为元明粉、食盐、醋酸的一种或者两种以上的组合。
作为本发明抗菌纱线的制备方法的一种改进，所述步骤S03中，脱水后纱线的含水率为10~40%，烘干温度为80~120℃。
作为本发明抗菌纱线的制备方法的一种改进，所述步骤S03中，脱水后的纱线先经过皂洗和固色剂固色过程，然后再烘干得到得到抗菌纱线；所述固色剂为二烷基氨基甲基丙烯酸乙酯、聚二甲基二烯丙基氯化铵、二乙烯三胺-二甲胺-环氧氯丙烷共聚物的一种或者两种以上的组合。
一种抗菌面料，由上述抗菌纱线制备得到的抗菌面料。
抗菌纱线的应用，由上述抗菌纱线制成纺织品；该纺织品包括衣着用纺织品、室内装饰用纺织品、医用纺织品、床上用品、毛巾、浴巾、手帕、眼罩、口罩、美容护肤用品。
与现有技术相比，本发明实现的有益效果至少包括：
本发明提供一种抗菌纱线及其制备方法，本发明的抗菌纱线，该抗菌纱线在实现纱线色彩可选性和符合纺织品多样性需求的同时，兼具石墨烯安全无毒、高效持久的抗菌性能，对常见致病菌抑菌率高，而且经50次洗涤后，仍保持优异的抗菌效果，符合国家抗菌纺织品最高标准。
本发明的抗菌纱线由普通纱线和抗菌石墨烯浆料复合获得，该抗菌石墨烯浆料中的分散剂能使各组分在抗菌石墨烯浆料中均匀分散性且长时间稳定存在不易沉降；润湿剂能大大降低原本疏水的普通纱线与抗菌石墨烯浆料的表面张力，使普通纱线即使表层有存在过多或者不匀的油剂，也能在浆料中快速润湿和浸泡完全，降低浸泡难度和提高浸泡速率；染色剂能够使纱线在具有高效抗菌的同时，实现纱线的色彩可选性，从而更加符合纺织品多样性的需求；促染剂能够提高浆料对纱线的上染率，缩短浸泡时间；固色剂能够显著增强抗菌石墨烯和普通纱线之间、染料剂和普通纱线之间的作用力，使抗菌纱线保持稳定长久的抗菌性能和色牢性能。
本发明抗菌纱线的制备方法，是先超声分散石墨烯，使亲水基团、染色基团通过氢键、共价键等作用力插入到石墨烯基团上，同时通过浸泡染色作用，在普通纱线上均匀原位地植入抗菌石墨烯基团，然后通过皂洗和固色作用，再次增强抗菌石墨烯基团、染色基团与纱线的结合，最后脱水烘干得到抗菌纱线。该制备方法通过在浆料制备和浸泡过程进行工艺设计和参数控制，不仅工艺简单、节能高效，可制备出一致性和稳定性好的产品，而且环境友好，充分实现精细化工和绿色环保的可持续发展理念，适合大规模推广和使用。
附图说明
下面就根据附图和具体实施方式对本发明及其有益的技术效果作进一步详细的描述，其中：
图1是本发明实施例1制备的抗菌纱线的扫描电镜图片。
图2是本发明实施例2制备的抗菌纱线的扫描电镜图片。
具体实施方式
下面就根据附图和具体实施例对本发明作进一步描述，但本发明的实施方式不局限于此。
实施例1：一种抗菌纱线的制备方法，其特征在于，包括以下步骤：
S01、按比例称取石墨烯材料、分散剂、润湿剂、染色剂至水中，超声分散均匀，其中各组分按重量百分比的构成为：氧化石墨烯0.2%、分散剂十二烷基苯磺酸钠0.6%、染色剂0%、润湿剂二辛基磺化琥珀酸钠0.02%；
S02、将棉材质纱线松解、除杂处理后，按纱线与浆料按质量比为1:10进行混合，在60℃的浆料中浸泡1h，浸泡过程中不断进行搅动作用；
S03、将浸泡好的纱线进行皂洗，接着加入固色剂二烷基氨基甲基丙烯酸乙酯进行固色，然后进行脱水，脱水后的纱线的含水率为20%，最后将其在95℃下烘干，得到抗菌纱线。
实施例2：一种抗菌纱线的制备方法，其特征在于，包括以下步骤：
S01、按比例称取石墨烯材料、分散剂、润湿剂、染色剂至水中，超声分散均匀，其中各组分按重量百分比的构成为：石墨烯0.1%、分散剂十二烷基硫酸钠0.1%、染色剂活性染料5%、润湿剂炔二醇乙氧基化合物0.05%；
S02、将棉材质纱线松解、除杂处理后，按纱线与浆料按质量比为1:12进行混合，在85℃的浆料中浸泡3h，浸泡过程中不断进行搅动作用，浸泡2.5h后加入食盐促染剂进行促染；
S03、将浸泡好的纱线进行皂洗，接着加入固色剂聚二甲基二烯丙基氯化铵进行固色，然后进行脱水，脱水后的纱线的含水率为35%，最后将其在100℃下烘干，得到抗菌纱线。
实施例3：一种抗菌纱线的制备方法，其特征在于，包括以下步骤：
S01、按比例称取石墨烯材料、分散剂、润湿剂、染色剂至水中，超声分散均匀，其中各组分按重量百分比的构成为：改性石墨烯2%、分散剂聚乙烯吡咯烷酮0.5%、染色剂酸性染料10%、润湿剂聚醚改性硅氧烷共聚物0.5%；
S02、将涤纶材质纱线松解、除杂处理后，按纱线与浆料按质量比为1:18进行混合，在90℃的浆料中浸泡5h，浸泡过程中不断进行搅动作用，浸泡4h后加入醋酸促染剂进行促染；
S03、将浸泡好的纱线进行皂洗，接着加入固色剂二乙烯三胺-二甲胺-环氧氯丙烷共聚物进行固色，然后进行脱水，脱水后的纱线的含水率为15%，最后将其在80℃下烘干，得到抗菌纱线。
实施例4：一种抗菌纱线的制备方法，其特征在于，包括以下步骤：
S01、按比例称取石墨烯材料、分散剂、润湿剂、染色剂至水中，超声分散均匀，其中各组分按重量百分比的构成为：氧化还原石墨烯0.5%、分散剂聚山梨酯1.2%、染色剂阳离子染料1%、润湿剂二辛基磺化琥珀酸钠0.8%；
S02、将羊毛材质纱线松解、除杂处理后，按纱线与浆料按质量比为1:16进行混合，在75℃的浆料中浸泡4h，浸泡过程中不断进行搅动作用，浸泡3.5h后加入元明粉促染剂进行促染；
S03、将浸泡好的纱线进行皂洗，接着加入固色剂聚二甲基二烯丙基氯化铵进行固色，然后进行脱水，脱水后的纱线的含水率为30%，最后将其在90℃下烘干，得到抗菌纱线。
实施例5：一种抗菌纱线的制备方法，其特征在于，包括以下步骤：
S01、按比例称取石墨烯材料、分散剂、润湿剂、染色剂至水中，超声分散均匀，其中各组分按重量百分比的构成为：石墨烯1%、分散剂六偏磷酸钠1.8%、染色剂硫化染料15%、润湿剂炔二醇乙氧基化合物1%；
S02、将棉和腈纶混纺材质的纱线松解、除杂处理后，按纱线与浆料按质量比为1:20进行混合，在80℃的浆料中浸泡2h，浸泡过程中不断进行搅动作用，浸泡1.5h后加入元明粉促染剂进行促染；
S03、将浸泡好的纱线进行皂洗，接着加入固色剂二乙烯三胺-二甲胺-环氧氯丙烷共聚物进行固色，然后进行脱水，脱水后的纱线的含水率为25%，最后将其在105℃下烘干，得到抗菌纱线。
实施例6：一种抗菌纱线的制备方法，其特征在于，包括以下步骤：
0S01、按比例称取石墨烯材料、分散剂、润湿剂、染色剂至水中，超声分散均匀，其中各组分按重量百分比的构成为：改性石墨烯2.5%、分散剂聚乙二醇2.5%、染色剂分散染料8%、润湿剂聚醚改性硅氧烷共聚物0.1%；
S02、将锦纶和丙纶混纺材质的纱线松解、除杂处理后，按纱线与浆料按质量比为1:25进行混合，在65℃的浆料中浸泡6h，浸泡过程中不断进行搅动作用，浸泡5.5h后加入食盐促染剂进行促染；
S03、将浸泡好的纱线进行皂洗，接着加入固色剂聚二甲基二烯丙基氯化铵进行固色，然后进行脱水，脱水后的纱线的含水率为40%，最后将其在110℃下烘干，得到抗菌纱线。
对实施例1至6的抗菌纱线进行抗菌性能检测，抗细菌和白色念珠菌性能参照GB/T20944.3-2008震荡法：将试样置于烧瓶中、加入接种菌液、震荡，吸取瓶中液体，置于平板培养48小时（白色念珠菌72小时），记录菌落数（cfu/ml）计算抑菌率。测试对象包括金黄色葡萄球菌(Staphylococcus aureus) ATCC 6538、大肠埃希氏菌(Escherichia coli) ATCC25922、白色念珠菌(Canidia Albicans) ATCC 10231。实施例1至6的抗菌纱线分别编号为S1~S6，测试编号为S1~S6的抗菌纱线的抗菌性能，所得结果见表1。
表1：编号为S1~S6的抗菌纱线的抗细菌/白色念珠菌性能
Figure 1
*参照标准，抗菌率标准要求≥70%。
对实施例2的抗菌纱线按照纺织标准《FZ/T 73023－2006 抗菌针织品》分别进行水洗10次、20次和50次后的抗菌性能测试，所得结果见表2，从测试结果可知，经50次洗涤后，制得的抗菌纱线仍保持优异的抗菌效果，符合国家抗菌纺织品最高标准。
表2：实施例2的抗菌纱线分别进行水洗10次、20次和50次后的抗菌性能
Figure 2
采用本领域常规方法对上述实施例1至6的抗菌纱线制成纺织品；该纺织品包括衣着用纺织品、室内装饰用纺织品、医用纺织品、床上用品、毛巾、浴巾、手帕、眼罩、口罩、美容护肤用品。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和结构的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同范围限定。

Claims (14)

1.一种抗菌纱线，所述抗菌纱线由普通纱线和抗菌石墨烯浆料制备获得，所述抗菌石墨烯浆料的各组分按重量百分比的构成为：石墨烯材料0.01%~5%、分散剂0.1%~3%、润湿剂0.01%~1%、染色剂0%~25%，余量为水。
2.根据权利要求1所述的一种抗菌纱线，其特征在于，所述石墨烯材料为石墨烯、氧化石墨烯、氧化还原石墨烯、改性石墨烯的一种或两种以上的组合，所述石墨烯材料在所述抗菌纱线上的负载比例为0.1%~5%。
3.根据权利要求1所述的一种抗菌纱线，其特征在于，所述分散剂为十二烷基苯磺酸钠、聚乙二醇、三聚磷酸钠、六偏磷酸钠、聚丙烯酰胺、聚乙烯吡咯烷酮、聚山梨酯、微晶纤维素、十二烷基硫酸钠的一种或者两种以上的组合。
4.根据权利要求1所述的一种抗菌纱线，其特征在于，所述润湿剂为二辛基磺化琥珀酸钠、炔二醇乙氧基化合物、聚醚改性硅氧烷共聚物的一种或者两种以上的组合。
5.根据权利要求1所述的一种抗菌纱线，其特征在于，所述普通纱线的材质为棉、麻、真丝、羊毛、腈纶、涤纶、锦纶、丙纶、氯纶、粘纤的一种或两种以上的组合。
6.根据权利要求1所述的一种抗菌纱线，其特征在于，所述染色剂为酸性染料、阳离子染料、偶氮染料、活性染料、分散染料、硫化染料、还原染料的一种或两种以上的组合。
7.一种如权利要求1所述的抗菌纱线的制备方法，其特征在于，包括如下步骤：
S01、按比例称取石墨烯材料、分散剂、润湿剂、染色剂至水中，超声分散均匀，其中浆料中各组分按重量百分比的构成为：石墨烯材料0.01%~5%、分散剂0.1%~3%、润湿剂0.01%~1%、染色剂0%~25%；
S02、将普通纱线与浆料按质量比为1:10~25进行混合，浸泡；
S03、将浸泡好的纱线进行脱水、烘干，得到抗菌纱线。
8.根据权利要求7所述的一种抗菌纱线的制备方法，其特征在于，所述步骤S02中，普通纱线使用前先进行松解和除杂处理，除杂处理包括煮练、除油、烧毛、食毛、漂白、丝光一种或两种以上的组合。
9.根据权利要求7所述的一种抗菌纱线的制备方法，其特征在于，所述步骤S02中，普通纱线与浆料浸泡温度为45~120℃，浸泡时间为0.5~8h，浸泡过程中不断进行浆料搅动作用。
10.根据权利要求7所述的一种抗菌纱线的制备方法，其特征在于，所述步骤S02中，浸泡时加入促染剂，所述促染剂为元明粉、食盐、醋酸的一种或者两种以上的组合。
11.根据权利要求7所述的一种抗菌纱线的制备方法，其特征在于，所述步骤S03中，脱水后的纱线先经过皂洗和固色剂固色过程，然后再烘干得到得到抗菌纱线；所述固色剂为二烷基氨基甲基丙烯酸乙酯、聚二甲基二烯丙基氯化铵、二乙烯三胺-二甲胺-环氧氯丙烷共聚物的一种或者两种以上的组合。
12.根据权利要求7所述的一种抗菌纱线的制备方法，其特征在于，所述步骤S03中，脱水后纱线的含水率为10~40%，烘干温度为80~120℃。
13.一种抗菌面料，其制备所用纱线为权利要求1~6任一所述的抗菌纱线。
14.根据权利要求1~6任一所述的抗菌纱线的应用，其特征在于，由所述抗菌纱线制成纺织品；该纺织品包括衣着用纺织品、室内装饰用纺织品、医用纺织品、床上用品、毛巾、浴巾、手帕、眼罩、口罩、美容护肤用品。
CN202010204245.1A 2020-03-21 2020-03-21 一种抗菌纱线及其制备方法 Withdrawn CN111206418A (zh)