CN111205811A - 一种阻燃粘合膜的配方及屋面防滑防水塑料合成衬垫及其制造方法 - Google Patents

一种阻燃粘合膜的配方及屋面防滑防水塑料合成衬垫及其制造方法 Download PDF

Info

Publication number
CN111205811A
CN111205811A CN202010053999.1A CN202010053999A CN111205811A CN 111205811 A CN111205811 A CN 111205811A CN 202010053999 A CN202010053999 A CN 202010053999A CN 111205811 A CN111205811 A CN 111205811A
Authority
CN
China
Prior art keywords
flame
retardant
retardant adhesive
polypropylene
polyethylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010053999.1A
Other languages
English (en)
Inventor
孙正火
刘姜翠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hangzhou Qiyao New Material Co ltd
Original Assignee
Hangzhou Qiyao New Material Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hangzhou Qiyao New Material Co ltd filed Critical Hangzhou Qiyao New Material Co ltd
Priority to CN202010053999.1A priority Critical patent/CN111205811A/zh
Publication of CN111205811A publication Critical patent/CN111205811A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃粘合膜的配方及屋面防滑防水塑料合成衬垫及其制造方法，衬垫，包括：第一阻燃粘合层，复合于第一阻燃粘合层上的内层阻燃层，复合于内层阻燃层上的第二阻燃粘合层，复合于第二阻燃粘合层上的防滑外层阻燃层；阻燃粘合层的配方按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5‑25％，热塑性树脂10‑29％，乙烯基芳香族单体—马来酸酐无规共聚物3‑10％，4‑胺基苯基‑二苯基磷酸酯3‑10％；用这样的配方和方法制造出的衬垫具有安装安全，高强度，可直接接触人体、高防滑、高阻燃、易降解、重量轻、高防水的优点。

Description

一种阻燃粘合膜的配方及屋面防滑防水塑料合成衬垫及其制 造方法
技术领域
本发明涉及建筑材料领域，特别是一种屋面防滑防水塑料合成衬垫及其制造方法。
背景技术
目前市面上大部分木质墙面或屋顶结构的房屋需要铺设上传统的沥青纸或改性沥青胶功能型的防水材料以便达到房顶防水的作用，包括沥青基材，200-500gsm纸，改性沥青胶(主要成分：沥青25-50％，橡胶粉10-20％，抗氧化剂4-10％，填充剂20-45％，松香5-15％，SBS0.5-5％，纳米二氧化硅0.1-0.3％，余料为有机溶剂)；200-2000gsm聚丙烯或聚酯无纺布层及玻纤网格基布层等材料组成，由于玻纤网格布本身强度低，克重太高，安装不方便、不环保、与沥青及聚酯无纺布结合力差，导致很多交叉点或结合点不牢固，容易发生渗漏水，最终导致屋面使用寿命周期短，房屋长期需要翻修或更换材料，致使房屋安装或维护成本高、对居民长期居住带来一定的影响，而且因翻修房屋而摈弃的防水保温材料不容易分解，并且腐蚀性强，进而影响土壤生长质量或居民居住的环境质量；另外普通的防水合成垫层由于塑料材料不具备高阻隔性能，当木质房屋遇到火灾时，容易加速房屋的燃烧性，进而给居民的长期生活将会造成巨大的安全隐患；市场需要一种高防滑、高阻燃、高防水性能的屋面防滑防水塑料合成衬垫，本发明解决这样的问题。
发明内容
为解决现有技术的不足，本发明的目的在于提供一种阻燃粘合膜的配方及屋面防滑防水塑料合成衬垫及其制造方法，用这样的配方制造出的防水衬垫具有安装安全，高强度，可直接接触人体、高防滑、高阻燃、易降解、重量轻、高防水的优点。
为了实现上述目标，本发明采用如下的技术方案：
一种阻燃粘合膜的配方，按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5-25％，热塑性树脂10-29％，乙烯基芳香族单体—马来酸酐无规共聚物3-10％，4-胺基苯基-二苯基磷酸酯3-10％；改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯。
前述的一种阻燃粘合膜的配方，热塑性高弹性体包括：TPE，TPR，TPU，TPO，EVA，SEBS。
前述的一种阻燃粘合膜的配方，乙烯基芳香族单体—马来酸酐无规共聚物为苯乙烯-马来酸酐无规共聚物。
前述的一种阻燃粘合膜的配方，热塑性树脂包括：PE-聚乙烯，PA-聚酰胺，POM-聚甲醛。
前述的一种阻燃粘合膜的配方，按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯12％，热塑性树脂18％，苯乙烯-马来酸酐无规共聚物5％，4-胺基苯基-二苯基磷酸酯5％；改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯。
一种屋面防滑防水塑料合成衬垫，包括：第一阻燃粘合层，复合于第一阻燃粘合层上的内层阻燃层，复合于内层阻燃层上的第二阻燃粘合层，复合于第二阻燃粘合层上的防滑外层阻燃层；第一阻燃粘合层、第二阻燃粘合层的配方按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5-25％，热塑性树脂10-29％，乙烯基芳香族单体—马来酸酐无规共聚物3-10％,4-胺基苯基-二苯基磷酸酯3-10％；改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯。
前述的一种屋面防滑防水塑料合成衬垫，内层阻燃层为聚丙烯或聚乙烯或聚酯无纺布。
前述的一种屋面防滑防水塑料合成衬垫，防滑外层阻燃层为设置有花纹的聚丙烯无纺布。
一种屋面防滑防水塑料合成衬垫的制造方法，包括如下步骤：
步骤一，按照如下的阻燃粘合膜的配方准备材料，混合搅拌均匀，得到阻燃粘合膜原材料；
配方按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5-25％，热塑性树脂10-29％，乙烯基芳香族单体—马来酸酐无规共聚物3-10％，4-胺基苯基-二苯基磷酸酯3-10％；所述改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯；
步骤二，阻燃粘合膜原材料放入双螺杆挤出机中平均停留时间为1-15分钟，在180-300℃高温下，经高速运转流延挤出形成阻燃粘合膜；
步骤三，将防滑外层阻燃层放入顶层放卷架中，内层阻燃层放入底层放卷架中经双膜头高速流延挤出机；最终经280-350℃膜头流延复合而成经冷却收卷形成一种屋面防滑防水塑料合成衬垫。
本发明的有益之处在于：
防滑外层阻燃层设置为菱形或三角形或椭圆形等其他不规则的凹凸形状，使得防水衬垫具有高防滑性能；
阻燃粘合膜的配方中改性聚丙烯和改性聚乙烯具有协同作用，能够大程度的改进防水衬垫的阻燃能力并提高附着力；
这样结构的防水衬垫具有安装安全，高强度，可直接接触人体、高防滑、高阻燃、易降解、重量轻、高防水的优点。
具体实施方式
以下结合具体实施例对本发明作具体的介绍。
一种屋面防滑防水塑料合成衬垫，包括：第一阻燃粘合层，复合于第一阻燃粘合层上的内层阻燃层，复合于内层阻燃层上的第二阻燃粘合层，复合于第二阻燃粘合层上的防滑外层阻燃层；第一阻燃粘合层、第二阻燃粘合层的配方按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5-25％，热塑性树脂10-29％，乙烯基芳香族单体—马来酸酐无规共聚物3-10％,4-胺基苯基-二苯基磷酸酯3-10％；改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯。作为一种实施例，热塑性高弹性体包括：TPE，TPR，TPU，TPO，EVA，SEBS；乙烯基芳香族单体—马来酸酐无规共聚物为苯乙烯-马来酸酐无规共聚物；热塑性树脂包括：PE-聚乙烯、PA-聚酰胺、POM-聚甲醛。
作为一种实施例，内层阻燃层为聚丙烯或聚乙烯或聚酯无纺布(涤纶)；防滑外层阻燃层为设置有花纹的聚丙烯无纺布，作为一种实施例，花纹包括：凹凸花纹，菱形花纹，其他异形花纹。
一种屋面防滑防水塑料合成衬垫的制造方法，包括如下步骤：
步骤一，按照如下的阻燃粘合膜的配方准备材料，混合搅拌均匀，得到阻燃粘合膜原材料；
配方按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5-25％，热塑性树脂10-29％，乙烯基芳香族单体—马来酸酐无规共聚物3-10％,4-胺基苯基-二苯基磷酸酯3-10％；改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯；作为一种实施例，热塑性高弹性体包括：TPE，TPR，TPU，TPO，EVA，SEBS；活性氢单元的磷酸酯类化合物包括：4-胺基苯基-二苯基磷酸酯；热塑性树脂包括：PE-聚乙烯、PA-聚酰胺、POM-聚甲醛。
步骤二，阻燃粘合膜原材料放入双螺杆挤出机中平均停留时间为1-15分钟，在180-300℃高温下，经高速运转流延挤出形成阻燃粘合膜；
步骤三，将防滑外层阻燃层放入顶层放卷架中，内层阻燃层放入底层放卷架中经双膜头高速流延挤出机；最终经280-350℃膜头流延复合而成经冷却收卷形成一种屋面防滑防水塑料合成衬垫。
改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5-25％，热塑性树脂10-29％，乙烯基芳香族单体—马来酸酐无规共聚物3-10％,4-胺基苯基-二苯基磷酸酯3-10％；改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯
阻燃粘合膜配方验证：
用以下的实施例的配方和上文的方法制造出样品进行实验：
实施例1，改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5％，PA-聚酰胺29％，苯乙烯-马来酸酐无规共聚物3％,4-胺基苯基-二苯基磷酸酯3％，改性聚丙烯为添加8％热塑性高弹性体TPE的聚丙烯；改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯。增塑剂具体的化学名称是邻苯二甲酸二丁酯(DBP)；溶剂的化学名称是丙酮。
实施例2，改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯24％，PA-聚酰胺10％，苯乙烯-马来酸酐无规共聚物3％,4-胺基苯基-二苯基磷酸酯3％；
实施例3，改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯12％，PA-聚酰胺18％，苯乙烯-马来酸酐无规共聚物5％，4-胺基苯基-二苯基磷酸酯5％；
对比实施例1：改性聚丙烯28％，改性聚乙烯35％，聚碳酸酯10％，PA-聚酰胺12％，苯乙烯-马来酸酐无规共聚物8％,4-胺基苯基-二苯基磷酸酯7％；
对比实施例2：改性聚丙烯30％，聚乙烯30％，聚碳酸酯12％，PA-聚酰胺18％，苯乙烯-马来酸酐无规共聚物5％，4-胺基苯基-二苯基磷酸酯5％。(除了使用了聚乙烯其他与实施例3相同)
对比实施例2：聚丙烯30％，改性聚乙烯30％，聚碳酸酯12％，PA-聚酰胺18％，苯乙烯-马来酸酐无规共聚物5％,4-胺基苯基-二苯基磷酸酯5％。(除了使用了聚丙烯其他与实施例3相同)
实验一，黏度试验和阻燃实验。
粘度实验
实验过程：将普通阻燃膜与高粘度的阻燃膜附着在聚丙烯或聚酯无纺布或PE编织布上面后用包装胶带同样力度贴合好，如用50N/5cm力度去撕裂或剥离，普通阻燃膜会破裂甚至大块脱皮现象(平均6-7cm/10X10cm位置处)；但是高粘度的阻燃膜基本完好无损，仅仅点碎片(约1-3cm/10X10cm位置处)现象产生。观察撕裂的脱皮现象。
实验结果：高阻燃粘合膜有很好的附着力，更好保护产品每个角度渗水或透气。
阻燃实验
实验过程：将两份同样尺寸的普通复合膜与阻燃复合膜同时用酒精灯外焰水平持续点燃5-10秒，普通膜10秒内放烟量超过120；阻燃膜10秒内放烟量仅仅20-30；垂直点燃3-5秒，普通膜10秒内放烟量超过50；阻燃膜10秒内放烟量仅仅5-10。
实验结果：如表1所示。
表1
脱皮现象 点燃时间 放烟量
实施例1 4％面积 10s 9
实施例2 3％面积 10s 7
实施例3 0.4％面积 10s 5
对比实施例1 10％面积 12S 40
对比实施例2 11％面积 15s 60
对比实施例3 15％面积 15s 50
结果分析：由以上实验结果中实施例1-3和对比实施例1相比可知，本发明配方制造出的产品阻燃效果和附着力均优秀；对比实施例2-3与实施例1-3对比可知，改性聚丙烯和改性聚乙烯具有协同作用，二者一起加入配方能够使得产品具有更好的阻燃效果和附着力。
实验二，拿实施例3的样品做防滑防水验证实验；
防滑实验：
实验过程：将普通等级复合布与防滑等级的复合布同时放在木质的台板或桌子上，用50N/5cm力度以5m/min的速度从离桌边缘1米的距离同时移动，普通复合布基本10-15秒完成移动；防滑复合布基本25-30秒才能完成移动。
实验结果：高强度防滑复合布基本可以达到1.0Ftf摩擦系数，较好的效果可以避免工人施工时容易滑倒或跌倒。
防水实验：
实验过程：将无防水膜复合的复合布与有防水膜的复合布同时放在内温60-80摄氏度以上的桑拿保温箱，存放大60min后，无防水膜复合布透水蒸汽量达到3300g/m2.24h；有防水膜的复合布透水蒸汽量仅达1200g/m2.24h。
实验结果：防水效果可以达到低于1000g/m2.24h，高效防止木质结构房屋因长期使用不通风或透气而发霉。
本发明提供一种阻燃粘合膜的配方及屋面防滑防水塑料合成衬垫及其制造方法，用这样的配方制造出的防水衬垫具有安装安全，高强度，可直接接触人体、高防滑、高阻燃、易降解、重量轻、高防水的优点。
以上显示和描述了本发明的基本原理、主要特征和优点。本行业的技术人员应该了解，上述实施例不以任何形式限制本发明，凡采用等同替换或等效变换的方式所获得的技术方案，均落在本发明的保护范围内。

Claims (9)

1.一种阻燃粘合膜的配方，其特征在于，按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5-25％，热塑性树脂10-29％，乙烯基芳香族单体—马来酸酐无规共聚物3-10％，4-胺基苯基-二苯基磷酸酯3-10％；所述改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；所述改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯。
2.根据权利要求1所述的一种阻燃粘合膜的配方，其特征在于，所述热塑性高弹性体包括：TPE，TPR，TPU，TPO，EVA，SEBS。
3.根据权利要求1所述的一种阻燃粘合膜的配方，其特征在于，所述乙烯基芳香族单体—马来酸酐无规共聚物为苯乙烯-马来酸酐无规共聚物。
4.根据权利要求1所述的一种阻燃粘合膜的配方，其特征在于，所述热塑性树脂包括：PE-聚乙烯、PA-聚酰胺、POM-聚甲醛。
5.根据权利要求1所述的一种阻燃粘合膜的配方，其特征在于，按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯12％，热塑性树脂18％，苯乙烯-马来酸酐无规共聚物5％，4-胺基苯基-二苯基磷酸酯5％；所述改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；所述改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯。
6.一种屋面防滑防水塑料合成衬垫，其特征在于，包括：第一阻燃粘合层，复合于所述第一阻燃粘合层上的内层阻燃层，复合于所述内层阻燃层上的第二阻燃粘合层，复合于所述第二阻燃粘合层上的防滑外层阻燃层；所述第一阻燃粘合层、第二阻燃粘合层的配方按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5-25％，热塑性树脂10-29％，乙烯基芳香族单体—马来酸酐无规共聚物3-10％，4-胺基苯基-二苯基磷酸酯3-10％；所述改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；所述改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯。
7.根据权利要求6所述的一种屋面防滑防水塑料合成衬垫，其特征在于，所述内层阻燃层为聚丙烯或聚乙烯或聚酯无纺布。
8.根据权利要求6所述的一种屋面防滑防水塑料合成衬垫，其特征在于，所述防滑外层阻燃层为设置有花纹的聚丙烯无纺布。
9.一种屋面防滑防水塑料合成衬垫的制造方法，其特征在于，包括如下步骤：
步骤一，按照如下的阻燃粘合膜的配方准备材料，混合搅拌均匀，得到阻燃粘合膜原材料；
配方按照质量百分数包括：改性聚丙烯30％，改性聚乙烯30％，聚碳酸酯5-25％，热塑性树脂10-29％，乙烯基芳香族单体—马来酸酐无规共聚物3-10％,4-胺基苯基-二苯基磷酸酯3-10％；所述改性聚丙烯为添加8％热塑性高弹性体的聚丙烯；所述改性聚乙烯为添加3％增塑剂和2％溶剂的聚乙烯；
步骤二，阻燃粘合膜原材料放入双螺杆挤出机中平均停留时间为1-15分钟，在180-300℃高温下，经高速运转流延挤出形成阻燃粘合膜；
步骤三，将防滑外层阻燃层放入顶层放卷架中，内层阻燃层放入底层放卷架中经双膜头高速流延挤出机；最终经280-350℃膜头流延复合而成经冷却收卷形成一种屋面防滑防水塑料合成衬垫。
CN202010053999.1A 2020-01-17 2020-01-17 一种阻燃粘合膜的配方及屋面防滑防水塑料合成衬垫及其制造方法 Pending CN111205811A (zh)