CN111032777A - 高耐受性防水组合物及使用其制备的产品 - Google Patents

高耐受性防水组合物及使用其制备的产品 Download PDF

Info

Publication number
CN111032777A
CN111032777A CN201880053583.0A CN201880053583A CN111032777A CN 111032777 A CN111032777 A CN 111032777A CN 201880053583 A CN201880053583 A CN 201880053583A CN 111032777 A CN111032777 A CN 111032777A
Authority
CN
China
Prior art keywords
waterproofing composition
waterproofing
composition
present
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201880053583.0A
Other languages
English (en)
Inventor
维克托·帕戈扎-梅勒洛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wei KetuoPagezha Meileluo
Original Assignee
Wei KetuoPagezha Meileluo
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wei KetuoPagezha Meileluo filed Critical Wei KetuoPagezha Meileluo
Publication of CN111032777A publication Critical patent/CN111032777A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种防水组合物以及基于该防水组合物的材料，该防水组合物具有对不同天气条件的高耐受性和改进的绝热和抗冲击性能，并且该防水组合物易于施用且更耐用。该组合物包含丙烯酸树脂、水、聚合物颗粒和添加剂。

Description

高耐受性防水组合物及使用其制备的产品
技术领域
本发明涉及一种防水丙烯酸组合物，该防水丙烯酸组合物对各种气象条件具有高耐受性，该防水丙烯酸组合物用于使用该组合物制备防水材料，其具有改进的绝热和抗冲击特性，该防水丙烯酸组合物易于应用并具有延长的耐久性。
背景技术
由于很大程度上由人类活动排放的温室气体造成的全球气温上升，地球上包括人类居住的许多地区的气象条件经常发生变化，例如日照时间较长或日照强度较大、暴雨甚至冰雹。上述情况意味着，经受所述条件的表面，如屋顶，会因高温、潮湿和冲击而磨损，这取决于所显现的各种气象条件，在短期内，由于上述事件的连续发生，情况会变得更糟。
在这方面，已经设计了一些组合物，其可用于建筑物和其他相关结构的外部。一些所述组合物本身或与其它组合的材料除了其它功能之外具有隔热和防水的目的。丙烯酸树脂是所述材料的一个示例。
隔热和防水组合物的已知技术有各种示例。其中一些描述如下。
申请MX/a/2011/002241描述了一种防水组合物，其包含丙烯酸树脂或用选自玻璃、陶瓷或聚合物和/或其混合物的微球的颗粒改性的丙烯酸树脂。此外，它包含来自研磨轮胎的颗粒；填料；诸如分散剂、湿润剂、硅氧烷/矿物油消泡剂、杀菌剂、乙二醇防冻剂、聚结剂、增稠剂、铵离子的pH调节剂等的添加剂，和纤维；颜料和水，任选还包含水硬度控制物、阻燃剂和颜料。
在专利KR 101522550 B1中，描述了一种防水片材，其包含异戊二烯-异丁烯橡胶、回收的丁基橡胶或合成橡胶以及其他组分，例如乙二醇、苯并三唑封闭剂和丙烯酸类单体。
申请JP 2004035681 A涉及一种具有优异抗渗性和耐候性的低成本防水材料，其可与用作填充材料各种废料一起使用，并且可用作再回收的来源。该发明的防水材料包括作为粘合剂的丙烯酸树脂，和作为填充材料的各种类型的无机物和废料。
另一个涉及防水组合物和材料的发明在美国专利7,760,518 B2中提出，该专利教导了一种形成复合材料的方法，该复合材料包括基材材料，其选自木质纤维素材料；橡胶和诸如聚乙烯、聚丙烯、聚苯乙烯或PET等不可回收塑料；与回收的塑料、热水和乳化剂形成乳液的粘合剂。
根据前述内容，所示技术和其他技术是基于聚合物和颗粒以及其他添加剂设计的。然而，尽管所述组合物和使用该组合物制成的材料可能具有防水和隔热性能，但在我们现在所经历的极端气候下通常具有有限的耐久性。市场上常见的防水剂必须定期(例如1至2年)重新涂用，因为它们所使用的材料没有适当地配制成对极端气候或连续的极端气候具有更高耐久性的特性。换句话说，增加的太阳辐射和长时间的降雨会导致所述商业防水剂，甚至上述技术的防水剂的快速劣化。此外，所述组合物、材料和防水剂没有提及抗冲击性能或似乎没有抗冲击性能，而该抗冲击性能在除了太阳辐射和雨水的极端气候之外还会发生冰雹的地区是必要的，这就是为什么它们经常更快地恶化。所述技术是基于特定类型材料的特性而制定的，但是它们并未提供显著的结果，并且还没有确定有助于延长其在任何上述气候条件下的耐久性的特定有效的材料及限定的量。
因此，需要提供一种具有抗渗透性、绝热性和抗冲击性能的组合物，该组合物具有使用该组合物制备的材料的高耐久性，该组合物用于希望利用所述性能的建筑物中。
发明内容
本发明的一个目的是提供一种防水组合物，其具有对各种气象条件的高耐受性和延长的耐久性。
本发明的另一个目的是提供一种防水材料，该防水材料具有对各种气象条件的高耐受性和延长的耐久性，该防水材料易于施加于待防水的表面，而无论施加时的气候条件如何。
本发明的另一个目的是提供了一种制备防水材料的方法，该防水材料具有对各种气象条件的高耐受性和延长的耐久性。
具体实施方式
总体而言，本发明的一个目的是涉及一种包含水基丙烯酸树脂、聚合物颗粒、水和添加剂的防水组合物，其具有对各种气象条件的高耐受性和延长的耐久性，其中，所述聚合物颗粒由橡胶及其衍生物的颗粒、聚苯乙烯泡沫及其衍生物的颗粒和一种或多种硬质聚合物的颗粒组成，所述硬质聚合物选自包括PET、PEAD、PEBD、PVC、PP、PS、PU及其混合物的组。
如上所述，现有技术中已知的组合物的主要组分显示出非常宽泛的用量，这不能确保单个组分相对于其余组分在整个所述范围内的突出特性，当未对其其余组分的用量进行优化以获得耐久性、抗渗透性和抗冲击性方面的突出结果时，情况更是如此。因此，在本发明的优选实施方式中，相对于防水组合物的总量，在约15wt％至约35wt％的水基丙烯酸树脂、约15wt％至约25wt％的聚合物颗粒、约30wt％至约50wt％的水以及约15wt％至约25wt％的添加剂的范围内，已证实所述防水组合物显示出优异的结果。在更优选的实施方式中，相对于防水组合物的总量，所述防水组合物包含约16wt％至约31wt％的水基丙烯酸树脂、约17wt％至约20wt％的聚合物颗粒、约32wt％至约46wt％的水以及约19wt％至约21wt％的添加剂。
丙烯酸树脂是一种来自苯乙烯-丙烯酸共聚物的丙烯酸树脂，其具有本发明目的所需的塑性，包括两种或更多种丙烯酸树脂的混合物。
如上所述的聚合物颗粒分为三种类型，即橡胶及其衍生物、聚苯乙烯泡沫及其衍生物和硬质聚合物，硬质聚合物选自包括PET、PEAD、PEBD、PVC、PP、PS、PU及其混合物的组。优选地，来自橡胶及其衍生物的材料的比例高于其他两种类型，因为其密度通常大于其他类型的密度，在组合物中占据了与其他两种类型相似的体积。在前述说明性但非限制性的示例中，相对于聚合物颗粒的总量，所述聚合物颗粒包含约65wt％至约80wt％的橡胶颗粒或其衍生物，约5wt％至约10wt％的聚苯乙烯泡沫及其衍生物，以及约15wt％至约25wt％的硬质聚合物。与聚合物颗粒对应的材料中的至少一种可以是废料，这是由于其显现的环境优势。优选地，这三种聚合物颗粒是废料。例如，在橡胶及其衍生物的情况下，其可以理解为从天然来源或人造来源(橡胶)获得和加工的材料，来自废轮胎的硫化橡胶是优选的，此外，聚苯乙烯泡沫的材料可以是由被称为为尤尼赛尔Unicel(泡沫塑料(Styrofoam))的材料制成的物质，并且硬质聚合物可以来自用于各种用途的瓶子和其它废塑料物品，优选的硬质聚合物是PET。
在下文将详细描述的由所述聚合物制造产品期间，橡胶及其衍生物以及聚苯乙烯泡沫及其衍生物赋予所述组合物强度、韧性、隔音和介电性能，而硬质聚合物赋予所述组合物坚固性。膨胀的苯乙烯聚合物通过其余材料热膨胀至产品中而提供良好的绝热性和低压缩强度，这使得由该组合物制成的产品具有低热膨胀，从耐久性的观点来看是理想的。
对于本发明的防水组合物，橡胶颗粒具有的尺寸介于约80目(0.177mm)和约3目(6.73mm)之间。可膨胀聚苯乙烯颗粒具有的尺寸介于约0.177mm和约10mm之间。硬质聚合物颗粒具有的尺寸介于约0.01mm和约1mm之间。当然，在所述组合物及其实例中，在所述防水组合物中可以使用并表示为在给定范围内的若干不同尺寸的颗粒，或者也可以使用并表示为在相应颗粒类型的范围内由全部颗粒尺寸得到的颗粒平均尺寸。
关于可用于本发明的添加剂，它们可以是增稠剂、杀生物剂、pH中和/稳定剂、消泡剂、分散剂、填料、聚结剂、干燥剂、颜料等。
在一个实施方式中，本发明的防水组合物包括至少一种增稠剂。优选地，本发明的组合物具有至少一种基于非离子醚化多糖化合物的增稠剂和至少另一种基于聚乙二醇的氨基塑料(aminoplast)化合物的增稠剂。基于非离子醚化多糖化合物的增稠剂可以本发明防水组合物总量的约0.15wt％至约0.35wt％的量存在。基于聚乙二醇的氨基塑料化合物的增稠剂可以本发明防水组合物总量的约0.35wt％至约0.50wt％的量存在。
在一个实施方式中，本发明的防水组合物包括至少一种杀生物剂，其可以是诸如1,2-苯并异噻唑啉-3-酮的有机化合物，或诸如氢氧化钠的无机化合物。杀生物剂可以本发明防水组合物总量的约0.10wt％至约0.20wt％的量存在。
在一个实施方式中，本发明的防水组合物包括至少一种pH中和/稳定剂，其优选为基于铵化合物、有机胺或其衍生物。也可以使用两种或多种pH中和/稳定剂的混合物。pH中和剂/稳定剂可以本发明防水组合物总量的约0.01wt％至约0.05wt％的量存在。
在一个实施方式中，本发明的防水组合物包括至少一种基于疏水组分的消泡剂。具体而言，包含石蜡矿物油和硅氧烷的混合物的消泡剂是优选的。消泡剂可以本发明防水组合物总量的约0.25wt％至约0.35wt％的量存在。
在一个实施方式中，本发明的防水组合物包括至少一种分散剂，其优选基于丙烯酸酯共聚物的铵化合物、诸如AMP的氨基醇或其混合物。分散剂可以本发明防水组合物总量的约0.25wt％至约0.35wt％的量存在。
在一个实施方式中，本发明的防水组合物包括至少一种可以是各种类型的填料。优选的类型包括无机碳酸盐，如碳酸钙和硅砂及其混合物。填料可以本发明防水组合物总量的约10wt％至约20wt％的量存在。
在一个实施方式中，本发明的防水组合物包括至少一种基于乙二醇醚的粘合聚结剂。聚结剂可以本发明防水组合物总量的约0.3wt％至约0.7wt％的量存在。
在一个实施方式中，本发明的防水组合物包括至少一种基于乙二醇化合物的干燥剂。具体而言，MEG是优选的，它还赋予防水组合物流平剂的功能。干燥剂可以本发明防水组合物总量的约1wt％至约1.25wt％的量存在。
在一个实施方式中，本发明的防水组合物包括至少一种颜料。所述至少一种颜料可以是可用于防水组合物的现有技术中的任意一种，例如有机性质的，例如耐光化合物，或者无机性质的，例如金属氧化物。在用于本发明的无机颜料组中，二氧化钛是本发明的优选颜料之一，但是在本发明中，并不限于此。颜料可以本发明防水组合物总量的约1wt％至约2wt％的量存在。
可用于本发明的其它添加剂可根据对特定添加剂的需要任选地包括在本发明中，这些添加剂提供了对于熟悉本技术领域的人来说显而易见的所需性能。
本发明的组合物是根据其特殊考虑而制备的，从而获得其优异的结果。由于组分具有不同的化学性质，组分的简单混合使得它们无法合适的一体化，因此形成了特定组分的团块和/或具有不同密度和不同免受微生物侵蚀的区域，这将导致防水组合物的突出特性缺乏均匀性，这对其不利。因此，本发明创造性地发现，本发明防水组合物的制备必须在两个主要步骤中进行。第一步骤包括制备初级溶液，这将有助于加入第二步骤中指出的后续组分。所述第一步骤包括向容器中加入一部分包含在防水组合物的水，包含至少一种基于非离子醚化多糖化合物的增稠剂、一部分用于防水组合物的至少一种杀生物剂以及至少一种pH中和/稳定剂的添加剂并混合。第二步骤包括在含有初级溶液的容器中加入其余的水、添加剂、水基丙烯酸树脂、聚合物颗粒和至少一种基于聚乙二醇的氨基塑料化合物的增稠剂，并混合。优选地，用于第一步骤的一部分水为防水组合物中水总量的约15wt％至约30wt％，并且用于第一步骤的一部分杀生物剂为防水组合物中杀生物剂总量的约6wt％至约20wt％。为了方便地进行合适的均化，用于混合的搅拌在第一步骤中是连续的，直到在第二步骤中加入添加剂，但是在加入水基丙烯酸树脂时暂停搅拌，然后再次开始搅拌。聚合物颗粒是在没有暂停对此前添加的组分进行搅拌的情况下添加的，对于基于聚乙二醇的氨基塑料化合物的至少一种增稠剂也是如此。
本发明的另一个目的是涉及由防水组合物制成的防水材料，该防水材料具有对各种气象条件的高耐受性和延长的耐久性。所述防水材料为片材形式。
在一个实施方式中，防水材料包括本发明的防水组合物。
在一个实施方式中，防水材料包括由本发明的防水组合物制成的多个(两个或更多个)层和至少一个网，其中，至少一个网的每一个通过其上部和下部连接到由本发明的防水组合物制成的层。显而易见的是，本发明的防水材料构成了两层之间的每个网的限制，基于这样的理解，即在防水材料的上极端和下极端总是有层，而在所述极端则没有网，一个网的下层也不可以是另一个网的上层，并且当防水材料中存在两个或更多个网时，层和网相继布置。在一个更优选的实施方式中，防水材料包括由本发明的防水组合物制成的下层、由本发明的防水组合物制成的上层和位于所述下层和上层之间的网。在所有这些实施方式中，所述网可以是金属的或塑料的，对材料更大的耐受性做出贡献而不影响其柔性例如它允许所述防水材料能够卷起。
本发明的防水材料的厚度可以是可变的，起始为约1mm。优选地，本发明的防水材料的厚度为约1mm至约15mm，更优选的厚度为约3mm、约5mm和约10mm。
在本发明的另一个目的中，提供了一种制备本发明防水材料的方法，该方法通常包括以下步骤：将本发明的防水组合物供应到具有搅拌和分配装置的料斗中；将防水组合物分配到模具中；将倒入模具中的防水组合物调节至预定高度；在模具中干燥防水组合物以获得片材，和从模具中取出片材。
在用于制备本发明防水材料的方法的一个实施方式中，调节高度的步骤通过调平刮刀进行，并且干燥步骤通过烘箱、空气干燥或通风进行。
在制备本发明防水材料的方法的一个实施方式中，模具通过传送带传送通过烘箱。在烘箱出口处，将获得的片材取出并再次置于在分配器下方的传送带上，并将网放置在所述片材上，以及使模具定位成使其与片材和网状物的边缘对齐。接下来，将防水组合物再次分配到模具中，调节模具中防水组合物的高度，并再次进行烘箱中的干燥步骤，以获得具有防水组合物的两层或两片以及一个网的中间层的叠层。按照所示的步骤，可以向防水材料中添加更多的网。
在所有前述实施例中，可以在调平和干燥步骤之间进行在模具上喷洒涂防水组合物的附加步骤，目的是减少粗糙或填充大的空间，例如由气泡产生的空间。此外，防水材料是柔性的，并且能够卷起，以便于处理和运输。
在所有前述实施方式中，所获得的片材和叠层可以在其外表面(与环境接触)上覆盖有由弹性丙烯酸化合物制成的防水组合物的饰面层，其目的是用于对小的表面孔隙进行密封，以得到基本平滑的饰面。
实施例
这些实施例基于本发明的至少一个优选实施方式，因此被认为是对本发明防水组合物范围的说明性而非限制。
实施例1.防水组合物的制备
在常规大小(例如1000至10000L)的混合容器中，通过加入约80.44L水(1L＝1kg)、约2.26kg ESACOL ED 30W(基于醚化多糖的增稠剂)、约0.14kg Proxel GXL(杀生物剂)和约0.28kg AMP-
Figure BDA0002386177330000082
(pH中和/稳定剂)，连续混合3分钟，以制备初级溶液。接下来，倒入约382.46L的水，均化3分钟，倒入约1.98kg Proxel GXL并均化3分钟，倒入约4.09kg BYK-035(消泡剂)并均化3分钟，倒入约4.09kg BYK-156(分散剂)并均化3分钟，倒入约218.47kg
Figure BDA0002386177330000083
10-SJ(碳酸钙)并均化10分钟，倒入约7.34kg丁基溶纤剂(Butyl
Figure BDA0002386177330000084
粘合聚结剂)并均化3分钟，约15.67kg MEG(干燥剂)并均化3分钟，倒入约19.62kg TI
Figure BDA0002386177330000085
(颜料、二氧化钛)，均化10分钟并停止混合。接下来，加入约426.21kg DC EA 15S(水基丙烯酸树脂)，并然后再次开始混合16分钟，加入约173.02kg尺寸介于0.80mm至5mm之间的废轮胎硫化橡胶颗粒，混合8分钟，加入约19.62kg平均尺寸约为5mm的Unicel废料珠粒，混合8分钟，加入约49.11kg平均尺寸约为0.05mm的PET粉末并混合8分钟，加入约6.49kg OPTIFLO H370(增稠剂)并均化8至16分钟。
所得组合物如下：
Figure BDA0002386177330000081
Figure BDA0002386177330000091
由此获得的组合物具有以下特性：
表观密度 956.58kg/m3
导热率 0.0570W/mK
对水蒸气的渗透性 0.003ng/Pa-s-m
湿气吸附 5.34wt％；5.007vol％
吸水性 4.62wt％
实施例2.防水组合物的制备
在常规大小(例如1000至10000L)的混合容器中，通过加入约128.35L水(1L＝1kg)、约3.26kg ESACOL ED 30W、约0.25kg Proxel GXL和约0.38kg AMP-
Figure BDA0002386177330000093
连续混合3分钟，以制备初级溶液。接下来，倒入约382.79L的水，均化3分钟，倒入约1.76kg ProxelGXL并均化3分钟，倒入约3.63kg BYK-035并均化3分钟，倒入约3.63kg BYK-156并均化3分钟，倒入约198.42kg
Figure BDA0002386177330000094
10-SJ并均化10分钟，倒入约6.64kg丁基溶纤剂(Butyl
Figure BDA0002386177330000095
)并均化3分钟，约14.29kg MEG并均化3分钟，以及倒入约17.80kg TI
Figure BDA0002386177330000096
均化10分钟并停止混合。接下来，加入约267.86kg的DALECRYL，然后再次开始混合16分钟，加入约157.18kg平均尺寸约为0.25mm的废轮胎硫化橡胶并混合8分钟，加入约17.80kg平均尺寸约为6mm的Unicel废料颗粒并混合8分钟，加入约44.62kg平均尺寸约为0.03mm的PE-PP-PET混合物粉末(1:1:3，w/w)并混合8分钟，以及加入约4.76kgOPTIFLO H370并均化8至16分钟。
所得组合物如下：
Figure BDA0002386177330000092
Figure BDA0002386177330000101
由此获得的组合物具有以下特性：
表观密度 1003.4kg/m<sup>3</sup>
导热率 0.0589W/mK
对水蒸气的渗透性 0.004ng/Pa-s-m
湿气吸附 5.35wt％；5.570vol％
吸水性 5.90wt％
实施例3.防水组合物的制备
在常规大小(例如1000至10000L)的混合容器中，通过加入约109.19L水(1L＝1kg)、约2.63kg ESACOL ED 30W、约0.25kg Proxel GXL和约0.34kg MCR-95(pH中和/稳定剂)，连续混合3分钟，以制备初级溶液。接下来，倒入约275.77L的水，均化3分钟，约1.19kgProxel GXL并均化3分钟，倒入约2.46kg BYK-035并均化3分钟，倒入约2.46kg BYK-156并均化3分钟，倒入约134.05kg
Figure BDA0002386177330000103
10-SJ并均化10分钟，倒入约4.49kg丁基溶纤剂(Butyl
Figure BDA0002386177330000104
)并均化3分钟，倒入约9.65kg MEG并均化3分钟，倒入约9.65kg MEG并均化3分钟，以及倒入约12.02kg E172(红色颜料，氧化铁)，均化10分钟并停止混合。接下来，加入约140.74kg DC EA 15S，然后再次开始混合16分钟，加入约106.19kg平均尺寸约为0.7mm的废轮胎硫化橡胶颗粒并混合8分钟，加入约12.02kg平均尺寸约为4mm的Unicel珠粒并混合8分钟，加入约30.15kg平均尺寸约为0.05mm的PET粉末并混合8分钟，以及加入约3.22kg OPTIFLO H370并均化8至16分钟。
所得组合物如下：
Figure BDA0002386177330000102
Figure BDA0002386177330000111
由此获得的组合物具有以下特性：
表观密度 1022.12kg/m<sup>3</sup>
导热率 0.0597W/mK
对水蒸气的渗透性 0.005ng/Pa-s-m
湿气吸附 5.36wt％；5.795vol％
吸水性 6.41wt％
来自上述实施例的组合物可以应用于暴露于露天的表面。
实施例4.由本发明的组合物制备叠层制品
将实施例1的防水组合物置于带有搅拌和分配装置的料斗中，并将其分配到传送带上的模具中，通过调平刮刀将模具中防水组合物的高度调节至预定高度，并将模具置于烘箱中进行干燥。将形成的片材从模具中取出；它具有约10mm的厚度。对实施例2和3的防水组合物进行相同的过程，进行必要的高度调节，以分别获得5mm和3mm的厚度。由此获得的材料可以放置在暴露于露天的表面上。
实施例5.由本发明的组合物制备具有内部网的叠层制品
取出实施例4中获得的三个片材，并将每片再次独立地放置在传送带上的分配器下方。放置金属网并与每一个片材和模具对齐，并且模具的边缘与其边缘重合。将各自的防水组合物分配到放置在每个片材上的网上，根据相应片材的高度，在模具中通过刮刀调节防水组合物的高度，并在烘箱中干燥。获得双层叠层制品，具有两个防水组合物片材以及两片材之间的金属网。由此获得的材料可以放置在暴露于露天的表面上。
例6.由本发明的组合物制备片材和叠层制品
再次制备实施例4中的片材。在这些片材的一个面上涂上一层
Figure BDA0002386177330000112
饰面层以覆盖孔隙，并提供基本光滑的表面。由此获得的材料可以放置在暴露于露天的表面上。
再次制备实施例5中的层压品。，在这些层压品的片材外表面上涂上一层
Figure BDA0002386177330000121
饰面层以覆盖孔隙并得到基本上平滑的饰面。由此获得的材料可以放置在暴露于露天的表面上。
尽管本文已经说明和描述了本发明的某些特征，但是本领域的技术人员将会想到许多修改、替换、变化和等同物。参考一些特定实施方式详细描述了本发明，但是应当理解，在本发明的精神和范围内，可以进行各种其他修改。因此，必须理解，所附权利要求旨在覆盖落入本发明真实精神内的所有修改和变化。

Claims (30)

1.一种防水组合物，所述防水组合物包括水基丙烯酸树脂、聚合物颗粒、水和添加剂的，其中，所述聚合物颗粒由橡胶及其衍生物的颗粒、聚苯乙烯泡沫及其衍生物的颗粒和一种或多种硬质聚合物的颗粒组成，所述硬质聚合物选自包括PET、PEAD、PEBD、PVC、PP、PS、PU及其混合物的组。
2.根据权利要求1所述的防水组合物，其中，相对于所述防水组合物的总量，所述水基丙烯酸树脂存在的量为约16wt％至约31wt％，所述聚合物颗粒存在的量为17wt％至约20wt％，水存在的量为约32wt％至约46wt％，并且所述添加剂存在的量为约19wt％至约21wt％。
3.根据权利要求1或2所述的防水组合物，其中，相对于所述聚合物颗粒的总量，所述聚合物颗粒包括约65wt％至约80wt％的所述橡胶颗粒或其衍生物，约5wt％至约10wt％的所述聚苯乙烯泡沫及其衍生物，和约15wt％至约25wt％的所述硬质聚合物。
4.根据前述权利要求中任一项所述的防水组合物，其中，所述聚合物颗粒的材料是新制的或来自废料。
5.根据权利要求4所述的防水组合物，其中，所述橡胶及其衍生物的颗粒包括来自废轮胎的硫化橡胶，所述聚苯乙烯泡沫的颗粒包括尤尼赛尔(Unicel)，并且所述硬质聚合物的颗粒包括PET。
6.根据前述权利要求中任一项所述的防水组合物，其中，所述橡胶颗粒具有的尺寸介于约80目(0.177mm)和约3目(6.73mm)之间，所述可膨胀聚苯乙烯颗粒具有的尺寸介于约0.177mm和约10mm之间，并且所述硬质聚合物颗粒具有的尺寸介于约0.01mm和约1mm之间。
7.根据前述权利要求中任一项所述的防水组合物，其中，所述添加剂包括增稠剂、杀生物剂、pH中和/稳定剂、消泡剂、分散剂、填料、聚结剂、干燥剂和颜料。
8.根据权利要求7所述的防水组合物，其中，所述防水组合物包括所述防水组合物总量的约0.15wt％至约0.35wt％的量的至少一种基于非离子醚化多糖的化合物的增稠剂，和所述防水组合物总量的约0.35wt％至约0.50wt％的量的至少另一种基于聚乙二醇的氨基塑料化合物的增稠剂。
9.根据权利要求7所述的防水组合物，其中，所述防水组合物包括至少一种杀生物剂，并且其中，所述至少一种杀生物剂以所述防水组合物总量的约0.10wt％至约0.20wt％的量存在。
10.根据权利要求7所述的防水组合物，其中，所述防水组合物包括至少一种pH中和/稳定剂，并且其中，所述至少一种pH中和/稳定剂以所述防水组合物总量的约0.01wt％至约0.05wt％的量存在。
11.根据权利要求7所述的防水组合物，其中，所述防水组合物包括至少一种基于疏水组分的消泡剂，并且其中，所述至少一种消泡剂以所述防水组合物总量的约0.25wt％至约0.35wt％的量存在。
12.根据权利要求7所述的防水组合物，其中，所述防水组合物包括至少一种分散剂，并且其中，所述至少一种分散剂以所述防水组合物总量的约0.25wt％至约0.35wt％的量存在。
13.根据权利要求7所述的防水组合物，其中，所述防水组合物包括至少一种填料，并且其中，所述至少一种填料以所述防水组合物总量的约10wt％至约20wt％的量存在。
14.根据权利要求7所述的防水组合物，其中，所述防水组合物包括至少一种基于乙二醇醚的粘合聚结剂，并且其中所述至少一种粘合聚结剂以所述防水组合物总量的约0.3wt％至约0.7wt％的量存在。
15.根据权利要求7所述的防水组合物，其中，所述防水组合物包括至少一种基于乙二醇化合物的干燥剂，并且其中所述一种干燥剂以所述防水组合物总量的约1wt％至约1.25wt％的量存在。
16.根据权利要求7所述的防水组合物，其中，所述防水组合物包括至少一种颜料，并且其中所述颜料以所述防水组合物总量的约1wt％至约2wt％的量存在。
17.一种制备根据权利要求1至16所述的防水组合物的方法，包括以下步骤：
a)通过混合一部分包含在所述防水组合物中的水、基于非离子醚化多糖的化合物的至少一种增稠剂、一部分至少一种杀生物剂和至少一种pH中和/稳定剂来制备初级溶液，和
b)加入并混合其余的水、添加剂、水基丙烯酸树脂、聚合物颗粒和基于聚乙二醇的氨基塑料化合物的至少一种增稠剂并混合。
18.根据权利要求17所述的方法，其中，用于制备所述初级溶液的一部分水为所述防水组合物中水总量的约15wt％至约30wt％，并且用于制备所述初级溶液的一部分杀生物剂为所述防水组合物中杀生物剂总量的约6wt％至约20wt％。
19.根据权利要求17或18所述的方法，其中，从所述初级溶液的制备和添加剂的加入开始，混合物的搅拌是连续的，并且在加入水基丙烯酸树脂时，停止所述混合物的搅拌，然后再次开始所述混合物的搅拌，并且在加入其余组分时保持搅拌。
20.一种片材形式的防水材料，所述防水材料包括根据权利要求1至16所述的防水组合物。
21.根据权利要求20所述的防水材料，其中，所述防水材料进一步包括由本发明的防水组合物制成的多个层和至少一个网，其中，所述至少一个网的每一个通过它的上部和下部连接到由所述防水组合物制成的层。
22.根据权利要求21所述的防水材料，其中，所述防水材料包括由所述防水组合物制成的下层、由所述防水组合物制成的上层和位于所述下层和所述上层之间的网。
23.根据权利要求21或22中任一项所述的防水材料，其中，所述网的材料选自金属或塑料。
24.根据权利要求20至23中任一项所述的防水材料，其中，所述防水材料的厚度为约1mm至约15mm。
25.根据权利要求20至24中任一项所述的防水材料，其中，所述防水材料进一步包括在其一面上的由弹性丙烯酸化合物制成的防水组合物的层。
26.一种制备权利要求20至25中任一项所述的防水材料的方法，所述方法包括以下步骤：将权利要求1至16中任一项所述的防水组合物供应到具有搅拌和分配装置的料斗中，将所述防水组合物分配到模具中，将倒入所述模具中的所述防水组合物调节至预定高度，在所述模具中干燥所述防水组合物以获得片材，以及从模具中取出所述片材。
27.根据权利要求26所述的方法，其中，调节高度的步骤通过调平刮刀进行，并且所述干燥步骤通过烘箱、空气干燥或通风进行。
28.根据权利要求26或27所述的方法，其中，干燥在烘箱中进行，所述模具通过传送带输送通过所述烘箱，并且在所述烘箱的出口处，将所获得的片材取出并再次放置在所述传送带上的所述分配器下方，将网放置在所述片材上，并且模具被定位成与所述片材和所述网的边缘对齐，将所述防水组合物再次分配到模具中，调节模具中所述防水组合物的高度，并再次在所述烘箱中进行干燥步骤，以获得具有两层或两片防水组合物以及中间层网的叠层，并且任选地，重复所述步骤以向所述防水材料中添加更多的网。
29.根据权利要求26至28中任一项所述的方法，其中，在调平和干燥步骤之间进行在模具上喷洒防水组合物的附加步骤。
30.根据权利要求26至29中任一项所述的方法，其中，基于弹性丙烯酸化合物的防水组合物层被额外施加在其一个面上。
CN201880053583.0A 2017-08-18 2018-08-17 高耐受性防水组合物及使用其制备的产品 Pending CN111032777A (zh)