CN110981553A - 一种仿透明琥珀陶瓷砖及其制备方法 - Google Patents

一种仿透明琥珀陶瓷砖及其制备方法 Download PDF

Info

Publication number
CN110981553A
CN110981553A CN201911300688.4A CN201911300688A CN110981553A CN 110981553 A CN110981553 A CN 110981553A CN 201911300688 A CN201911300688 A CN 201911300688A CN 110981553 A CN110981553 A CN 110981553A
Authority
CN
China
Prior art keywords
layer
transparent
ceramic tile
amber
microcrystalline
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201911300688.4A
Other languages
English (en)
Other versions
CN110981553B (zh
Inventor
周营
柯善军
马超
田维
孙飞野
朱志超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foshan Oceano Ceramics Co Ltd
Original Assignee
Foshan Oceano Ceramics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Foshan Oceano Ceramics Co Ltd filed Critical Foshan Oceano Ceramics Co Ltd
Priority to CN201911300688.4A priority Critical patent/CN110981553B/zh
Publication of CN110981553A publication Critical patent/CN110981553A/zh
Application granted granted Critical
Publication of CN110981553B publication Critical patent/CN110981553B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种仿透明琥珀陶瓷砖，其特征在于：其结构自下而上包括坯体层、面釉层，第一图案层、微晶层、第二图案层、透明釉层和液态玻璃层；所述微晶层由彩色透明微晶玻璃粉烧制而成，所述彩色透明微晶玻璃粉，按照重量百分比组成如下：SiO2:65‑75％、Al2O3:15‑20％、Li2O：3‑5％、MgO:3‑5％、ZnO:0.7‑1.5％、Na2O:1‑2％、B2O3:3‑5％、Pb2O5:0.2‑0.4％和着色剂；其中，所述着色剂由TiO2:0.1％‑0.3％和CeO2:1‑2％组成，或由CuO:0.3％‑0.7％和Cr2O3:0.8‑1.5％组成。通过在陶瓷砖面釉层上铺一层彩色透明微晶玻璃粉，并结合发光陶瓷墨水，使面釉层和微晶层上打印有图案层，再经过二次烧结工艺，使制备出的陶瓷砖具有质感细腻，透明似玻璃，层次分明，富含生命力的奇特色彩的特点，可完美展现琥珀石，尤其是金珀和绿珀自然而不失尊贵的美感。

Description

一种仿透明琥珀陶瓷砖及其制备方法
技术领域
本发明涉及建筑陶瓷领域，特别涉及到一种仿透明琥珀陶瓷砖及其制备方法。
背景技术
随着科技水平的不断提高，喷墨打印技术也得到突飞猛进的发展，目前已广泛应于陶瓷生产，推动釉面砖迈入第三次革命。抛釉砖也凭借喷墨打印出的纹理细腻、颜色个性鲜明的图案花色而逐渐取代了抛光砖，成为最受消费者喜爱的家居装修材料。目前市场上出现了很多种类的抛釉砖，如具有下陷效果，裂纹效果、金属光泽等。釉面砖的销量得到了井喷式的发展，行业内也积累了一大批生产陶瓷釉面砖的厂家。同时也带来了一些问题，如市场上呈现在消费者面前都是千篇一律的产品，当前单纯的依靠版面设计对陶瓷砖的提升意义已经不那么重大，只有通过开发个性化的陶瓷砖产品才能满足消费者日益增长的需求。
琥珀外观晶莹剔透，触感温润细腻，在人们心中一直是尊贵、美好的代表。琥珀颜色种类多而富有变化，大部分球珀外观是透明的，又称透明琥珀，比较常见的是黄色的，也有红色、绿色和极为罕见的蓝色，分具有赏玩价值。透明琥珀不仅外观自然尊贵，还具有宝石般的光泽与晶莹度，受到很多收藏者的喜爱。金珀是透明琥珀的一种，是一种即常见又珍贵的琥珀品种，金珀古代被称为“财石”，其色彩鲜明，华贵引人，具有富贵之美。其金黄色的光辉会给你带来财运和福气，在未来的市场上它的价值不可估量。绿珀因颜色青绿，坊间称之为“绿珀”，商家谓之天然而罕见，可遇而不可求，无数猎奇贪靓的消费者心甘情愿的掏出腰包献上巨资，将稀世绿珀恭请回家。现有市售的仿透明琥珀陶瓷砖，尤其是仿金珀、绿珀陶瓷砖比较少见，如若出现类似的产品必定会掀起一股抢购热潮。
发明内容
本发明的目的在于提供一种仿透明琥珀陶瓷砖及其制备方法。
为了达到上述目的，本发明采取了以下技术方案：
一种仿透明琥珀陶瓷砖,其结构自下而上包括坯体层、面釉层，第一图案层、微晶层、第二图案层、透明釉层和液态玻璃层；所述微晶层由彩色透明微晶玻璃粉烧制而成，所述彩色透明微晶玻璃粉，按照重量百分比组成如下：SiO2:65-75％、Al2O3:15-20％、Li2O：3-5％、 MgO:3-5％、ZnO:0.7-1.5％、Na2O:1-2％、B2O3:3-5％、Pb2O5:0.2-0.4％和着色剂；其中，所述着色剂由TiO2:0.1％-0.3％和CeO2:1-2％组成，或由CuO:0.3％-0.7％和Cr2O3:0.8-1.5％组成。
所述的一种仿透明琥珀陶瓷砖中，所述坯体层的原料中包含了低温莫来石晶须；所述莫来石晶须是以SiCl4、乙醚、Al(NO3)3、AlF3、乙醇、NH4Cl、ZnO、La2O3为原料通过溶胶凝胶法制得。
所述的一种仿透明琥珀陶瓷砖中，所述面釉层的颜色与微晶层的颜色相同。
所述的一种仿透明琥珀陶瓷砖中，所述彩色透明微晶玻璃粉粒径为50-75μm。
所述的一种仿透明琥珀陶瓷砖中，所述液态玻璃层为由液态玻璃组成的超薄膜层。
一种包括上述仿透明琥珀陶瓷砖的制备方法，其中，包括以下步骤:
1):将坯体层的原料进行压制得坯体层；
2):在坯体层施一层面釉，得面釉层；
3):在面釉层上打印图案，得第一图案层；
4):打印第一图案层后的砖体，经过干燥后，铺上一层厚度为2-3mm的彩色透明微晶玻璃粉，进窑炉烧制，得微晶层；
5):经过窑炉烧制得到微晶层后，在微晶层上打印图案，得第二图案层；
6):在第二图案层上施一层透明釉，进窑炉二次烧制，得透明釉层；
7):二次烧制后得陶瓷砖经过打磨、抛光工序后，得到具有透明琥珀质感的陶瓷砖。
所述的仿透明琥珀陶瓷砖的制备方法中，步骤1)中坯体层的压制压力为3800T-5000T。
所述的仿透明琥珀陶瓷砖的制备方法中，步骤4)中所述烧制温度为1200℃-1250℃。
所述的仿透明琥珀陶瓷砖的制备方法中，步骤6)中所述最佳烧成温度为1130℃-1180℃。
有益效果
本发明提供了一种仿透明琥珀陶瓷砖及其制备方法，通过在陶瓷砖面釉层上铺上一层含金色或绿色色彩的透明微晶玻璃粉，结合发光陶瓷墨水，使面釉层和微晶层上打印有第一图案层和第二图案层，再经过二次烧结工艺，使制备出的陶瓷砖具有质感细腻，透明似玻璃，层次分明，富含生命力的奇特色彩的特点，可完美展现琥珀石，尤其是金珀和绿珀自然而不失尊贵的美感。
附图说明
图1为本发明提供的一种仿透明琥珀陶瓷砖的结构示意图。
具体实施方式
请参阅图1，本发明提供的一种仿透明琥珀陶瓷砖中，其结构自下而上包括坯体层1、面釉层2，第一图案层3、微晶层4、第二图案层5、透明釉层6和液态玻璃层7。
更进一步地，坯体层的原料中包含了低温莫来石晶须；所述莫来石晶须是以SiCl4、乙醚、Al(NO3)3、AlF3、乙醇、NH4Cl、ZnO、La2O3为原料通过溶胶凝胶法制得。其中，ZnO可作为烧结助剂；通过掺杂 La2O3，改变莫来石晶须的微观结构，使莫来石晶须的长径比提高，有助力提高坯体的强度，同时溶胶凝胶工艺获得的莫来石晶须的纯度更高，杂质含量少。
更进一步地，所述面釉层的颜色与微晶层的颜色相同。面釉层的颜色与微晶层的颜色相同可以确保陶瓷砖表面达到类似金珀、绿珀的那种晶莹度，不会因面釉发色差异使陶瓷砖表面的晶莹度大大折扣。
更进一步地，所述彩色透明微晶玻璃粉粒径为50-75μm，粒径分布范围程对称分布，微晶玻璃粉粒之间接触程度更高，有助于高粉粒之间进行反应，降低烧制温度。
更进一步地，所述第一图案层和第二图案层由发光陶瓷墨水形成图案，有助于提高图案的层次感，丰富图案的表现形式。
更进一步地，所述液态玻璃层是采用纳米液态玻璃喷剂喷涂形成的一层相当于15～30个分子的厚度超薄膜层，液态玻璃几乎由纯二氧化硅构成，因此惰性十足，无毒无污染，对水、污垢和细菌具有排斥性，可使陶瓷砖表面具有一定的抑菌作用，同时提高陶瓷砖表面的耐酸性能。
下面进一步例举实施例以详细说明本发明。下述示例具体的工艺参数等也仅是合适范围中的一个示例，即本领域技术人员可以通过本文的说明做合适的范围内选择，而并非要限定于下文示例的具体数值。
实施例一
一种仿透明琥珀陶瓷砖，微晶层所用的彩色透明微晶玻璃粉，按照重量百分比组成如下：SiO2:65％、Al2O3:20％、Li2O:3％，MgO:4％、 ZnO:1％、Na2O：l:1％、B2O3:4％、Pb2O5:0.2％、TiO2：0.15％和CeO2： 1.35％。
一种仿透明琥珀陶瓷砖的制备方法，其工艺包含以下步骤：
1):将混有低温莫来石晶须的坯体原料经过压机干压成型方式获得坯体层，其中压机压力为3800T。
2):在坯体层上通过淋釉或喷釉的方式施加一层面釉，得面釉层，面釉层原料中通过加入着色剂TiO2和CeO2并经过实验确保与微晶层发色一致。
3):按照陶瓷砖版面设计图案，通过喷墨打印机在面釉层上打印图案，得第一图案层。
4):面釉层打印出第一图案层后，经过干燥窑干燥，使第一图案层上发光陶瓷墨水中油性溶剂成分挥发掉，便于后续布料。经过干燥窑干燥后，使用布料车在第一图案层上铺一层彩色透明微晶玻璃粉，彩色透明微晶玻璃粉的厚度太薄时，不耐高温，析晶度不高，形成不了微晶的效果，因此彩色透明微晶玻璃粉最佳铺料厚度为2～3mm。铺料完毕后进窑炉在1200℃下烧制，得微晶层。彩色透明微晶玻璃粉的厚度太厚，烧制后的微晶析晶量大，微晶层的透明度降低，
5):采用步骤3)的方法在上述微晶层上打印图案，得第二图案层；更优地，当第二图案层打印完毕后，使陶瓷砖砖体进入干燥窑干燥，将第二图案层上发光陶瓷墨水中油性溶剂成分挥发掉，使后道工序施釉完毕后，釉面不容易出现凹釉等釉面缺陷。
6):在步骤5)的陶瓷砖上通过淋釉或喷釉方式施一层透明釉，进行烧制；烧制过程中，透明釉能对第二图案层的色彩进行保护；此外烧成温度较低或较高，都会影响釉的透明度，并且烧成温度较低时，釉面少量针孔和大量气泡，在本实施例中，烧制温度为1150℃，得透明釉层。
7):将经过二次烧制地陶瓷砖稍稍打磨、抛光后，在透明釉层表面喷涂一层纳米“液态玻璃”喷剂，得到具有金珀质感的陶瓷砖
本实施例中彩色透明微晶玻璃粉，以TiO2和CeO2为着色剂，铈和钛能使玻璃产生金黄色，通过改变两着色剂之间的比例，使微晶层的颜色与金珀的颜色接近，同时通过二次打印图案以及二次烧成工艺后，使烧制出的陶瓷砖具有透明琥珀系类中的金珀质感。
实施例二
一种仿透明琥珀陶瓷砖，所述微晶层所用的彩色透明微晶玻璃粉，按照重量百分比组成如下:SiO2:69％、Al2O3:15％、Li2O:3％，MgO:3％、 ZnO:1％、NaCl:1％、B2O3:5％、Pb2O5:0.4％、CuO:0.5％和Cr2O3:1.5％。
一种仿绿珀陶瓷砖的制备方法，其工艺包含以下步骤：
1):将混有低温莫来石晶须的坯体原料经过压机干压成型方式获得坯体层，其中压机压力为4500T。
2):在坯体层上通过淋釉或喷釉的方式施加一层面釉，得面釉层，面釉层通过加入着色剂CuO和Cr2O3并经过实验确保与微晶层发色一致。
3):按照陶瓷砖版面设计图案，通过喷墨打印机在面釉层上打印图案，得第一图案层。
4):面釉层打印出第一图案层后，经过干燥窑干燥，使第一图案层上发光陶瓷墨水中油性溶剂成分挥发掉，便于后续布料。经过干燥窑干燥后，使用布料车在第一图案层上铺一层厚度为2～3mm的彩色透明微晶玻璃粉，进窑炉在1230℃下烧制，得微晶层。
5):采用步骤3)的方法在上述微晶层上打印图案，得第二图案层；更优地，当第二图案层打印完毕后，使陶瓷砖砖体进入干燥窑干燥，将第二图案层上发光陶瓷墨水中油性溶剂成分挥发掉，使后道工序施釉完毕后，釉面不容易出现凹釉等釉面缺陷。
6):在步骤5)的陶瓷砖上通过淋釉或喷釉方式施一层透明釉，进行烧制；烧制过程中，透明釉能对第二图案层的色彩进行保护；此外烧成温度较低或较高，都会影响釉的透明度，并且烧成温度较低时，釉面少量针孔和大量气泡，在本实施例中，烧制温度为1180℃，得透明釉层。
7):将经过二次烧制地陶瓷砖稍稍打磨、抛光后，在透明釉层表面喷涂一层纳米“液态玻璃”喷剂，得到具有绿珀质感的陶瓷砖
本实施例中彩色透明微晶玻璃粉，以CuO和Cr2O3为着色剂，通过实验得出增加铬的用量，会使铜和铬的混合色由绿色向黄色发展，因此通过调整优化两着色剂之间的比例，使微晶层的颜色符合绿珀的那种黄绿色的要求，同时通过二次打印图案以及二次烧成工艺，使烧制出的陶瓷砖具有透明琥珀系类中的绿珀质感。
可以理解的是，对本领域普通技术人员来说，可以根据本发明的技术方案及其发明构思加以等同替换或改变，而所有的这些替换或改变都应属于本发明所附的权利要求书的保护范围内。

Claims (9)

1.一种仿透明琥珀陶瓷砖，其特征在于：其结构自下而上包括坯体层、面釉层，第一图案层、微晶层、第二图案层、透明釉层和液态玻璃层；所述微晶层由彩色透明微晶玻璃粉烧制而成，所述彩色透明微晶玻璃粉，按照重量百分比组成如下：SiO2:65-75％、Al2O3:15-20％、Li2O：3-5％、MgO:3-5％、ZnO:0.7-1.5％、Na2O:1-2％、B2O3:3-5％、Pb2O5:0.2-0.4％和着色剂；其中，所述着色剂由TiO2:0.1％-0.3％和CeO2:1-2％组成，或由CuO:0.3％-0.7％和Cr2O3:0.8-1.5％组成。
2.根据权利要求1所述的一种仿透明琥珀陶瓷砖，其特征在于：所述坯体层的原料中包含了低温莫来石晶须；所述莫来石晶须以SiCl4、乙醚、Al(NO3)3、AlF3、乙醇、NH4Cl、ZnO、La2O3为原料通过溶胶凝胶法制得。
3.根据权利要求1所述的一种仿透明琥珀陶瓷砖，其特征在于：所述面釉层的颜色与微晶层的颜色相同。
4.根据权利要求1所述的一种仿透明琥珀陶瓷砖，其特征在于：所述彩色透明微晶玻璃粉粒径为50-75μm。
5.根据权利要求1所述的一种仿透明琥珀陶瓷砖，其特征在于：所述液态玻璃层为由液态玻璃组成的超薄膜层。
6.一种如权利要求1-5所述的仿透明琥珀陶瓷砖的制备方法，其特征在于:包含以下步骤：
1):将坯体层的原料进行压制得坯体层；
2):在坯体层施一层面釉，得面釉层；
3):在面釉层上打印图案，得第一图案层；
4):打印第一图案层后的砖体，经过干燥后，铺上一层厚度为2-3mm的彩色透明微晶玻璃粉，进窑炉烧制，得微晶层；
5):经过窑炉烧制得到微晶层后，在微晶层上打印图案，得第二图案层；
6):在第二图案层上施一层透明釉，进窑炉二次烧制，得透明釉层；
7):二次烧制后得陶瓷砖经过打磨、抛光工序后，得到具有透明琥珀质感的陶瓷砖。
7.根据权利要求6所述的一种仿透明琥珀陶瓷砖的制备方法，其特征在于：步骤1)中坯体层的压制压力为3800T-5000T。
8.根据权利要求6中所述的一种仿透明琥珀陶瓷砖的制备方法，其特征在于：步骤4)中所述烧制温度为1200℃-1250℃。
9.根据权利要求6中所述的一种仿透明琥珀陶瓷砖的制备方法，其特征在于：步骤6)中所述最佳烧成温度为1130℃-1180℃。
CN201911300688.4A 2019-12-17 2019-12-17 一种仿透明琥珀陶瓷砖及其制备方法 Active CN110981553B (zh)