CN110924135A - 一种基于fg-910的涤棉混纺织物的易去污整理新工艺 - Google Patents

一种基于fg-910的涤棉混纺织物的易去污整理新工艺 Download PDF

Info

Publication number
CN110924135A
CN110924135A CN201811101835.0A CN201811101835A CN110924135A CN 110924135 A CN110924135 A CN 110924135A CN 201811101835 A CN201811101835 A CN 201811101835A CN 110924135 A CN110924135 A CN 110924135A
Authority
CN
China
Prior art keywords
fabric
finishing
baking
cotton blended
easy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811101835.0A
Other languages
English (en)
Inventor
陶晓华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SANCANAL CLOTHING Co Ltd
Original Assignee
SANCANAL CLOTHING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SANCANAL CLOTHING Co Ltd filed Critical SANCANAL CLOTHING Co Ltd
Priority to CN201811101835.0A priority Critical patent/CN110924135A/zh
Publication of CN110924135A publication Critical patent/CN110924135A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种基于FG‑910的涤棉混纺织物的易去污整理新工艺，工艺步骤包括（1）将织物进行前处理得到半成品，（2）将半成品放入配置好的整理液进行浸轧功能整理，（3）将整理后的织物于105～115℃预烘2～3min，150～180℃焙烘1～2min，（4）待烘焙后的织物自然冷却后收卷，本发明工艺步骤中的整理液加入了增强剂FBA和聚醚衍生物HP，显著提高了织物的易去污性能。

Description

一种基于FG-910的涤棉混纺织物的易去污整理新工艺
技术领域
本发明涉及纺织技术后整理领域，具体地说，是一种涤棉混纺织物的后整理工艺。
背景技术
涤棉混纺织物由于涤纶纤维的疏水性和亲油性，其织物在服用过程中容易沾污油渍且油渍不易被洗掉，另外洗掉的油污还会再沾污。因此，有必要对涤棉织物进行易去污整理。
易去污整理实际上是促进水向纤维内部和油污-纤维界面的扩散，由于促进了界面的水化，因而易使油污与纤维分离。水越易扩散，油污就越易脱落。而水的扩散取决于易去污剂的溶胀能力，而溶胀能力来源于其化学性能、亲水性、交联度及水洗温度等。当然，纤维内部进水后，使油污“卷珠”离去还需要一定的机械作用力。总的来说，只要使纤维亲水性增加，就能加快水的渗入，就能有利于去污。
目前，市场上应用效果较好的亲水易去污整理剂是改性氟碳树脂类助剂，氟碳树脂类整理剂分子中既含有拒油性的氟烷基链段，又含有亲水性的聚氧乙烯链段，如北京洁尔爽高科技公司生产的FG-910易去污整理剂就是这样一种氟碳树脂溶液，外观呈乳白色乳液，兼具易去污和防止再沾污性能，但其易去污性能还有待进一步提高。
发明内容
本发明的目的在于克服上述不足，提供一种基于FG-910的涤棉混纺织物的易去污整理新工艺，以实现涤棉混纺织物更好地易去污性能。
本发明一种基于FG-910的涤棉混纺织物的易去污整理新工艺，所采用的工艺步骤包括：
（1）织物前处理：将织物于150～175℃条件下预定型，洗涤去除油污，用水冲洗至洗液pH为5～7，在95～120℃条件下将织物烘干，烘干结束后在150～180℃之间进行高温定型1～2min，得到半成品；
（2）将步骤（1）中烘干后的半成品放入整理液进行浸轧功能整理，轧余率为60～70％，所述整理液由以下浓度的组份组成：
北京洁尔爽高科技的易去污整理剂FG-910 20～50g/L，增强剂FBA 3～6g/L，聚醚衍生物HP 8～15g/L，防凝胶剂12～20g/L，所述整理液用1mol/L醋酸调节pH值为5～6；
（3）预烘、焙烘：将经过浸轧功能整理后的织物于105～115℃进行预烘，停留时间2～3min，再于150～180℃进行焙烘，停留时间1～2min；
（4）收卷：待焙烘后的织物自然冷却后收卷。
优选的，所述浸轧的方式为一浸一轧。
优选的，所述防凝胶剂为三乙基己基磷酸、十二烷基硫酸钠、聚丙烯酰胺、脂肪酸聚乙二醇酯中的一种或几种混合。
优选的，所述焙烘温度为170℃，停留时间1.5min。
本发明的有益效果：在浸轧的整理液中加入增强剂FBA，提高了织物上易去污整理剂FG-910的含量，在提高织物易去污性能的同时提高了织物的强度；加入聚醚衍生物HP，可与易去污整理剂FG-910发生协同作用，能够提高织物的亲水性，同时大大提高了织物的易去污性能。
具体实施方式
实施例1
一种基于FG-910的涤棉混纺织物的易去污整理新工艺，所采用的工艺步骤包括：
（1）织物前处理：将织物于150℃预定型，洗涤去除油污，用水冲洗至洗液pH为7，在95℃将织物烘干，烘干结束后在150℃高温定型2min，得到半成品；
（2）将步骤（1）中烘干后的半成品放入整理液进行浸轧功能整理，浸轧方式为一浸一轧,轧余率为60％，所述整理液由以下浓度的组份组成：
易去污整理剂FG-910 20g/L，增强剂FBA 3g/L，聚醚衍生物HP 8g/L，脂肪酸聚乙二醇酯12g/L，所述整理液用1mol/L醋酸调节pH值为6；
（3）预烘、焙烘：将经过浸轧功能整理后的织物于105℃进行预烘，停留时间3min，再于150℃进行焙烘，停留时间2min；
（4） 收卷：待焙烘后的织物自然冷却后收卷；
（5）易去污性能测试，按AATCC-130-2000标准和测试方法，分为1～5级，级别高的效果好，测试用油为玉米油。
实施例2
一种基于FG-910的涤棉混纺织物的易去污整理新工艺，所采用的工艺步骤包括：
（1）织物前处理：将织物于165℃预定型，洗涤去除油污，用水冲洗至洗液pH为6，在110℃将织物烘干，烘干结束后在170℃进行高温定型1.5min，得到半成品；
（2）将步骤（1）中烘干后的半成品放入整理液进行浸轧功能整理，浸轧方式为一浸一轧,轧余率为65％，所述整理液由以下浓度的组份组成：
易去污整理剂FG-910 30g/L，增强剂FBA 4g/L，聚醚衍生物HP 12g/L，聚丙烯酰胺15g/L，所述整理液用1mol/L醋酸调节pH值为5；
（3）预烘、焙烘：将经过浸轧功能整理后的织物于110℃进行预烘，停留时间1min，再于170℃进行焙烘，停留时间1.5min；
（4） 收卷：待焙烘后的织物自然冷却后收卷；
（5）易去污性能测试，按AATCC-130-2000标准和测试方法，分为1～5级，级别高的效果好，测试用油为玉米油。
实施例3
一种基于FG-910的涤棉混纺织物的易去污整理新工艺，所采用的工艺步骤包括：
（1）织物前处理：将织物于175℃预定型，洗涤去除油污，用水冲洗至洗液pH为5，在120℃将织物烘干，烘干结束后在180℃高温定型1min，得到半成品；
（2）将步骤（1）中烘干后的半成品放入整理液进行浸轧功能整理，浸轧方式为一浸一轧,轧余率为70％，所述整理液由以下浓度的组份组成：
易去污整理剂FG-910 50g/L，增强剂FBA 6g/L，聚醚衍生物HP 15g/L，三乙基己基磷酸10g/L，十二烷基硫酸钠10g/L，所述整理液用1mol/L醋酸调节pH值为5；
（3）预烘、焙烘：将经过浸轧功能整理后的织物于115℃进行预烘，停留时间2min，再于180℃进行焙烘，停留时间1min；
（4） 收卷：待焙烘后的织物自然冷却后收卷；
（5）易去污性能测试，按AATCC-130-2000标准和测试方法，分为1～5级，级别高的效果好，测试用油为玉米油。
实施例4（空白测试）
以实施例2为基准，在整理液中不加入增强剂FBA和聚醚衍生物HP，其他工艺条件不变，进行易去污性能测试。
易去污性能测试结果如下表：
Figure 574429DEST_PATH_IMAGE001
由上表的测试结果可知，整理液中加入增强剂FBA和聚醚衍生物HP后，织物的易去污性能有显著提高。
以上已对本发明创造的较佳实施例进行了具体说明，但本发明创造并不限于所述实施例，熟悉本领域的技术人员在不违背本发明创造精神的前提下还可做出种种的等同的变型或替换，这些等同的变型或替换均包含在本申请权利要求所限定的范围内。

Claims (4)

1.一种基于FG-910的涤棉混纺织物的易去污整理新工艺，其特征在于，所采用的工艺步骤包括：
（1）织物前处理：将织物于150～175℃条件下预定型，洗涤去除油污，用水冲洗至洗液pH为5～7，在95～120℃条件下将织物烘干，烘干结束后在150～180℃之间进行高温定型1～2min，得到半成品；
（2）将步骤（1）中烘干后的半成品放入整理液进行浸轧功能整理，轧余率为60～70％，所述整理液由以下浓度的组份组成：
北京洁尔爽高科技公司的易去污整理剂FG-910 20～50g/L，增强剂FBA 3～6g/L，聚醚衍生物HP 8～15g/L，防凝胶剂12～20g/L，所述整理液用1mol/L醋酸调节pH值为5～6；
（3）预烘、焙烘：将经过浸轧功能整理后的织物于105～115℃进行预烘，停留时间2～3min，再于150～180℃进行焙烘，停留时间1～2min；
（4）收卷：待焙烘后的织物自然冷却后收卷。
2.如权利要求1所述的一种基于FG-910的涤棉混纺织物的易去污整理新工艺，其特征在于，所述浸轧的方式为一浸一轧。
3.如权利要求1所述的一种基于FG-910的涤棉混纺织物的易去污整理新工艺，其特征在于，所述防凝胶剂为三乙基己基磷酸、十二烷基硫酸钠、聚丙烯酰胺、脂肪酸聚乙二醇酯中的一种或几种混合。
4.如权利要求1所述的一种基于FG-910的涤棉混纺织物的易去污整理新工艺，其特征在于，所述焙烘温度为170℃，停留时间为1.5min。
CN201811101835.0A 2018-09-20 2018-09-20 一种基于fg-910的涤棉混纺织物的易去污整理新工艺 Withdrawn CN110924135A (zh)