CN110804261A - 一种绿色环保消防喷淋用pvc-c管材及其制备方法 - Google Patents
一种绿色环保消防喷淋用pvc-c管材及其制备方法 Download PDFInfo
- Publication number
- CN110804261A CN110804261A CN201911100806.7A CN201911100806A CN110804261A CN 110804261 A CN110804261 A CN 110804261A CN 201911100806 A CN201911100806 A CN 201911100806A CN 110804261 A CN110804261 A CN 110804261A
- Authority
- CN
- China
- Prior art keywords
- pvc
- parts
- pipe
- environment
- friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种绿色环保消防喷淋用PVC‑C管材及其制备方法,属于塑料管道领域。本发明的PVC‑C管材的制备原料包含如下重量份的组分:PVC‑C树脂100份、环保无毒稀土复合稳定剂5~10份、抗冲改性剂3~6份、内润滑剂0.2~1份、外润滑剂1~2份、阻燃剂A 0.1~1份、阻燃剂B 1~5份、填充剂2~10份、抗氧剂1~2份、颜料0.01~0.2份。本发明的PVC‑C管材的耐高温、防腐、抗压、抗菌、耐酸碱性和耐候性能等得到大幅提升,同时具备良好的物理机械性能和成型加工性能;并且所用的原料均为无毒、无害物质,绿色环保,不会产生污染及二次污染,具有广阔的应用前景。
Description
技术领域
本发明涉及一种绿色环保消防喷淋用PVC-C管材及其制备方法,属于塑料管道领域。
背景技术
消防喷淋用管道顾名思义是为了消防喷淋建立的管道系统,由于其特殊性,消防管道的厚度与材质都有特殊要求。消防喷淋管材应根据设计要求选用,国内目前一般采用镀锌碳素钢管及管件,目前镀锌工艺主要有电镀锌、热浸镀锌等。电镀锌工艺中含有Cd、Hg、Pb、Cr6+等有毒物质,产生严重的环境污染。热浸镀锌工艺具有明显锌耗高、能耗大及废液污染严重的局限性。而且随着使用时间的延长,镀锌钢管内壁会被带氯的自来水逐渐腐蚀,脱落的铁渣会堵塞消防系统中的管路和喷头,严重影响消防灭火效率;此外,镀锌钢管的自重大,单位长度的成本高,安装也不方便,连接处容易漏水。塑料管材虽然绿色节能,能克服管壁生锈,但大多数塑料管材不能在高温下工作,且多为易燃性材料,燃烧时会生烟,在很大程度上限制了塑料管材在消防管道系统的应用。
PVC-C管材以其高维卡、阻燃、消烟、耐用等优点已经在国外被成功地应用于消防管道系统多年。但由于氯化聚氯乙烯含氯量高加工难度大,目前消防用PVC-C管材多数采用复合铅或有机锡热稳定剂生产。这种工艺生产出的PVC-C管材不环保且耐热性能、机械性能和加工性能等也较差。因此,很有必要研发一种耐高温、具有良好的机械性能和加工性能且绿色环保的消防用PVC-C管材及其制备方法。
发明内容
本发明的目的在于克服上述现有技术的不足之处而提供一种绿色环保消防喷淋用PVC-C管材及其制备方法,本发明提供的PVC-C管材的耐高温、防腐、抗压、抗菌、耐酸碱性和耐候性能等得到大幅提升,同时具备良好的物理机械性能和成型加工性能。
为实现上述目的,本发明采取的技术方案为:一种绿色环保消防喷淋用PVC-C管材,所述PVC-C管材的制备原料包含如下重量份的组分:PVC-C树脂100份、环保无毒稀土复合稳定剂5~10份、抗冲改性剂3~6份、内润滑剂0.2~1份、外润滑剂1~2份、阻燃剂A 0.1~1份、阻燃剂B1~5份、填充剂2~10份、抗氧剂1~2份、颜料0.01~0.2份。
本发明的技术领域为绿色环保消防喷淋用PVC-C管材领域,主要解决应用于绿色环保消防喷淋用PVC-C管材中的阻燃性问题。本发明采用环保无毒稀土复合稳定剂,同时选用特定的阻燃剂A、阻燃剂B,制备得到的PVC-C管材耐高温、具有良好的机械性能和加工性能,且绿色环保,适用于消防喷淋领域。
作为本发明所述PVC-C管材的优选实施方式,所述PVC-C树脂的含氯量为67%~70%。
作为本发明所述PVC-C管材的优选实施方式,所述环保无毒稀土复合稳定剂包含稀土元素的乙酰丙酮盐或脂肪酸盐,所述稀土元素为镧元素、镨元素、钕元素中的至少一种。
作为本发明所述PVC-C管材的优选实施方式,所述抗冲改性剂为MBS树脂或ACR树脂。
作为本发明所述PVC-C管材的优选实施方式,所述内润滑剂为脂肪酸酯或金属皂类,所述外润滑剂为聚乙烯蜡或氧化聚乙烯蜡。
作为本发明所述PVC-C管材的优选实施方式,所述阻燃剂A为硼酸锌或偏硼酸钡,所述阻燃剂B为含卤磷酸酯。
作为本发明所述PVC-C管材的优选实施方式,所述填充剂为碳酸钙或滑石粉,所述填充剂的目数为2500~3000目。
作为本发明所述PVC-C管材的优选实施方式,所述抗氧剂为β-(4-羟基-3,5-二叔丁基苯基)丙酸正十八酯。
作为本发明所述PVC-C管材的优选实施方式,所述颜料为质量比为2:1的永固橘黄和耐晒大红的混合物。
第二方面,本发明提供了上述PVC-C管材的制备方法,包括以下步骤:
(1)将各原料组分加入高低混料机中,混合到110~130℃时转入冷混,降温至40~50℃,得到混配料;
(2)将步骤(1)所得的混配料加入平行双螺杆挤出机,通过模具进行挤出,经过定型冷却后切割,得到绿色环保消防喷淋用PVC-C管材。
作为本发明所述PVC-C管材的制备方法的优选实施方式,所述步骤(2)中,平行双螺杆挤出机的机筒温度设置为150~180℃,模具的温度设置为160~210℃进行挤出。
与现有技术相比,本发明的有益效果为:本发明采用无毒无铅环保的稀土复合稳定剂,不但改善了PVC-C管材熔体黏度大、难生产的问题,而且得到了耐高温、防腐、抗压、抗菌、耐酸碱性和不易老化的管材,同时具备良好的物理机械性能和成型加工性能,其维卡软化温度达到110℃以上;并且原料均为无毒、无害物质,绿色环保,不会产生污染及二次污染,具有广阔的应用前景。
具体实施方式
为更好地说明本发明的目的、技术方案和优点,下面将结合具体实施例对本发明作进一步说明。
本发明实施例中的所用试剂和材料均为市购。其中,环保无毒稀土复合稳定剂采用包头稀土研究院“稀牛”牌BRE-G系列管材用稀土复合稳定剂,PVC-C树脂的含氯量为67%~70%。
实施例1
一种绿色环保消防喷淋用PVC-C管材,制备原料包含如下重量份的组分:PVC-C树脂100份、环保无毒稀土复合稳定剂6份、聚乙烯蜡1.5份、氧化聚乙烯蜡0.3份、单甘酯0.5份、MBS树脂5份、活性轻质碳酸钙(2500目)5份、阻燃剂A为硼酸锌0.3份、阻燃剂B为三(二氯异丙基)磷酸酯2份、β-(4-羟基-3,5-二叔丁基苯基)丙酸正十八酯1.5份、质量比为2:1的永固橘黄和耐晒大红的混合物0.05份。
本实施例绿色环保消防喷淋用PVC-C管材的制备方法如下:
(1)将各原料组分加入高低混料机中,混合到110~130℃时转入冷混,降温至40~50℃,得到混配料;
(2)将步骤(1)所得的混配料加入平行双螺杆挤出机,通过模具进行挤出,经过定型冷却后切割,得到绿色环保消防喷淋用PVC-C管材,平行双螺杆挤出机的机筒温度设置为150~180℃,模具的温度设置为160~210℃进行挤出。
实施例2
一种绿色环保消防喷淋用PVC-C管材,制备原料包含如下重量份的组分:PVC-C树脂100份、环保无毒稀土复合稳定剂7份、聚乙烯蜡1.2份、硬脂酸0.3份、单甘酯0.3份、ACR树脂6份、滑石粉(2500目)5份、阻燃剂A为偏硼酸钡0.4份、阻燃剂B为三(二氯异丙基)磷酸酯3份、β-(4-羟基-3,5-二叔丁基苯基)丙酸正十八酯1.5份、质量比为2:1的永固橘黄和耐晒大红的混合物0.05份。
本实施例绿色环保消防喷淋用PVC-C管材的制备方法同实施例1。
实施例3
一种绿色环保消防喷淋用PVC-C管材,制备原料包含如下重量份的组分:PVC-C树脂100份、环保无毒稀土复合稳定剂8份、聚乙烯蜡1.2份、氧化聚乙烯蜡0.4份、单甘酯0.3份、MBS树脂6份、重质碳酸钙(2500目)5份、阻燃剂A为偏硼酸钡0.5份、阻燃剂B为三(二氯异丙基)磷酸酯4份、β-(4-羟基-3,5-二叔丁基苯基)丙酸正十八酯1.5份、质量比为2:1的永固橘黄和耐晒大红的混合物0.05份。
本实施例绿色环保消防喷淋用PVC-C管材的制备方法同实施例1。
实施例4
一种绿色环保消防喷淋用PVC-C管材,制备原料包含如下重量份的组分:PVC-C树脂100份、环保无毒稀土复合稳定剂9份、聚乙烯蜡1.0份、氧化聚乙烯蜡0.3份、单甘酯0.3份、MBS树脂6份、活性重质碳酸钙(2500目)8份、阻燃剂A为硼酸锌0.8份、阻燃剂B为三(二氯异丙基)磷酸酯5份、β-(4-羟基-3,5-二叔丁基苯基)丙酸正十八酯1.5份、质量比为2:1的永固橘黄和耐晒大红的混合物0.05份。
本实施例绿色环保消防喷淋用PVC-C管材的制备方法同实施例1。
实施例5
一种绿色环保消防喷淋用PVC-C管材,其特征在于,所述PVC-C管材的制备原料包含如下重量份的组分:PVC-C树脂100份、环保无毒稀土复合稳定剂5份、ACR树脂6份、单甘酯0.2份、聚乙烯蜡2份、硼酸锌0.1份、三(二氯异丙基)磷酸酯1份、滑石粉(3000目)10份、β-(4-羟基-3,5-二叔丁基苯基)丙酸正十八酯1份、质量比为2:1的永固橘黄和耐晒大红的混合物0.01份。
本实施例绿色环保消防喷淋用PVC-C管材的制备方法同实施例1。
实施例6
一种绿色环保消防喷淋用PVC-C管材,其特征在于,所述PVC-C管材的制备原料包含如下重量份的组分:PVC-C树脂100份、环保无毒稀土复合稳定剂10份、MBS树脂3份、单甘酯1份、聚乙烯蜡1份、硼酸锌1份、三(二氯异丙基)磷酸酯5份、滑石粉(3000目)2份、β-(4-羟基-3,5-二叔丁基苯基)丙酸正十八酯2份、质量比为2:1的永固橘黄和耐晒大红的混合物0.2份。
本实施例绿色环保消防喷淋用PVC-C管材的制备方法同实施例1。
效果例1
将采用实施例1~6所制得的1英寸消防PVC-C管材,按照GB/T5135.19-2010标准测试所得的结果,测试结果如表1所示。
表1
由表1可知,采用本发明的组分制备得到的PVC-C管材,具备良好的耐高温、防腐、抗压、抗菌、耐酸碱性和耐候性能,同时具备良好的物理机械性能和成型加工性能,其维卡软化温度达到110℃以上;并且所用的原料均为无毒、无害物质,绿色环保,不会产生污染及二次污染,具有广阔的应用前景。
最后所应当说明的是,以上实施例仅用以说明本发明的技术方案而非对本发明保护范围的限制,尽管参照较佳实施例对本发明作了详细说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的实质和范围。
Claims (10)
1.一种绿色环保消防喷淋用PVC-C管材,其特征在于,所述PVC-C管材的制备原料包含如下重量份的组分:PVC-C树脂100份、环保无毒稀土复合稳定剂5~10份、抗冲改性剂3~6份、内润滑剂0.2~1份、外润滑剂1~2份、阻燃剂A 0.1~1份、阻燃剂B 1~5份、填充剂2~10份、抗氧剂1~2份、颜料0.01~0.2份。
2.如权利要求1所述的PVC-C管材,其特征在于,所述PVC-C树脂的含氯量为67%~70%。
3.如权利要求1所述的PVC-C管材,其特征在于,所述环保无毒稀土复合稳定剂包含稀土元素的乙酰丙酮盐或脂肪酸盐,所述稀土元素为镧元素、镨元素、钕元素中的至少一种。
4.如权利要求1所述的PVC-C管材,其特征在于,所述抗冲改性剂为MBS树脂或ACR树脂。
5.如权利要求1所述的PVC-C管材,其特征在于,所述内润滑剂为脂肪酸酯或金属皂类,所述外润滑剂为聚乙烯蜡或氧化聚乙烯蜡。
6.如权利要求1所述的PVC-C管材,其特征在于,所述阻燃剂A为硼酸锌或偏硼酸钡,所述阻燃剂B为含卤磷酸酯。
7.如权利要求1所述的PVC-C管材,其特征在于,所述填充剂为碳酸钙或滑石粉,所述填充剂的目数为2500~3000目。
8.如权利要求1所述的PVC-C管材,其特征在于,所述抗氧剂为β-(4-羟基-3,5-二叔丁基苯基)丙酸正十八酯。
9.如权利要求1所述的PVC-C管材,其特征在于,所述颜料为质量比为2:1的永固橘黄和耐晒大红的混合物。
10.如权利要求1~9所述的PVC-C管材的制备方法,其特征在于,包括以下步骤:
(1)将各原料组分加入高低混料机中,混合到110~130℃时转入冷混,降温至40~50℃,得到混配料;
(2)将步骤(1)所得的混配料加入平行双螺杆挤出机,通过模具进行挤出,经过定型冷却后切割,得到绿色环保消防喷淋用PVC-C管材。