CN110730719B - 含有助滑剂的多层薄膜和层合物 - Google Patents

含有助滑剂的多层薄膜和层合物 Download PDF

Info

Publication number
CN110730719B
CN110730719B CN201780091804.9A CN201780091804A CN110730719B CN 110730719 B CN110730719 B CN 110730719B CN 201780091804 A CN201780091804 A CN 201780091804A CN 110730719 B CN110730719 B CN 110730719B
Authority
CN
China
Prior art keywords
layer
ethylene
film
fatty acid
acid amide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201780091804.9A
Other languages
English (en)
Other versions
CN110730719A (zh
Inventor
苏凤宜
刘安栋
陈红宇
潘健平
云小兵
T·奥尔戈尔
陈尔强
赵体鹏
廖桂红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Global Technologies LLC
Original Assignee
Dow Global Technologies LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Global Technologies LLC filed Critical Dow Global Technologies LLC
Publication of CN110730719A publication Critical patent/CN110730719A/zh
Application granted granted Critical
Publication of CN110730719B publication Critical patent/CN110730719B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本公开提供共挤压多层薄膜。共挤压多层薄膜具有至少两个层，包括密封层和与密封层接触的第二层。密封层含有(A)第一乙烯类聚合物，其密度是0.865g/cc到0.930g/cc且熔融指数是0.5g/10min到25g/10min；(B)不饱和一级脂肪酸酰胺，其熔点是100℃或更低；和(C)饱和一级脂肪酸酰胺，其熔点超过100℃。不饱和一级脂肪酸酰胺与饱和一级脂肪酸酰胺具有3:1到1:6的重量比。第二层含有第二乙烯类聚合物。本公开还提供含有所述密封层的层合物。

Description

含有助滑剂的多层薄膜和层合物
背景技术
本公开涉及具有密封层的多层薄膜和层合物，所述密封层含有包括助滑剂的乙烯类组合物。
由乙烯类聚合物形成的薄膜层用于多层薄膜中以用于多种应用，包括例如食品包装和特殊包装。乙烯类聚合物外薄膜层需要低摩擦系数(COF)(例如小于0.40)以用于薄膜的有效处理，如生产线或包装线。为了获得低COF，通常向乙烯类聚合物外层(其可以是密封层)中添加助滑剂。常规助滑剂包括不饱和脂肪酸酰胺，如二十二烯酰胺和油酰胺，已知其可以通过迁移到薄膜的表面来降低薄膜的COF。但是，难以使用常规迁移性助滑剂在不同环境条件(如时间、高温、高压和各种转化过程)下保持恒定的低COF。也向乙烯类聚合物外层中添加非迁移性助滑剂，如聚硅氧，但已知其在实现低COF(例如小于0.40)方面不太有效。此外，非迁移性助滑剂比迁移性助滑剂更昂贵。
所属领域中认识到，需要包括可以在无非迁移性增滑剂的情况下呈现低COF(例如小于0.40)的乙烯类聚合层的薄膜。所属领域中还认识到，需要包括可以在无非迁移性增滑剂的情况下呈现低COF(例如小于0.40)的乙烯类聚合层的层合物。
发明内容
本公开提供共挤压多层薄膜。共挤压多层薄膜具有至少两个层，包括密封层和与密封层接触的第二层。密封层含有(A)第一乙烯类聚合物，其密度是0.865g/cc到0.930g/cc且熔融指数是0.5g/10min到25g/10min；(B)不饱和一级脂肪酸酰胺，其熔点是100℃或更低；和(C)饱和一级脂肪酸酰胺，其熔点超过100℃。不饱和一级脂肪酸酰胺与饱和一级脂肪酸酰胺具有3:1到1:6的重量比。第二层含有第二乙烯类聚合物。本公开还提供含有所述密封层的层合物。
本公开还提供层合物。层合物包括第一薄膜和第二薄膜，其中第一薄膜层合到第二薄膜。第一薄膜包括密封层，其含有(A)第一乙烯类聚合物，其密度是0.865g/cc到0.930g/cc且熔融指数是0.5g/10min到25g/10min；(B)不饱和一级脂肪酸酰胺，其熔点是100℃或更低；和(C)饱和一级脂肪酸酰胺，其熔点超过100℃。不饱和一级脂肪酸酰胺与饱和一级脂肪酸酰胺具有3:1到1:6的重量比。
定义
对元素周期表的任何参考是如由CRC Press,Inc.,1990-1991所出版的元素周期表。参考这一表中的元素族群是编号族群的新符号。
出于美国专利实务的目的，任何所参考的专利案、专利申请案或公开案的内容都以全文引用的方式并入(或其等效US版本如此以引用的方式并入)，尤其在所属领域中的定义(在与本公开中具体提供的任何定义无不一致的程度上)和常识的公开方面。
本文所公开的数值范围包括来自下限值和上限值的所有值，且包括下限值和上限值。对于含有确切值的范围(例如，1或2或3到5或6或7)，包括任何两个确切值之间的任何子范围(例如，1到2；2到6；5到7；3到7；5到6等)。
除非相反陈述、自上下文暗示或所属领域中惯用，否则所有份数和百分比都按重量计，且所有测试方法都是截至本公开的申请日为止的现行方法。
如本文中所描述，术语“烷基”(或“烷基部分”)指从脂族烃通过删除其一个氢原子而获得的有机基团。烷基部分可以是直链、支链、环状或其组合。
如本文中所使用，术语“掺合物”或“聚合物掺合物”是两种或更多种聚合物的掺合物。这类掺合物可以是或可以不是可混溶的(并非在分子程度上相分离)。这类掺合物可以是或可以不是相分离的。如由透射电子光谱法、光散射、x射线散射和所属领域中已知的其它方法所测定，这类掺合物可能含有或可能不含有一种或多种域组态。
术语“组合物”指构成所述组合物的材料混合物以及由所述组合物的材料形成的反应产物和分解产物。
术语“包含”、“包括”、“具有”和其衍生词并不意图排除任何额外组分、步骤或程序的存在，无论其是否具体地公开。为了避免任何疑问，除非相反陈述，否则经由使用术语“包含”所主张的所有组合物都可以包括任何额外添加剂、佐剂或化合物，无论聚合或以其它方式。相比之下，术语“基本上由……组成”从任何随后列举的范围中排除任何其它组分、步骤或程序，除了对可操作性来说并非必不可以少的那些以外。术语“由……组成”排除未具体叙述或列出的任何组分、步骤或程序。除非另外说明，否则术语“或”指单独地以及呈任何组合形式的所列举成员。单数的使用包括使用复数，且反之亦然。
“乙烯类聚合物”是含有超过50重量百分比聚合乙烯单体(以可聚合单体的总量计)且任选地可以含有至少一种共聚单体的聚合物。乙烯类聚合物包括乙烯均聚物和乙烯共聚物(意指来源于乙烯和一种或多种共聚单体的单元)。术语“乙烯类聚合物”与“聚乙烯”可以互换使用。乙烯类聚合物(聚乙烯)的非限制性实例包括低密度聚乙烯(LDPE)和线性聚乙烯。线性聚乙烯的非限制性实例包括线性低密度聚乙烯(LLDPE)、超低密度聚乙烯(ULDPE)、极低密度聚乙烯(VLDPE)、多组分乙烯类共聚物(EPE)、乙烯/α-烯烃多嵌段共聚物(也称为烯烃嵌段共聚物(OBC))、单点催化线性低密度聚乙烯(m-LLDPE)、基本上线性或线性塑性体/弹性体和高密度聚乙烯(HDPE)。通常，聚乙烯可以在气相流体化床反应器、液相浆液法反应器或液相溶液法反应器中使用非均相催化剂系统(如齐格勒-纳塔催化剂(Ziegler-Natta catalyst))、均相催化剂系统制造，所述均相催化剂系统包含第4族过渡金属和配位体结构，如茂金属、非茂金属金属中心、杂芳基、杂价芳氧基醚、膦亚胺等。非均质和/或均质催化剂的组合还可以在单反应器或双反应器配置中使用。在一个实施例中，乙烯类聚合物不含聚合于其中的芳族共聚单体。
“乙烯塑性体/弹性体”是含有均匀短链分支分布的基本上线性或线性乙烯/α-烯烃共聚物，包括来源于乙烯的单元和来源于至少一种C3-C10α-烯烃共聚单体或至少一种C4-C8α-烯烃共聚单体或至少一种C6-C8α-烯烃共聚单体的单元。乙烯塑性体/弹性体的密度是0.870g/cc，或0.880g/cc，或0.890g/cc到0.900g/cc，或0.902g/cc，或0.904g/cc，或0.909g/cc，或0.910g/cc，或0.917g/cc。乙烯塑性体/弹性体的非限制性实例包括AFFINITYTM塑性体和弹性体(可以从The Dow Chemical Company购得)、EXACTTM塑性体(可以从ExxonMobil Chemical购得)、TafmerTM(可以从Mitsui购得)、NexleneTM(可以从SKChemicals Co.购得)和LuceneTM(可以从LG Chem Ltd.购得)。
“脂肪酸”是具有烃链和末端羧基的羧酸。脂肪酸可以含有超过一个羧基(例如含有两个羧基的二羧基脂肪酸)。
“高密度聚乙烯”(或“HDPE”)是具有至少一种C4-C10α-烯烃共聚单体或C4-C8α-烯烃共聚单体的乙烯均聚物或乙烯/α-烯烃共聚物且密度大于0.94g/cc，或0.945g/cc，或0.95g/cc，或0.955g/cc到0.96g/cc，或0.97g/cc，或0.98g/cc。HDPE可以是单峰共聚物或多峰共聚物。“单峰乙烯共聚物”是在显示分子量分布的凝胶渗透色谱(GPC)中具有一个独特峰的乙烯/C4-C10α-烯烃共聚物。“多峰乙烯共聚物”是在显示分子量分布的GPC中具有至少两个明显的峰的乙烯/C4-C10α-烯烃共聚物。多峰包含具有两个峰(双峰)的共聚物以及具有超过两个峰的共聚物。HDPE的非限制性实例包括DOWTM高密度聚乙烯(HDPE)树脂(可以从TheDow Chemical Company购得)、ELITETM增强型聚乙烯树脂(可以从The Dow ChemicalCompany购得)、CONTINUUMTM双峰聚乙烯树脂(可以从The Dow Chemical Company购得)、LUPOLENTM(可以从LyondellBasell购得)，以及来自Borealis、Ineos和ExxonMobil的HDPE产品。
“烃”是仅含有氢原子和碳原子的化合物。烃可以是(i)支链或非支链，(ii)饱和或不饱和，(iii)环状或非环状，和(iv)(i)-(iii)的任何组合。烃的非限制性实例包括烷烃、烯烃和炔烃。
“互聚物”是通过使至少两种不同单体聚合来制备的聚合物。这一通用术语包括共聚物，其通常用于指由两种不同单体制备的聚合物，和由超过两种不同单体制备的聚合物，例如三聚物、四聚物等。
“低密度聚乙烯”(或“LDPE”)由乙烯均聚物，或包含至少一种C3-C10α-烯烃，优选密度是0.915g/cc到0.940g/cc的C3-C4且含有具有宽MWD的长链分支的乙烯/α-烯烃共聚物组成。LDPE通常通过高压自由基聚合(具有自由基引发剂的管状反应器或高压釜)制备。LDPE的非限制性实例包括MarFlexTM(Chevron Phillips)、LUPOLENTM(LyondellBasell)以及来自Borealis、Ineos、ExxonMobil的LDPE产品等。
“线性低密度聚乙烯”(或“LLDPE”)是含有非均匀短链分支分布的线性乙烯/α-烯烃共聚物，包含来源于乙烯的单元和来源于至少一种C3-C10α-烯烃共聚单体或至少一种C4-C8α-烯烃共聚单体或至少一种C6-C8α-烯烃共聚单体的单元。LLDPE的特征在于，相比于常规LDPE，长链分支极少(若存在)。LLDPE的密度是0.910g/cc，或0.915g/cc，或0.920g/cc，或0.925g/cc到0.930g/cc，或0.935g/cc，或0.940g/cc。LLDPE的非限制性实例包括TUFLINTM线性低密度聚乙烯树脂(可以从The Dow Chemical Company购得)、DOWLEXTM聚乙烯树脂(可以从Dow Chemical Company购得)和MARLEXTM聚乙烯(可以从Chevron Phillips购得)。
“多组分乙烯类共聚物”(或“EPE”)包括来源于乙烯的单元和来源于至少一种C3-C10α-烯烃共聚单体，或至少一种C4-C8α-烯烃共聚单体或至少一种C6-C8α-烯烃共聚单体的单元，如专利参考文献USP 6,111,023；USP 5,677,383；和USP6,984,695中所描述。EPE树脂的密度是0.905g/cc，或0.908g/cc，或0.912g/cc，或0.920g/cc到0.926g/cc，或0.929g/cc，或0.940g/cc，或0.962g/cc。EPE树脂的非限制性实例包括ELITETM增强型聚乙烯(可以从TheDow Chemical Company购得)、ELITE ATTM先进技术树脂(可以从The Dow ChemicalCompany购得)、SURPASSTM聚乙烯(PE)树脂(可以从Nova Chemicals购得)和SMARTTM(可以从SK Chemicals Co.购得)。
“烯烃类聚合物”或“聚烯烃”是含有(以可聚合单体的总量计)超过50重量百分比的聚合烯烃单体且任选地可以含有至少一种共聚单体的聚合物。烯烃类聚合物的非限制性实例包括乙烯类聚合物和丙烯类聚合物。
“聚合物”是通过使以聚合形式提供组成聚合物的多个和/或重复“单元”或“单体单元(mer unit)”的单体(不论相同或不同类型)聚合而制备的化合物。因此，通用术语聚合物涵盖术语均聚物，均聚物通常用于指由仅一种类型的单体制备的聚合物，和术语互聚物，互聚物通常用于指由至少两种类型的单体制备的聚合物。其还涵盖共聚物的所有形式，例如无规、嵌段等。术语“乙烯/α-烯烃聚合物”和“丙烯/α-烯烃聚合物”指示如上文所描述的分别由乙烯或丙烯和一种或多种其它可聚合α-烯烃单体聚合制备的共聚物。应注意，尽管聚合物通常称为“由一种或多种具体单体制成”、“基于”具体单体或单体类型、“含有”具体单体含量或其类似表述，但在这种情形下，术语“单体”应理解为指具体单体的聚合遗留物，且不指未聚合物种。一般来说，本文中的聚合物指基于作为对应单体的聚合形式的“单元”。
“丙烯类聚合物”是含有(以可聚合单体的总量计)超过50重量百分比的聚合丙烯单体且任选地可以含有至少一种共聚单体的聚合物。
“单点催化线性低密度聚乙烯”(或“m-LLDPE”)是含有均匀短链分支分布的线性乙烯/α-烯烃共聚物，包含来源于乙烯的单元和来源于至少一种C3-C10α-烯烃共聚单体或至少一种C4-C8α-烯烃共聚单体或至少一种C6-C8α-烯烃共聚单体的单元。m-LLDPE的密度是0.913g/cc，或0.918g/cc，或0.920g/cc到0.925g/cc，或0.940g/cc。m-LLDPE的非限制性实例包括EXCEEDTM茂金属PE(可以从ExxonMobil Chemical购得)、LUFLEXENTM m-LLDPE(可以从LyondellBasell购得)和ELTEXTM PF m-LLDPE(可以从Ineos Olefins&Polymers购得)。
“超低密度聚乙烯”(或“ULDPE”)和“极低密度聚乙烯”(或“VLDPE”)各自是含有非均匀短链分支分布、包含来源于乙烯的单元和来源于至少一种C3-C10α-烯烃共聚单体，或至少一种C4-C8α-烯烃共聚单体或至少一种C6-C8α-烯烃共聚单体的单元的线性乙烯/α-烯烃共聚物。ULDPE和VLDPE的密度各自是0.885g/cc，或0.90g/cc到0.915g/cc。ULDPE和VLDPE的非限制性实例包括ATTANETM ULDPE树脂(可以从The Dow Chemical Company购得)和FLEXOMERTM VLDPE树脂(可以从The Dow Chemical Company购得)。
测试方法
根据ASTM D1894测量摩擦系数(COF)。使用含有DOWLEXTM 2045G和1000ppm二十二烯酰胺的基体薄膜，固定到来自Guangzhou Biaoji Packaging Instrument Co.Ltd.的GM-1COF测试仪上，COF测量为薄膜与薄膜动态COF。在室温(25℃)和35％相对湿度下测量COF。在100毫米/分钟的滑动速度下，沿机器方向测量COF。在未层合的薄膜样品上测量“层合前COF”。在40℃下固化48小时之后，在层合结构上测量“层合物40℃固化COF”。在55℃下固化48小时之后，在层合结构上测量“层合物55℃固化COF”。
“分解温度”是二质子脂肪酸发生化学分解(即，一个或多个化学键断裂)的温度。通过将20mg样品放入铂盘中，随后引入TGA Q500仪器的转盘中来测量分解温度。在氮/空气气氛中，以10℃/分钟的速率将样品从室温(25℃)加热到700℃。TA软件报道分解温度。
根据ASTM D792，方法B测量密度。结果以克/立方厘米(g/cc)记录。
使用ASTM D-1238-04(190℃/2.16kg)测量熔融指数(MI)(I2)(g/10min)。
差示扫描热量测定(DSC)
差示扫描热量测定法(DSC)可以用于测量经历大范围温度的聚合物的熔融、结晶和玻璃转移行为。举例来说，使用配备有RCS(冷冻冷却系统)和自动取样器的TAInstruments Q1000 DSC进行这一分析。在测试期间，使用50ml/min的氮气冲洗气流。将各样品在190℃下熔融压成薄膜；随后使熔融样品空气冷却到室温(25℃)。将3-10mg、6mm直径样品从被冷却的聚合物取出，称重，置放于轻质铝盘(50mg)中，且卷曲关闭。随后进行分析，以确定其热特性。
通过缓慢升高和降低样品温度以建立热流相对于温度分布曲线来确定样品的热特性。首先，样品快速加热到180℃，且保持等温3分钟，以去除其热历程。接着，样品以10℃/分钟冷却速率冷却到-80℃，且在-80℃下保持等温3分钟。接着，样品以10℃/分钟加热速率加热到180℃(这是“第二加热”匀变)。记录冷却和第二加热曲线。所确定的值是外推的熔融起始Tm和外推的结晶起始Tc。对于聚乙烯样品，熔化热(Hf)(以焦耳/克为单位)、所计算的结晶度％使用以下等式：结晶度％＝((Hf)/292J/g)×100；且对于聚乙烯样品所计算的结晶度％使用以下等式：结晶度％＝((Hf)/292J/g)×100。熔化热(Hf)和峰值熔融温度由第二加热曲线报道。峰值结晶温度由冷却曲线测定。
熔点Tm由DSC加热曲线通过在熔融转移开始与结束之间第一次绘制基线来判定。随后绘制在熔融峰的低温侧上的数据的切线。此线与基线相交之处是外推熔融起始(Tm)。这是如Bernhard Wunderlich,《热表征聚合材料92的热分析基础(The Basis of ThermalAnalysis,in Thermal Characterization of Polymeric Materials 92)》,277-278(Edith A.Turi编，1997年第2版)中所描述。
具体实施方式
本公开提供共挤压多层薄膜。共挤压多层薄膜具有至少两个层，包括密封层和与密封层接触的第二层。密封层含有(A)第一乙烯类聚合物，其密度是0.865g/cc到0.930g/cc且熔融指数是0.5g/10min到25g/10min；(B)不饱和一级脂肪酸酰胺，其熔点是100℃或更低；和(C)饱和一级脂肪酸酰胺，其熔点超过100℃。不饱和一级脂肪酸酰胺与饱和一级脂肪酸酰胺具有3:1到1:6的重量比。第二层含有第二乙烯类聚合物。
多层薄膜含有两个层，或超过两个层。举例来说，多层薄膜可以具有两个、三个、四个、五个、六个、七个、八个、九个、十个、十一个或更多个层。在一个实施例中，多层薄膜含有仅两个层，或仅三个层。
1.密封层
共挤压多层薄膜含有密封层。密封层含有(A)第一乙烯类聚合物，其密度是0.865g/cc到0.930g/cc且熔融指数是0.5g/10min到25g/10min；(B)不饱和一级脂肪酸酰胺，其熔点是100℃或更低；(C)饱和一级脂肪酸酰胺，其熔点超过100℃；(D)任选的二质子脂肪酸，其熔点超过100℃且分解温度超过200℃；和(E)任选的添加剂。不饱和一级脂肪酸酰胺与饱和一级脂肪酸酰胺具有3:1到1:6的重量比。
密封层具有两个相对表面。在一个实施例中，密封层是具有两个相对表面的连续层。
A.第一乙烯类聚合物
密封层含有第一乙烯类聚合物。乙烯类聚合物的密度是0.865g/cc到0.930g/cc且熔融指数是0.5g/10min到25g/10min。适合的乙烯类聚合物的非限制性实例包括LDPE和线性聚乙烯。线性聚乙烯的非限制性实例包括LLDPE、ULDPE、VLDPE、EPE、乙烯/α-烯烃多嵌段共聚物(也称为OBC)、m-LLDPE、基本上线性或线性塑性体/弹性体和其组合。适合的乙烯类聚合物的非限制性实例还包括乙烯/α-烯烃互聚物和乙烯/α-烯烃共聚物。适合的α-烯烃的非限制性实例包括C3-C20α-烯烃，或C4-C20α-烯烃，或C3-C10α-烯烃，或C4-C10α-烯烃，或C4-C8α-烯烃。代表性α-烯烃包含丙烯、1-丁烯、1-戊烯、1-己烯、1-庚烯和1-辛烯。在一个实施例中，乙烯类聚合物是乙烯/1-辛烯互聚物。
在一个实施例中，以乙烯类聚合物的重量计，乙烯类聚合物含有超过50重量％的来源于乙烯的单元，或51重量％，或55重量％，或60重量％到70重量％，或80重量％，或90重量％，或95重量％，或99重量％，或100重量％的来源于乙烯的单元；和倒数量的来源于α-烯烃共聚单体的单元，或小于50重量％，或49重量％，或45重量％，或40重量％到30重量％，或20重量％，或10重量％，或5重量％，或1重量％，或0重量％的来源于α-烯烃共聚单体的单元。
乙烯类聚合物的密度是0.865g/cc，或0.870g/cc，或0.875g/cc，或0.880g/cc，或0.885g/cc，或0.890g/cc，或0.895g/cc，或0.900g/cc，或0.910g/cc，或0.915g/cc到0.920g/cc，或0.925g/cc，或0.930g/cc。
乙烯类聚合物的熔融指数是0.5g/10min，或1.0g/10min到1.5g/10min，或2.0g/10min，或3.0g/10min，或4.0g/10min，或5.0g/10min，或8.0g/10min，或10g/10min，或15g/10min，或20g/10min，或25g/10min。
在一个实施例中，乙烯类聚合物是LLDPE。LLDPE是乙烯均聚物或乙烯/α-烯烃共聚物，其由来源于乙烯的单元和C3-C10α-烯烃共聚单体或C4-C8α-烯烃共聚单体或C6-C8α-烯烃共聚单体组成。在一个实施例中，LLDPE的密度是0.910g/cc，或0.915g/cc，或0.920g/cc到0.925g/cc，或0.930g/cc；且熔融指数是0.5g/10min，或1.0g/10min到1.5g/10min，或2.0g/10min，或3.0g/10min，或4.0g/10min，或5.0g/10min，或8.0g/10min，或10g/10min，或15g/10min，或20g/10min，或25g/10min。在一个实施例中，乙烯类聚合物是LLDPE，其是乙烯/1-辛烯共聚物。
在一个实施例中，乙烯类聚合物是LDPE。LDPE是乙烯均聚物或乙烯/α-烯烃共聚物，其由来源于乙烯的单元和C3-C10α-烯烃共聚单体或C4-C8α-烯烃共聚单体或C6-C8α-烯烃共聚单体组成。在一个实施例中，LDPE的密度是0.915g/cc，0.916g/cc到0.918g/cc，或0.920g/cc，或0.925g/cc，或0.930g/cc；且熔融指数是0.5g/10min，或1.0g/10min，或1.5g/10min，或2.0g/10min，或3.0g/10min，或4.0g/10min，或5.0g/10min，或8.0g/10min到10g/10min，或11g/10min，或15g/10min，或20g/10min，或25g/10min。
密封层可以含有超过一种乙烯类聚合物。在一个实施例中，密封层包括至少两种乙烯类聚合物，其中每种乙烯类聚合物彼此在组成上、结构上和/或物理上不同。举例来说，密封层可以含有LLDPE和LDPE。
在一个实施例中，以密封层的总重量计，密封层含有70重量％，或75重量％，或80重量％，或85重量％，或90重量％到93重量％，或94重量％，或95重量％，或98重量％，或99重量％，或99.5重量％，或99.99重量％的乙烯类聚合物。在另一实施例中，以密封层的总重量计，密封层含有94重量％，或95重量％，或99重量％到99.99重量％的乙烯类聚合物。
在一个实施例中，乙烯类聚合物选自LLDPE、LDPE和其组合。以密封层的总重量计，密封层含有85重量％，或90重量％，或92重量％到93重量％，或94重量％的LLDPE；和1重量％，或2重量％，或3重量％，或4重量％，或5重量％，或6重量％，或7重量％到8重量％，或9重量％，或10重量％的LDPE。
乙烯类聚合物可以包含两种或更多种本文中所公开的实施例。
B.不饱和一级脂肪酸酰胺
密封层含有具有100℃或更低的熔点的不饱和一级脂肪酸酰胺。“不饱和一级脂肪酸酰胺”是具有结构(I)的分子：
Figure BDA0002308597080000111
其中R是C3到C24烷基部分，其是单不饱和或多不饱和。在一个实施例中，R是C11到C24，或C15到C23烷基部分，或C17到C21烷基部分，其是单不饱和或多不饱和。“单不饱和”烷基部分是具有一个双键(C＝C键)的烷基，其中所有其余碳原子都经由单键(C-C键)连接。“多不饱和”烷基部分是具有至少两个双键(C＝C键)的烷基。在一个实施例中，R选自C17烷基部分和C21烷基部分，其是单不饱和或多不饱和。在一个实施例中，R是单不饱和。适合的不饱和一级脂肪酸酰胺的非限制性实例包括二十二烯酰胺、油酰胺和其组合。
在一个实施例中，在结构(I)的不饱和一级脂肪酸酰胺中，R是C21烷基部分，其是单不饱和。在另一实施例中，不饱和一级脂肪酸酰胺是二十二烯酰胺。二十二烯酰胺具有以下结构(II)：
Figure BDA0002308597080000121
在一个实施例中，在结构(I)的不饱和一级脂肪酸酰胺中，R是C17烷基部分，其是单不饱和。在另一实施例中，不饱和一级脂肪酸酰胺是油酰胺。油酰胺具有以下结构(III)：
Figure BDA0002308597080000122
不饱和一级脂肪酸酰胺具有100℃或更低的熔点。在一个实施例中，不饱和一级脂肪酸酰胺的熔点是40℃，或50℃，或60℃，或65℃，或70℃，或75℃到80℃，或85℃，或90℃，或95℃，或100℃。在一个实施例中，不饱和一级脂肪酸酰胺是二十二烯酰胺，其熔点是75℃-80℃。在另一实施例中，不饱和一级脂肪酸酰胺是油酰胺，其熔点是70℃。
密封层可以含有超过一种不饱和一级脂肪酸酰胺。在一个实施例中，密封层包括至少两种不饱和一级脂肪酸酰胺，其中每种不饱和一级脂肪酸酰胺在组成上、结构上和/或物理学上彼此不同。
在一个实施例中，以密封层的总重量计，密封层含有0.0016重量％(16百万分率(ppm))，或0.0075重量％(75ppm)，或0.04重量％(400ppm)，或0.06重量％(600ppm)到0.12重量％(1200ppm)，或0.18重量％(1800ppm)，或0.83重量％(8300ppm)，或1.0重量％(10000ppm)，或2.0重量％(20000ppm)，或3.0重量％(30000ppm)，或3.83重量％(38300ppm)的不饱和一级脂肪酸酰胺。
不饱和一级脂肪酸酰胺可以包含两种或更多种本文中所公开的实施例。
C.饱和一级脂肪酸酰胺
密封层含有饱和一级脂肪酸酰胺，其熔点超过100℃。“饱和一级脂肪酸酰胺”是具有结构(IV)的分子：
Figure BDA0002308597080000131
其中R1是C3到C27烷基部分，其是饱和的。在一个实施例中，R1是C11到C25，或C15到C23烷基部分，或C15到C21烷基部分，其是饱和的。“饱和”烷基部分是其中所有碳原子经由单键(C-C键)彼此连接的烷基。换句话说，饱和烷基部分不包括经由双键(C＝C键)连接的碳原子。在一个实施例中，R1选自饱和的C17烷基部分和C21烷基部分。适合的饱和一级脂肪酸酰胺的非限制性实例包括山嵛酰胺、棕榈酸酰胺、硬脂酰胺和其组合。
在一个实施例中，在结构(IV)的饱和一级脂肪酸酰胺中，R1是饱和的C21烷基部分。在另一实施例中，饱和一级脂肪酸酰胺是山嵛酰胺。山嵛酰胺具有以下结构(V)：
Figure BDA0002308597080000132
在一个实施例中，在结构(IV)的饱和一级脂肪酸酰胺中，R1是饱和的C15烷基部分。在另一实施例中，饱和一级脂肪酸酰胺是棕榈酸酰胺。
在一个实施例中，在结构(IV)的饱和一级脂肪酸酰胺中，R1是饱和的C17烷基部分。在另一实施例中，饱和一级脂肪酸酰胺是硬脂酰胺。
饱和一级脂肪酸酰胺的熔点超过100℃。在一个实施例中，饱和一级脂肪酸酰胺的熔点是从超过100℃到150℃，或从101℃，或102℃，或103℃，或104℃，或105℃，或106℃到113℃，或115℃，或120℃，或125℃，或130℃，或135℃，或140℃，或145℃，或150℃。在一个实施例中，饱和一级脂肪酸酰胺是山嵛酰胺，其熔点是108℃-113℃。在另一实施例中，饱和一级脂肪酸酰胺是棕榈酸酰胺，其熔点是106℃-107℃。在另一实施例中，饱和一级脂肪酸酰胺是硬脂酰胺，其熔点是109℃。
密封层可以含有超过一种饱和一级脂肪酸酰胺。在一个实施例中，密封层包括至少两种饱和一级脂肪酸酰胺，其中每种饱和一级脂肪酸酰胺在组成上、结构上和/或物理学上彼此不同。
在一个实施例中，以密封层的总重量计，密封层含有0.0025重量％(25ppm)，或0.0083重量％(83ppm)，或0.01重量％(100ppm)，或0.06重量％(600ppm)到0.12重量％(1200ppm)，或0.18重量％(1800ppm)，或1.0重量％(10000ppm)，或1.25重量％(12500ppm)，或2.0重量％(20000ppm)，或3.0重量％(30000ppm)，或4.0重量％(40000ppm)，或4.1重量％(41000ppm)的饱和一级脂肪酸酰胺。
饱和一级脂肪酸酰胺可以包含两种或更多种本文中所公开的实施例。
D.任选的二质子脂肪酸
在一个实施例中，密封层包括二质子脂肪酸，其熔点超过100℃且分解温度超过200℃。“二质子脂肪酸”是每个分子具有两个可以电离氢原子的脂肪酸。适合的二质子脂肪酸的非限制性实例是二羧基脂肪酸。在一个实施例中，二质子脂肪酸是二羧基脂肪酸。适合的二羧基脂肪酸的非限制性实例包括丁二酸、己二酸、辛二酸、癸二酸和十二烷二酸。
二质子脂肪酸的熔点超过100℃。在一个实施例中，二质子脂肪酸的熔点是从100℃到250℃，或从101℃，或105℃，或110℃，或120℃，或130℃，或140℃，或150℃，或160℃，或170℃，或180℃到185℃，或190℃，或200℃，或210℃，或220℃，或230℃，或240℃，或250℃。
二质子脂肪酸的分解温度超过200℃。在一个实施例中，二质子脂肪酸的分解温度是从超过200℃到500℃，或从201℃，或210℃，或220℃，或225℃，或230℃，或235℃到240℃，或245℃，或250℃，或270℃，或300℃，或310℃，或320℃，或330℃，或350℃，或380℃，或400℃，或450℃，或500℃。
在一个实施例中，二质子脂肪酸是丁二酸，其熔点是184℃且分解温度是235℃。丁二酸具有以下结构(VI)：
Figure BDA0002308597080000141
在一个实施例中，以密封层的总重量计，密封层含有0.0025重量％(25ppm)，或0.0050重量％(50ppm)，或0.01重量％(100ppm)，或0.02重量％(200ppm)到0.06重量％(600ppm)，或0.12重量％(1200ppm)，或0.18重量％(1800ppm)，或1.0重量％(10000ppm)，或2.0重量％(20000ppm)，或3.0重量％(30000ppm)，或4.0重量％(40000ppm)的二质子脂肪酸。
二质子脂肪酸可以包含两种或更多种本文中所公开的实施例。
E.任选的添加剂
在一个实施例中，密封层包括一种或多种任选的添加剂。适合的添加剂的非限制性实例包括防粘剂、抗氧化剂、抗静电剂、稳定剂、成核剂、着色剂、颜料、紫外线(UV)吸收剂或稳定剂、阻燃剂、兼容剂、增塑剂、填充剂、加工助剂、防雾添加剂、交联剂(例如过氧化物)和其组合。
在一个实施例中，密封层包括防粘剂。“抗结块剂”是一种化合物，其通过在薄膜层表面产生微观粗糙化(其降低相邻层之间可以获得的接触面积)来最小化或防止薄膜的两个相邻层之间的结块(即粘着)。防粘剂可以是有机或无机的。适合的防粘剂的非限制性实例包括二氧化硅、滑石、碳酸钙和其组合。在一个实施例中，防粘剂是二氧化硅(SiO2)。二氧化硅可以是有机二氧化硅或合成二氧化硅。在一个实施例中，防粘剂是合成二氧化硅。在一个实施例中，以密封层的总重量计，密封层含有0重量％，或0.10重量％(1000ppm)，或0.20重量％(2000ppm)，或0.25重量％(2500ppm)到0.3重量％(3000ppm)，或0.4重量％(4000ppm)，或0.5重量％(5000ppm)，或1.0重量％(10000ppm)，或1.5重量％(15000ppm)，或2.0重量％(20000ppm)的防粘剂。
在一个实施例中，以密封层的总重量计，密封层含有0重量％，或0.01重量％，或0.05重量％，或0.1重量％，或0.2重量％到0.3重量％，或0.4重量％，或0.5重量％，或1.0重量％，或2.0重量％，或3.0重量％，或4.0重量％，或5.0重量％的添加剂。
添加剂可以包含两种或更多种本文中所公开的实施例。
在一个实施例中，以密封层的总重量计，密封层含有0.01重量％，或0.10重量％，或0.20重量％到0.24重量％，或0.25重量％，或0.30重量％，或0.35重量％，或0.40重量％，或0.45重量％，或0.50重量％，或0.80重量％，或1.0重量％，或1.5重量％，或2.0重量％，或2.5重量％，或3.0重量％，或3.5重量％，或4.0重量％，或4.5重量％，或5重量％的组合量的不饱和一级脂肪酸酰胺和饱和一级脂肪酸酰胺。
不饱和一级脂肪酸酰胺与饱和一级脂肪酸酰胺具有3:1到1:6的重量比。在一个实施例中，不饱和一级脂肪酸酰胺与饱和一级脂肪酸酰胺具有3:1，或1:1到1:3，或1:5，或1:6的重量比。
在一个实施例中，密封层的层合前COF是从0.01，或0.05，或0.10到0.17，或0.20，或0.25，或0.27，或0.30，或0.35，或0.39，或小于0.40。
在一个实施例中，密封层的厚度是5μm，或8μm，或10μm，或15μm到20μm，或25μm，或30μm，或35μm，或40μm，或45μm，或50μm，或55μm，或60μm，或65μm，或70μm，或75μm，或80μm，或90μm，或100μm，或120μm，或150μm。
密封层可以包含两种或更多种本文中所公开的实施例。
2.第二层
多层薄膜包括第二层。第二层含有第二乙烯类聚合物。
第二层具有两个相对表面。在一个实施例中，第二层是具有两个相对表面的连续层。
第二层与密封层接触。第二层可以与密封层直接接触或间接接触。在一个实施例中，第二层与密封层直接接触。如本文中所使用，术语“直接接触”是一种层配置，其中第二层定位成紧邻密封层且密封层与第二层之间不存在介入层或介入结构。
在另一实施例中，第二层与密封层间接接触。如本文中所使用，术语“间接接触”是一种层配置，其中密封层与第二层之间存在介入层或介入结构。
第二乙烯类聚合物可以是本文中所公开的任何乙烯类聚合物。第二乙烯类聚合物可以与密封层的乙烯类聚合物相同或不同。在一个实施例中，第二乙烯类聚合物与密封层的乙烯类聚合物相同。在另一实施例中，第二乙烯类聚合物与密封层的乙烯类聚合物不同。
在一个实施例中，第二乙烯类聚合物是LLDPE、LDPE或其组合。在另一实施例中，LLDPE是乙烯/1-辛烯共聚物。在一个实施例中，以第二层的总重量计，第二层含有5重量％，或10重量％，或20重量％，或30重量％，或40重量％，或50重量％，或60重量％，或70重量％，或80重量％到90重量％，或95重量％，或99重量％的LLDPE；和倒数量的LDPE，或从1重量％，或5重量％，或10重量％，或20重量％到30重量％，或40重量％，或50重量％，或60重量％，或70重量％，或80重量％，或90重量％或95重量％的LDPE。
在一个实施例中，第二层含有一种或多种任选的添加剂。添加剂可以是本文中所公开的任何添加剂。在一个实施例中，以第二层的总重量计，第二层含有0重量％，或0.01重量％到0.5重量％，或1.0重量％，或3.0重量％，或5.0重量％的添加剂。
在一个实施例中，第二层的厚度是从5μm，或8μm，或10μm，或15μm到20μm，或25μm，或30μm，或35μm，或40μm，或45μm，或50μm，或55μm，或60μm，或65μm，或70μm，或75μm，或80μm，或85μm，或90μm，或100μm，或120μm，或150μm。
第二层可以是基板层或核心层。在一个实施例中，第二层是核心层。“核心层”是薄膜结构的层，其是内部层。换句话说，核心层的每个表面都不是薄膜的最外表面。在一个实施例中，第二层是基板层。“基板层”是薄膜结构的层，其可以是内部层或表层。“表层”是薄膜结构的最外层。换句话说，表层的至少一个表面是薄膜的最外表面。
第二层可以包含两种或更多种本文中所公开的实施例。
3.任选的第三层
在一个实施例中，多层薄膜包括任选的第三层。第三层含有第三乙烯类聚合物。
第三层具有两个相对表面。在一个实施例中，第三层是具有两个相对表面的连续层。第三层与第二层接触。第三层可以与第二层直接接触或间接接触。在一个实施例中，第三层与第二层直接接触。在另一实施例中，第三层与第二层间接接触。
第三乙烯类聚合物可以是本文中所公开的任何乙烯类聚合物。第三乙烯类聚合物可以与密封层的第一乙烯类聚合物相同或不同，且第三乙烯类聚合物可以与第二层的第二乙烯类聚合物相同或不同。在一个实施例中，第三乙烯类聚合物与第二层的第二乙烯类聚合物相同。在另一实施例中，第三乙烯类聚合物与第二层的第二乙烯类聚合物不同。
在一个实施例中，第三乙烯类聚合物是LLDPE、LDPE或其组合。在一个实施例中，以第三层的总重量计，第三层含有5重量％，或10重量％，或20重量％，或30重量％，或40重量％，或50重量％，或60重量％，或70重量％，或80重量％到90重量％，或99重量％的LLDPE；和倒数量的LDPE，或1重量％，或5重量％，或10重量％，或20重量％到30重量％，或40重量％，50重量％，或60重量％，或70重量％，或80重量％，或90重量％，或95重量％的LDPE。
在一个实施例中，第三层含有一种或多种任选的添加剂。添加剂可以是本文中所公开的任何添加剂。在一个实施例中，以第三层的总重量计，第三层含有0重量％，或0.01重量％到0.5重量％，或1.0重量％，或3.0重量％，或5.0重量％的添加剂。
在一个实施例中，第三层的厚度是5μm，或8μm，或10μm，或15μm到20μm，或25μm，或30μm，或35μm，或40μm，或45μm，或50μm，或55μm，或60μm，或65μm，或70μm，或75μm，或80μm，或85μm，或90μm，或100μm，或120μm，或150μm。
第三层可以是基板层或核心层。在另一实施例中，第三层是基板层。
第三层可以包含两种或更多种本文中所公开的实施例。
在一个实施例中，多层薄膜具有以下结构(VII)：
密封层/第二层 结构(VII)。
在一个实施例中，密封层和第三层是第二层的相对侧上的表层，所述第二层是核心层。在另一实施例中，密封层与第二层直接接触，且第二层与第三层直接接触。在一个实施例中，多层薄膜具有以下结构(VIII)：
密封层/第二层/第三层 结构(VIII)。
在一个实施例中，多层薄膜基本上由以下组成或由以下组成：密封层和第二层。在另一实施例中，多层薄膜基本上由以下组成或由以下组成：密封层、第二层和第三层。
在一个实施例中，多层薄膜的厚度是15μm，或20μm，或25μm，或30μm，或35μm，或40μm，或45μm，或50μm到55μm，或60μm，或65μm，或70μm，或75μm，或80μm，或85μm，或90μm，或95μm，或100μm，或150μm，或200μm，或250μm，或300μm。
在一个实施例中，多层薄膜含有以下、基本上由以下组成或由以下组成：
(1)密封层，其含有以下、基本上由以下组成或由以下组成：
(A)以密封层的总重量计，75重量％，或80重量％，或85重量％，或90重量％到93重量％，或94重量％，或95重量％，或98重量％，或99重量％，或99.5重量％，或99.99重量％的第一乙烯类聚合物(如LLDPE和/或LDPE)，所述第一乙烯类聚合物具有(i)0.865g/cc到0.930g/cc，或从0.900g/cc，或0.910g/cc，或0.915g/cc到0.920g/cc，或0.925g/cc，或0.930g/cc的密度；和(ii)从0.5g/10min到25g/10min，或从0.5g/10min，或1.0g/10min到1.5g/10min，或2.0g/10min，或3.0g/10min，或5.0g/10min，或8.0g/10min的熔融指数；
(B)以密封层的总重量计，从0.0016重量％，或0.0075重量％，或0.04重量％，或0.06重量％到0.12重量％，或0.18重量％，或0.83重量％，或1.0重量％，或2.0重量％，或3.0重量％，或3.83重量％的不饱和一级脂肪酸酰胺(如二十二烯酰胺和/或油酰胺)，所述不饱和一级脂肪酸酰胺的熔点是从65℃，或70℃，或75℃到80℃，或85℃，或90℃；
(C)以密封层的总重量计，从0.0025重量％，或0.0083重量％，或0.01重量％，或0.06重量％到0.12重量％，或0.18重量％，或1.0重量％，或1.25重量％，或2.0重量％，或3.0重量％，或4.0重量％，或4.1重量％的饱和一级脂肪酸酰胺(如山嵛酰胺)，所述饱和一级脂肪酸酰胺的熔点是从101℃，或103℃，或106℃到113℃，或115℃，或120℃；
(D)任选地，以密封层的总重量计，从0.0025重量％，或0.0050重量％，或0.01重量％，或0.06重量％到0.12重量％，或0.18重量％，或1.0重量％，或1.25重量％，或2.0重量％，或3.0重量％，或4.0重量％的二质子脂肪酸(如丁二酸)，所述二质子脂肪酸具有(i)从110℃，或130℃，或150℃，或170℃，或180℃到185℃，或190℃，或200℃，或210℃，或220℃，或230℃的较高熔点；和(ii)从220℃，或225℃，或230℃，或235℃到240℃，或245℃，或250℃，或270℃，或300℃，或310℃，或320℃，或330℃的分解温度；
(E)任选地，以密封层的总重量计，从0重量％，或0.01重量％，或0.05重量％，或0.1重量％，或0.2重量％到0.3重量％，或0.4重量％，或0.5重量％，或1.0重量％，或2.0重量％，或3.0重量％，或4.0重量％，或5.0重量％的添加剂(如防粘剂)；和所述不饱和一级脂肪酸酰胺与所述饱和一级脂肪酸酰胺具有从3:1，或1:1到1:3，或1:5，或1:6的重量比；和
(2)与密封层接触的第二层，所述第二层含有第二乙烯类聚合物(如LLDPE、LDPE或其组合)；和
(3)任选地，与第二层接触的第三层，所述第三层含有第三乙烯类聚合物(如LLDPE、LDPE或其组合)；和
多层薄膜具有一种、一些或所有以下特性：(i)密封层的厚度是从5μm，或8μm，或10μm，或15μm到20μm，或25μm，或30μm，或35μm，或40μm，或50μm，或60μm，或70μm，或80μm，或90μm；和/或(ii)以密封层的总重量计，密封层含有从0.01重量％，或0.10重量％，或0.20重量％到0.24重量％，或0.25重量％，或0.30重量％，或0.35重量％，或0.40重量％，或0.45重量％，或0.50重量％，或0.80重量％，或1.0重量％，或1.5重量％，或2.0重量％，或2.5重量％，或3.0重量％，或3.5重量％，或4.0重量％，或4.5重量％，或5重量％的组合量的不饱和一级脂肪酸酰胺和饱和一级脂肪酸酰胺；和/或(iii)密封层的层合前COF是从0.01，或0.05，或0.10到0.17，或0.20，或0.25，或0.27，或0.30，或0.35，或0.39，或小于0.40；和/或(iv)第二层的厚度是从5μm，或8μm，或10μm，或15μm到20μm，或25μm，或30μm，或35μm，或40μm，或50μm，或60μm，或70μm，或80μm，或90μm；和/或(v)第三层的厚度是从5μm，或8μm，或10μm，或15μm到20μm，或25μm，或30μm，或35μm，或40μm，或50μm，或60μm，或70μm，或80μm，或90μm；和/或(vi)多层薄膜的厚度是从20μm，或30μm，或40μm，或50μm到55μm，或60μm，或70μm，或80μm，或90μm，或100μm，或150μm，或200μm，或250μm。
应理解，以每个各别层的总重量计，本文中所公开的每个层(包括前述层)中的组分的总和是100重量百分比(重量％)。
在一个实施例中，共挤压多层薄膜不包括非迁移性助滑剂，如聚硅氧。
举例来说，一些用于构筑薄膜的方法是通过浇铸共挤压或吹塑共挤压方法进行。这些方法的组合也是可能的。在一个实施例中，多层薄膜是共挤压吹塑薄膜。
共挤压多层薄膜可以经或可以未经定向。在一个实施例中，共挤压多层薄膜不是定向薄膜。在另一实施例中，共挤压多层薄膜不是双轴定向。换句话说，共挤压多层薄膜在挤压之后未拉伸。在另一实施例中，共挤压多层薄膜被定向(例如双轴定向)。
在一个实施例中，共挤压多层薄膜包括于层合物中。在这类实施例中，密封层的最外表面是层合物的最外表面。
共挤压多层薄膜可以包含两种或更多种本文中所公开的实施例。
层合物
本公开提供层合物。层合物包括含有密封层的第一薄膜和第二薄膜，其中第一薄膜层合到第二薄膜。密封层含有(A)第一乙烯类聚合物，其密度是0.865g/cc到0.930g/cc且熔融指数是0.5g/10min到25g/10min；(B)不饱和一级脂肪酸酰胺，其熔点是100℃或更低；和(C)饱和一级脂肪酸酰胺，其熔点超过100℃。不饱和一级脂肪酸酰胺与饱和一级脂肪酸酰胺具有3:1到1:6的重量比。
层合物含有至少两个薄膜，或超过两个薄膜。举例来说，层合物可以具有两个、三个、四个、五个、六个、七个、八个、九个、十个、十一个或更多个薄膜。在一个实施例中，层合物含有仅两个薄膜，或仅三个薄膜。
在一个实施例中，层合物具有以下结构(IX)：
第一薄膜/第二薄膜 结构(IX)。
在一个实施例中，层合物包括第一薄膜、与第一薄膜接触的粘着剂层和与粘着剂层接触的第二薄膜。在一个实施例中，层合物具有以下结构(X)：
第一薄膜/粘着剂层/第二薄膜 结构(X)。
在一个实施例中，第一薄膜是含有密封层的单层膜且第二薄膜是含有基板层的单层膜，且层合物具有以下结构(XI)：
密封层/粘着剂层/基板层 结构(XI)。
在一个实施例中，层合物包括任选的层合到第二薄膜的第三薄膜。在另一实施例中，层合物包括任选的与第二薄膜接触的第二粘着剂层，和任选的与第二粘着剂层接触的第三薄膜。在一个实施例中，层合物具有以下结构(XII)：
第一薄膜/粘着剂层/第二薄膜/第二粘着剂层/第三薄膜 结构(XII)
1.第一薄膜
层合物包括第一薄膜。第一薄膜包括密封层。
第一薄膜具有两个相对表面。第一薄膜可以是单层膜或多层膜。在一个实施例中，第一薄膜是多层膜，其含有至少两个层，或超过两个层。举例来说，第一薄膜可以具有两个、三个、四个、五个、六个、七个、八个、九个、十个或更多个层。在一个实施例中，第一薄膜含有仅一个层，或仅三个层。
在一个实施例中，第一薄膜是多层膜，其包括任选的与密封层接触的核心层和任选的与核心层接触的第三基板层。在一个实施例中，第三基板的最外表面层合到第二薄膜的最外表面。
A.密封层
第一薄膜含有密封层。密封层可以是本文中所公开的任何密封层。在一个实施例中，密封层是表层。换句话说，密封层的最外表面是第一薄膜的最外表面，且也是层合物的最外表面。
B.任选的核心层和任选的第三基板层
在一个实施例中，第一薄膜是多层膜，其包括核心层和第三基板层。
核心层具有两个相对表面。在一个实施例中，核心层是具有两个相对表面的连续层。核心层与密封层接触。核心层可以与密封层直接接触或间接接触。在一个实施例中，核心层与密封层直接接触。在另一实施例中，核心层与密封层间接接触。
在一个实施例中，核心层含有第三乙烯类聚合物。第三乙烯类聚合物可以是本文中所公开的任何乙烯类聚合物。第三乙烯类聚合物可以与密封层的乙烯类聚合物相同或不同。在一个实施例中，第三乙烯类聚合物是LLDPE、LDPE或其组合。在一个实施例中，以核心层的总重量计，核心层含有从5重量％，或10重量％，或20重量％，或30重量％，或40重量％，或50重量％，或60重量％，或70重量％，或80重量％到90重量％，或95重量％，或99重量％的LLDPE；和倒数量的LDPE，或从1重量％，或5重量％，或10重量％，或20重量％到30重量％，或40重量％，或50重量％，或60重量％，或70重量％，或80重量％，或90重量％或95重量％的LDPE。
在一个实施例中，核心层含有一种或多种任选的添加剂。添加剂可以是本文中所公开的任何添加剂。在一个实施例中，以核心层的总重量计，核心层含有从0重量％，或0.01重量％到0.5重量％，或1.0重量％，或3.0重量％，或5.0重量％的添加剂。在一个实施例中，核心层含有添加剂，其是选自以下的增滑剂：不饱和一级脂肪酸酰胺，其熔点是100℃或更低；饱和一级脂肪酸酰胺，其熔点超过100℃；二质子脂肪酸，其熔点超过100℃且分解温度超过200℃；和其组合。
在一个实施例中，核心层的厚度是从5μm，或8μm，或10μm，或15μm到20μm，或25μm，或30μm，或35μm，或40μm，或45μm，或50μm，或55μm，或60μm，或65μm，或70μm，或75μm，或80μm，或85μm，或90μm，或100μm，或120μm，或150μm。
第三基板层具有两个相对表面。在一个实施例中，第三基板层是具有两个相对表面的连续层。第三基板层与核心层和第二薄膜接触。第三基板层可以与核心层直接接触或间接接触。在一个实施例中，第三基板层与核心层直接接触。在另一实施例中，第三基板层与核心层间接接触。第三基板层可以与第二薄膜直接接触或间接接触。在一个实施例中，第三基板层与第二薄膜直接接触。在另一实施例中，第三基板层与第二薄膜间接接触。
在一个实施例中，第三基板层含有第四乙烯类聚合物。第四乙烯类聚合物可以是本文中所公开的任何乙烯类聚合物。第四乙烯类聚合物可以与密封层的乙烯类聚合物相同或不同，且第四乙烯类聚合物可以与核心层的第三乙烯类聚合物相同或不同。在一个实施例中，第四乙烯类聚合物是LLDPE、LDPE或其组合。在一个实施例中，以第三基板层的总重量计，第三基板层含有从5重量％，或10重量％，或20重量％，或30重量％，或40重量％，或50重量％，或60重量％，或70重量％，或80重量％到90重量％，或95重量％，或99重量％的LLDPE；和倒数量的LDPE，或从1重量％，或5重量％，或10重量％，或20重量％到30重量％，或40重量％，或50重量％，或60重量％，或70重量％，或80重量％，或90重量％，或95重量％的LDPE。
在一个实施例中，第三基板层含有一种或多种任选的添加剂。添加剂可以是本文中所公开的任何添加剂。在一个实施例中，以第三基板层的总重量计，核心层含有从0重量％，或0.01重量％到0.5重量％，或1.0重量％，或3.0重量％，或5.0重量％的添加剂。
在一个实施例中，第三基板层的厚度是从5μm，或8μm，或10μm，或15μm到20μm，或25μm，或30μm，或35μm，或40μm，或45μm，或50μm，或55μm，或60μm，或65μm，或70μm，或75μm，或80μm，或85μm，或90μm，或100μm，或120μm，或150μm。
在一个实施例中，第三基板层被电晕处理。
核心层和第三基板层可以包含两种或更多种本文中所公开的实施例。
第一薄膜可以包含两种或更多种本文中所公开的实施例。
2.第二薄膜
层合物包括第二薄膜。第一薄膜层合到第二薄膜。
第二薄膜具有两个相对表面。第二薄膜可以是单层膜或多层膜。在一个实施例中，第二薄膜是单层膜。在另一实施例中，第二薄膜是多层膜，其含有至少两个层，或超过两个层。在一个实施例中，第二薄膜含有仅一个层，或仅两个层，或仅三个层。
在一个实施例中，第二薄膜包括基板层。基板层具有两个相对表面。在一个实施例中，基板层是具有两个相对表面的连续层。
基板层与第一薄膜接触。基板层可以与第一薄膜直接接触或间接接触。在一个实施例中，基板层与第一薄膜直接接触。在另一实施例中，基板层与第一薄膜间接接触。
在一个实施例中，基板层与任选的粘着剂层接触。基板层可以与粘着剂层直接接触或间接接触。在一个实施例中，基板层与粘着剂层直接接触。在另一实施例中，基板层与粘着剂层间接接触。
在一个实施例中，基板层含有选自以下的组分：第二乙烯类聚合物、丙烯类聚合物、聚酰胺(如尼龙)、聚酯、乙烯乙烯醇共聚物、聚对苯二甲酸乙二醇酯(PET)、乙烯丙烯酸乙烯酯共聚物、乙烯丙烯酸甲酯共聚物、乙烯丙烯酸乙酯共聚物、乙烯丙烯酸丁酯共聚物、乙烯丙烯酸共聚物、乙烯甲基丙烯酸共聚物、乙烯丙烯酸的离聚物、甲基丙烯酸的离聚物、顺丁烯二酸酐接枝型乙烯类聚合物、聚苯乙烯、金属箔和其组合。在一个实施例中，基板层含有PET。在另一实施例中，基板层含有第二乙烯类聚合物。第二乙烯类聚合物可以是本文中所公开的任何乙烯类聚合物。第二乙烯类聚合物可以与密封层的乙烯类聚合物相同或不同。
在一个实施例中，第二薄膜，或此外基板层的厚度是从5μm，或8μm，或10μm，或12μm，或15μm到20μm，或25μm，或30μm，或35μm，或40μm，或45μm，或50μm，或55μm，或60μm，或65μm，或70μm，或75μm，或80μm，或85μm，或90μm，或100μm，或150μm。
基板层可以包含两种或更多种本文中所公开的实施例。
第二薄膜可以包含两种或更多种本文中所公开的实施例。
3.任选的粘着剂层
在一个实施例中，层合物包括粘着剂层。粘着剂层与第一薄膜和第二薄膜接触。
粘着剂层具有两个相对表面。在一个实施例中，粘着剂层是具有两个相对表面的连续层。粘着剂层与第一薄膜接触。粘着剂层可以与第一薄膜直接接触或间接接触。在一个实施例中，粘着剂层与第一薄膜直接接触。在另一实施例中，粘着剂层与第一薄膜间接接触。
粘着剂层含有粘着剂。适合的粘着剂的非限制性实例包括聚氨基甲酸酯粘着剂(例如MOR-FREETM 706A/C-79，可以从Rohm and Haas购得)、聚丙烯酸酯粘着剂(例如ROBONDTM L-168/CR3A，可以从The Dow Chemical Company购得)和其组合。
在一个实施例中，粘着剂层的干燥涂层重量是从0.5克/平方米(g/m2)，或1.0g/m2，或1.5g/m2，或1.8g/m2到1.9g/m2，或2.0g/m2，或2.5g/m2，或3.0g/m2。
粘着剂层可以包含两种或更多种本文中所公开的实施例。
4.任选的第三薄膜
在一个实施例中，层合物包括第三薄膜。第三薄膜层合到第二薄膜。
第三薄膜具有两个相对表面。第三薄膜可以是单层膜或多层膜。在一个实施例中，第三薄膜是单层膜。在另一实施例中，第三薄膜是多层膜，其含有至少两个层，或超过两个层。在一个实施例中，第三薄膜含有仅一个层，或仅两个层，或仅三个层。
在一个实施例中，第三薄膜包括第二基板层。第二基板层可以是本文中所公开的任何基板层。
第二基板层与第二薄膜接触。第二基板层可以与第二薄膜直接接触或间接接触。在一个实施例中，第二基板层与第二薄膜直接接触。在另一实施例中，第二基板层与第二薄膜间接接触。
第二基板层可以包含两种或更多种本文中所公开的实施例。
第三薄膜可以包含两种或更多种本文中所公开的实施例。
5.任选的第二粘着剂层
在一个实施例中，层合物包括第二粘着剂层。第二粘着剂层与第二薄膜接触。第二粘着剂层可以是本文中所公开的任何粘着剂层。
第二粘着剂层与第二薄膜接触。第二粘着剂层可以与第二薄膜直接接触或间接接触。在一个实施例中，第二粘着剂层与第二薄膜直接接触。在另一实施例中，第二粘着剂层与第二薄膜间接接触。在一个实施例中，第二粘着剂层与任选的第三薄膜接触。第二粘着剂层可以与第三薄膜直接接触或间接接触。在一个实施例中，第二粘着剂层与第三薄膜直接接触。在另一实施例中，第二粘着剂层与第三薄膜间接接触。
第二粘着剂层可以包含两种或更多种本文中所公开的实施例。
在一个实施例中，第一薄膜是多层膜，其具有密封层、核心层和第三基板层；且第二薄膜是单层膜，其含有基板层；且层合物具有以下结构(XIII)：
密封层/核心层/第三基板层/粘着剂层/基板层结构(XIII)。
在一个实施例中，第一薄膜是多层膜，其具有密封层、核心层和第三基板层；且第二薄膜是单层膜，其含有基板层；第三薄膜是单层膜，其含有第二基板层；且层合物具有以下结构(XIV)：
密封层/核心层/第三基板层/粘着剂层/基板层/第二粘着剂层/第二基板层
结构(XIV)。
在一个实施例中，层合物的密封层的层合前COF是从0.01，或0.05，或0.10到0.17，或0.20，或0.25，或0.27，或0.30，或0.35，或0.39，或小于0.40。
在一个实施例中，在40℃下固化48小时之后，层合物的密封层的COF是从0.01，或0.05，或0.10到0.18，或0.20，或0.25，或0.27，或0.30，或0.34，或0.36，或0.39，或小于0.40(“层合物40℃固化COF”)。在一个实施例中，在40℃固化之后，层合物的密封层的COF的变化小于0.22，或小于0.15，或小于0.10。在另一实施例中，在40℃固化之后，层合物的密封层的COF的变化是从-0.20，或-0.10，或-0.05，或0到0.01，或0.05，或0.10，或0.15，或0.20，或0.21。根据以下等式计算在40℃固化之后的COF的变化：在40℃固化之后的COF变化＝层合物40℃固化COF-层合前COF。
在一个实施例中，在55℃下固化48小时之后，层合物的密封层的COF是从0.01，或0.05，或0.10到0.15，或0.17，或0.19，或0.20，或0.25，或0.27，或0.30，或0.35，或0.36，或0.38，或0.39，或小于0.40(“层合物55℃固化COF”)。高温固化(55℃固化)在层合物制造过程期间是有利的，因为其可以实现更快的处理时间。在一个实施例中，在55℃固化之后，层合物的密封层的COF的变化小于24，或小于0.22，或小于0.15，或小于0.05。在另一实施例中，在55℃固化之后，层合物的密封层的COF的变化是从-0.20，或-0.10，或-0.06或0到0.01，或0.03，或0.05，或0.10，或0.20，或0.23。根据以下等式计算在55℃固化之后的COF的变化：在55℃固化之后的COF变化＝层合物55℃固化COF-层合前COF。
在一个实施例中，层合物含有以下、基本上由以下组成或由以下组成：
(1)第一薄膜，其含有
(A)密封层，其含有以下、基本上由以下组成或由以下组成：(i)以密封层的总重量计，从70重量％，或75重量％，或80重量％，或85重量％，或90重量％到93重量％，或94重量％，或95重量％，或98重量％，或99重量％，或99.5重量％，或99.99重量％的乙烯类聚合物(如LLDPE和/或LDPE)，乙烯类聚合物具有(a)0.865g/cc到0.930g/cc，或从0.900g/cc，或0.910g/cc，或0.915g/cc到0.920g/cc，或0.925g/cc，或0.930g/cc的密度；和(b)0.5g/10min到25g/10min，或从0.5g/10min，或1.0g/10min到1.5g/10min，或2.0g/10min，或3.0g/10min，或4.0g/10min，或5.0g/10min，或8.0g/10min的熔融指数；(ii)以密封层的总重量计，从0.0016重量％，或0.0075重量％，或0.04重量％，或0.06重量％到0.12重量％，或0.18重量％，或0.83重量％，或1.0重量％，或2.0重量％，或3.0重量％，或3.83重量％的不饱和一级脂肪酸酰胺(如二十二烯酰胺和/或油酰胺)，所述不饱和一级脂肪酸酰胺的熔点是从65℃，或70℃，或75℃到80℃，或85℃，或90℃；(iii)以密封层的总重量计，从0.0025重量％，或0.0083重量％，或0.01重量％，或0.06重量％到0.12重量％，或0.18重量％，或1.0重量％，或1.25重量％，或2.0重量％，或3.0重量％，或4.0重量％，或4.1重量％的饱和一级脂肪酸酰胺(如山嵛酰胺)，所述饱和一级脂肪酸酰胺的熔点是从101℃，或103℃，或106℃到113℃，或115℃，或120℃，或125℃，或130℃，或135℃，或140℃；(iv)任选地，以密封层的总重量计，从0.0025重量％，或0.0050重量％，或0.01重量％，或0.06重量％到0.12重量％，或0.18重量％，或1.0重量％，或1.25重量％，或2.0重量％，或3.0重量％，或4.0重量％的二质子脂肪酸(如丁二酸)，所述二质子脂肪酸具有(a)从101℃，110℃，或130℃，或150℃，或170℃，或180℃到185℃，或190℃，或200℃，或210℃，或220℃，或230℃，或240℃的熔点；和(b)从220℃，或225℃，或230℃，或235℃到240℃，或245℃，或250℃，或270℃，或300℃，或310℃，或320℃，或330℃，或340℃，或350℃的分解温度；(v)任选地，以密封层的总重量计，从0重量％，或0.01重量％，或0.05重量％，或0.1重量％，或0.2重量％到0.3重量％，或0.4重量％，或0.5重量％，或1.0重量％，或2.0重量％，或3.0重量％，或4.0重量％，或5.0重量％的添加剂(如防粘剂)；所述不饱和一级脂肪酸酰胺与饱和一级脂肪酸酰胺具有从3:1，或1:1到1:3，或1:5，或1:6的重量比；和
(B)任选地，与密封层接触的核心层，核心层含有第三乙烯类聚合物(如LLDPE和/或LDPE)；
(C)任选地，与核心层接触的第三基板，所述第三基板层含有第四乙烯类聚合物(如LLDPE和/或LDPE)；
(2)任选地，与第一薄膜接触的粘着剂层；
(3)第二薄膜，其含有与粘着剂层接触的基板层，所述基板层含有选自以下的组分：第二乙烯类聚合物、丙烯类聚合物、聚酰胺(如尼龙)、聚酯、PET、金属箔和其组合；
其中第一薄膜层合到第二薄膜；且层合物具有一种、一些或所有以下特性；且层合物具有一种、一些或所有以下特性：(i)以密封层的总重量计，密封层含有从0.01重量％，或0.10重量％，或0.20重量％到0.24重量％，或0.25重量％，或0.30重量％，或0.35重量％，或0.40重量％，或0.45重量％，或0.50重量％，或0.80重量％，或1.0重量％，或1.5重量％，或2.0重量％，或2.5重量％，或3.0重量％，或3.5重量％，或4.0重量％，或4.5重量％，或5重量％的组合量的不饱和一级脂肪酸酰胺和饱和一级脂肪酸酰胺；和/或(ii)密封层的层合前COF是从0.01，或0.05，或0.10到0.17，或0.20，或0.25，或0.27，或0.30，或0.35，或0.39，或小于0.40；和/或(iii)密封层的层合物40℃固化COF是从0.01，或0.05，或0.10到0.18，或0.20，或0.25，或0.27，或0.30，或0.34，或0.36，或0.39，或小于0.40；和/或(iv)在40℃固化之后，层合物的密封层的COF的变化是从-0.20，或-0.10，或-0.05，或0到0.01，或0.05，或0.10，或0.15，或0.20，或0.21；和/或(v)密封层的层合物55℃固化COF是从0.01，或0.05，或0.10到0.15，或0.17，或0.19，或0.20，或0.25，或0.27，或0.30，或0.35，或0.36，或0.38，或0.39，或小于0.40；和/或(vi)在55℃固化之后，层合物的密封层的COF的变化是从-0.20，或-0.10，或-0.06，或0到0.01，或0.03，或0.05，或0.10，或0.15，或0.20，或0.23；和/或(vii)层合物的厚度是从15μm，或20μm，或30μm，或40μm，或45μm，或50μm到55μm，或60μm，或65μm，或70μm，或75μm，或80μm，或85μm，或90μm，或95μm，或100μm，或150μm，或200μm，或250μm，或300μm。
在一个实施例中，不饱和一级脂肪酸酰胺与饱和一级脂肪酸酰胺具有1:1到1:3，或1:5，或1:6的重量比，且层合物的密封层具有一种、一些或所有以下特性：(i)层合前COF是从0.01，或0.05，或0.10到0.17，或0.20，或0.25，或0.27；和/或(ii)层合物40℃固化COF是从0.01，或0.05，或0.10到0.18；和/或(iii)在40℃固化之后，COF的变化是从-0.10，或-0.05，或0到0.01，或0.05；和/或(iv)层合物55℃固化COF是从0.01，或0.10到0.15，或0.17，或0.19，或0.21；和/或(v)在55℃固化之后，COF的变化是从-0.10，或-0.06，或0到0.01，或0.03，或0.05。
在一个实施例中，层合物不包括非迁移性助滑剂，如聚硅氧。
层合物的第一薄膜、第二薄膜和任选的第三薄膜可以是共挤压多层结构。
举例来说，一些用于构筑层合物的方法是通过粘着剂层合、挤压层合、热层合、干式层合和无溶剂层合。这些方法的组合也是可能的。
层合物的第一薄膜、第二薄膜和任选的第三薄膜可以被或可以未被定向。在一个实施例中，第一薄膜、第二薄膜和任选的第三薄膜中的一个或多个或每一个不是定向膜。在另一实施例中，第一薄膜、第二薄膜和任选的第三薄膜中的一个或多个或每一个被定向(例如双轴定向)。
层合物可以包含两种或更多种本文中所公开的实施例。
本公开还提供含有共挤压多层膜和/或层合物的对象，如包装。适合的包装的非限制性实例包括食品包装、特殊包装和清洁剂包装(液体和粉末)。在一个实施例中，提供包装，所述包装由两个相对层合物形成。在一个实施例中，第一层合物的密封层与第二层合物的密封层接触。在另一实施例中，由相对密封剂层形成热封以产生包装。
作为实例但非限制，现将于以下实例中详细描述本公开的一些实施例。
实例
实例中使用的材料提供于以下表1中。
表1
Figure BDA0002308597080000321
共挤压3层吹塑膜
使用Jinming Machinery吹塑膜生产线，使用表1的材料制备共挤压3层吹塑膜样品。挤压参数如下：7层饼状模具直径＝120mm；模具间隙＝1.5mm；输出＝25千克/小时；模具温度概况＝200℃/200℃/200℃；吹胀比(BUR)＝2.3；平折＝43cm；第一牵引速度＝6.8-8.1m/min；挤压机直径＝30mm；长度/直径(L/D)＝30；挤压机温度概况＝180℃/205℃/205℃/205℃/200℃。所得共挤压3层吹塑膜样品各自具有以下结构(A)：密封层/核心层/基板层A 结构(A)。
各共挤压吹塑膜样品的厚度是50μm，且各层的厚度具有1:1:1的比率。因此，密封层、核心层和基板层A各自具有约16.67μm的厚度。基板层A经历电晕处理，其中在线薄膜表面能是40-42达因/厘米。在线进行薄膜的分切缠绕。层配置提供于以下表2中。
在形成共挤压3层吹塑膜样品之后第七天，测试共挤压3层吹塑膜样品的层合前COF。在测试各样本之前，丢弃至少10米最开始的样本薄膜卷。测试各样品的至少两个样本，且报道平均层合前COF。结果报道于表2中。
层合物
具有结构(A)的被电晕处理的3层吹塑膜样品经由来自Nordmeccanica Group的Labo CombiTM 400层合机(先导涂布机)与具有12μm的厚度的PET薄膜和MOR-FREETM 706A/C-79(可以从Rohm and Haas购得的无溶剂型聚氨基甲酸酯粘着剂)层合在一起。层合条件如下：粘着剂层(MOR-FREETM 706A/C-79)干燥涂层重量＝1.8g/m2；进行先导操作速度＝50m/min；夹持点温度＝60℃。所得层合物具有以下结构(B)：PET薄膜基板层B/粘着剂层/基板层A/核心层/密封层。
层合物在烘箱中，在40℃或55℃的温度下固化48小时，且形成薄膜卷。在40℃固化或55℃固化之后三到六天，分别测试层合物样品的层合物40℃固化COF或层合物55℃固化COF。在测试各样本之前，丢弃至少10米最开始的样本薄膜卷。测试各样品的至少两个样本，且报道平均层合物40℃固化COF和层合物55℃固化COF。结果报道于表2中。在表2中，“CS”指比较性样品。
如所示，具有粘着剂层、PET薄膜基板层和具有密封层的薄膜(含有(A)乙烯类聚合物(DOWLEXTM 2045G和LDPE)和(B)具有100℃或更低的熔点的不饱和一级脂肪酸酰胺(二十二烯酰胺))的比较性层合物(CS 2)(且无饱和一级脂肪酸酰胺)呈现高层合物55℃固化COF(0.48)，和在55℃固化之后的高COF变化(0.40)。
此外，具有粘着剂层、PET薄膜基板层和具有密封层的薄膜(含有(A)乙烯类聚合物(DOWLEXTM 2045G和LDPE)；(B)具有100℃或更低的熔点的不饱和一级脂肪酸酰胺(二十二烯酰胺)；和(C)具有超过100℃的熔点的饱和一级脂肪酸酰胺(山嵛酰胺)，所述二十二烯酰胺和山嵛酰胺具有5:1的重量比)的比较性层合物(CS 3)(并非具有3:1到1:6的重量比的二十二烯酰胺和山嵛酰胺)呈现高层合物55℃固化COF(0.43)，和在55℃固化之后的高COF变化(0.34)。申请人意外发现，具有粘着剂层、PET薄膜基板层和具有密封层的薄膜(含有(A)乙烯类聚合物(DOWLEXTM 2045G和LDPE)；(B)具有100℃或更低的熔点的不饱和一级脂肪酸酰胺(二十二烯酰胺)；和(C)具有超过100℃的熔点的饱和一级脂肪酸酰胺(山嵛酰胺)，所述二十二烯酰胺和山嵛酰胺具有3:1到1:6的重量比)的层合物(实例4-7)有利地呈现小于0.40的层合物55℃固化COF，且在55℃固化之后的COF的变化是0.23或更小。
表2
Figure BDA0002308597080000351
1密封层由上述3层吹塑膜形成。密封层的厚度是约16.67μm。
2以密封层的总重量计。
3以核心层的总重量计。
4核心层由上述3层吹塑膜形成。核心层的厚度是约16.67μm。
5外层由上述3层吹塑膜形成。外层的厚度是约16.67μm。
6以基板层A的总重量计。
7粘着剂层由MOR-FREETM 706A/C-79形成，其干燥涂层重量是1.8g/m2。重量百分比是以粘着剂层的总重量计。
8PET薄膜基板层B的厚度是12μm。
9以PET薄膜基板层B的总重量计。
特别期望的是，本公开不限于本文中所含有的实施例和说明，但包括这些实施例的修改形式，所述修改形式包括在以下权利要求书的范围内出现的实施例的部分和不同实施例的要素的组合。

Claims (22)

1.一种包含至少两个层的共挤压多层膜，所述至少两个层包含：
密封层，其包含
(A)第一乙烯类聚合物，其密度是0.865g/cc到0.930g/cc且熔融指数是0.5g/10min到25g/10min；
(B)不饱和一级脂肪酸酰胺，其熔点是100℃或更低；
(C)饱和一级脂肪酸酰胺，其熔点超过100℃，所述不饱和一级脂肪酸酰胺与所述饱和一级脂肪酸酰胺具有3:1到1:6的重量比；和
与所述密封层直接接触的核心层，所述核心层包含第二乙烯类聚合物；和
与所述核心层直接接触的基板层，所述基板层包含第二乙烯类聚合物。
2.根据权利要求1所述的共挤压多层膜，其中所述不饱和一级脂肪酸酰胺选自：二十二烯酰胺、油酰胺和其组合。
3.根据权利要求1所述的共挤压多层膜，其中所述饱和一级脂肪酸酰胺选自：山嵛酰胺、棕榈酸酰胺、硬脂酰胺和其组合。
4.根据权利要求2所述的共挤压多层膜，其中所述饱和一级脂肪酸酰胺选自：山嵛酰胺、棕榈酸酰胺、硬脂酰胺和其组合。
5.根据权利要求1至4中任一项所述的共挤压多层膜，其中所述第一乙烯类聚合物选自：乙烯均聚物、乙烯/α-烯烃共聚物和其组合。
6.根据权利要求1至4中任一项所述的共挤压多层膜，其中所述密封层进一步包含二质子脂肪酸，其熔点超过100℃且分解温度超过200℃。
7.根据权利要求1至4中任一项所述的共挤压多层膜，其中以所述密封层的总重量计，所述密封层包含0.01重量％到5重量％的组合量的所述不饱和一级脂肪酸酰胺和所述饱和一级脂肪酸酰胺。
8.一种层合物，其包含根据权利要求1至7中任一项所述的共挤压多层膜。
9.一种层合物，其包含：
第一薄膜，其包含
(i)密封层，其包含：
(A)第一乙烯类聚合物，其密度是0.865g/cc到0.930g/cc且熔融指数是0.5g/10min到25g/10min；
(B)不饱和一级脂肪酸酰胺，其熔点是100℃或更低；
(C)饱和一级脂肪酸酰胺，其熔点超过100℃，所述不饱和一级脂肪酸酰胺与所述饱和一级脂肪酸酰胺具有3:1到1:6的重量比；和
(ii)与所述密封层直接接触的核心层，所述核心层包含第二乙烯类聚合物；和
(iii)与所述核心层直接接触的基板层，所述基板层包含第二乙烯类聚合物；
第二薄膜，其中所述第一薄膜层合到所述第二薄膜。
10.根据权利要求9所述的层合物，其中所述不饱和一级脂肪酸酰胺选自：二十二烯酰胺、油酰胺和其组合。
11.根据权利要求9所述的层合物，其中所述饱和一级脂肪酸酰胺选自：山嵛酰胺、棕榈酸酰胺、硬脂酰胺和其组合。
12.根据权利要求10所述的层合物，其中所述饱和一级脂肪酸酰胺选自：山嵛酰胺、棕榈酸酰胺、硬脂酰胺和其组合。
13.根据权利要求9至12中任一项所述的层合物，其中所述第一乙烯类聚合物选自：乙烯均聚物、乙烯/α-烯烃共聚物和其组合。
14.根据权利要求9至12中任一项所述的层合物，其中所述密封层进一步包含二质子脂肪酸，其熔点超过100℃且分解温度超过200℃。
15.根据权利要求9至12中任一项所述的层合物，其中所述密封层的层合物55℃固化摩擦系数(COF)是0.01到小于0.4。
16.根据权利要求9至12中任一项所述的层合物，其中所述第二薄膜包含基板层，其包含选自以下的组分：第二乙烯类聚合物、丙烯类聚合物、聚酰胺、聚酯、乙烯乙烯醇共聚物、乙烯丙烯酸乙烯酯共聚物、乙烯丙烯酸甲酯共聚物、乙烯丙烯酸乙酯共聚物、乙烯丙烯酸丁酯共聚物、乙烯丙烯酸共聚物、乙烯甲基丙烯酸共聚物、乙烯丙烯酸的离聚物、甲基丙烯酸的离聚物、顺丁烯二酸酐接枝型乙烯类聚合物、金属箔和其组合。
17.根据权利要求9至12中任一项所述的层合物，其进一步包含第三薄膜，其中所述第三薄膜层合到所述第二薄膜。
18.根据权利要求16所述的层合物，其中所述聚酯是聚对苯二甲酸乙二醇酯。
19.根据权利要求1至4中任一项所述的共挤压多层膜，其中所述核心层和所述基板层各自包含第一乙烯类聚合物。
20.根据权利要求1至4中任一项所述的共挤压多层膜，其中第二乙烯类聚合物是低密度聚乙烯。
21.根据权利要求9至12中任一项所述的层合物，其中所述核心层和所述基板层各自包含第一乙烯类聚合物。
22.根据权利要求9至12中任一项所述的层合物，其中第二乙烯类聚合物是低密度聚乙烯。
CN201780091804.9A 2017-06-09 2017-06-09 含有助滑剂的多层薄膜和层合物 Active CN110730719B (zh)