CN110683864A - 一种氧化锆全瓷牙用比色片的制备方法 - Google Patents
一种氧化锆全瓷牙用比色片的制备方法 Download PDFInfo
- Publication number
- CN110683864A CN110683864A CN201910984990.XA CN201910984990A CN110683864A CN 110683864 A CN110683864 A CN 110683864A CN 201910984990 A CN201910984990 A CN 201910984990A CN 110683864 A CN110683864 A CN 110683864A
- Authority
- CN
- China
- Prior art keywords
- zirconia
- dyeing
- color
- cutting
- crown
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种氧化锆全瓷牙用比色片的制备方法，包括以下步骤：切削氧化锆块，切削出基牙形的氧化锆基牙材料后，使用染色液浸染，烧结后制得基牙；切削氧化锆块，切削出牙冠形的氧化锆牙冠材料后，使用染色液和切端液对氧化锆牙冠材料进行内染和外染，烧结、上釉、再次烧结、抛光，即得牙冠；将所述牙冠内表面用粘结剂粘结于所述基牙上，即得色片。本发明制备方法与全锆修复体材料及染色工艺基本统一，本发明制备方法制备而成的比色片，颜色、光泽度以及通透度与全锆修复体及天然牙齿更为接近，显色效果稳定持久，色彩立体感强，比色精准度高，在色彩的传递与再现上能够更为准确。
Description
技术领域
本发明涉及一种氧化锆全瓷牙用比色片的制备方法。
背景技术
比色板在口腔修复中起传递色彩的作用，先由医生根据比色板挑选出色彩最为接近的比色片，再由制作修复体的技师将所选比色片上色彩再现于修复体上。目前，现有的比色片都是基于烤瓷牙原理制作出来的，结构为基底层、饰面层，显色效果由基底层色、饰面层色、上釉复合而成，其材料和成色原理与氧化锆修复体截然不同，在色彩传递和再现的两个过程中，易出现偏差，导致现有比色板在全瓷修复体尤其是氧化锆修复体比色中存在缺陷。
发明内容
本发明所要解决的技术问题是提供一种氧化锆全瓷牙用比色片的制备方法，该制备方法与全锆修复体材料及染色工艺基本统一，制备而成的比色片，颜色、光泽度以及通透度与全锆修复体及天然牙齿更为接近，显色效果稳定持久，色彩立体感强，比色精准度高，在色彩的传递与再现上能够更为准确。
本发明的技术方案如下：
一种氧化锆全瓷牙用比色片的制备方法，包括以下步骤：
S1.制备基牙：切削氧化锆块，切削出基牙形的氧化锆基牙材料后，使用染色液浸染，烧结后制得基牙；
S2.制备牙冠：切削氧化锆块，切削出牙冠形的氧化锆牙冠材料后，使用染色液和切端液对氧化锆牙冠材料进行内染和外染，烧结、上釉、再次烧结、抛光，即得牙冠；
S3.制备色片：将所述牙冠内表面用粘结剂粘结于所述基牙上，即得色片。
进一步的，步骤S1和步骤S2中，采用CAD/CAM技术切削氧化锆块。
进一步的，步骤S1和步骤S2中，烧结温度不超过830℃，烧结时间为2-3min。
进一步的，步骤S1中浸染时间为5-20s。
进一步的，步骤S2中所述内染为：先将切端液涂布于氧化锆牙冠材料切端，再将氧化锆牙冠材料浸泡于染色液中，浸染5-20s，取出后干燥、结晶。
进一步的，干燥温度为100-110℃，干燥时间为30-35min。
进一步的，结晶温度不超过1450℃，结晶时间为8.5-9h。
进一步的，步骤S2中所述外染为：将染色液涂布于内染后的氧化锆牙冠材料外表面，再在其切端涂布切端液。
进一步的，所述染色液包括以下按重量份数计算的组分：去离子水1000份、硝酸盐着色剂6-85份、渗透剂40份、指示剂5份。
进一步的，所述硝酸铁染色剂为硝酸铒、硝酸铁；所述渗透剂为聚乙二醇；所述指示剂为胭脂红。
本发明具有如下有益效果：
本发明选用氧化锆作为比色片的材料，与全锆修复体所用材料相同，其具有与天然牙齿相似的颜色、通透性和光学效果；比色片通过基牙和牙冠粘结而成，充分还原了全锆修复体及天然牙齿的光泽度，赋予了比色片立体的显色效果；牙冠通过用染色液和切端液对其进行内染和外染，能够模拟全锆修复体及天然牙齿颜色的渐变特点；选用的染色液，具有良好的渗透性能，染色渗透时间短，所染色彩具有良好的均匀度和光泽度，染色效果稳定持久，不影响氧化锆材料的通透性和光学效果。采用本发明制备方法制备而成的比色片，颜色、光泽度以及通透度与全锆修复体及天然牙齿更为接近，显色效果稳定持久，色彩立体感强，比色精准度高，减少了色彩传递与再现过程中出现的误差，保证了制作全锆修复体色彩效果的准确性。
具体实施方式
下面结合实施例对本发明进行详细的说明，实施例仅是本发明的优选实施方式，不是对本发明的限定。
实施例1
一种氧化锆全瓷牙用比色片的制备方法，包括以下步骤：
S1.制备基牙：采用CAD/CAM技术切削日本TOSOH氧化锆块，切削出基牙形的氧化锆基牙材料后，使用爱迪特HONOR ANTERIOR A1色染色液浸染10s，浸染后烧结，烧结温度为830℃，烧结时间为2min，即得A1色基牙；
S2.制备牙冠：采用CAD/CAM技术切削日本TOSOH氧化锆块，切削出牙冠形的氧化锆牙冠材料后，进行内染：先将D-MAX ICE-BLUE切端液涂布于氧化锆牙冠材料切端，再将氧化锆牙冠材料浸泡于爱迪特HONOR ANTERIOR A1色染色液中，浸染10s，取出后干燥，干燥温度为110℃，干燥时间为30min。干燥后结晶，结晶温度为1450℃，结晶时间为8.5h；再进行外染：将爱迪特HONOR ANTERIOR A1色染色液涂布于内染后的氧化锆牙冠材料外表面，再在其切端涂布切端液；外染后烧结，烧结温度为830℃，烧结时间为2min；冷却后，将EMAX CeramGlaze釉粉和EMAX Ceram Glaze and Stain Liquid allround釉液混合，涂布于氧化锆牙冠材料外表面；上釉后进行再次烧结，烧结温度为830℃，烧结时间为2min；冷却后如需再次调整可进行第三次烧结，烧结温度不超过820℃，烧结时间为2min；冷却后用抛光绒纶抛光氧化锆牙冠材料表面，即得A1色牙冠；
S3.制备色片：将所述A1色牙冠内表面用粘结剂粘结于所述A1色基牙上，即得A1色色片。
实施例2
一种染色液，以去离子水1000份作为溶剂，加入硝酸铒着色剂18份、硝酸铁着色剂8份、聚乙二醇40份、胭脂红5份，搅拌至完全溶解，即得A1色染色液。
一种氧化锆全瓷牙用比色片的制备方法，包括以下步骤：
S1.制备基牙：采用CAD/CAM技术切削氧化锆块，切削出基牙形的氧化锆基牙材料后，使用A1色染色液浸染20s，浸染后烧结，烧结温度为830℃，烧结时间为2min，即得A1色基牙；
S2.制备牙冠：采用CAD/CAM技术切削氧化锆块，切削出牙冠形的氧化锆牙冠材料后进行内染，先将切端液涂布于氧化锆牙冠材料切端，再将氧化锆牙冠材料浸泡于A1色染色液中，浸染10s，取出后干燥，干燥温度为110℃，干燥时间为30min；干燥后结晶，结晶温度为1450℃，结晶时间为8.5h；再进行外染，将A1色染色液涂布于内染后的氧化锆牙冠材料外表面，再在其切端涂布切端液；外染后烧结，烧结温度为830℃，烧结时间为2min，上釉后进行再次烧结，烧结温度为830℃，烧结时间为2min，冷却后抛光，即得A1色牙冠；
S3.制备色片：将所述牙冠内表面用粘结剂粘结于所述基牙上，即得A1色色片。
实施例3
一种染色液，以去离子水1000份作为溶剂，加入硝酸铒着色剂10份、硝酸铁着色剂20份、聚乙二醇40份、胭脂红5份，搅拌至完全溶解，即得D4色染色液。
一种氧化锆全瓷牙用比色片的制备方法，包括以下步骤：
S1.制备基牙：采用CAD/CAM技术切削氧化锆块，切削出基牙形的氧化锆基牙材料后，使用D4色染色液浸染20s，浸染后烧结，烧结温度为830℃，烧结时间为2min，即得D4色基牙；
S2.制备牙冠：采用CAD/CAM技术切削氧化锆块，切削出牙冠形的氧化锆牙冠材料后进行内染，先将切端液涂布于氧化锆牙冠材料切端，再将氧化锆牙冠材料浸泡于D4色染色液中，浸染10s，取出后干燥，干燥温度为110℃，干燥时间为30min。干燥后结晶，结晶温度为1450℃，结晶时间为8.5h；再进行外染，将D4色染色液涂布于内染后的氧化锆牙冠材料外表面，再在其切端涂布切端液；外染后烧结，烧结温度为830℃，烧结时间为2min，釉后进行再次烧结，烧结温度为830℃，烧结时间为2min，冷却后抛光，即得D4色牙冠；
S3.制备色片：将所述牙冠内表面用粘结剂粘结于所述基牙上，即得D4色色片。
本发明制备方法与全锆修复体材料及染色工艺基本统一，本发明制备方法制备而成的比色片，颜色、光泽度以及通透度与全锆修复体及天然牙齿更为接近，显色效果稳定持久，色彩立体感强，比色精准度高，在色彩的传递与再现上能够更为准确。
Claims (10)
1.一种氧化锆全瓷牙用比色片的制备方法，其特征在于，包括以下步骤：
S1.制备基牙：切削氧化锆块，切削出基牙形的氧化锆基牙材料后，使用染色液浸染，烧结后制得基牙；
S2.制备牙冠：切削氧化锆块，切削出牙冠形的氧化锆牙冠材料后，使用染色液和切端液对氧化锆牙冠材料进行内染和外染，烧结、上釉、再次烧结、抛光，即得牙冠；
S3.制备色片：将所述牙冠内表面用粘结剂粘结于所述基牙上，即得色片。
2.根据权利要求1所述的氧化锆全瓷牙用比色片的制备方法，其特征在于，步骤S1和步骤S2中，采用CAD/CAM技术切削氧化锆块。
3.根据权利要求1所述的氧化锆全瓷牙用比色片的制备方法，其特征在于，步骤S1和步骤S2中，烧结温度不超过830℃，烧结时间为2-3min。
4.根据权利要求1所述的氧化锆全瓷牙用比色片的制备方法，其特征在于，步骤S1中浸染时间为5-20s。
5.根据权利要求1所述的氧化锆全瓷牙用比色片的制备方法，其特征在于，步骤S2中所述内染为：先将切端液涂布于氧化锆牙冠材料切端，再将氧化锆牙冠材料浸泡于染色液中，浸染5-20s，取出后干燥、结晶。
6.根据权利要求5所述的氧化锆全瓷牙用比色片的制备方法，其特征在于，干燥温度为100-110℃，干燥时间为30-35min。
7.根据权利要求5所述的氧化锆全瓷牙用比色片的制备方法，其特征在于，结晶温度不超过1450℃，结晶时间为8.5-9h。
8.根据权利要求1所述的氧化锆全瓷牙用比色片的制备方法，其特征在于，步骤S2中所述外染为：将染色液涂布于内染后的氧化锆牙冠材料外表面，再在其切端涂布切端液。
9.根据权利要求1所述的氧化锆全瓷牙用比色片的制备方法，其特征在于，所述染色液包括以下按重量份数计算的组分：去离子水1000份、硝酸盐着色剂6-85份、渗透剂40份、指示剂5份。
10.根据权利要求9所述的氧化锆全瓷牙用比色片的制备方法，其特征在于，所述硝酸铁染色剂为硝酸铒、硝酸铁；所述渗透剂为聚乙二醇；所述指示剂为胭脂红。