CN110641009A - 一种高分子发泡无缝缓冲管的制备方法 - Google Patents

一种高分子发泡无缝缓冲管的制备方法 Download PDF

Info

Publication number
CN110641009A
CN110641009A CN201910907890.7A CN201910907890A CN110641009A CN 110641009 A CN110641009 A CN 110641009A CN 201910907890 A CN201910907890 A CN 201910907890A CN 110641009 A CN110641009 A CN 110641009A
Authority
CN
China
Prior art keywords
foaming
buffer
tube
buffer sleeve
seamless
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910907890.7A
Other languages
English (en)
Inventor
王小卫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU ZHENQUAN RUBBER & PLASTIC TECHNOLOGY Co Ltd
Original Assignee
SUZHOU ZHENQUAN RUBBER & PLASTIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU ZHENQUAN RUBBER & PLASTIC TECHNOLOGY Co Ltd filed Critical SUZHOU ZHENQUAN RUBBER & PLASTIC TECHNOLOGY Co Ltd
Priority to CN201910907890.7A priority Critical patent/CN110641009A/zh
Publication of CN110641009A publication Critical patent/CN110641009A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高分子发泡无缝缓冲管的制备方法，所述无缝缓冲管包括管本体以及包覆在所述管本体表面的发泡缓冲套，所述发泡缓冲套的轴心线与所述管本体的轴心线相重叠，它依次包括以下步骤：（a）将发泡缓冲套套在管本体外；（b）调节管本体两端面与发泡缓冲套对应端面的间距，使其间距为‑2~2mm；（c）控制管本体外表面与发泡缓冲套内表面的间距，使其间距为1~2mm；（d）对所述管本体和发泡缓冲套进行加热，使得发泡缓冲套热缩至紧贴在管本体表面即可。通过控制发泡缓冲套和管本体外的位置和间距，并采用加热、热缩的方式使其贴合，不仅简化了无缝缓冲管的结构，也简化了其制作工艺，从而有效地提高了其生产效率并降低了成本。

Description

一种高分子发泡无缝缓冲管的制备方法
技术领域
本发明属于膜类产品包装领域，涉及一种无缝缓冲管，具体涉及一种高分子发泡无缝缓冲管的制备方法。
背景技术
申请号为201910284093.8的中国发明专利公开了一种用于膜类产品包装的无缝缓冲管，包括内管、两个粘结圈和缓冲外管；所述内管长于所述缓冲外管，且所述内管安插在所述缓冲外管内，并将所述内管的两端等长度的暴露在所述缓冲外管两端各一段过渡端；所述两个粘结圈分别粘结在所述缓冲外管两端内壁上，并将所述缓冲外管与所述内管粘结牢固；该述缓冲外管还包括特定组分含量和种类的原料组分。然而该无缝缓冲管需要借助于两个粘结圈进行粘结，导致结构和生产工艺变得复杂，生产效率低下。
发明内容
本发明目的是为了克服现有技术的不足而提供一种高分子发泡无缝缓冲管的制备方法。
为达到上述目的，本发明所采用的技术方案为：一种高分子发泡无缝缓冲管的制备方法，所述无缝缓冲管包括管本体以及包覆在所述管本体表面的发泡缓冲套，所述发泡缓冲套的轴心线与所述管本体的轴心线相重叠，它依次包括以下步骤：
（a）将发泡缓冲套套在管本体外；
（b）调节管本体两端面与发泡缓冲套对应端面的间距，使其间距为-2~2mm；
（c）控制管本体外表面与发泡缓冲套内表面的间距，使其间距为1~2mm；
（d）对所述管本体和发泡缓冲套进行加热，使得发泡缓冲套热缩至紧贴在管本体表面即可。
优化地，所述管本体为牛皮纸筒。
优化地，所述发泡缓冲套的材质为高分子发泡材料。
进一步地，所述发泡缓冲套的压缩强度为80~100Kpa，拉伸强度为1800~2500Kpa。
进一步地，所述发泡缓冲套的软硬度为32度~65度。
优化地，步骤（a）中，先用夹具对所述管本体进行定位，再套入发泡缓冲套。
优化地，步骤（d）中，加热的温度为60~70℃、加热的时间为20~40分钟。
优化地，所述管本体的外径为170.4~182.4mm、厚度为9~15mm，所述发泡缓冲套（2）的厚度为2~8mm。
由于上述技术方案运用，本发明与现有技术相比具有下列优点：本发明高分子发泡无缝缓冲管的制备方法，通过控制发泡缓冲套和管本体外的位置和间距，并采用加热、热缩的方式使其贴合，不仅简化了无缝缓冲管的结构，也简化了其制作工艺，从而有效地提高了其生产效率并降低了成本。
附图说明
图1为本发明无缝缓冲管的结构示意图。
具体实施方式
下面将结合附图对本发明优选实施方案进行详细说明：
如图1所示的无缝缓冲管，包括管本体1以及包覆在管本体1表面的发泡缓冲套2，使得发泡缓冲套2的轴心线与管本体1的轴心线相重叠；具体地，管本体1的材质通常为牛皮纸筒，其外径可以为170.4~182.4mm、厚度为9~15mm；发泡缓冲套2的材质为高分子发泡材料（如EVA泡棉等市售的即可），其厚度为2~8mm，该发泡缓冲套2的物理性能优选如下：压缩强度为80~100Kpa，拉伸强度为1800~2500Kpa，软硬度为32度~65度。
上述高分子发泡无缝缓冲管的制备方法，它依次包括以下步骤：
（a）用夹具对管本体1进行定位，再将发泡缓冲套2套在管本体1外；
（b）调节管本体1两端面与发泡缓冲套2对应端面的间距，使其间距为-2~2mm；
（c）控制管本体1外表面与发泡缓冲套2内表面的间距，使其间距为1~2mm；
（d）对管本体1和发泡缓冲套2进行加热，使得发泡缓冲套2热缩至紧贴在管本体1表面即可；具体地，加热的温度为60~70℃、加热的时间为20~40分钟。
虽然通过实施例描绘了本申请，本领域普通技术人员知道，本申请有许多变形和变化而不脱离本申请的精神，希望所附的权利要求包括这些变形和变化而不脱离本申请的精神。

Claims (8)

1.一种高分子发泡无缝缓冲管的制备方法，所述无缝缓冲管包括管本体（1）以及包覆在所述管本体（1）表面的发泡缓冲套（2），所述发泡缓冲套（2）的轴心线与所述管本体（1）的轴心线相重叠，其特征在于，它依次包括以下步骤：
（a）将发泡缓冲套（2）套在管本体（1）外；
（b）调节管本体（1）两端面与发泡缓冲套（2）对应端面的间距，使其间距为-2~2mm；
（c）控制管本体（1）外表面与发泡缓冲套（2）内表面的间距，使其间距为1~2mm；
（d）对所述管本体（1）和发泡缓冲套（2）进行加热，使得发泡缓冲套（2）热缩至紧贴在管本体（1）表面即可。
2.根据权利要求1所述的高分子发泡无缝缓冲管的制备方法，其特征在于：所述管本体（1）为牛皮纸筒。
3.根据权利要求1所述的高分子发泡无缝缓冲管的制备方法，其特征在于：所述发泡缓冲套（2）的材质为高分子发泡材料。
4.根据权利要求3所述的高分子发泡无缝缓冲管的制备方法，其特征在于：所述发泡缓冲套（2）的压缩强度为80~100Kpa，拉伸强度为1800~2500Kpa。
5.根据权利要求3所述的高分子发泡无缝缓冲管的制备方法，其特征在于：所述发泡缓冲套（2）的软硬度为32度~65度。
6.根据权利要求1所述的高分子发泡无缝缓冲管的制备方法，其特征在于：步骤（a）中，先用夹具对所述管本体（1）进行定位，再套入发泡缓冲套（2）。
7.根据权利要求1所述的高分子发泡无缝缓冲管的制备方法，其特征在于：步骤（d）中，加热的温度为60~70℃、加热的时间为20~40分钟。
8.根据权利要求1所述的高分子发泡无缝缓冲管的制备方法，其特征在于：所述管本体（1）的外径为170.4~182.4mm、厚度为9~15mm，所述发泡缓冲套（2）的厚度为2~8mm。
CN201910907890.7A 2019-09-25 2019-09-25 一种高分子发泡无缝缓冲管的制备方法 Pending CN110641009A (zh)