CN110591801A - 一种压缩机润滑油组合物及其制备方法 - Google Patents
一种压缩机润滑油组合物及其制备方法 Download PDFInfo
- Publication number
- CN110591801A CN110591801A CN201910972678.9A CN201910972678A CN110591801A CN 110591801 A CN110591801 A CN 110591801A CN 201910972678 A CN201910972678 A CN 201910972678A CN 110591801 A CN110591801 A CN 110591801A
- Authority
- CN
- China
- Prior art keywords
- lubricating oil
- oil composition
- compressor
- polyalkylene glycol
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种压缩机润滑油组合物，由包括以下组分的原料制备而成：聚烷撑二醇95wt％～99.9wt％；抗氧剂0.05wt％～2.5wt％；腐蚀抑制剂0.05wt％～2.5wt％；所述聚烷撑二醇在40℃的运动黏度为50mm2/s～400mm2/s。与现有技术相比，本发明提供的压缩机润滑油组合物以特定性质的聚烷撑二醇为主要组分，并与其它特定含量组分实现较好的相互作用，得到的压缩机润滑油组合物具有良好的热氧化安定性、优良的润滑性能、较好的黏温性能、较低的积碳倾向、优异的抗腐蚀防锈性能，为烃类气体压缩机提供良好润滑、密封、冷却等作用，同时，具备优良的抵抗轻烃稀释能力，有效防止黏度过度下降造成压缩机润滑不良。
Description
技术领域
本发明涉及润滑油技术领域，更具体地说，是涉及一种压缩机润滑油组合物及其制备方法。
背景技术
在石化等行业天然气、瓦斯气、丙烷、乙烯、丁二烯、氯乙烯等烃类气体的输送、灌瓶以及分离回收等，需要通过气体压缩机得以实现，而压缩机润滑油则为烃类气体压缩机提供可靠的润滑、密封、冷却等作用。由于压缩机润滑油与压缩气体直接接触，易受压缩气体性质的影响而加剧氧化、老化变质；烃类气体中的H2S成分、工艺气体SO2、NH3等组分，对压缩机轴承活塞、转子等核心部件有腐蚀性；另外，很多气体压缩工艺对压缩后的气体纯度有严格要求，需要考虑润滑油添加剂的毒性，确保润滑油不与气体反应，不影响气体的纯度。这就决定了压缩机润滑油应具有适当的粘度、积碳倾向小、氧化安定性好、抗腐蚀防锈性好等性能特点。
烃类气体压缩机具体工况条件决定了所使用的压缩机润滑油需要具备如下的主要性能：(1)应该具有良好的黏温性能，低温时，润滑油黏度不能太大，润滑油能够充分流到润滑部位；高温时，润滑油黏度不能太小，润滑油在润滑部位形成足够厚的油膜，保证良好润滑；(2)在低温下具备良好的流动性；(3)具备良好的热氧化安定性和化学稳定性，压缩机润滑油在使用过程中，由于受高温、高压和金属催化作用，容易老化变质，生成各种酸和沉淀物，润滑油热氧化安定性的好坏，不仅影响油品的使用寿命，还最终影响压缩机运行的可靠性；(4)具备良好的润滑性能，减少摩擦面的磨损，保证设备正常运行；(5)较低的积碳倾向；(6)能抵抗轻烃的稀释，防止黏度过度下降造成压缩机润滑不良；(7)具有良好的抗腐蚀防锈性能，保证设备正常运转。但是，现有技术中的压缩机润滑油还不能完全满足上述各项性能的要求。
发明内容
有鉴于此，本发明的目的在于提供一种压缩机润滑油组合物及其制备方法，本发明提供的压缩机润滑油组合物具有良好的热氧化安定性、优良的润滑性能、较好的黏温性能、较低的积碳倾向、优异的抗腐蚀防锈性能，为烃类气体压缩机提供良好润滑、密封、冷却等作用，同时，具备优良的抵抗轻烃稀释能力，有效防止黏度过度下降造成压缩机润滑不良。
本发明提供了一种压缩机润滑油组合物，由包括以下组分的原料制备而成：
聚烷撑二醇95wt％～99.9wt％；
抗氧剂0.05wt％～2.5wt％；
腐蚀抑制剂0.05wt％～2.5wt％；
所述聚烷撑二醇在40℃的运动黏度为50mm2/s～400mm2/s。
优选的，所述聚烷撑二醇选自环氧丙烷均聚单羟基醚和/或环氧乙烷环氧丙烷共聚单羟基醚。
优选的，所述抗氧剂选自有机酚类抗氧剂和/或有机胺类抗氧剂。
优选的，所述腐蚀抑制剂选自磺酸盐、脂肪酸、脂肪酸衍生化合物和复合磷酸酯类化合物中的一种或多种。
本发明还提供了一种上述技术方案所述的压缩机润滑油组合物的制备方法，包括以下步骤：
a)将聚烷撑二醇、抗氧剂和腐蚀抑制剂混合后，进行调合，得到压缩机润滑油组合物；所述聚烷撑二醇在40℃的运动黏度为50mm2/s～400mm2/s。
优选的，步骤a)中所述混合的过程具体为：
将抗氧剂、腐蚀抑制剂依次加入聚烷撑二醇中，完成混合过程。
优选的，步骤a)中所述调合的过程在真空条件下进行；所述真空条件的真空度小于-0.8MPa。
优选的，步骤a)中所述调合的方式为搅拌；所述搅拌的温度为80℃～120℃。
本发明提供了一种压缩机润滑油组合物，由包括以下组分的原料制备而成：聚烷撑二醇95wt％～99.9wt％；抗氧剂0.05wt％～2.5wt％；腐蚀抑制剂0.05wt％～2.5wt％；所述聚烷撑二醇在40℃的运动黏度为50mm2/s～400mm2/s。与现有技术相比，本发明提供的压缩机润滑油组合物以特定性质的聚烷撑二醇为主要组分，并与其它特定含量组分实现较好的相互作用，得到的压缩机润滑油组合物具有良好的热氧化安定性、优良的润滑性能、较好的黏温性能、较低的积碳倾向、优异的抗腐蚀防锈性能，为烃类气体压缩机提供良好润滑、密封、冷却等作用，同时，具备优良的抵抗轻烃稀释能力，有效防止黏度过度下降造成压缩机润滑不良。
另外，本发明提供的制备方法简单、条件温和，适合大规模工业生产。
具体实施方式
下面将结合本发明实施例，对本发明的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供了一种压缩机润滑油组合物，由包括以下组分的原料制备而成：
聚烷撑二醇95wt％～99.9wt％；
抗氧剂0.05wt％～2.5wt％；
腐蚀抑制剂0.05wt％～2.5wt％；
所述聚烷撑二醇在40℃的运动黏度为50mm2/s～400mm2/s。
在本发明中，所述压缩机润滑油组合物包括聚烷撑二醇、抗氧剂和腐蚀抑制剂，优选由聚烷撑二醇、抗氧剂和腐蚀抑制剂组成。
在本发明中，所述聚烷撑二醇在40℃的运动黏度为50mm2/s～400mm2/s，优选为100mm2/s～200mm2/s；所述聚烷撑二醇优选选自环氧丙烷均聚单羟基醚和/或环氧乙烷环氧丙烷共聚单羟基醚，更优选为环氧乙烷环氧丙烷共聚单羟基醚。本发明对所述聚烷撑二醇的来源没有特殊限制，采用本领域技术人员熟知的上述环氧丙烷均聚单羟基醚和环氧乙烷环氧丙烷共聚单羟基醚的市售商品或自制品均可。
在本发明中，所述压缩机润滑油组合物包括95wt％～99.9wt％的聚烷撑二醇，优选为97.3wt％～99.6wt％，更优选为99.6wt％。
在本发明中，所述抗氧剂优选选自有机酚类抗氧剂和/或有机胺类抗氧剂，更优选为有机酚类抗氧剂或有机胺类抗氧剂。在本发明一个优选的实施例中，所述抗氧剂为有机胺类抗氧剂，具体为二异辛基二苯胺抗氧剂；在本发明另一个优选的实施例中，所述抗氧剂为有机胺类抗氧剂，具体为4,4’-双(二甲基苄基)二苯胺抗氧剂；在本发明另一个优选的实施例中，所述抗氧剂为有机酚类抗氧剂，具体为TH-330酚类抗氧剂。本发明对所述抗氧剂的来源没有特殊限制，采用本领域技术人员熟知的上述有机酚类抗氧剂和有机胺类抗氧剂的市售商品即可。
在本发明中，所述压缩机润滑油组合物包括0.05wt％～2.5wt％的抗氧剂，优选为0.3wt％。
在本发明中，所述腐蚀抑制剂优选选自磺酸盐、脂肪酸、脂肪酸衍生化合物和复合磷酸酯类化合物中的一种或多种，更优选为脂肪酸或脂肪酸衍生化合物，更更优选为脂肪酸衍生化合物。在本发明一个优选的实施例中，所述腐蚀抑制剂为十二烯基丁二酸；在本发明另一个优选的实施例中，所述腐蚀抑制剂为烯基丁二酸半酯。本发明对所述腐蚀抑制剂的来源没有特殊限制，采用本领域技术人员熟知的上述磺酸盐、脂肪酸、脂肪酸衍生化合物和复合磷酸酯类化合物的市售商品即可。
在本发明中，所述压缩机润滑油组合物包括0.05wt％～2.5wt％的腐蚀抑制剂，优选为0.1wt％～1wt％，更优选为0.1wt％。
本发明提供的压缩机润滑油组合物以特定性质的聚烷撑二醇为主要组分，并与其它特定含量组分实现较好的相互作用，得到的压缩机润滑油组合物具有良好的热氧化安定性、优良的润滑性能、较好的黏温性能、较低的积碳倾向、优异的抗腐蚀防锈性能，为烃类气体压缩机提供良好润滑、密封、冷却等作用，同时，具备优良的抵抗轻烃稀释能力，有效防止黏度过度下降造成压缩机润滑不良。因此，本发明提供的压缩机润滑油组合物特别适用于烃类气体压缩机的润滑，可以为压缩机提供良好的润滑、密封、冷却等作用，能够大大降低设备的维护成本，具备优良的抵抗轻烃稀释能力，有效防止黏度过度下降造成压缩机润滑不良，具有广阔的应用前景。
本发明还提供了一种上述技术方案所述的压缩机润滑油组合物的制备方法，包括以下步骤：
a)将聚烷撑二醇、抗氧剂和腐蚀抑制剂混合后，进行调合，得到压缩机润滑油组合物；所述聚烷撑二醇在40℃的运动黏度为50mm2/s～400mm2/s。
本发明首先将聚烷撑二醇、抗氧剂和腐蚀抑制剂混合。在本发明中，所述聚烷撑二醇、抗氧剂和腐蚀抑制剂与上述技术方案中所述的相同，在此不再赘述。
在本发明中，所述混合的过程优选具体为：
将抗氧剂、腐蚀抑制剂依次加入聚烷撑二醇中，完成混合过程。
完成混合过程后，本发明将混合后的原料进行调合，得到压缩机润滑油组合物。在本发明中，所述调合的过程优选在真空条件下进行；所述真空条件的真空度优选小于-0.8MPa。
在本发明中，所述调合的方式优选为搅拌；本发明对所述搅拌的方式没有特殊限制，采用本领域技术人员熟知的人工搅拌或机械搅拌的技术方案均可。在本发明中，所述搅拌的温度优选为80℃～120℃，更优选为100℃；保证搅拌均匀即可。
本发明提供的制备方法简单、条件温和，适合大规模工业生产。
本发明提供了一种压缩机润滑油组合物，由包括以下组分的原料制备而成：聚烷撑二醇95wt％～99.9wt％；抗氧剂0.05wt％～2.5wt％；腐蚀抑制剂0.05wt％～2.5wt％；所述聚烷撑二醇在40℃的运动黏度为50mm2/s～400mm2/s。与现有技术相比，本发明提供的压缩机润滑油组合物以特定性质的聚烷撑二醇为主要组分，并与其它特定含量组分实现较好的相互作用，得到的压缩机润滑油组合物具有良好的热氧化安定性、优良的润滑性能、较好的黏温性能、较低的积碳倾向、优异的抗腐蚀防锈性能，为烃类气体压缩机提供良好润滑、密封、冷却等作用，同时，具备优良的抵抗轻烃稀释能力，有效防止黏度过度下降造成压缩机润滑不良。
另外，本发明提供的制备方法简单、条件温和，适合大规模工业生产。
为了进一步说明本发明，下面通过以下实施例进行详细说明。
实施例1
将0.05g二异辛基二苯胺抗氧剂、1.0g十二烯基丁二酸腐蚀抑制剂依次加入98.95g聚烷撑二醇(环氧丙烷均聚单羟基醚)中，在100℃、＜-0.80MPa的真空条件下搅拌均匀，得到压缩机润滑油组合物。
实施例2
将2.5g二异辛基二苯胺抗氧剂、0.2g十二烯基丁二酸腐蚀抑制剂依次加入97.3g聚烷撑二醇(环氧丙烷均聚单羟基醚)中，在100℃、＜-0.80MPa的真空条件下搅拌均匀，得到压缩机润滑油组合物。
实施例3
将0.3g二异辛基二苯胺抗氧剂、0.1g烯基丁二酸半酯腐蚀抑制剂依次加入99.6g聚烷撑二醇(环氧乙烷环氧丙烷共聚单羟基醚)中，在100℃、＜-0.80MPa的真空条件下搅拌均匀，得到压缩机润滑油组合物。
实施例4
将0.3g 4,4’-双(二甲基苄基)二苯胺抗氧剂、0.1g烯基丁二酸半酯腐蚀抑制剂依次加入99.6g聚烷撑二醇(环氧乙烷环氧丙烷共聚单羟基醚)中，在100℃、＜-0.80MPa的真空条件下搅拌均匀，得到压缩机润滑油组合物。
实施例5
将0.3g TH-330酚类抗氧剂、0.1g烯基丁二酸半酯腐蚀抑制剂依次加入99.6g聚烷撑二醇(环氧乙烷环氧丙烷共聚单羟基醚)中，在100℃、＜-0.80MPa的真空条件下搅拌均匀，得到压缩机润滑油组合物。
对本发明实施例1～5提供的压缩机润滑油组合物的各项性能进行测试，结果参见表1所示。
表1本发明实施例1～5提供的压缩机润滑油组合物的各项性能数据
由表1可知，本发明实施例1～5提供的压缩机润滑油组合物具有良好的热氧化安定性、优良的润滑性能、较好的黏温性能、较低的积碳倾向、优异的抗腐蚀防锈性能，为烃类气体压缩机提供良好润滑、密封、冷却等作用，同时，具备优良的抵抗轻烃稀释能力，有效防止黏度过度下降造成压缩机润滑不良。
所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (8)
1.一种压缩机润滑油组合物，由包括以下组分的原料制备而成：
聚烷撑二醇95wt％～99.9wt％；
抗氧剂0.05wt％～2.5wt％；
腐蚀抑制剂0.05wt％～2.5wt％；
所述聚烷撑二醇在40℃的运动黏度为50mm2/s～400mm2/s。
2.根据权利要求1所述的压缩机润滑油组合物，其特征在于，所述聚烷撑二醇选自环氧丙烷均聚单羟基醚和/或环氧乙烷环氧丙烷共聚单羟基醚。
3.根据权利要求1所述的压缩机润滑油组合物，其特征在于，所述抗氧剂选自有机酚类抗氧剂和/或有机胺类抗氧剂。
4.根据权利要求1所述的压缩机润滑油组合物，其特征在于，所述腐蚀抑制剂选自磺酸盐、脂肪酸、脂肪酸衍生化合物和复合磷酸酯类化合物中的一种或多种。
5.一种权利要求1～4任一项所述的压缩机润滑油组合物的制备方法，包括以下步骤：
a)将聚烷撑二醇、抗氧剂和腐蚀抑制剂混合后，进行调合，得到压缩机润滑油组合物；所述聚烷撑二醇在40℃的运动黏度为50mm2/s～400mm2/s。
6.根据权利要求5所述的制备方法，其特征在于，步骤a)中所述混合的过程具体为：
将抗氧剂、腐蚀抑制剂依次加入聚烷撑二醇中，完成混合过程。
7.根据权利要求5所述的制备方法，其特征在于，步骤a)中所述调合的过程在真空条件下进行；所述真空条件的真空度小于-0.8MPa。
8.根据权利要求5所述的制备方法，其特征在于，步骤a)中所述调合的方式为搅拌；所述搅拌的温度为80℃～120℃。