CN110561874A - 一种新型暖软表面板的制备工艺 - Google Patents

一种新型暖软表面板的制备工艺 Download PDF

Info

Publication number
CN110561874A
CN110561874A CN201910888665.3A CN201910888665A CN110561874A CN 110561874 A CN110561874 A CN 110561874A CN 201910888665 A CN201910888665 A CN 201910888665A CN 110561874 A CN110561874 A CN 110561874A
Authority
CN
China
Prior art keywords
paper
decorative paper
glue
decorative
curing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910888665.3A
Other languages
English (en)
Inventor
孙晓义
孙学民
高聪民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGZHOU TIANRUN WOOD INDUSTRY Co Ltd
Original Assignee
CHANGZHOU TIANRUN WOOD INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGZHOU TIANRUN WOOD INDUSTRY Co Ltd filed Critical CHANGZHOU TIANRUN WOOD INDUSTRY Co Ltd
Priority to CN201910888665.3A priority Critical patent/CN110561874A/zh
Publication of CN110561874A publication Critical patent/CN110561874A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新型暖软表面板，包括芯板以及设置在芯板两个表面上的装饰纸；其中，芯板是由若干层浸胶纸复合后通过热压工艺制成的芯板；装饰纸的表面涂刷UV胶，UV胶经过弱处理灯组光照固化后，再经过EB能量固化，装饰纸表面形成装饰图案；装饰纸的外表面上粘结有保护膜。一种新型暖软表面板的制备工艺的步骤如下：1)、三聚氰胺浸胶纸和装饰纸的制备；2)、装饰纸的涂胶及其双重固化；3)、热压成型；4)、覆膜；5)、打包入库。本发明的装饰纸采用UV固化和EB(加速高能电子束)固化利用电子束加工多种不同的花纹，而且还保证了无指纹残留，保证板面的清洁，进而可以大大地降低装饰板的生产成本。

Description

一种新型暖软表面板的制备工艺
技术领域
本发明属于装饰板领域，更具体地说，涉及一种新型暖软表面板的制备工艺。
背景技术
装饰板用在装饰行业，其有稳定性高、防震防摔、耐寒耐热且有耐火防潮及耐烟烧的特性，其密度多在1.4-1.5g/cm3之间。装饰板的应用范围极为广泛，家居生活中的厨具台面、盥洗台面、餐桌、书桌、门扇，乃至公共场所的浴厕隔间、洗手台、接待柜台、置物柜、天花板、办公桌和办公隔间等，皆可采用装饰板制作。
装饰板在使用的时候，由于经常有人去接触，就会印上指纹，所以无指纹板成为一种装修板的趋势。
目前传统的无指纹板表面很硬，冬季使用的时候会产生很严重的凉凉的感觉，影响了使用效果。
发明内容
针对现有技术存在的不足，本发明的目的在于提供了一种新型暖软表面板的制备工艺，设计合理，利用准处理灯和EB加工双重固化工艺，在装饰纸表面形成一层软软的表层，表层通过EB加工不同的花纹，提高了装饰板的表面花纹的美观，而且摸上去暖暖的，不凉手，并且还具有耐刮耐磨的特征，实用性强，便于在各个行业进行普及使用。
为实现上述目的，本发明提供了如下技术方案：
一种新型暖软表面板，其特征在于：暖软表面板包括芯板以及设置在芯板两个表面上的装饰纸；其中，芯板是由若干层浸胶纸复合后通过热压工艺制成的芯板；装饰纸的表面涂刷UV胶，UV胶经过弱处理灯组光照固化后，再经过EB能量固化，装饰纸表面形成装饰图案；装饰纸的外表面上粘结有保护膜。
一种新型暖软表面板的制备工艺的步骤如下：
1)、三聚氰胺浸胶纸和装饰纸的制备；
2)、装饰纸的涂胶及其双重固化；
3)、热压成型；
4)、覆膜；
5)、打包入库。
作为一种优化的技术方案，所述三聚氰胺浸胶纸的制备步骤是：采用涂烘一体机进行加工，将外购的三聚氰胺胶水加入到浸胶槽中，采购的装饰纸自动上纸，装饰纸经过浸胶槽中；沾有三聚氰胺胶水的胶辊与装饰纸表面均匀接触，在装饰纸表面形成胶水层；随后表面附着胶水层的装饰纸进入烘箱内进行烘干，烘箱温度从低到高再到低，烘箱热源由管道蒸汽或天然气锅炉蒸汽提供；浸渍装饰纸烘干后，切除多余原纸边角料，即为成品的三聚氰胺浸胶纸；装饰纸采用的是牛皮白板纸，只需要裁剪成符合要求的尺寸即可。
作为一种优化的技术方案，装饰纸的涂胶及其双重固化的步骤如下：将UV胶水添加至装饰板生产线的胶槽中，然后通过涂胶辊对三聚氰胺浸渍纸的贴合面进行涂胶，在装饰纸的表面形成涂胶层；涂胶层通过15-30盏弱处理灯组进行第一次固化，工作温度控制在20℃-28℃之间；接下来通过加速高能电子束工艺实现二次固化，最后制成双重固化的装饰纸。
作为一种优化的技术方案，热压成型的步骤如下：将浸胶防火芯纸和装饰纸进行搭配，输送到全自动智能高温高压大型真空压机，热压热源由管道蒸汽和天然气锅炉蒸汽提供，真空压机的温度控制在120℃-160℃中，将配好的纸卷上下碾压，利用高温使覆合在纸上的胶水相互进行粘合，制得暖软表面板。
作为一种优化的技术方案，覆膜的步骤如下：通过覆膜机在暖软表面板的表面覆一层PVC薄膜做的保护膜，PVC薄膜的软化温度为80℃。
EB固化是辐射固化的一种形式。它是一个以电子束为辐射源，诱导经特殊配制的百分之百反应性液体快速转变成固体的过程。其原理为：首先，高能电子与涂料或油墨分子相互作用，使之分解成自由基；然后，该自由基与C＝C双键反应，形成增长链；最后，增长链与涂料或油墨的其余组分反应，使固化涂层产生交联，交联密度增加。由于辐照的电子能量较高，上述反应常常伴随分子降解、分子离子重排等负反应。因而EB固化的涂层产生了更大的支化度和更高的交联密度。
EB固化需要专用的固化设备。其工作原理为：电子从一组线形阴极板发出后，经过垂直均匀电场加速，在加速器辐照箱下得到帘状电子束。由于辐照制品距电场较近，因而其加速电压不高(低于500kV)，但由于输出电流大，因而功率较高。直线阴极枪远比扫描型设备紧凑，更易安装到生产线上，也更易屏蔽。
由于采用了上述技术方案，与现有技术相比，本发明的有益效果是：
1、本发明的装饰纸采用UV固化和EB(加速高能电子束)固化利用电子束加工多种不同的花纹，而且还保证了无指纹残留，保证板面的清洁，进而可以大大地降低装饰板的生产成本。
2、本发明中使用弱处理灯处理，弱处理灯的数目为15-30盏，工作温度控制在20℃-28℃之间，就能实现涂胶的预处理，通过改变涂胶层表面的松度，进而产生软接触表面。这样形成的软表面具有隔温效果，手摸上去是暖暖的，而且本身还具有强大的耐刮耐磨性能，冬天使用本发明产品会很舒服，丝毫没有凉的感觉。
3、本发明中制成的涂胶层还具有良好的耐酸碱腐蚀性能。
4、本发明使用加速高能电子束工艺加工花纹图案，表面无收缩，最终形成的花纹结构十分稳固。另外就是实现一套设备加工多种花纹，减少了费用，提高了加工的效率。
具体实施方式
实施例
一种新型暖软表面板，暖软表面板包括芯板以及设置在芯板两个表面上的装饰纸；其中，芯板是由若干层浸胶纸复合后通过热压工艺制成的芯板；装饰纸的表面涂刷UV胶，UV胶经过弱处理灯组光照固化后，再经过EB能量固化，装饰纸表面形成装饰图案；装饰纸的外表面上粘结有保护膜。
一种新型暖软表面板的制备工艺，步骤如下：
1)、三聚氰胺浸胶纸和装饰纸的制备。所述三聚氰胺浸胶纸的制备步骤是：采用涂烘一体机进行加工，将外购的三聚氰胺胶水加入到浸胶槽中，采购的装饰纸自动上纸，装饰纸经过浸胶槽中；沾有三聚氰胺胶水的胶辊与装饰纸表面均匀接触，在装饰纸表面形成胶水层；随后表面附着胶水层的装饰纸进入烘箱内进行烘干，烘箱温度从低到高再到低，烘箱热源由管道蒸汽或天然气锅炉蒸汽提供；浸渍装饰纸烘干后，切除多余原纸边角料，即为成品的三聚氰胺浸胶纸；装饰纸采用的是牛皮白板纸，只需要裁剪成符合要求的尺寸即可。
2)、装饰纸的涂胶及其双重固化。装饰纸的涂胶及其双重固化的步骤如下：将UV胶水添加至装饰板生产线的胶槽中，然后通过涂胶辊对三聚氰胺浸渍纸的贴合面进行涂胶，在装饰纸的表面形成涂胶层；涂胶层通过15-30盏弱处理灯组进行第一次固化，工作温度控制在20℃-28℃之间；接下来通过加速高能电子束工艺实现二次固化，最后制成双重固化的装饰纸。
3)、热压成型。热压成型的步骤如下：将浸胶防火芯纸和装饰纸进行搭配，输送到全自动智能高温高压大型真空压机，热压热源由管道蒸汽和天然气锅炉蒸汽提供，真空压机的温度控制在120℃-160℃中，将配好的纸卷上下碾压，利用高温使覆合在纸上的胶水相互进行粘合，制得暖软表面板。
4)、覆膜。覆膜的步骤如下：通过覆膜机在暖软表面板的表面覆一层PVC薄膜做的保护膜，PVC薄膜的软化温度为80℃。
5)、打包入库。
本发明的装饰纸采用UV固化和EB(加速高能电子束)固化利用电子束加工多种不同的花纹，而且还保证了无指纹残留，保证板面的清洁，进而可以大大地降低装饰板的生产成本。
本发明中使用弱处理灯处理，弱处理灯的数目为15-30盏，工作温度控制在20℃-28℃之间，就能实现涂胶的预处理，通过改变涂胶层表面的松度，进而产生软接触表面。这样形成的软表面具有隔温效果，手摸上去是暖暖的，而且本身还具有强大的耐刮耐磨性能，冬天使用本发明产品会很舒服，丝毫没有凉的感觉。本发明中制成的涂胶层还具有良好的耐酸碱腐蚀性能。
本发明使用加速高能电子束工艺加工花纹图案，表面无收缩，最终形成的花纹结构十分稳固。另外就是实现一套设备加工多种花纹，减少了费用，提高了加工的效率。
本发明的保护范围并不仅局限于上述实施例，凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理前提下的若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (5)

1.一种新型暖软表面板的制备工艺，其特征在于：
暖软表面板包括芯板以及设置在芯板两个表面上的装饰纸；
其中，芯板是由若干层浸胶纸复合后通过热压工艺制成的芯板；
装饰纸的表面涂刷UV胶，UV胶经过弱处理灯组光照固化后，再经过EB能量固化，装饰纸表面形成装饰图案；装饰纸的外表面上粘结有保护膜；
制备工艺的步骤如下：
1)、三聚氰胺浸胶纸和装饰纸的制备；
2)、装饰纸的涂胶及其双重固化；
3)、热压成型；
4)、覆膜；
5)、打包入库。
2.根据权利要求1所述的一种新型暖软表面板的制备工艺，其特征在于：
所述三聚氰胺浸胶纸的制备步骤是：
采用涂烘一体机进行加工，将外购的三聚氰胺胶水加入到浸胶槽中，采购的装饰纸自动上纸，装饰纸经过浸胶槽中；沾有三聚氰胺胶水的胶辊与装饰纸表面均匀接触，在装饰纸表面形成胶水层；随后表面附着胶水层的装饰纸进入烘箱内进行烘干，烘箱温度从低到高再到低，烘箱热源由管道蒸汽或天然气锅炉蒸汽提供；浸渍装饰纸烘干后，切除多余原纸边角料，即为成品的三聚氰胺浸胶纸；
装饰纸采用的是牛皮白板纸，只需要裁剪成符合要求的尺寸即可。
3.根据权利要求2所述的一种新型暖软表面板的制备工艺，其特征在于：
装饰纸的涂胶及其双重固化的步骤如下：
将UV胶水添加至装饰板生产线的胶槽中，然后通过涂胶辊对三聚氰胺浸渍纸的贴合面进行涂胶，在装饰纸的表面形成涂胶层；涂胶层通过15-30盏弱处理灯组进行第一次固化，工作温度控制在20℃-28℃之间；接下来通过加速高能电子束工艺实现二次固化，最后制成双重固化的装饰纸。
4.根据权利要求3所述的一种新型暖软表面板的制备工艺，其特征在于：热压成型的步骤如下：
将浸胶防火芯纸和装饰纸进行搭配，输送到全自动智能高温高压大型真空压机，热压热源由管道蒸汽和天然气锅炉蒸汽提供，真空压机的温度控制在120℃-160℃中，将配好的纸卷上下碾压，利用高温使覆合在纸上的胶水相互进行粘合，制得暖软表面板。
5.根据权利要求4所述的一种新型暖软表面板的制备工艺，其特征在于：覆膜的步骤如下：通过覆膜机在暖软表面板的表面覆一层PVC薄膜做的保护膜，PVC薄膜的软化温度为80℃。
CN201910888665.3A 2019-09-19 2019-09-19 一种新型暖软表面板的制备工艺 Pending CN110561874A (zh)