CN110554094A - 一种人工模拟缺陷及其制备方法 - Google Patents

一种人工模拟缺陷及其制备方法 Download PDF

Info

Publication number
CN110554094A
CN110554094A CN201910660742.XA CN201910660742A CN110554094A CN 110554094 A CN110554094 A CN 110554094A CN 201910660742 A CN201910660742 A CN 201910660742A CN 110554094 A CN110554094 A CN 110554094A
Authority
CN
China
Prior art keywords
polytetrafluoroethylene
films
defect
polytetrafluoroethylene film
layers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910660742.XA
Other languages
English (en)
Other versions
CN110554094B (zh
Inventor
徐振业
孟超
殷宗凯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AVIC Research Institute Special Structures Aeronautical Composites
Original Assignee
AVIC Research Institute Special Structures Aeronautical Composites
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by AVIC Research Institute Special Structures Aeronautical Composites filed Critical AVIC Research Institute Special Structures Aeronautical Composites
Priority to CN201910660742.XA priority Critical patent/CN110554094B/zh
Publication of CN110554094A publication Critical patent/CN110554094A/zh
Application granted granted Critical
Publication of CN110554094B publication Critical patent/CN110554094B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于无损检测领域，特别涉及一种人工模拟缺陷及其制备方法，用于制备对复合材料产品进行对比检测的模拟缺陷。四氟乙烯薄膜在制造过程中产生了滑移导致无法形成所预先设计的尺寸大小的空气腔体而使预埋人工缺陷不合格。对比试块在热压制造过程中，流入的胶液在降温后固化两层薄膜粘在一起，导致预埋人工缺陷不合格。本发明的人工模拟缺陷，包括上、下两层聚四氟乙烯薄膜，在聚四氟乙烯薄膜表面涂有脱模剂，在两层聚四氟乙烯薄膜之间、沿边缘粘接有室温双面胶，内部是密封的空气腔体。实现了人工模拟缺陷对比试块的制造，保证了产品无损检测的有效实施，同时提高了对比试块的制造成功率，节省了制造成本。

Description

一种人工模拟缺陷及其制备方法
技术领域
本发明属于无损检测领域，特别涉及一种人工模拟缺陷及其制备方法，用于制备对复合材料产品进行对比检测的模拟缺陷。
背景技术
复合材料产品在无损检测尤其是采用超声波检测时，需要制备预埋有人工缺陷的对比试块，对比试块内部的预埋人工缺陷用来模拟产品制造过程中的实际缺陷。检测时，对比试块与产品同时进行检测，其中对比试块的检测结果用来作为评判产品内部是否存在缺陷以及缺陷大小的参考，因此，合格的对比试块是保证复合材料产品无损检测正常实施的关键，而对比试块是否合格的评判依据是内部预制的人工缺陷是否合格。
目前，无损检测标准及规范中普遍采用的对比试块人工缺陷模拟方式是预埋两层聚四氟乙烯薄膜单层厚度不超过0.15mm，而其中的主要原理是通过预埋的两层聚四氟乙烯薄膜之间形成空气腔体来模拟复合材料内部的分层或脱粘缺陷。但在对比试块的实际制造过程中存在以下问题：
1.两层聚四氟乙烯薄膜在制造过程中产生了滑移导致无法形成所预先设计的尺寸大小的空气腔体而使预埋人工缺陷不合格。
2.对比试块在热压制造过程中，预浸料中的胶液由于高温融化而流入了两层聚四氟乙烯薄膜中，流入的胶液在降温后固化，两层薄膜粘在一起，导致预埋人工缺陷不合格。
发明内容
本发明提出一种人工模拟缺陷及其制备方法，解决目前对比试块制造过程中预埋的两层聚四氟乙烯薄膜之间产生滑移以及两层薄膜之间胶液流入而引起粘连的问题。
一种人工模拟缺陷，用于对复合材料产品进行对比检测，包括上、下两层聚四氟乙烯薄膜，在聚四氟乙烯薄膜表面涂有脱模剂，在两层聚四氟乙烯薄膜之间、沿边缘粘接有室温双面胶，内部是密封的空气腔体。
所述上、下两层聚四氟乙烯薄膜的形状、尺寸相同或者相近。
在聚四氟乙烯薄膜表面涂有多层脱模剂。
所述室温双面胶的宽度适度。
一种人工模拟缺陷的制备方法，用于制备对复合材料产品进行对比检测的模拟缺陷，该方法包括以下步骤：
S1、准备一对聚四氟乙烯薄膜，在每片聚四氟乙烯薄膜两侧涂抹脱模剂；
S2、在聚四氟乙烯薄膜相对的表面边缘粘贴室温双面胶，构成密封的空气腔体。
在S1中，多次涂抹脱模剂。
两片聚四氟乙烯薄膜的形状、尺寸相同或者相近。
所述室温双面胶的宽度适度。
有益效果：本发明实现了人工模拟缺陷对比试块的制造，保证了产品无损检测的有效实施，同时提高了对比试块的制造成功率，节省了制造成本。
附图说明
图1为人工模拟缺陷的组成示意图。
1-聚四氟乙烯薄膜；2-空气腔体；3-室温双面胶；4-脱模剂
具体实施方式
如图所示的人工模拟缺陷，包括上、下两层涂有脱模剂4的聚四氟乙烯薄膜1，其形状、尺寸相同或者相近。在聚四氟乙烯薄膜1之间沿边缘粘接有1室温双面胶3，形成密封的空气腔体2。
上述人工模拟缺陷的制备方法，包括以下步骤：
1在两层聚四氟乙烯薄膜1两侧涂抹多次脱模剂4，由于脱模剂4的存在这样能够避免固化过程中室温双面胶3挥发掉时胶液流入而引起两层聚四氟乙烯薄膜1粘在一起。
2采用室温双面胶3将预埋的两层聚四氟乙烯薄膜1的边缘密封起来，为保证人工缺陷尺寸，室温双面胶3的宽度适度，以能够将两层聚四氟乙烯薄膜1粘在一起为准。通过这样的处理，两层聚四氟乙烯薄膜1预先形成了空气腔体2，如图1所示，同时保证了在后续制造以及热压固化过程中两层聚四氟乙烯薄膜1不会出现滑移，确保人工缺陷尺寸；室温双面胶3在固化温度下熔化挥发掉，对缺陷的尺寸不会产生较大的影响。

Claims (8)

1.一种人工模拟缺陷，用于对复合材料产品进行对比检测，其特征在于：包括上、下两层聚四氟乙烯薄膜(1)，在聚四氟乙烯薄膜(1)表面涂有脱模剂(4)，在两层聚四氟乙烯薄膜(1)之间、沿边缘粘接有室温双面胶(3)，内部是密封的空气腔体(2)。
2.根据权利要求1所述的人工模拟缺陷，其特征在于：所述上、下两层聚四氟乙烯薄膜(1)的形状、尺寸相同或者相近。
3.根据权利要求1所述的人工模拟缺陷，其特征在于：在聚四氟乙烯薄膜(1)表面涂有多层脱模剂。
4.根据权利要求1所述的人工模拟缺陷，其特征在于：所述室温双面胶(3)的宽度适度。
5.一种人工模拟缺陷的制备方法，用于制备对复合材料产品进行对比检测的模拟缺陷，其特征在于，该方法包括以下步骤：
S1、准备一对聚四氟乙烯薄膜(1)，在每片聚四氟乙烯薄膜(1)两侧涂抹脱模剂(4)；
S2、在聚四氟乙烯薄膜相对的表面边缘粘贴室温双面胶(3)，构成密封的空气腔体(2)。
6.根据权利要求5所述的人工模拟缺陷的制备方法，其特征在于：在S1中，多次涂抹脱模剂。
7.根据权利要求5所述的人工模拟缺陷的制备方法，其特征在于：两片聚四氟乙烯薄膜(1)的形状、尺寸相同或者相近。
8.根据权利要求1所述的人工模拟缺陷的制备方法，其特征在于：所述室温双面胶(3)的宽度适度。
CN201910660742.XA 2019-07-22 2019-07-22 一种人工模拟缺陷及其制备方法 Active CN110554094B (zh)