CN110396762A - Four Jacquard systems and its warp-knitted spacer fabric - Google Patents
Four Jacquard systems and its warp-knitted spacer fabric Download PDFInfo
- Publication number
- CN110396762A CN110396762A CN201910701946.3A CN201910701946A CN110396762A CN 110396762 A CN110396762 A CN 110396762A CN 201910701946 A CN201910701946 A CN 201910701946A CN 110396762 A CN110396762 A CN 110396762A
- Authority
- CN
- China
- Prior art keywords
- sley bar
- follows
- raw material
- completely wear
- woven
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of four Jacquard systems and its warp-knitted spacer fabrics, which is characterized in that sley bar is woven using eight, sley bar JB1-1, sley bar JB1-2 are woven into surface layer in preceding needle bed band yarn lopping；Sley bar JB2-1, sley bar JB2-2, sley bar JB3-1, JB3-2 carry out band yarn lopping in preceding needle bed and rear needle bed and are woven into middle layer, and sley bar JB4-1, sley bar JB4-2 are woven into bottom in rear needle bed band yarn lopping；Eight sley bar cooperations are woven into knitted fabric.The sley bar of the application can be with independent design, to meet individual requirements.
Description
Technical field
The present invention relates to screen cloth technical fields, specifically, being four sets of Jacquard systems of one kind and its warp-knitted spacer fabric.
Background technique
Knitted fabric is woven knitting made of lopping, mutually string set as one group or several groups of warp thread simultaneously on warp knitting machine
Object.In this knitted fabric, every one thread of one group of warp thread only forms one or two coil in a row, then
Coil is re-formed in next row.The coil that is formed from an one thread is along knitted fabric through to configuration.Double comb warp-knittings
Each coil of object is substantially all to be woven by two one threads, and loop construction is stablized, surfacing.More comb knitted fabrics one
As by two sley bars be made into ground cloth, make fabric that there is required performance, and remaining sley bar penetrates warp thread, forms flower on ground cloth
Line.Warp-knitted fabric has single side and two-sided two class.Single warp knitted fabric is made into single needle bar warp knitting machine, the one side of fabric
It is made of coil, and another side is then dispersed with the underlap of coil.Double tricot is made into double rib warp loom,
Fabric two sides is all made of coil, and the underlap of coil is among two planar coils.Warp-knitted fabric is various in style, can be used as
Underwear, coat and curtain, lace etc. are also widely used in fields such as industry, agricultural and health cares.Wherein Jacquard class pattern
The jacquard weave performance of fabric Jacquard machine forms the coat fabric of unique decorative pattern.1. this kind of fabric of spun rayon yarn's Jacquard T-shirt fabric is being washed
Synthetic fibre on cloth using people's cotton staple yarn as fabric, configured using Jacquard flower pattern eyelet, Bao Qu, thick area by floral designs, formation flower pattern
Unique style, men and women's T-shirt fabric comfortable and easy to wear, typically now using the production of the Jacquard machine of E14 or thicker machine number.With acrylic fibers
When yarn or blended hair nitrile, the Bao Qu and Hou Qu of Jacquard flower pattern can be only utilized, relatively warming long sleeves T-shirt fabric is made, also once met
Using synthetic cotton and wool-rich blended yarns.2. Jacquard lappet fashion material this be by RJWB series Jacquard raschel machine produce
's.Typically a kind of type is RJWB3/2F type for it, and this machine has schlagblech, and wire gauze comb and inlaid thread are followed successively by after schlagblech
Jacquard comb, the ground tissue of fabric intricate detail is cooperatively formed by the two, and has pressure yarn Jacquard flower comb before schlagblech, and have list
Yarn selection device (EFS) and its cooperating, to form the three-dimensional relief-type decorative pattern (culvert of WB in type in thin ground tissue
Justice).Due to using single thread selection device to Jacquard flower comb before schlagblech, so every Jacquard yarn can be selected at accordingly
Row enter work or exit work, can form independent impression segment in this way, and longitudinal connecting line segment
Through being cut off.So fabric is produced closely similar with more combs with Jacquard, high-grade female's fashion material can be used as, it also can be more
Add a spandex to comb, produce elastic fabric, needs to use to adapt to high-grade lingerie, swimming suit, brassiere, type at this moment will be
RJWB4/2F.There are also RJWB8/2F types for this system, and at this moment increased sley bar can be used to expand more comb flower pattern, or make four comb elastic force
Net ground.Separately there are RJWBS4/2F type and RJWBS5/1F type.These machines are used to produce lace (indicating with S), the former has two
Jacquard comb, the latter then only has schlagblech previous jacquard comb, the jacquard comb after schlagblech be then two ground is combed replaced, so
Its ground tissue is then at simple type.RJWB Series machine system is wholly computer controlled, expensive, about combs more comb-Jacquard machines with 56-78
Phase brothers.
Summary of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of four sets of Jacquard systems and its warp-knitted spacer to knit
Object.
The purpose of the present invention is achieved through the following technical solutions:
A kind of four Jacquard systems, are uniformly arranged guide holder along central axis on fanning strip, and eight are arranged on sector portion
Guide holder or ten guide holders, guide holder is for fixing sley bar；
A kind of four jacquard warp-knitting space fabrics, which is characterized in that sley bar is woven using eight, sley bar JB1-1, sley bar
JB1-2 is woven into surface layer in preceding needle bed band yarn lopping；
Sley bar JB2-1, sley bar JB2-2, sley bar JB3-1, JB3-2 carry out band yarn lopping in preceding needle bed and rear needle bed and are woven into
Middle layer,
Sley bar JB4-1, sley bar JB4-2 are woven into bottom in rear needle bed band yarn lopping；
Eight sley bar cooperations are woven into four jacquard warp-knitting space fabrics；
Sley bar JB1-1, sley bar JB1-2, sley bar JB2-1, sley bar JB2-2, sley bar JB3-1, sley bar JB3-2, sley bar JB4-
1, sley bar JB4-2 is successively arranged in order；
Sley bar JB1-1, sley bar JB1-2 can design lines；
Sley bar JB2-1, sley bar JB2-2, can design lines；
Sley bar JB3-1, sley bar JB3-2 can design lines；
Sley bar JB4-1, sley bar JB4-2 can design lines；
Specific technique are as follows:
Sley bar JB1-1:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB1-2:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB2-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB2-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-1:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-2:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
The raw material that sley bar JB1-1 is used is 150D cation low stretch yarn；
The raw material that sley bar JB1-2 is used is 150D cation low stretch yarn；
The raw material that sley bar JB2-1 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB2-2 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB3-1 is used is 30D polyester monofilament；
The raw material that sley bar JB3-2 is used is 30D polyester monofilament；
The raw material that sley bar JB4-1 is used is 150D low elastic polyester filament；
The raw material that sley bar JB4-2 is used is 150D low elastic polyester filament.
A kind of four jacquard warp-knitting space fabrics, which is characterized in that sley bar is woven using ten, sley bar GB1, sley bar
JB2-1, sley bar JB2-2 are woven into surface layer in preceding needle bed band yarn lopping；
Sley bar JB3-1, sley bar JB3-2, sley bar JB4-1, sley bar JB4-2 carry out band yarn lopping volume in preceding needle bed and rear needle bed
It is made into middle layer；
Sley bar JB5-1, sley bar JB5-2, sley bar GB6 are woven into bottom in rear needle bed band yarn lopping；
Ten sley bar cooperations are woven into four jacquard warp-knitting space fabrics；
Sley bar GB1, sley bar JB2-1, sley bar JB2-2, sley bar JB3-1, sley bar JB3-2, sley bar JB4-1, sley bar JB4-2,
Sley bar JB5-1, sley bar JB5-2, sley bar GB6 are successively arranged in order；
Sley bar JB2-1, sley bar JB2-2, can design lines；
Sley bar JB3-1, sley bar JB3-2, can design lines；
Sley bar JB4-1, sley bar JB4-2 can design lines；
Sley bar JB5-1, sley bar JB5-2 can design lines；
Specific technique are as follows:
Sley bar GB1:1-0-0-0/0-1-1-1//
It entrys mode are as follows: completely wear
Sley bar JB2-1:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB2-2:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB3-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB5-1:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB5-2:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
Sley bar GB6:0-0-0-1/1-1-1-0//
It entrys mode are as follows: completely wear.
Sley bar GB1 is raw materials used for the low bullet terylene of 150D cation；
The raw material that sley bar JB2-1 is used is 150D cation low stretch yarn；
The raw material that sley bar JB2-2 is used is 150D cation low stretch yarn；
The raw material that sley bar JB3-1 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB3-2 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB4-1 is used is 30D polyester monofilament；
The raw material that sley bar JB4-2 is used is 30D polyester monofilament；
The raw material that sley bar JB5-1 is used is 150D low elastic polyester filament；
The raw material that sley bar JB5-2 is used is 150D low elastic polyester filament；
Sley bar GB6 raw materials used is the low bullet terylene of 150D；
The raw material of polyester monofilament is compound PBT master batch and PET raw material, quality of the compound PBT master batch in polyester monofilament
Score is 10~50%；
Polyester monofilament is prepared by the preparation process of melt spinning, and wherein spinning technique is using UDY-DT technique；Wherein
The type of cooling uses quenching or natural cooling, obtains the non-oriented silk of terylene, then drawn obtains flame-resistant terylene monofilament, wherein
2~4 times of stretching process stretching ratio.
Polyester monofilament spinning technique: spinning temperature is 280~320 DEG C；Cooling wind temperature is 15~25 DEG C, wind speed 0.1m/s
~5m/s or natural cooling；Spinning speed is 1000~1200m/min.
The raw material of compound PBT master batch is three layers of core-skin and mixes antimony zinc oxide complexing agent and PBT slice, and three layers of core-skin are mixed antimony two
Mass fraction of the zinc oxide complexing agent in compound PBT master batch is 6~16%；Melting extrusion is granulated after raw material is blended.
It is three-decker that three layers of core-skin, which are mixed antimony zinc oxide complexing agent, and sandwich layer is cuprous oxide, and middle layer is silver oxide, outside
Layer is to mix antimony zinc oxide.
The preparation method of the compound PBT master batch, the specific steps are that:
Silver nitrate solution is added with stirring in the solution high speed of stannous chloride, 600~1200 turns of high-speed stirred rate/
Point, so that silver ion and stannous chloride is carried out co-precipitation production bactericidal composition, it is to be precipitated not after continuing growing, it is obtained by filtration anti-
Bacteria composition；Then bactericidal composition is dispersed in pentanediol solvent, makes bactericidal composition dispersion activation, obtains antibacterial combination
The pentanediol solution of object；Nano antimony doped zinc oxide is added in the pentanediol solution of bactericidal composition, makes bactericidal composition table
Nano antimony doped zinc oxide is adsorbed in face, and isolated filter residue after filtering, aerobic calcining is prepared with three filter residue at high temperature
Layer structure mixes antimony zinc oxide complexing agent；Antimony zinc oxide complexing agent and PBT slice will be mixed by being granulated after melt blending
To compound PBT master batch.
The solution of the stannous chloride is the stannous chloride aqueous solution that mass fraction is 11~16%, and silver nitrate solution is
The silver nitrate aqueous solution that mass fraction is 6~11%, and the volume ratio of cuprous chloride solution and silver nitrate solution is 1:0.1~1:
0.3；
The mass fraction of bactericidal composition is 16~22% in the pentanediol solution of the bactericidal composition；
The mass ratio of the pentanediol solution of the nano antimony doped zinc oxide and bactericidal composition is 1:5~1:12；
By three-layer composite structure, combined oxidation is cuprous on the basis of nano antimony doped zinc oxide is antistatic plays antibacterial
Effect, while keeping mixing antimony zinc oxide using silver nanostructured double bridge effect is aoxidized in three layers of nanostructure
On the basis of antibacterial, using the dielectric effect of silver oxide, transmit as cuprous oxide, so that the high activity of zinc oxide structures be avoided to bring
The degradation of polyester segment improve the strand of polyester while using the polycondensation catalytic action of antimony doped zinc oxide sb structure is mixed, from
And have the function that protect polyester segment, and since this is as low temperature during antibacterial, the antibacterial that mainly rises of zinc oxide is lived
Property, while the method by coating plays the role of protection to internal oxidizable cuprous oxide, mixes antimony zinc oxide to realize
The dual antibacterial functions of modifying agent.
Compared with prior art, the positive effect of the present invention is:
Four Jacquards a set of Jacquard system more than three Jacquards, mostly a set of Jacquard system increase with the difficulty of technique change.
Four Jacquards a set of Jacquard system more than three Jacquards, decorative pattern change richer, three-layer network face, bottom, middle layer variation, merchant
Card combs more control freely to that can increase, and design difficulty, which can also increase, can more enrich the jacquard effect of part.Fabric
Application field is more extensive, is able to satisfy more design requirements.
Detailed description of the invention
Fig. 1 a schematic structural view of Embodiment 1 of the present invention；
Fig. 2 a schematic structural view of Embodiment 3 of the present invention.
Specific embodiment
The specific embodiment of the present invention four sets of Jacquard systems of one kind presented below and its warp-knitted spacer fabric.
Embodiment 1
Attached drawing 1 is referred to, a kind of four Jacquard systems are uniformly arranged guide holder along central axis on fanning strip, in scallop
Divide upper setting eight guide holders, guide holder is for fixing sley bar；
A kind of four jacquard warp-knitting space fabrics, which is characterized in that sley bar is woven using eight, sley bar JB1-1, sley bar
JB1-2 is woven into surface layer in preceding needle bed band yarn lopping；
Sley bar JB2-1, sley bar JB2-2, sley bar JB3-1, JB3-2 carry out band yarn lopping in preceding needle bed and rear needle bed and are woven into
Middle layer,
Sley bar JB4-1, sley bar JB4-2 are woven into bottom in rear needle bed band yarn lopping；
Eight sley bar cooperations are woven into four jacquard warp-knitting space fabrics；
Sley bar JB1-1, sley bar JB1-2 can design lines；
Sley bar JB2-1, sley bar JB2-2, can design lines；
Sley bar JB3-1, sley bar JB3-2 can design lines；
Sley bar JB4-1, sley bar JB4-2 can design lines；
The raw material that sley bar JB1-1 is used is 150D cation low stretch yarn；
The raw material that sley bar JB1-2 is used is 150D cation low stretch yarn；
The raw material that sley bar JB2-1 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB2-2 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB3-1 is used is 30D polyester monofilament；
The raw material that sley bar JB3-2 is used is 30D polyester monofilament；
The raw material that sley bar JB4-1 is used is 150D low elastic polyester filament；
The raw material that sley bar JB4-2 is used is 150D low elastic polyester filament；
Sley bar JB1-1:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB1-2:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB2-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB2-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-1:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-2:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
The raw material of polyester monofilament is compound PBT master batch and PET raw material, quality of the compound PBT master batch in polyester monofilament
Score is 30%；
Polyester monofilament is prepared by the preparation process of melt spinning, and wherein spinning technique is using UDY-DT technique；Wherein
The type of cooling uses quenching or natural cooling, obtains the non-oriented silk of terylene, then drawn obtains flame-resistant terylene monofilament, wherein
2~4 times of stretching process stretching ratio；Polyester monofilament spinning technique: spinning temperature is 280~320 DEG C；Cooling wind temperature be 15~
25 DEG C, wind speed 0.1m/s~5m/s or natural cooling；Spinning speed is 1000~1200m/min.
The raw material of compound PBT master batch is three layers of core-skin and mixes antimony zinc oxide complexing agent and PBT slice, and three layers of core-skin are mixed antimony two
Mass fraction of the zinc oxide complexing agent in compound PBT master batch is 10%；
It is three-decker that three layers of core-skin, which are mixed antimony zinc oxide complexing agent, and sandwich layer is cuprous oxide, and middle layer is silver oxide, outside
Layer is to mix antimony zinc oxide.
The preparation method of the compound PBT master batch, the specific steps are that:
It is added with stirring silver nitrate solution in the solution high speed of stannous chloride, 900 revs/min of high-speed stirred rate, makes silver
Ion and stannous chloride carry out co-precipitation production bactericidal composition, to be precipitated not after continuing growing, and antibacterial combination is obtained by filtration
Object；Then bactericidal composition is dispersed in pentanediol solvent, makes bactericidal composition dispersion activation, obtains the penta of bactericidal composition
Glycol solution；Nano antimony doped zinc oxide is added in the pentanediol solution of bactericidal composition, makes bactericidal composition adsorption
Nano antimony doped zinc oxide, isolated filter residue after filtering, aerobic calcining is prepared with three-decker filter residue at high temperature
Mix antimony zinc oxide complexing agent；To mix antimony zinc oxide complexing agent and PBT slice by be granulated after melt blending obtain it is compound
PBT master batch.
The solution of the stannous chloride is the stannous chloride aqueous solution that mass fraction is 13%, and silver nitrate solution is quality
The silver nitrate aqueous solution that score is 9%, and the volume ratio of cuprous chloride solution and silver nitrate solution is 1:0.15；
The mass fraction of bactericidal composition is 19% in the pentanediol solution of the bactericidal composition；
The mass ratio of the pentanediol solution of the nano antimony doped zinc oxide and bactericidal composition is 1:8；
Polyester monofilament is 96.0% to the antibiotic rate of staphylococcus glucose coccus, and bacteriostatic activity value is 5.1；To Escherichia coli
Antibiotic rate be 96.1%, bacteriostatic activity value be 5.3.
Embodiment 2
Attached drawing 1 is referred to, a kind of four Jacquard systems are uniformly arranged guide holder along central axis on fanning strip, in scallop
Divide upper setting eight guide holders, guide holder is for fixing sley bar；
A kind of four jacquard warp-knitting space fabrics, which is characterized in that sley bar is woven using eight, sley bar JB1-1, sley bar
JB1-2 is woven into surface layer in preceding needle bed band yarn lopping；
Sley bar JB2-1, sley bar JB2-2, sley bar JB3-1, JB3-2 carry out band yarn lopping in preceding needle bed and rear needle bed and are woven into
Middle layer,
Sley bar JB4-1, sley bar JB4-2 are woven into bottom in rear needle bed band yarn lopping；
Eight sley bar cooperations are woven into four jacquard warp-knitting space fabrics；
Sley bar JB1-1, sley bar JB1-2 can design lines；
Sley bar JB2-1, sley bar JB2-2, can design lines；
Sley bar JB3-1, sley bar JB3-2 can design lines；
Sley bar JB4-1, sley bar JB4-2 can design lines；
The raw material that sley bar JB1-1 is used is 150D cation low stretch yarn；
The raw material that sley bar JB1-2 is used is 150D cation low stretch yarn；
The raw material that sley bar JB2-1 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB2-2 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB3-1 is used is 30D polyester monofilament；
The raw material that sley bar JB3-2 is used is 30D polyester monofilament；
The raw material that sley bar JB4-1 is used is 150D low elastic polyester filament；
The raw material that sley bar JB4-2 is used is 150D low elastic polyester filament；
Sley bar JB1-1:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB1-2:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB2-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB2-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-1:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-2:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
The raw material of polyester monofilament is compound PBT master batch and PET raw material, quality of the compound PBT master batch in polyester monofilament
Score is 30%；
The raw material of compound PBT master batch is that bactericidal composition and PBT are sliced, matter of the bactericidal composition in compound PBT master batch
Measuring score is 10%；
The preparation method of the compound PBT master batch, the specific steps are that:
It is added with stirring silver nitrate solution in the solution high speed of stannous chloride, 900 revs/min of high-speed stirred rate, makes silver
Ion and stannous chloride carry out co-precipitation production bactericidal composition, to be precipitated not after continuing growing, and antibacterial combination is obtained by filtration
Object；Bactericidal composition and PBT slice are obtained into compound PBT master batch by being granulated after melt blending.
The solution of the stannous chloride is the stannous chloride aqueous solution that mass fraction is 13%, and silver nitrate solution is quality
The silver nitrate aqueous solution that score is 9%, and the volume ratio of cuprous chloride solution and silver nitrate solution is 1:0.15；
Polyester monofilament is 89.0% to the antibiotic rate of staphylococcus glucose coccus, and bacteriostatic activity value is 4.6；To Escherichia coli
Antibiotic rate be 88.1%, bacteriostatic activity value be 4.7.Compared with Example 1, anti-microbial property has dropped 10%, mixes antimony two
The addition of zinc oxide is essential technical step；And after antimony zinc oxide is mixed in addition, it can keep mixing antimony titanium dioxide
On the basis of the antibacterial of zinc, using the dielectric effect of silver oxide, transmit as cuprous oxide, to avoid the high activity of zinc oxide structures
The degradation of bring polyester segment, while using the polycondensation catalytic action for mixing antimony doped zinc oxide sb structure, improve the molecule of polyester
Chain, to have the function that protect polyester segment, and since this is as low temperature during antibacterial, main rise of zinc oxide resists
Bacterium activity, while the method by coating plays the role of protection to internal oxidizable cuprous oxide, mixes antimony oxygen to realize
Change the dual antibacterial functions of zinc modification agent.
Embodiment 3
Attached drawing 2 is referred to, a kind of four Jacquard systems are uniformly arranged guide holder along central axis on fanning strip, in scallop
Divide upper setting ten guide holders, guide holder is for fixing sley bar；
A kind of four jacquard warp-knitting space fabrics, which is characterized in that sley bar is woven using ten, sley bar GB1, sley bar
JB2-1, sley bar JB2-2 are woven into surface layer in preceding needle bed band yarn lopping；
Sley bar JB3-1, sley bar JB3-2, sley bar JB4-1, sley bar JB4-2 carry out band yarn lopping volume in preceding needle bed and rear needle bed
It is made into middle layer；
Sley bar JB5-1, sley bar JB5-2, sley bar GB6 are woven into bottom in rear needle bed band yarn lopping；
Ten sley bar cooperations are woven into four jacquard warp-knitting space fabrics；
Sley bar JB2-1, sley bar JB2-2, can design lines；
Sley bar JB3-1, sley bar JB3-2, can design lines；
Sley bar JB4-1, sley bar JB4-2 can design lines；
Sley bar JB5-1, sley bar JB5-2 can design lines；
Sley bar GB1 is raw materials used for the low bullet terylene of 150D cation；
The raw material that sley bar JB2-1 is used is 150D cation low stretch yarn；
The raw material that sley bar JB2-2 is used is 150D cation low stretch yarn；
The raw material that sley bar JB3-1 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB3-2 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB4-1 is used is 30D polyester monofilament；
The raw material that sley bar JB4-2 is used is 30D polyester monofilament；
The raw material that sley bar JB5-1 is used is 150D low elastic polyester filament；
The raw material that sley bar JB5-2 is used is 150D low elastic polyester filament；
Sley bar GB6 raw materials used is the low bullet terylene of 150D；
Specific technique are as follows:
Sley bar GB1:1-0-0-0/0-1-1-1//
It entrys mode are as follows: completely wear
Sley bar JB2-1:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB2-2:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB3-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB5-1:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB5-2:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
Sley bar GB6:0-0-0-1/1-1-1-0//
It entrys mode are as follows: completely wear.
The 30D polyester monofilament, the preparation of polyester monofilament is the same as embodiment 1.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
Member, without departing from the inventive concept of the premise, can also make several improvements and modifications, these improvements and modifications also should be regarded as
In protection scope of the present invention.
Claims (5)
1. a kind of four jacquard warp-knitting space fabrics, which is characterized in that sley bar is woven using eight, sley bar JB1-1, sley bar
JB1-2 is woven into surface layer in preceding needle bed band yarn lopping；
Sley bar JB2-1, sley bar JB2-2, sley bar JB3-1, JB3-2 carry out band yarn lopping in preceding needle bed and rear needle bed and are woven into centre
Layer,
Sley bar JB4-1, sley bar JB4-2 are woven into bottom in rear needle bed band yarn lopping；
Eight sley bar cooperations are woven into four jacquard warp-knitting space fabrics；
Specific technique are as follows:
Sley bar JB1-1:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB1-2:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB2-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB2-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-1:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-2:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear.
2. four jacquard warp-knitting space fabrics of one kind as described in claim 1, which is characterized in that the raw material that sley bar JB1-1 is used
For 150D cation low stretch yarn；
The raw material that sley bar JB1-2 is used is 150D cation low stretch yarn；
The raw material that sley bar JB2-1 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB2-2 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB3-1 is used is 30D polyester monofilament；
The raw material that sley bar JB3-2 is used is 30D polyester monofilament；
The raw material that sley bar JB4-1 is used is 150D low elastic polyester filament；
The raw material that sley bar JB4-2 is used is 150D low elastic polyester filament.
3. a kind of four jacquard warp-knitting space fabrics, which is characterized in that sley bar is woven using ten, sley bar GB1, sley bar JB2-
1, sley bar JB2-2 is woven into surface layer in preceding needle bed band yarn lopping；
Sley bar JB3-1, sley bar JB3-2, sley bar JB4-1, sley bar JB4-2 carry out band yarn lopping in preceding needle bed and rear needle bed and are woven into
Middle layer；
Sley bar JB5-1, sley bar JB5-2, sley bar GB6 are woven into bottom in rear needle bed band yarn lopping；
Ten sley bar cooperations are woven into four jacquard warp-knitting space fabrics；
Specific technique are as follows:
Sley bar GB1:1-0-0-0/0-1-1-1//
It entrys mode are as follows: completely wear
Sley bar JB2-1:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB2-2:1-0-1-1/1-2-1-1//
It entrys mode are as follows: completely wear
Sley bar JB3-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB3-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-1:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB4-2:1-0-0-1/0-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB5-1:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
Sley bar JB5-2:1-1-1-2/1-1-1-0//
It entrys mode are as follows: completely wear
Sley bar GB6:0-0-0-1/1-1-1-0//
It entrys mode are as follows: completely wear.
4. four jacquard warp-knitting space fabrics of one kind as claimed in claim 3, which is characterized in that
Sley bar GB1 is raw materials used for the low bullet terylene of 150D cation；
The raw material that sley bar JB2-1 is used is 150D cation low stretch yarn；
The raw material that sley bar JB2-2 is used is 150D cation low stretch yarn；
The raw material that sley bar JB3-1 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB3-2 is used is 140D polyamide fibre low stretch yarn；
The raw material that sley bar JB4-1 is used is 30D polyester monofilament；
The raw material that sley bar JB4-2 is used is 30D polyester monofilament；
The raw material that sley bar JB5-1 is used is 150D low elastic polyester filament；
The raw material that sley bar JB5-2 is used is 150D low elastic polyester filament；
Sley bar GB6 raw materials used is the low bullet terylene of 150D.
5. four jacquard warp-knitting space fabrics of one kind as claimed in claim 4, which is characterized in that
The raw material of polyester monofilament is compound PBT master batch and PET raw material, mass fraction of the compound PBT master batch in polyester monofilament
It is 10~50%；
The raw material of compound PBT master batch is three layers of core-skin and mixes antimony zinc oxide complexing agent and PBT slice, and three layers of core-skin are mixed antimony titanium dioxide
Mass fraction of the zinc complexing agent in compound PBT master batch is 6~16%；
It is three-decker that three layers of core-skin, which are mixed antimony zinc oxide complexing agent, and sandwich layer is cuprous oxide, and middle layer is silver oxide, and outer layer is
Mix antimony zinc oxide.