CN110373100A - 酒店卫生间用防水胶及渗水及时维修施工方法 - Google Patents
酒店卫生间用防水胶及渗水及时维修施工方法 Download PDFInfo
- Publication number
- CN110373100A CN110373100A CN201910635832.3A CN201910635832A CN110373100A CN 110373100 A CN110373100 A CN 110373100A CN 201910635832 A CN201910635832 A CN 201910635832A CN 110373100 A CN110373100 A CN 110373100A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- toilet
- hotel
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种酒店卫生间用防水胶及渗水及时维修施工方法，所述酒店卫生间用防水胶包括下述原料制备而成：聚氨酯改性丙烯酸乳液、醇酯十二、纳米二氧化钛、乙二醇、消泡剂、流平剂、增稠剂。本发明酒店卫生间用防水胶，采用特制的聚合物乳液，并添加纳米二氧化钛进一步增强了其粘结性能及防水性能，渗透进入混凝土结构的孔隙和缝隙中，防水性能优异，具有易于施工、涂膜表面平整、光滑、不沾灰尘，绿色环保的优点，能够在酒店卫生间渗水时进行及时快速维修，有广阔的市场和极大的经济效益。
Description
技术领域
本发明涉及建筑防水技术领域，具体涉及一种酒店卫生间用防水胶及渗水及时维修施工方法。
背景技术
建筑防水工程包括地上建筑防水与地下建筑防水工程。地上建筑防水通常做防水屋面，分为刚性和柔性两类防水屋面，过去许多建筑物采用刚性防水屋面，容易出现防水失效，原因主要有：温度变化引起热胀冷缩、屋面板受力引起的变形开裂、地基沉降或墙体承重引起的屋面变形及屋面板质量问题导致渗水或漏水。柔性防水屋面主要采用卷材，防水效果由防水设计、防水卷材质量和施工质量决定。通常是在屋面铺上沥青卷材，采用热熔法施工固化，会产生废气和沥青烟气，污染环境。作为绿色环保、低碳的种植屋面和光伏屋面受到成本等原因还未能在全国大范围推广。
防水技术是伴随建筑的发展而发展起来的，卫生间的防水技术也要跟随防水技术的脚步，为建筑业的发展奠定良好的基础。然而在现代防水工程中，尽管施工组织技术和建材品质以及施工设备的水平都已经在享誉国际，但仍存在这许多不足卫生间渗漏就仍是现代建设中一种常见且影响巨大的品质通病，甚至有的房屋刚建成两三年就出现卫生间渗漏现象。
卫生间是生活中用水最多的空间，最容易出现渗漏的情况。虽然当前的建筑施工标准在不断提高，但卫生间漏水仍然是建筑工程中存在的质量通病，也是多年来一直未能很好解决的难题，它影响了建筑物的正常使用，并进一步缩短建筑物的使用寿命。
主流的建筑防水材料有刚性防水堵漏材料、涂料、卷材、密封材料几大类。沥青类卷材由于污染环境和自身性能差，沥青油毡使用量大大降低至禁止生产和使用。
防水胶则具有较好的抗裂性，成膜致密程度高，隔水效果好，且温度适应性好，易于施工及维护，水性防水胶更具备环保优势，是未来防水胶发展的主要方向。刚性堵漏材料以水泥、砂石等为原材料，加入部分助剂配制成的水泥砂浆混凝土类防水材料，具有强度高、耐磨，抗渗透和寿命长等优点，但抗裂性能差。
尽管我国的防水水平已经得到长足的发展，但是在施工工艺、维修工艺上避免不了的有渗漏的现象。因此，研究卫生间渗漏原因，采用合适的防水材料、采取科学合理的技术措施及性价比最优的方案进行预防及及时快速维修就显得十分必要。
发明内容
本发明主要解决的技术问题是提供一种酒店卫生间用防水胶及渗水及时维修施工方法，能及时快速解决卫生间的渗水、漏水等问题。
本发明的技术方案如下：
一种酒店卫生间用防水胶，包括下述原料制备而成：聚氨酯改性丙烯酸乳液、醇酯十二、纳米二氧化钛、乙二醇、消泡剂、流平剂、增稠剂。
优选地，所述酒店卫生间用防水胶，包括下述原料制备而成：聚氨酯改性丙烯酸乳液、醇酯十二、功能化纳米二氧化钛、乙二醇、消泡剂、流平剂、增稠剂。
成膜助剂又称聚结助剂。能促进高分子化合物塑性流动和弹性变形，改善聚结性能，能在较广泛施工温度范围内成膜的物质。是一种易消失的增塑剂。常用的为醚醇类高聚物的强溶剂，如丙二醇丁醚、丙二醇甲醚醋酸酯等。以前常用的乙二醇丁醚由于对人体有生殖毒性，现在已被大多数国家禁用。醇酯十二成膜助剂的水解稳定性非常好，可以与包括pH很高的乳液在内的各类乳液一起使用。
进一步优选地，所述酒店卫生间用防水胶，由下述重量份的原料制备而成：聚氨酯改性丙烯酸乳液90-110份、醇酯十二3-7份、功能化纳米二氧化钛3-7份、乙二醇0.5-1.5份、消泡剂0.1-0.3份、流平剂0.5-1.5份、增稠剂1-4份。
所述消泡剂为磷酸三丁酯或二甲基硅油。
所述聚氨酯改性丙烯酸乳液的制备方法为：(1)将水95-105重量份、十二烷基硫酸钠5-6重量份、壬基酚聚氧乙烯醚2-3重量份、苯乙烯25-35重量份，甲基丙烯酸甲酯140-160重量份，丙烯酸丁酯16-20重量份，丙烯酸1-3重量份以转速为100-500r/min搅拌10-30min，得到预乳液；将水290-310重量份加入反应釜，升温到75-85℃，加入预乳液总重量9-11％的预乳液，引发剂过硫酸铵0.4-0.6重量份，以转速为100-300r/min搅拌反应30-40min，再加入引发剂过硫酸铵1.5-2.5重量份，并在转速为100-300r/min搅拌下滴加剩余的预乳液，剩余的预乳液滴加时间2.5-3.5小时，滴加完毕保温25-35min，得到预反应液；将丙烯酸丁酯140-160重量份，甲基丙烯酸甲酯50-60重量份，丙烯酸羟乙酯45-55重量份，丙烯酸4-6重量份混合均匀，得到第二步混合单体，将引发剂过硫酸铵0.5-1.5重量份加入预反应液中，并在转速为100-300r/min搅拌下滴加第二步混合单体，第二步混合单体滴加时间50-70min，滴加完保温反应50-70min，降温到40-50℃，用三乙醇胺调节pH至7.5-9，得到羟基丙烯酸酯乳液；(2)将聚醚多元醇45-55重量份加热至95-115℃并减压至0.005-0.015MPa抽真空1-2h，降温至80-90℃，加入异佛尔酮二异氰酸酯15-25重量份、六亚甲基二异氰酸酯25-35重量份、石墨烯0.5-1重量份、扩链剂5-12重量份、二月桂酸二丁基锡0.1-0.2重量份，保持温度为80-90℃以转速为100-300r/min搅拌反应1-3h，降温到30-40℃，加入丙酮5-10重量份降粘，再加入三乙醇胺1-5重量份，以转速为100-300r/min搅拌20-40min，得到聚氨酯预聚体；(3)将羟基丙烯酸酯乳液、聚氨酯预聚体、水按质量比为1：(0.5-0.8)：(1-1.5)混合，以转速为100-300r/min搅拌50-70min，然后加热至55-65℃并减压至0.005-0.015MPa抽真空1-2h，得到聚氨酯改性丙烯酸乳液。
所述聚醚多元醇为聚醚DL-3000D。
所述扩链剂为1,6-己二醇、1,2-癸二醇中的至少一种。优选地，所述扩链剂由1,6-己二醇、1,2-癸二醇按质量比为1：(0.2-0.3)组成。
所述增稠剂为聚丙烯酸钠。
所述流平剂为聚醚改性硅氧烷流平剂。
纳米二氧化钛是白色疏松粉末，屏蔽紫外线作用强，有良好的分散性和耐候性。可用于化妆品、功能纤维、塑料、涂料、油漆等领域，作为紫外线屏蔽剂，防止紫外线的侵害。也可用于高档汽车面漆，具有随角异色效应。所述功能化纳米二氧化钛的制备方法为：将纳米二氧化钛在质量分数3-7％的氨水中在温度为45-55℃浸渍10-20h，所述纳米二氧化钛、质量分数3-7％的氨水的质量比为1：(5-15)，离心分离，取沉淀用水洗涤1-4次，得到预处理纳米二氧化钛，将蓖麻油、十六烷基三甲基溴化铵、乙醇按质量比为1：(0.2-0.4)：(4-8)混合，再加入蓖麻油重量45-55％的预处理纳米二氧化钛，在温度为60-70℃以转速为500-900r/min搅拌2-3h，离心分离，在温度为90-100℃、绝对压强为0.01-0.02MPa真空干燥15-25h，得到功能化纳米二氧化钛。
上述酒店卫生间用防水胶，其制备方法为：将功能化纳米二氧化钛加入聚氨酯改性丙烯酸乳液中以转速为200-500r/min搅拌20-40min，然后依次加入醇酯十二、乙二醇、流平剂、增稠剂、消泡剂以转速为200-500r/min搅拌20-40min，即得。
本发明还提供了一种酒店卫生间渗水及时维修施工方法，在渗水时采用上述酒店卫生间用防水胶进行喷涂或涂刷。
本发明的有益效果是：
本发明酒店卫生间用防水胶，采用特制的聚合物乳液，并添加纳米二氧化钛进一步增强了其粘结性能及防水性能，渗透进入混凝土结构的孔隙和缝隙中，防水性能优异，具有易于施工、涂膜表面平整、光滑、不沾灰尘，绿色环保的优点，能够在酒店卫生间渗水时进行及时快速维修，有广阔的市场和极大的经济效益。
具体实施方式
为了进一步说明本发明，下面通过以下实施例进行详细说明。
使用原料介绍如下：十二烷基硫酸钠，CAS号：151-21-3。壬基酚聚氧乙烯醚是山东豪耀新材料有限公司提供的型号为TX-10的壬基酚聚氧乙烯醚。苯乙烯，CAS号：100-42-5。甲基丙烯酸甲酯，CAS号：80-62-6。丙烯酸丁酯，CAS号：141-32-2。丙烯酸，CAS号：79-10-7。过硫酸铵，CAS号：7727-54-0。丙烯酸羟乙酯，CAS号：818-61-1。三乙醇胺，CAS号：102-71-6。异佛尔酮二异氰酸酯，CAS号：4098-71-9。六亚甲基二异氰酸酯，CAS号：822-06-0。石墨烯是北京德科岛金科技有限公司提供的厚度为0.55～1.2nm、直径为0.5～3μm、层数为1-5层的氧化石墨烯。二月桂酸二丁基锡，CAS号：77-58-7。1,6-己二醇，CAS号：629-11-8。1,2-癸二醇，CAS号：1119-86-4。蓖麻油是文水县黄河油脂有限公司提供的精炼一级蓖麻油。十六烷基三甲基溴化铵，CAS号：57-09-0。醇酯十二，CAS号：25265-77-4。乙二醇，CAS号：107-21-1。聚醚改性硅氧烷流平剂是德国毕克、型号为BYK-349的流平剂。纳米二氧化钛是杭州吉康新材料有限公司提供的型号为SS-T30、一次粒径为30-50nm的纳米二氧化钛。聚丙烯酸钠是郑州千诺化工产品有限公司提供的工业级聚丙烯酸钠。磷酸三丁酯，CAS号：126-73-8。聚醚DL-3000D是山东蓝星东大化工有限责任公司提供的牌号为DL-3000D、羟值为36-39mgKOH/g的聚醚多元醇。
实施例1
酒店卫生间用防水胶，由下述重量份的原料制备而成：聚氨酯改性丙烯酸乳液100份、醇酯十二5份、纳米二氧化钛5份、乙二醇1份、消泡剂0.2份、流平剂0.9份、增稠剂2份。
所述消泡剂为磷酸三丁酯。
所述聚氨酯改性丙烯酸乳液的制备方法为：(1)将去离子水100重量份、十二烷基硫酸钠5.5重量份、壬基酚聚氧乙烯醚2.5重量份、苯乙烯30重量份，甲基丙烯酸甲酯150重量份，丙烯酸丁酯18重量份，丙烯酸2重量份以转速为300r/min搅拌20min，得到预乳液；将去离子水300重量份加入反应釜，升温到80℃，加入预乳液总重量10％的预乳液，引发剂过硫酸铵0.5重量份，以转速为150r/min搅拌反应35min，再加入引发剂过硫酸铵2重量份，并在转速为150r/min搅拌下滴加剩余的预乳液，剩余的预乳液滴加时间3小时，滴加完毕保温30min，得到预反应液；将丙烯酸丁酯150重量份，甲基丙烯酸甲酯55重量份，丙烯酸羟乙酯50重量份，丙烯酸5重量份混合均匀，得到第二步混合单体，将引发剂过硫酸铵1重量份加入预反应液中，并在转速为150r/min搅拌下滴加第二步混合单体，第二步混合单体滴加时间60min，滴加完保温反应60min，降温到45℃，用三乙醇胺调节pH至8，得到羟基丙烯酸酯乳液；(2)将聚醚多元醇50重量份加热至110℃并减压至0.01MPa抽真空1.5h，降温至85℃，加入异佛尔酮二异氰酸酯20重量份、六亚甲基二异氰酸酯30重量份、石墨烯0.8重量份、扩链剂8重量份、二月桂酸二丁基锡0.12重量份，保持温度为85℃以转速为150r/min搅拌反应2h，降温到35℃，加入丙酮8重量份降粘，再加入三乙醇胺1.5重量份，以转速为150r/min搅拌30min，得到聚氨酯预聚体；(3)将羟基丙烯酸酯乳液、聚氨酯预聚体、水按质量比为1：0.6：1.1混合，以转速为150r/min搅拌60min，然后加热至60℃并减压至0.01MPa抽真空1.5h，得到聚氨酯改性丙烯酸乳液。
所述聚醚多元醇为聚醚DL-3000D。
所述扩链剂为1,6-己二醇。
所述增稠剂为聚丙烯酸钠。
所述流平剂为聚醚改性硅氧烷流平剂。
上述酒店卫生间用防水胶，其制备方法为：将纳米二氧化钛加入聚氨酯改性丙烯酸乳液中以转速为300r/min搅拌30min，然后依次加入醇酯十二、乙二醇、流平剂、增稠剂、消泡剂以转速为300r/min搅拌25min，即得酒店卫生间用防水胶。
一种酒店卫生间渗水及时维修施工方法，在渗水时采用上述酒店卫生间用防水胶进行喷涂或涂刷。
实施例2
酒店卫生间用防水胶，由下述重量份的原料制备而成：聚氨酯改性丙烯酸乳液100份、醇酯十二5份、功能化纳米二氧化钛5份、乙二醇1份、消泡剂0.2份、流平剂0.9份、增稠剂2份。
所述消泡剂为磷酸三丁酯。
所述聚氨酯改性丙烯酸乳液的制备方法为：(1)将去离子水100重量份、十二烷基硫酸钠5.5重量份、壬基酚聚氧乙烯醚2.5重量份、苯乙烯30重量份，甲基丙烯酸甲酯150重量份，丙烯酸丁酯18重量份，丙烯酸2重量份以转速为300r/min搅拌20min，得到预乳液；将去离子水300重量份加入反应釜，升温到80℃，加入预乳液总重量10％的预乳液，引发剂过硫酸铵0.5重量份，以转速为150r/min搅拌反应35min，再加入引发剂过硫酸铵2重量份，并在转速为150r/min搅拌下滴加剩余的预乳液，剩余的预乳液滴加时间3小时，滴加完毕保温30min，得到预反应液；将丙烯酸丁酯150重量份，甲基丙烯酸甲酯55重量份，丙烯酸羟乙酯50重量份，丙烯酸5重量份混合均匀，得到第二步混合单体，将引发剂过硫酸铵1重量份加入预反应液中，并在转速为150r/min搅拌下滴加第二步混合单体，第二步混合单体滴加时间60min，滴加完保温反应60min，降温到45℃，用三乙醇胺调节pH至8，得到羟基丙烯酸酯乳液；(2)将聚醚多元醇50重量份加热至110℃并减压至0.01MPa抽真空1.5h，降温至85℃，加入异佛尔酮二异氰酸酯20重量份、六亚甲基二异氰酸酯30重量份、石墨烯0.8重量份、扩链剂8重量份、二月桂酸二丁基锡0.12重量份，保持温度为85℃以转速为150r/min搅拌反应2h，降温到35℃，加入丙酮8重量份降粘，再加入三乙醇胺1.5重量份，以转速为150r/min搅拌30min，得到聚氨酯预聚体；(3)将羟基丙烯酸酯乳液、聚氨酯预聚体、水按质量比为1：0.6：1.1混合，以转速为150r/min搅拌60min，然后加热至60℃并减压至0.01MPa抽真空1.5h，得到聚氨酯改性丙烯酸乳液。
所述聚醚多元醇为聚醚DL-3000D。
所述扩链剂为1,6-己二醇。
所述增稠剂为聚丙烯酸钠。
所述流平剂为聚醚改性硅氧烷流平剂。
所述功能化纳米二氧化钛的制备方法为：将纳米二氧化钛在质量分数5％的氨水中在温度为50℃浸渍15h，所述纳米二氧化钛、质量分数5％的氨水的质量比为1：10，以转速为6000r/min离心分离20min，弃上清液取沉淀用水洗涤3次，每次洗涤沉淀、水用量比为1：3，得到预处理纳米二氧化钛，将蓖麻油、十六烷基三甲基溴化铵、乙醇按质量比为1：0.3：5混合，再加入蓖麻油重量50％的预处理纳米二氧化钛，在温度为65℃以转速为600r/min搅拌2.5h，以转速为6000r/min离心分离20min，弃上清液取沉淀在温度为95℃、绝对压强为0.015MPa真空干燥20h，得到功能化纳米二氧化钛。
上述酒店卫生间用防水胶，其制备方法为：将功能化纳米二氧化钛加入聚氨酯改性丙烯酸乳液中以转速为300r/min搅拌30min，然后依次加入醇酯十二、乙二醇、流平剂、增稠剂、消泡剂以转速为300r/min搅拌25min，即得酒店卫生间用防水胶。
一种酒店卫生间渗水及时维修施工方法，在渗水时采用上述酒店卫生间用防水胶进行喷涂或涂刷。
对比例1
酒店卫生间用防水胶，由下述重量份的原料制备而成：羟基丙烯酸酯乳液100份、醇酯十二5份、功能化纳米二氧化钛5份、乙二醇1份、消泡剂0.2份、流平剂0.9份、增稠剂2份。
所述消泡剂为磷酸三丁酯。
所述羟基丙烯酸酯乳液的制备方法为：(1)将去离子水100重量份、十二烷基硫酸钠5.5重量份、壬基酚聚氧乙烯醚2.5重量份、苯乙烯30重量份，甲基丙烯酸甲酯150重量份，丙烯酸丁酯18重量份，丙烯酸2重量份以转速为300r/min搅拌20min，得到预乳液；将去离子水300重量份加入反应釜，升温到80℃，加入预乳液总重量10％的预乳液，引发剂过硫酸铵0.5重量份，以转速为150r/min搅拌反应35min，再加入引发剂过硫酸铵2重量份，并在转速为150r/min搅拌下滴加剩余的预乳液，剩余的预乳液滴加时间3小时，滴加完毕保温30min，得到预反应液；将丙烯酸丁酯150重量份，甲基丙烯酸甲酯55重量份，丙烯酸羟乙酯50重量份，丙烯酸5重量份混合均匀，得到第二步混合单体，将引发剂过硫酸铵1重量份加入预反应液中，并在转速为150r/min搅拌下滴加第二步混合单体，第二步混合单体滴加时间60min，滴加完保温反应60min，降温到45℃，用三乙醇胺调节pH至8，得到羟基丙烯酸酯乳液。
所述聚醚多元醇为聚醚DL-3000D。
所述扩链剂为1,6-己二醇。
所述增稠剂为聚丙烯酸钠。
所述流平剂为聚醚改性硅氧烷流平剂。
所述功能化纳米二氧化钛的制备方法为：将纳米二氧化钛在质量分数5％的氨水中在温度为50℃浸渍15h，所述纳米二氧化钛、质量分数5％的氨水的质量比为1：10，以转速为6000r/min离心分离20min，弃上清液取沉淀用水洗涤3次，每次洗涤沉淀、水用量比为1：3，得到预处理纳米二氧化钛，将蓖麻油、十六烷基三甲基溴化铵、乙醇按质量比为1：0.3：5混合，再加入蓖麻油重量50％的预处理纳米二氧化钛，在温度为65℃以转速为600r/min搅拌2.5h，以转速为6000r/min离心分离20min，弃上清液取沉淀在温度为95℃、绝对压强为0.015MPa真空干燥20h，得到功能化纳米二氧化钛。
上述酒店卫生间用防水胶，其制备方法为：将功能化纳米二氧化钛加入羟基丙烯酸酯乳液中以转速为300r/min搅拌30min，然后依次加入醇酯十二、乙二醇、流平剂、增稠剂、消泡剂以转速为300r/min搅拌25min，即得酒店卫生间用防水胶。
一种酒店卫生间渗水及时维修施工方法，在渗水时采用上述酒店卫生间用防水胶进行喷涂或涂刷。
实施例3
酒店卫生间用防水胶，由下述重量份的原料制备而成：聚氨酯改性丙烯酸乳液100份、醇酯十二5份、功能化纳米二氧化钛5份、乙二醇1份、消泡剂0.2份、流平剂0.9份、增稠剂2份。
所述消泡剂为磷酸三丁酯。
所述聚氨酯改性丙烯酸乳液的制备方法为：(1)将去离子水100重量份、十二烷基硫酸钠5.5重量份、壬基酚聚氧乙烯醚2.5重量份、苯乙烯30重量份，甲基丙烯酸甲酯150重量份，丙烯酸丁酯18重量份，丙烯酸2重量份以转速为300r/min搅拌20min，得到预乳液；将去离子水300重量份加入反应釜，升温到80℃，加入预乳液总重量10％的预乳液，引发剂过硫酸铵0.5重量份，以转速为150r/min搅拌反应35min，再加入引发剂过硫酸铵2重量份，并在转速为150r/min搅拌下滴加剩余的预乳液，剩余的预乳液滴加时间3小时，滴加完毕保温30min，得到预反应液；将丙烯酸丁酯150重量份，甲基丙烯酸甲酯55重量份，丙烯酸羟乙酯50重量份，丙烯酸5重量份混合均匀，得到第二步混合单体，将引发剂过硫酸铵1重量份加入预反应液中，并在转速为150r/min搅拌下滴加第二步混合单体，第二步混合单体滴加时间60min，滴加完保温反应60min，降温到45℃，用三乙醇胺调节pH至8，得到羟基丙烯酸酯乳液；(2)将聚醚多元醇50重量份加热至110℃并减压至0.01MPa抽真空1.5h，降温至85℃，加入六亚甲基二异氰酸酯50重量份、扩链剂8重量份、二月桂酸二丁基锡0.12重量份，保持温度为85℃以转速为150r/min搅拌反应2h，降温到35℃，加入丙酮8重量份降粘，再加入三乙醇胺1.5重量份，以转速为150r/min搅拌30min，得到聚氨酯预聚体；(3)将羟基丙烯酸酯乳液、聚氨酯预聚体、水按质量比为1：0.6：1.1混合，以转速为150r/min搅拌60min，然后加热至60℃并减压至0.01MPa抽真空1.5h，得到聚氨酯改性丙烯酸乳液。
所述聚醚多元醇为聚醚DL-3000D。
所述扩链剂为1,6-己二醇。
所述增稠剂为聚丙烯酸钠。
所述流平剂为聚醚改性硅氧烷流平剂。
所述功能化纳米二氧化钛的制备方法为：将纳米二氧化钛在质量分数5％的氨水中在温度为50℃浸渍15h，所述纳米二氧化钛、质量分数5％的氨水的质量比为1：10，以转速为6000r/min离心分离20min，弃上清液取沉淀用水洗涤3次，每次洗涤沉淀、水用量比为1：3，得到预处理纳米二氧化钛，将蓖麻油、十六烷基三甲基溴化铵、乙醇按质量比为1：0.3：5混合，再加入蓖麻油重量50％的预处理纳米二氧化钛，在温度为65℃以转速为600r/min搅拌2.5h，以转速为6000r/min离心分离20min，弃上清液取沉淀在温度为95℃、绝对压强为0.015MPa真空干燥20h，得到功能化纳米二氧化钛。
上述酒店卫生间用防水胶，其制备方法为：将功能化纳米二氧化钛加入聚氨酯改性丙烯酸乳液中以转速为300r/min搅拌30min，然后依次加入醇酯十二、乙二醇、流平剂、增稠剂、消泡剂以转速为300r/min搅拌25min，即得酒店卫生间用防水胶。
一种酒店卫生间渗水及时维修施工方法，在渗水时采用上述酒店卫生间用防水胶进行喷涂或涂刷。
实施例4
酒店卫生间用防水胶，由下述重量份的原料制备而成：聚氨酯改性丙烯酸乳液100份、醇酯十二5份、功能化纳米二氧化钛5份、乙二醇1份、消泡剂0.2份、流平剂0.9份、增稠剂2份。
所述消泡剂为磷酸三丁酯。
所述聚氨酯改性丙烯酸乳液的制备方法为：(1)将去离子水100重量份、十二烷基硫酸钠5.5重量份、壬基酚聚氧乙烯醚2.5重量份、苯乙烯30重量份，甲基丙烯酸甲酯150重量份，丙烯酸丁酯18重量份，丙烯酸2重量份以转速为300r/min搅拌20min，得到预乳液；将去离子水300重量份加入反应釜，升温到80℃，加入预乳液总重量10％的预乳液，引发剂过硫酸铵0.5重量份，以转速为150r/min搅拌反应35min，再加入引发剂过硫酸铵2重量份，并在转速为150r/min搅拌下滴加剩余的预乳液，剩余的预乳液滴加时间3小时，滴加完毕保温30min，得到预反应液；将丙烯酸丁酯150重量份，甲基丙烯酸甲酯55重量份，丙烯酸羟乙酯50重量份，丙烯酸5重量份混合均匀，得到第二步混合单体，将引发剂过硫酸铵1重量份加入预反应液中，并在转速为150r/min搅拌下滴加第二步混合单体，第二步混合单体滴加时间60min，滴加完保温反应60min，降温到45℃，用三乙醇胺调节pH至8，得到羟基丙烯酸酯乳液；(2)将聚醚多元醇50重量份加热至110℃并减压至0.01MPa抽真空1.5h，降温至85℃，加入异佛尔酮二异氰酸酯20重量份、六亚甲基二异氰酸酯30重量份、石墨烯0.8重量份、扩链剂8重量份、二月桂酸二丁基锡0.12重量份，保持温度为85℃以转速为150r/min搅拌反应2h，降温到35℃，加入丙酮8重量份降粘，再加入三乙醇胺1.5重量份，以转速为150r/min搅拌30min，得到聚氨酯预聚体；(3)将羟基丙烯酸酯乳液、聚氨酯预聚体、水按质量比为1：0.6：1.1混合，以转速为150r/min搅拌60min，然后加热至60℃并减压至0.01MPa抽真空1.5h，得到聚氨酯改性丙烯酸乳液。
所述聚醚多元醇为聚醚DL-3000D。
所述扩链剂为1,2-癸二醇。
所述增稠剂为聚丙烯酸钠。
所述流平剂为聚醚改性硅氧烷流平剂。
所述功能化纳米二氧化钛的制备方法为：将纳米二氧化钛在质量分数5％的氨水中在温度为50℃浸渍15h，所述纳米二氧化钛、质量分数5％的氨水的质量比为1：10，以转速为6000r/min离心分离20min，弃上清液取沉淀用水洗涤3次，每次洗涤沉淀、水用量比为1：3，得到预处理纳米二氧化钛，将蓖麻油、十六烷基三甲基溴化铵、乙醇按质量比为1：0.3：5混合，再加入蓖麻油重量50％的预处理纳米二氧化钛，在温度为65℃以转速为600r/min搅拌2.5h，以转速为6000r/min离心分离20min，弃上清液取沉淀在温度为95℃、绝对压强为0.015MPa真空干燥20h，得到功能化纳米二氧化钛。
上述酒店卫生间用防水胶，其制备方法为：将功能化纳米二氧化钛加入聚氨酯改性丙烯酸乳液中以转速为300r/min搅拌30min，然后依次加入醇酯十二、乙二醇、流平剂、增稠剂、消泡剂以转速为300r/min搅拌25min，即得酒店卫生间用防水胶。
一种酒店卫生间渗水及时维修施工方法，在渗水时采用上述酒店卫生间用防水胶进行喷涂或涂刷。
实施例5
酒店卫生间用防水胶，由下述重量份的原料制备而成：聚氨酯改性丙烯酸乳液100份、醇酯十二5份、功能化纳米二氧化钛5份、乙二醇1份、消泡剂0.2份、流平剂0.9份、增稠剂2份。
所述消泡剂为磷酸三丁酯。
所述聚氨酯改性丙烯酸乳液的制备方法为：(1)将去离子水100重量份、十二烷基硫酸钠5.5重量份、壬基酚聚氧乙烯醚2.5重量份、苯乙烯30重量份，甲基丙烯酸甲酯150重量份，丙烯酸丁酯18重量份，丙烯酸2重量份以转速为300r/min搅拌20min，得到预乳液；将去离子水300重量份加入反应釜，升温到80℃，加入预乳液总重量10％的预乳液，引发剂过硫酸铵0.5重量份，以转速为150r/min搅拌反应35min，再加入引发剂过硫酸铵2重量份，并在转速为150r/min搅拌下滴加剩余的预乳液，剩余的预乳液滴加时间3小时，滴加完毕保温30min，得到预反应液；将丙烯酸丁酯150重量份，甲基丙烯酸甲酯55重量份，丙烯酸羟乙酯50重量份，丙烯酸5重量份混合均匀，得到第二步混合单体，将引发剂过硫酸铵1重量份加入预反应液中，并在转速为150r/min搅拌下滴加第二步混合单体，第二步混合单体滴加时间60min，滴加完保温反应60min，降温到45℃，用三乙醇胺调节pH至8，得到羟基丙烯酸酯乳液；(2)将聚醚多元醇50重量份加热至110℃并减压至0.01MPa抽真空1.5h，降温至85℃，加入异佛尔酮二异氰酸酯20重量份、六亚甲基二异氰酸酯30重量份、石墨烯0.8重量份、1,6-己二醇1.6重量份、1,2-癸二醇6.4重量份、二月桂酸二丁基锡0.12重量份，保持温度为85℃以转速为150r/min搅拌反应2h，降温到35℃，加入丙酮8重量份降粘，再加入三乙醇胺1.5重量份，以转速为150r/min搅拌30min，得到聚氨酯预聚体；(3)将羟基丙烯酸酯乳液、聚氨酯预聚体、水按质量比为1：0.6：1.1混合，以转速为150r/min搅拌60min，然后加热至60℃并减压至0.01MPa抽真空1.5h，得到聚氨酯改性丙烯酸乳液。
所述聚醚多元醇为聚醚DL-3000D。
所述增稠剂为聚丙烯酸钠。
所述流平剂为聚醚改性硅氧烷流平剂。
所述功能化纳米二氧化钛的制备方法为：将纳米二氧化钛在质量分数5％的氨水中在温度为50℃浸渍15h，所述纳米二氧化钛、质量分数5％的氨水的质量比为1：10，以转速为6000r/min离心分离20min，弃上清液取沉淀用水洗涤3次，每次洗涤沉淀、水用量比为1：3，得到预处理纳米二氧化钛，将蓖麻油、十六烷基三甲基溴化铵、乙醇按质量比为1：0.3：5混合，再加入蓖麻油重量50％的预处理纳米二氧化钛，在温度为65℃以转速为600r/min搅拌2.5h，以转速为6000r/min离心分离20min，弃上清液取沉淀在温度为95℃、绝对压强为0.015MPa真空干燥20h，得到功能化纳米二氧化钛。
上述酒店卫生间用防水胶，其制备方法为：将功能化纳米二氧化钛加入聚氨酯改性丙烯酸乳液中以转速为300r/min搅拌30min，然后依次加入醇酯十二、乙二醇、流平剂、增稠剂、消泡剂以转速为300r/min搅拌25min，即得酒店卫生间用防水胶。
一种酒店卫生间渗水及时维修施工方法，在渗水时采用上述酒店卫生间用防水胶进行喷涂或涂刷。
测试例1
将实施例的酒店卫生间用防水胶按GB/T16777-2008《建筑防水涂料试验方法》进行性能测试。具体结果见表1。
表1：测试结果表
以上所揭露的仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到变化或变型，都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种酒店卫生间用防水胶，其特征在于，包括下述原料制备而成：聚氨酯改性丙烯酸乳液、醇酯十二、纳米二氧化钛、乙二醇、消泡剂、流平剂、增稠剂。
2.一种酒店卫生间用防水胶，其特征在于，包括下述原料制备而成：聚氨酯改性丙烯酸乳液、醇酯十二、功能化纳米二氧化钛、乙二醇、消泡剂、流平剂、增稠剂。
3.一种酒店卫生间用防水胶，其特征在于，所述酒店卫生间用防水胶，由下述重量份的原料制备而成：聚氨酯改性丙烯酸乳液90-110份、醇酯十二3-7份、功能化纳米二氧化钛3-7份、乙二醇0.5-1.5份、消泡剂0.1-0.3份、流平剂0.5-1.5份、增稠剂1-4份。
4.如权利要求3所述酒店卫生间用防水胶，其特征在于，所述消泡剂为磷酸三丁酯或二甲基硅油。
5.如权利要求3所述酒店卫生间用防水胶，其特征在于，所述聚氨酯改性丙烯酸乳液的制备方法为：(1)将水95-105重量份、十二烷基硫酸钠5-6重量份、壬基酚聚氧乙烯醚2-3重量份、苯乙烯25-35重量份，甲基丙烯酸甲酯140-160重量份，丙烯酸丁酯16-20重量份，丙烯酸1-3重量份以转速为100-500r/min搅拌10-30min，得到预乳液；将水290-310重量份加入反应釜，升温到75-85℃，加入预乳液总重量9-11％的预乳液，引发剂过硫酸铵0.4-0.6重量份，以转速为100-300r/min搅拌反应30-40min，再加入引发剂过硫酸铵1.5-2.5重量份，并在转速为100-300r/min搅拌下滴加剩余的预乳液，剩余的预乳液滴加时间2.5-3.5小时，滴加完毕保温25-35min，得到预反应液；将丙烯酸丁酯140-160重量份，甲基丙烯酸甲酯50-60重量份，丙烯酸羟乙酯45-55重量份，丙烯酸4-6重量份混合均匀，得到第二步混合单体，将引发剂过硫酸铵0.5-1.5重量份加入预反应液中，并在转速为100-300r/min搅拌下滴加第二步混合单体，第二步混合单体滴加时间50-70min，滴加完保温反应50-70min，降温到40-50℃，用三乙醇胺调节pH至7.5-9，得到羟基丙烯酸酯乳液；(2)将聚醚多元醇45-55重量份加热至95-115℃并减压至0.005-0.015MPa抽真空1-2h，降温至80-90℃，加入异佛尔酮二异氰酸酯15-25重量份、六亚甲基二异氰酸酯25-35重量份、石墨烯0.5-1重量份、扩链剂5-12重量份、二月桂酸二丁基锡0.1-0.2重量份，保持温度为80-90℃以转速为100-300r/min搅拌反应1-3h，降温到30-40℃，加入丙酮5-10重量份降粘，再加入三乙醇胺1-5重量份，以转速为100-300r/min搅拌20-40min，得到聚氨酯预聚体；(3)将羟基丙烯酸酯乳液、聚氨酯预聚体、水按质量比为1：(0.5-0.8)：(1-1.5)混合，以转速为100-300r/min搅拌50-70min，然后加热至55-65℃并减压至0.005-0.015MPa抽真空1-2h，得到聚氨酯改性丙烯酸乳液。
6.如权利要求5所述酒店卫生间用防水胶，其特征在于，所述聚醚多元醇为聚醚DL-3000D；所述扩链剂为1,6-己二醇、1,2-癸二醇中的至少一种。
7.如权利要求3所述酒店卫生间用防水胶，其特征在于，所述增稠剂为聚丙烯酸钠。
8.如权利要求3所述酒店卫生间用防水胶，其特征在于，所述流平剂为聚醚改性硅氧烷流平剂。
9.如权利要求3所述酒店卫生间用防水胶，其特征在于，所述功能化纳米二氧化钛的制备方法为：将纳米二氧化钛在质量分数3-7％的氨水中在温度为45-55℃浸渍10-20h，所述纳米二氧化钛、质量分数3-7％的氨水的质量比为1：(5-15)，离心分离，取沉淀用水洗涤1-4次，得到预处理纳米二氧化钛，将蓖麻油、十六烷基三甲基溴化铵、乙醇按质量比为1：(0.2-0.4)：(4-8)混合，再加入蓖麻油重量45-55％的预处理纳米二氧化钛，在温度为60-70℃以转速为500-900r/min搅拌2-3h，离心分离，在温度为90-100℃、绝对压强为0.01-0.02MPa真空干燥15-25h，得到功能化纳米二氧化钛。
10.一种酒店卫生间渗水及时维修施工方法，在渗水时采用权利要求1-9中任一项所述酒店卫生间用防水胶进行喷涂或涂刷。