CN110354105A - 一种用于治疗风湿病的膏药贴 - Google Patents
一种用于治疗风湿病的膏药贴 Download PDFInfo
- Publication number
- CN110354105A CN110354105A CN201910771784.0A CN201910771784A CN110354105A CN 110354105 A CN110354105 A CN 110354105A CN 201910771784 A CN201910771784 A CN 201910771784A CN 110354105 A CN110354105 A CN 110354105A
- Authority
- CN
- China
- Prior art keywords
- fibre
- plaster
- fiber
- patch
- flax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的一种用于治疗风湿病的膏药贴，属于医疗用品技术领域，包括膏药贴布、连接层和膏药药物层，所述膏药药物层、连接层和膏药贴布沿右上至下的方向依次设置，膏药药物层通过连接层的作用附着于膏药贴布上，膏药替补采用大麻纤维、罗布麻纤维、黄麻纤维、洋麻纤维、亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维，加入的剑麻纤维能显著的增加本发明中膏药贴布的透气性能，解决了以往普通膏药贴由于不透气容易造成皮肤溃烂的现象。
Description
技术领域
本发明属于医疗用品技术领域，尤其涉及一种用于治疗风湿病的膏药贴。
背景技术
众所周知，风湿病是一种侵犯关节、骨骼、肌肉、血管及有关软组织或结缔组织为主的疾病，其中多数为自身免疫性疾病，发病多较隐蔽而缓慢，病程较长，且大多具有遗传倾向，而且风湿病较为顽固，一些患上风湿病的患者大都采用往患处粘贴膏药的方式进行治疗、缓解风湿病的痛苦，但现有膏药贴的贴纸透气性极差，容易造成使用者皮肤溃烂。
发明内容
针对背景中的问题，本发明的目的在于提供一种用于治疗风湿病的膏药贴。
为实现上述目的，本发明提供了一种用于治疗风湿病的膏药贴，包括膏药贴布、连接层和膏药药物层，所述膏药药物层、连接层和膏药贴布沿右上至下的方向依次设置。
一种应用于权利要求1所述的一种用于治疗风湿病的膏药贴的膏药贴布，包括第一贴布层和第二层贴布层，所述第一贴布层的原材料包括亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维，所述第二贴布层的原材料包括大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维。
做为优选的，所述第一贴布层以及第二贴布层中原材料的质量百分比为：
第一贴布层中亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维的质量百分比为：亚麻纤维为14％-25％，胡麻纤维为28％-46％，剑麻纤维为14％-35％，蕉麻纤维为10％-27％，第二贴布层中大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维的质量百分比为：大麻纤维为23％-30％，罗布麻纤维为17％-35％，黄麻纤维为25％-55％，洋麻纤维为12％-24％。
做为优选的，所述第一贴布层以及第二贴布层中原材料的质量百分比为：
第一贴布层中亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维的质量百分比为：亚麻纤维为17％-20％，胡麻纤维为30％-42％，剑麻纤维为17％-30％，蕉麻纤维为12％-25％，第二贴布层中大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维的质量百分比为：大麻纤维为24％-29％，罗布麻纤维为20％-30％，黄麻纤维为30％-50％，洋麻纤维为15％-20％。
根据权利要求2所述的一种膏药贴布，包括以下步骤：
A：按照质量百分比将亚麻纤维与胡麻纤维送入开松机进行开松处理，并清除杂物；
B：向亚麻纤维和胡麻纤维的混合物中加入2，4-二氟苯甲酸溶液，室温下浸泡13分钟；
C：亚麻纤维和胡麻纤维送入甩干机，以每分钟30转的速度甩干15分钟后放入氢氧化钠溶液中，浸泡8分钟后取出，室温下进行干燥处理；
D：将剑麻纤维与蕉麻纤维送入开松机进行开松处理，并清除杂物；
E：将步骤D中得到的剑麻纤维与蕉麻纤维的混合物浸入到吲哚-2-甲酸溶液中，用清水浸泡15小时，至中性以后在150℃的环境下烘干，得到改性的剑麻纤维与蕉麻纤维；
F：将大麻纤维和罗布麻纤维送入开松机进行开松处理，并清除杂物；
G：向步骤F中得到的大麻纤维与罗布麻纤维混合物中加入醚化剂2，3-环氧丙基三甲基氯化铵溶液，在68℃温度下搅拌3小时，然后浸泡反应15个小时；
H：向步骤G中得到的大麻纤维与罗布麻纤维混合物中加入清水洗净，待至中性后再150℃环境下烘干，得到改性的大麻纤维和罗布麻纤维；
I：将黄麻纤维与洋麻纤维送入开松机进行开松处理，并清除杂物；
J：向步骤I中的黄麻纤维与洋麻纤维混合物中添加过冷水，在0℃的环境下浸泡13个小时；
K：向步骤J中的黄麻纤维与洋麻纤维混合物中加入γ-氨基丁酸水溶液，并加热至沸腾，加热40分钟后并洗净，室温环境下进行干燥处理；
L：将亚麻纤维和剑麻纤维混纺编制成第一贴布层的经线，将胡麻纤维和蕉麻纤维混纺编制成第一贴布层的纬线，将大麻纤维和黄麻纤维混纺编制成第二贴布层的经线，将罗布麻纤维和洋麻纤维混纺编制成第二贴布层的纬线，得到成品。
优选的，所述膏药药物层的厚度为1.5-3毫米。
与现有技术相比，本发明的有益效果有：本发明的一种用于治疗风湿病的膏药贴包括膏药贴布、连接层和膏药药物层，所述膏药药物层、连接层和膏药贴布沿右上至下的方向依次设置，膏药药物层通过连接层的作用附着于膏药贴布上，膏药替补采用大麻纤维、罗布麻纤维、黄麻纤维、洋麻纤维、亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维，加入的剑麻纤维能显著的增加本发明中膏药贴布的透气性能，解决了以往普通膏药贴由于不透气容易造成皮肤溃烂的现象。
附图说明
图1是本发明的结构示意图。
附图中标记：1、膏药贴布；2、连接层；3、膏药药物层。
具体实施方式
为了使本发明的技术方案更加明白，结合以下实例对本发明进行进一步的详细说明，应当理解，此处所描述的具体实施例仅仅用以解释发明，并不用于限定本发明。
实施例1
一种用于治疗风湿病的膏药贴，包括膏药贴布1、连接层2和膏药药物层3，所述膏药药物层3、连接层2和膏药贴布1沿右上至下的方向依次设置。
一种用于治疗风湿病的膏药贴的膏药贴布，包括第一贴布层和第二层贴布层，所述第一贴布层的原材料包括亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维，所述第二贴布层的原材料包括大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维。
第一贴布层以及第二贴布层中原材料的质量百分比为：
第一贴布层中亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维的质量百分比为：亚麻纤维为18％，胡麻纤维为39％，剑麻纤维为25％，蕉麻纤维为18％，第二贴布层中大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维的质量百分比为：大麻纤维为24％，罗布麻纤维为20％，黄麻纤维为40％，洋麻纤维为16％。
一种膏药贴布，包括以下步骤：
A：按照质量百分比将亚麻纤维与胡麻纤维送入开松机进行开松处理，并清除杂物；
B：向亚麻纤维和胡麻纤维的混合物中加入2，4-二氟苯甲酸溶液，室温下浸泡13分钟；
C：亚麻纤维和胡麻纤维送入甩干机，以每分钟30转的速度甩干15分钟后放入氢氧化钠溶液中，浸泡8分钟后取出，室温下进行干燥处理；
D：将剑麻纤维与蕉麻纤维送入开松机进行开松处理，并清除杂物；
E：将步骤D中得到的剑麻纤维与蕉麻纤维的混合物浸入到吲哚-2-甲酸溶液中，用清水浸泡15小时，至中性以后在150℃的环境下烘干，得到改性的剑麻纤维与蕉麻纤维；
F：将大麻纤维和罗布麻纤维送入开松机进行开松处理，并清除杂物；
G：向步骤F中得到的大麻纤维与罗布麻纤维混合物中加入醚化剂2，3-环氧丙基三甲基氯化铵溶液，在68℃温度下搅拌3小时，然后浸泡反应15个小时；
H：向步骤G中得到的大麻纤维与罗布麻纤维混合物中加入清水洗净，待至中性后再150℃环境下烘干，得到改性的大麻纤维和罗布麻纤维；
I：将黄麻纤维与洋麻纤维送入开松机进行开松处理，并清除杂物；
J：向步骤I中的黄麻纤维与洋麻纤维混合物中添加过冷水，在0℃的环境下浸泡13个小时；
K：向步骤J中的黄麻纤维与洋麻纤维混合物中加入γ-氨基丁酸水溶液，并加热至沸腾，加热40分钟后并洗净，室温环境下进行干燥处理；
L：将亚麻纤维和剑麻纤维混纺编制成第一贴布层的经线，将胡麻纤维和蕉麻纤维混纺编制成第一贴布层的纬线，将大麻纤维和黄麻纤维混纺编制成第二贴布层的经线，将罗布麻纤维和洋麻纤维混纺编制成第二贴布层的纬线，得到成品。
膏药药物层3的厚度为2毫米。
实施例2
一种用于治疗风湿病的膏药贴，包括膏药贴布1、连接层2和膏药药物层3，所述膏药药物层3、连接层2和膏药贴布1沿右上至下的方向依次设置。
一种用于治疗风湿病的膏药贴的膏药贴布，包括第一贴布层和第二层贴布层，所述第一贴布层的原材料包括亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维，所述第二贴布层的原材料包括大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维。
第一贴布层以及第二贴布层中原材料的质量百分比为：
第一贴布层中亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维的质量百分比为：亚麻纤维为19％，胡麻纤维为40％，剑麻纤维为26％，蕉麻纤维为15％，第二贴布层中大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维的质量百分比为：大麻纤维为25％，罗布麻纤维为21％，黄麻纤维为36％，洋麻纤维为18％。
一种膏药贴布，包括以下步骤：
A：按照质量百分比将亚麻纤维与胡麻纤维送入开松机进行开松处理，并清除杂物；
B：向亚麻纤维和胡麻纤维的混合物中加入2，4-二氟苯甲酸溶液，室温下浸泡13分钟；
C：亚麻纤维和胡麻纤维送入甩干机，以每分钟30转的速度甩干15分钟后放入氢氧化钠溶液中，浸泡8分钟后取出，室温下进行干燥处理；
D：将剑麻纤维与蕉麻纤维送入开松机进行开松处理，并清除杂物；
E：将步骤D中得到的剑麻纤维与蕉麻纤维的混合物浸入到吲哚-2-甲酸溶液中，用清水浸泡15小时，至中性以后在150℃的环境下烘干，得到改性的剑麻纤维与蕉麻纤维；
F：将大麻纤维和罗布麻纤维送入开松机进行开松处理，并清除杂物；
G：向步骤F中得到的大麻纤维与罗布麻纤维混合物中加入醚化剂2，3-环氧丙基三甲基氯化铵溶液，在68℃温度下搅拌3小时，然后浸泡反应15个小时；
H：向步骤G中得到的大麻纤维与罗布麻纤维混合物中加入清水洗净，待至中性后再150℃环境下烘干，得到改性的大麻纤维和罗布麻纤维；
I：将黄麻纤维与洋麻纤维送入开松机进行开松处理，并清除杂物；
J：向步骤I中的黄麻纤维与洋麻纤维混合物中添加过冷水，在0℃的环境下浸泡13个小时；
K：向步骤J中的黄麻纤维与洋麻纤维混合物中加入γ-氨基丁酸水溶液，并加热至沸腾，加热40分钟后并洗净，室温环境下进行干燥处理；
L：将亚麻纤维和剑麻纤维混纺编制成第一贴布层的经线，将胡麻纤维和蕉麻纤维混纺编制成第一贴布层的纬线，将大麻纤维和黄麻纤维混纺编制成第二贴布层的经线，将罗布麻纤维和洋麻纤维混纺编制成第二贴布层的纬线，得到成品。
膏药药物层3的厚度为2毫米。
实施例3
一种用于治疗风湿病的膏药贴，包括膏药贴布1、连接层2和膏药药物层3，所述膏药药物层3、连接层2和膏药贴布1沿右上至下的方向依次设置。
一种用于治疗风湿病的膏药贴的膏药贴布，包括第一贴布层和第二层贴布层，所述第一贴布层的原材料包括亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维，所述第二贴布层的原材料包括大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维。
第一贴布层以及第二贴布层中原材料的质量百分比为：
第一贴布层中亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维的质量百分比为：亚麻纤维为18.5％，胡麻纤维为35％，剑麻纤维为25％，蕉麻纤维为21.5％，第二贴布层中大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维的质量百分比为：大麻纤维为26％，罗布麻纤维为21.5％，黄麻纤维为33.5％，洋麻纤维为19％。
一种膏药贴布，包括以下步骤：
A：按照质量百分比将亚麻纤维与胡麻纤维送入开松机进行开松处理，并清除杂物；
B：向亚麻纤维和胡麻纤维的混合物中加入2，4-二氟苯甲酸溶液，室温下浸泡13分钟；
C：亚麻纤维和胡麻纤维送入甩干机，以每分钟30转的速度甩干15分钟后放入氢氧化钠溶液中，浸泡8分钟后取出，室温下进行干燥处理；
D：将剑麻纤维与蕉麻纤维送入开松机进行开松处理，并清除杂物；
E：将步骤D中得到的剑麻纤维与蕉麻纤维的混合物浸入到吲哚-2-甲酸溶液中，用清水浸泡15小时，至中性以后在150℃的环境下烘干，得到改性的剑麻纤维与蕉麻纤维；
F：将大麻纤维和罗布麻纤维送入开松机进行开松处理，并清除杂物；
G：向步骤F中得到的大麻纤维与罗布麻纤维混合物中加入醚化剂2，3-环氧丙基三甲基氯化铵溶液，在68℃温度下搅拌3小时，然后浸泡反应15个小时；
H：向步骤G中得到的大麻纤维与罗布麻纤维混合物中加入清水洗净，待至中性后再150℃环境下烘干，得到改性的大麻纤维和罗布麻纤维；
I：将黄麻纤维与洋麻纤维送入开松机进行开松处理，并清除杂物；
J：向步骤I中的黄麻纤维与洋麻纤维混合物中添加过冷水，在0℃的环境下浸泡13个小时；
K：向步骤J中的黄麻纤维与洋麻纤维混合物中加入γ-氨基丁酸水溶液，并加热至沸腾，加热40分钟后并洗净，室温环境下进行干燥处理；
L：将亚麻纤维和剑麻纤维混纺编制成第一贴布层的经线，将胡麻纤维和蕉麻纤维混纺编制成第一贴布层的纬线，将大麻纤维和黄麻纤维混纺编制成第二贴布层的经线，将罗布麻纤维和洋麻纤维混纺编制成第二贴布层的纬线，得到成品。
膏药药物层3的厚度为2毫米。
对比例
将对比例1中的剑麻纤维去除，其余配比和制备方法不变。
将实施例1-3中得到的膏药贴和对比例中得到的膏药贴各取500组应用到临床治疗中，并做病情回访，记录患者皮肤张贴膏药贴处的皮肤囊肿情况，所得数据如表1：
| 无囊肿(％) | 轻微囊肿(％) | 中度囊肿(％) | 严重囊肿(％) | |
| 实施例1 | 86 | 14 | ||
| 实施例2 | 87 | 13 | ||
| 实施例3 | 85 | 15 | ||
| 对比例 | 17 | 83 |
表1：患者皮肤囊肿对比数据
由以上数据可知，本发明的一种用于治疗风湿病的膏药贴具有良好的透气性，相比现有的膏药贴在透气性能上具有显著的优势，能有效防止患者皮肤由于膏药贴不透气引发的皮肤溃烂现象。
需要说明的是，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书及附图内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (6)
1.一种用于治疗风湿病的膏药贴，其特征在于，包括膏药贴布(1)、连接层(2)和膏药药物层(3)，所述膏药药物层(3)、连接层(2)和膏药贴布(1)沿右上至下的方向依次设置。
2.一种应用于权利要求1所述的一种用于治疗风湿病的膏药贴的膏药贴布，其特征在于，包括第一贴布层和第二层贴布层，所述第一贴布层的原材料包括亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维，所述第二贴布层的原材料包括大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维。
3.根据权利要求2所述的一种膏药贴布，其特征在于，所述第一贴布层以及第二贴布层中原材料的质量百分比为：
第一贴布层中亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维的质量百分比为：亚麻纤维为14％-25％，胡麻纤维为28％-46％，剑麻纤维为14％-35％，蕉麻纤维为10％-27％，第二贴布层中大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维的质量百分比为：大麻纤维为23％-30％，罗布麻纤维为17％-35％，黄麻纤维为25％-55％，洋麻纤维为12％-24％。
4.根据权利要求2所述的一种膏药贴布，其特征在于，所述第一贴布层以及第二贴布层中原材料的质量百分比为：
第一贴布层中亚麻纤维、胡麻纤维、剑麻纤维和蕉麻纤维的质量百分比为：亚麻纤维为17％-20％，胡麻纤维为30％-42％，剑麻纤维为17％-30％，蕉麻纤维为12％-25％，第二贴布层中大麻纤维、罗布麻纤维、黄麻纤维和洋麻纤维的质量百分比为：大麻纤维为24％-29％，罗布麻纤维为20％-30％，黄麻纤维为30％-50％，洋麻纤维为15％-20％。
5.根据权利要求2所述的一种膏药贴布，其特征在于，包括以下步骤：
A：按照质量百分比将亚麻纤维与胡麻纤维送入开松机进行开松处理，并清除杂物；
B：向亚麻纤维和胡麻纤维的混合物中加入2，4-二氟苯甲酸溶液，室温下浸泡13分钟；
C：亚麻纤维和胡麻纤维送入甩干机，以每分钟30转的速度甩干15分钟后放入氢氧化钠溶液中，浸泡8分钟后取出，室温下进行干燥处理；
D：将剑麻纤维与蕉麻纤维送入开松机进行开松处理，并清除杂物；
E：将步骤D中得到的剑麻纤维与蕉麻纤维的混合物浸入到吲哚-2-甲酸溶液中，用清水浸泡15小时，至中性以后在150℃的环境下烘干，得到改性的剑麻纤维与蕉麻纤维；
F：将大麻纤维和罗布麻纤维送入开松机进行开松处理，并清除杂物；
G：向步骤F中得到的大麻纤维与罗布麻纤维混合物中加入醚化剂2，3-环氧丙基三甲基氯化铵溶液，在68℃温度下搅拌3小时，然后浸泡反应15个小时；
H：向步骤G中得到的大麻纤维与罗布麻纤维混合物中加入清水洗净，待至中性后再150℃环境下烘干，得到改性的大麻纤维和罗布麻纤维；
I：将黄麻纤维与洋麻纤维送入开松机进行开松处理，并清除杂物；
J：向步骤I中的黄麻纤维与洋麻纤维混合物中添加过冷水，在0℃的环境下浸泡13个小时；
K：向步骤J中的黄麻纤维与洋麻纤维混合物中加入γ-氨基丁酸水溶液，并加热至沸腾，加热40分钟后并洗净，室温环境下进行干燥处理；
L：将亚麻纤维和剑麻纤维混纺编制成第一贴布层的经线，将胡麻纤维和蕉麻纤维混纺编制成第一贴布层的纬线，将大麻纤维和黄麻纤维混纺编制成第二贴布层的经线，将罗布麻纤维和洋麻纤维混纺编制成第二贴布层的纬线，得到成品。
6.根据权利要求1所述的一种用于治疗风湿病的膏药贴，其特征在于，所述膏药药物层(3)的厚度为1.5-3毫米。