CN110343863A - 一种碱浸分离锑铅的方法 - Google Patents
一种碱浸分离锑铅的方法 Download PDFInfo
- Publication number
- CN110343863A CN110343863A CN201910668299.0A CN201910668299A CN110343863A CN 110343863 A CN110343863 A CN 110343863A CN 201910668299 A CN201910668299 A CN 201910668299A CN 110343863 A CN110343863 A CN 110343863A
- Authority
- CN
- China
- Prior art keywords
- lead
- antimony
- hydrogen peroxide
- added
- filter residue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种碱浸分离锑铅的方法,将锑铅合金破碎成200目以下,加入氢氧化钠溶液中,搅拌条件下缓慢加入一定量双氧水,搅拌反应一段时间后,固液分离,滤液加入双氧水反应生成焦锑酸钠,滤渣熔融可直接进行铅电解精炼产生电解铅。本发明的环境友好,效率更高,回收时间更短,能耗更低,成本更低,可直接得到符合国家标准的焦锑酸钠。
Description
技术领域
本发明涉及一种碱浸分离锑铅的方法,属于有色金属湿法冶金领域。
背景技术
铅阳极泥还原熔炼初级阶段和贵铅氧化精炼初级阶段都会产生一种锑铅含量比较高的渣,工业上分别叫稀渣和锑渣,这两种渣除含锑铅外,还含有大量的硅铁钙钠,一般情况都是将渣加入还原碳粉进行还原熔炼,得到锑铅,这种情况得到锑铅合金,锑铅都有一定含量,锑占20-60%,铅占30-50%,若是直接进入铅电解精炼,锑含量太高会影响电解铅的精度,目前大部分是将锑铅进入转炉进行吹锑熔炼,使大部分的锑进入烟尘,从而达到锑铅的初步分离,剩余的锑铅锑含量比较小可以直接进入铅电解系统进行电解精炼,这种处理方法简单可靠,但是存在耗能高的缺点,高温冶炼环境恶劣。
发明内容
本发明的目的是提供一种环境友好、能耗低的碱浸分离锑铅的方法。
本发明一种碱浸分离锑铅的方法,分离步骤如下:
(1)将锑铅合金破碎至200目以下的锑铅合金粉末;
(2)将步骤(1)所得锑铅合金粉末加入氢氧化钠溶液中,搅拌10-30min后缓慢加入一定量双氧水,搅拌反应一定时间后过滤得滤液1和滤渣1;
(3)往步骤(2)所得滤液1搅拌条件下缓慢加入一定量的双氧水,搅拌氧化反应一定时间,过滤,滤渣即焦锑酸钠;
(4)步骤(2)所得滤渣1熔融后可直接进行铅电解精炼;
步骤(2)中氢氧化钠的浓度为100-300g/L,反应时间为1-3h,浸出温度为70-90℃,液固比为5-15:1,加入双氧水质量百分比为30%,加入双氧水的量为相当于把Sb单质氧化成三价锑理论量的1-1.2倍;
步骤(3)中双氧水用量为氧化溶液中三价锑所需理论量的1-1.5倍,反应时间为1-3h,反应温度为70-90℃。
所述滤渣1主要成分为Pb80-95%,Sb 1-5%。
本发明的有益效果:
(1)本发明在锑铅合金中,锑单质的还原能力强与铅单质,所以在碱液中,锑先被双氧水氧化,控制双氧水的加入量可以使锑单质被氧化而铅单质不被氧化,锑单质在碱液中最先被还原为亚锑酸钠,亚锑酸钠溶于氢氧化钠碱液中,过滤就可以使锑与铅分离,亚锑酸钠在氢氧化钠溶液中加双氧水反应生成难溶于水的焦锑酸钠;
(2)比起现有技术加入还原碳粉还原熔炼,得锑铅合金,再转炉进行吹锑熔炼的技术手段,采用加氢氧化钠溶液和两次加双氧水,环境更友好,效率更高,回收时间更短,能耗更低,成本更低,可直接得到符合国家标准的焦锑酸钠。
具体实施方案
实施例1
所用锑铅合金,锑52%,铅43%;
称取100g锑铅合金粉末(粒度≤200目)加入100g/L氢氧化钠溶液中,液固比10:1,温度80℃,搅拌20min,缓慢滴加1倍双氧水氧化锑单质为三价锑理论量的双氧水,搅拌反应2h,趁热过滤,得滤液1和滤渣2。滤液1在搅拌条件下滴加1倍双氧水氧化溶液中三价锑所需理论量的双氧水,氧化反应2h,温度80℃,过滤,洗涤,干燥,得到焦锑酸钠93.9g,锑含量为47.9%,锑直收率86.5%。滤渣2重46.7g,铅含量90.1%,锑含量8.02%,滤渣2可直接送铅电解工序。
Claims (1)
1.一种碱浸分离锑铅的方法,其特征在于:分离步骤如下:
(1)将锑铅合金破碎至200目以下的锑铅合金粉末;
(2)将步骤(1)所得锑铅合金粉末加入氢氧化钠溶液中,搅拌10-30min后缓慢加入一定量双氧水,搅拌反应一定时间后过滤得滤液1和滤渣1;
(3)往步骤(2)所得滤液1搅拌条件下缓慢加入一定量的双氧水,搅拌氧化反应一定时间,过滤,滤渣即焦锑酸钠;
(4)步骤(2)所得滤渣1熔融后可直接进行铅电解精炼;
步骤(2)中氢氧化钠的浓度为100-300g/L,反应时间为1-3h,浸出温度为70-90℃,液固比为5-15:1,加入双氧水质量百分比为30%,加入双氧水的量为相当于把Sb单质氧化成三价锑理论量的1-1.2倍;
步骤(3)中双氧水用量为氧化溶液中三价锑所需理论量的1-1.5倍,反应时间为1-3h,反应温度为70-90℃。