CN110306023A - 一种棕榈油制作的金属热处理淬火油 - Google Patents

一种棕榈油制作的金属热处理淬火油 Download PDF

Info

Publication number
CN110306023A
CN110306023A CN201910487896.3A CN201910487896A CN110306023A CN 110306023 A CN110306023 A CN 110306023A CN 201910487896 A CN201910487896 A CN 201910487896A CN 110306023 A CN110306023 A CN 110306023A
Authority
CN
China
Prior art keywords
oil
palm oil
metal heat
heat treatmet
follows
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910487896.3A
Other languages
English (en)
Inventor
于程歆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201910487896.3A priority Critical patent/CN110306023A/zh
Publication of CN110306023A publication Critical patent/CN110306023A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种棕榈油造成的金属热处理油，采用棕榈油为基础油，添加多种功能性复合添加剂，包括冷却性能改进剂、抗氧防腐剂、清净分散剂、光亮剂、防锈剂，可有效改善热处理油各冷却阶段的冷却速度分布，消除热处理淬火油的膜沸腾阶段，特别适用于金属工件的分级淬火和等温淬火，延长热处理油高、中、低温度下的使用寿命和安全性，提高热处理工件的工序间防锈能力和工件清洗性，所用添加剂均具有化学稳定性和250℃以下高温耐受性。

Description

一种棕榈油制作的金属热处理淬火油
技术领域
本发明涉及金属热处理淬火冷却介质领域。
背景技术
1)在世界范围内，金属热处理长期以来都是以石油基淬火油为淬火主要冷却介质，但由于石油属于不可再生能源，且石油基淬火介质存在开口闪点低和烟点低、作业过程中产生大量油烟、废油难以降解污染环境、安全隐患大等固有弊病。
2)从技术性能看，石油基淬火油的上特性温度低，蒸汽膜破裂时间长，对提高钢制工件的淬硬性和机械强度不利，而在进入Ms点以下马氏体转变区时，冷速又较快，容易造成工件变形甚至开裂。
3)棕榈油属于可再生能源，其闪点比常用全损系统用油的开口闪点高出60～100℃，烟点高出50℃左右。在复合添加剂的作用下，上特性温度高出100℃左右，进入Ms点以下马氏体转变区时，调整冷却性能改进剂的加入量，冷速又明显降低，可有效降低淬火工件变形和开裂，从而提高热处理成品率和产品质量。
发明内容
本发明要解决的技术问题是，压榨或溶剂萃取棕榈油，及其与各种功能添加剂的配伍性；筛选和确定具有互补作用的冷却性能改进剂，将其添加到所述基础油中，改变基础油的冷却特性，合理分配淬火油的膜沸腾、泡沸腾和对流三个冷却阶段的冷却速度；筛选和确定具有复合增效作用的抗氧防腐剂；筛选和确定清净分散剂、光亮剂和防锈剂三种单剂。
本发明为实现上述目的所采用的技术方案是：采用棕榈油为基础油，添加多种功能性添加剂，各组分及其质量百分数如下：
棕榈油 88.0～99.95
冷却性能改进剂 0.01～3
抗氧防腐剂 0.01～5
清净分散剂 0.01～2
光亮剂 0.01～1
防锈剂0.01～1，以上各组分百分数总和为100％。
进一步地，所述冷却性能改进剂的组成及质量比为：
古马隆树脂 40～70
低分子聚丁烯 30～60
石油树脂 0.005～3。
进一步地，所述抗氧防腐剂的组成及质量百分比为：
进一步地，各组分及其质量百分数为：
棕榈油 90～95
冷却性能改进剂 1.0～2.5
抗氧防腐剂 0.5～2.5
清净分散剂 0.5～2.5
光亮剂 0.5～1
防锈剂0.2～1，以上各组分百分数总和为100％。
进一步地，各组分及其质量百分数为：
棕榈油 92～93
冷却性能改进剂 1.5～2
抗氧防腐剂 1～2
清净分散剂 1～2
光亮剂 0.6～0.8
防锈剂0.5～0.8，以上各组分百分数总和为100％。
本发明的有益效果为：采用棕榈油为基础油，添加多种功能性复合添加剂，包括冷却性能改进剂、抗氧防腐剂、清净分散剂、光亮剂、防锈剂，可有效改善热处理油各冷却阶段的冷却速度分布，消除热处理淬火油的膜沸腾阶段，特别适用于金属工件的分级淬火和等温淬火，延长热处理油高、中、低温度下的使用寿命和安全性，提高热处理工件的工序间防锈能力和工件清洗性，所用添加剂均具有化学稳定性和250℃以下高温耐受性。
具体实施方式
下面结合具体实施例对本发明作进一步解释说明。
实施实例1
将下列组分按质量百分比，在搅拌状态下，加温调和而成。
以上组分总和为100％。
实例1质量指标：
实施实例2
将下列组分按质量百分比，在搅拌状态下，加温调和而成。
以上组分总和为100％。
实例2质量指标：

Claims (5)

1.一种棕榈油制作的金属热处理淬火油，其特征在于，采用棕榈油为基础油，添加多种功能性添加剂，各组分及其质量百分数如下：
棕榈油 88.0～99.95
冷却性能改进剂 0.01～3
抗氧防腐剂 0.01～5
清净分散剂 0.01～2
光亮剂 0.01～1
防锈剂 0.01～1，以上各组分百分数总和为100%。
2.根据权利要求1所述的一种棕榈油制作的金属热处理淬火油，其特征在于，冷却性能改进剂的组成及质量比为：
古马隆树脂 40～70
低分子聚丁烯 30～60
石油树脂 0.005～3。
3.根据权利要求1所述的一种棕榈油制作的金属热处理淬火油，其特征在于，所述抗氧防腐剂的组成及质量百分比为：
2,6二叔丁基对甲酚 0.01～1
苯三唑醛-胺缩合物 0.01～1
4.4-亚甲基-二-（2.6-二叔丁基苯酚） 0.01～1
丁基羟基茴香醚 0.01～1。
4.根据权利要求1所述的一种棕榈油制作的金属热处理淬火油，其特征在于，各组分及其质量百分数为：
棕榈油 90～95
冷却性能改进剂 1.0～2.5
抗氧防腐剂 0.5～2.5
清净分散剂 0.5～2.5
光亮剂 0.5～1
防锈剂 0.2～1，以上各组分百分数总和为100%。
5.根据权利要求4所述的一种棕榈油制作的金属热处理淬火油，其特征在于，各组分及其质量百分数为：
棕榈油 92～93
冷却性能改进剂 1.5～2
抗氧防腐剂 1～2
清净分散剂 1～2
光亮剂 0.6～0.8
防锈剂 0.5～0.8，以上各组分百分数总和为100%。
CN201910487896.3A 2019-06-05 2019-06-05 一种棕榈油制作的金属热处理淬火油 Pending CN110306023A (zh)