CN110273222A - A kind of preparation process of the jacquard double needle-bar flannel fabric with plastic effect - Google Patents
A kind of preparation process of the jacquard double needle-bar flannel fabric with plastic effect Download PDFInfo
- Publication number
- CN110273222A CN110273222A CN201910531463.3A CN201910531463A CN110273222A CN 110273222 A CN110273222 A CN 110273222A CN 201910531463 A CN201910531463 A CN 201910531463A CN 110273222 A CN110273222 A CN 110273222A
- Authority
- CN
- China
- Prior art keywords
- comb
- semi
- bar
- gloss
- terylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The preparation process of the invention discloses a kind of jacquard double needle-bar flannel fabric with plastic effect.On the double-needle bed raschel tricot machine of 7 combs, wherein sley bar is worn semi-gloss Polyester Yarns by the 1st, 2,6 and 7, walks chaining, inlaid thread or double warp plain stitch, and the intermediate the 3rd connects front and back needle bed sley bar, with chaining, forms under hair;4th, 5 wear cationic Polyester Yarns sley bar, with through needle bed before and after flushconnection, form the longer lint for being higher than the 3rd comb.The present invention combs using the 3rd suede as under hair, and another two suede comb shapes it is show-through to solve the problems, such as that routine is formed due to flower pattern demand sley bar sky is worn, and have concave-convex sense plastic effect at the flower pattern of protrusion.The flower pattern of the fabric is more beautiful characteristic, and fabric is more three-dimensional plentiful, soft.
Description
Technical field
The preparation process of the present invention relates to a kind of jacquard double needle-bar flannel fabric with plastic effect, belong to weaving plus
Work technical field.
Background technique
Two-needle bar flange suede product is a kind of two-needle bar suede class product popular in recent years, be widely used in home textile and
The fields such as clothes.Have the characteristics that gloss is bright, soft, good heat preservation performance, environmental protection.Its appearance characteristics is mainly reflected in villus
On face.Traditional jacquard double needle-bar machine with 1-2 suede comb shape at flower pattern, due to the limitation of sley bar, the limitation of the decorative pattern of formation is more.
The final finishing usually from fabric of the intricate detail effect of other suede class products carries out stamp, etching, embossing etc. to flannelette
Processing generates decorative pattern and pique effect.With the continuous development of crosspointer bed technique, the 7 comb warp knits for having had 3 suede combs are double
Needle bed jacquard.This machine can form more flower pattern effects complicated and changeable, be formed relative to final finishings such as printing and embossings
Design, jacquard weave formed pattern be more persistently unlikely to deform, flower pattern is more three-dimensional plentiful.
Summary of the invention
For overcome the deficiencies in the prior art, the present invention provides a kind of jacquard double needle-bar flannel with plastic effect
The preparation process of fabric.
The present invention is achieved through the following technical solutions:
A kind of preparation process of the jacquard double needle-bar flannel fabric with plastic effect, in the double-needle bed raschel of 7 combs
On tricot machine, wherein sley bar is worn semi-gloss Polyester Yarns by the 1st, 2,6 and 7, walks chaining, inlaid thread or double warp plain stitch, and the intermediate the 3rd
Sley bar, front and back needle bed is connected with chaining, forms under hair;4th, 5 wear cationic Polyester Yarns sley bar, with through needle before and after flushconnection
Bed forms the longer lint for being higher than the 3rd comb.
A kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect, specifically includes following several
A step:
1) sorting: selection semi-gloss polyester FDY, semi-gloss polyester DTY, cationic terylene or color knit polyester DTY;
2) warping: semi-gloss terylene, cationic terylene or color are knitted into terylene, carry out warping on computer copy warping machine;
3) it weaves: being weaved using 7 comb double-needle bed raschel tricot machines, blank cloth is obtained after weaving;
4) final finishing;
5) it detects, packaging.
A kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect, the warping and weaving
When single comb institutional framework apolegamy and mode of entrying are as follows:
GB1 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear;
GB2 comb: 0-1-1-1/1-0-0-0//, completely wear;
GB3 comb: 0-1-0-1/1-0-1-0//, completely wear;
GB4 comb:
23-22-21-20/22-23-20-21/21-20-19-18/20-21-18-19/19-18-17-16/18-19-16-
17/17-16-15-14/16-17-14-15/15-14-13-12/14-15-12-13/13-12-11-10/12-13-10-11/
11-10-9-8/10-11-8-9/9-8-7-6/8-9-6-7/7-6-5-4/6-7-4-5/5-4-3-2/4-5-2-3/3-2-1-0/
2-3-0-1/3-2-1-0/2-3-0-1/3-2-5-4/2-3-4-5/5-4-7-6/4-5-6-7/7-6-9-8/6-7-8-9/9-8-
11-10/8-9-10-11/11-10-13-12/10-11-12-13/13-12-15-14/12-13-14-15/15-14-17-16/
14-15-16-17/17-16-19-18/16-17-18-19/19-18-21-20/18-19-20-21/21-20-23-22/20-
21-22-23/23-22-25-24/22-23-25-24/25-24-23-22/25-24-22-23//, 44 skies 4 are worn;
GB5 comb:
2-3-4-5/3-2-5-4/4-5-6-7/5-4-7-6/6-7-8-9/7-6-9-8/8-9-10-11/9-8-11-10/
10-11-12-13/11-10-13-12/12-13-14-15/13-12-15-14/14-15-16-17/15-14-17-16/16-
17-18-19/17-16-19-18/18-19-20-21/19-18-21-20/20-21-22-23/21-20-23-22/22-23-
24-25/23-22-25-24/22-23-24-25/23-22-25-24/22-23-20-21/23-22-21-20/20-21-18-
19/21-20-19-18/18-19-16-17/19-18-17-16/16-17-14-15/17-16-15-14/14-15-12-13/
15-14-13-12/12-13-10-11/13-12-11-10/10-11-8-9/11-10-9-8/8-9-6-7/9-8-7-6/6-7-
4-5/7-6-5-4/4-5-2-3/5-4-3-2/2-3-0-1/3-2-0-1/0-1-2-3/0-1- 3-2//, 4 wear 44 skies;
GB6 comb: 1-0-0-0/0-1-1-1//, completely wear;
GB7 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear.
Or
GB1 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear;
GB2 comb: 0-1-1-1/1-0-0-0//, completely wear;
GB3 comb: 0-1-0-1/1-0-1-0//, completely wear;
GB4 comb:
28-29-26-27/29-28-27-26/28-29-26-27/29-28-27-26/26-27-24-25/27-26-25-
24/26-27-24-25/27-26-25-24/26-27-24-25/27-26-25-24/24-25-22-23/25-24-23-22/
24-25-22-23/25-24-23-22/24-25-22-23/25-24-23-22/22-23-20-21/23-22-21-20/22-
23-20-21/23-22-21-20/22-23-20-21/23-22-21-20/20-21-18-19/21-20-19-18/20-21-
18-19/21-20-19-18/20-21-18-19/21-20-19-18/18-19-16-17/17-16-15-14/14-15-12-
13/13-12-11-10/10-11-8-9/9-8-7-6/6-7-4-5/5-4-3-2/2-3-0-1/5-4-3-2/6-7-4-5/9-8-
7-6/10-11-8-9/13-12-11-10/14-15-12-13/17-16-15-14/18-19-16-17/21-20-19-18/20-
21-18-19/21-20-19-18/20-21-18-19/21-20-19-18/20-21-18-19/23-22-21-20/22-23-
20-21/23-22-21-20/22-23-20-21/25-24-23-22/24-25-22-23/25-24-23-22/24-25-22-
23/25-24-23-22/24-25-22-23/27-26-25-24/26-27-24-25/27-26-25-24/26-27-24-25/
27-26-25-24/26-27-24-25/29-28-27-26/28-29-26-27/29-28-27-26/28-29-26-27/28-
28-28-28/28-28-28-28/28-28-28-28/28-28-28-28/28-28-28-28/28-28-28-28/28-28-
28-28/28-28-28-28/28-28-28-28,72 skies 4 are worn;
GB5 comb:
2-3-0-1/3-2-1-0/2-3-0-1/3-2-1-0/4-5-2-3/5-4-3-2/4-5-2-3/5-4-3-2/4-5-
2-3/5-4-3-2/6-7-4-5/7-6-5-4/6-7-4-5/7-6-5-4/6-7-4-5/7-6-5-4/8-9-6-7/9-8-7-6/
8-9-6-7/9-8-7-6/8-9-6-7/9-8-7-6/10-11-8-9/11-10-9-8/10-11-8-9/11-10-9-8/10-
11-8-9/11-10-9-8/12-13-10-11/15-14-13-12/16-17-14-15/19-18-17-16/20-21-18-19/
23-22-21-20/24-25-22-23/27-26-25-24/28-29-26-27/27-26-25-24/24-25-22-23/23-
22-21-20/20-21-18-19/19-18-19-18/16-17-14-15/15-14-13-12/12-13-10-11/11-10-9-
8/10-11-8-9/11-10-9-8/10-11-8-9/11-10-9-8/10-11-8-9/9-8-7-6/8-9-6-7/9-8-7-6/
8-9-6-7/7-6-5-4/6-7-4-5/7-6-5-4/6-7-4-5/7-6-5-4/6-7-4-5/5-4-3-2/4-5-2-3/5-4-
3-2/4-5-2-3/5-4-3-2/4-5-2-3/3-2-1-0/2-3-0-1/3-2-1-0/2-3-0-1/2-2-2-2/2-2-2-2/
2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2,72 skies 4 are worn;
GB6 comb: 1-0-0-0/0-1-1-1//, completely wear;
GB7 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear.
A kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect, single comb tissue
Component used in structure and blend proportion are as follows:
GB1 comb: 50~100D semi-gloss polyester FDY;
GB2 comb: 50~100D semi-gloss polyester FDY;
GB3 comb: 100~200D semi-gloss polyester DTY;
GB4 comb: 100~200D cation terylene or color knit polyester DTY;
GB5 comb: 100~200D cation terylene or color knit polyester DTY;
GB6 comb: 50~100D semi-gloss polyester FDY;
GB7 comb: 50~100D semi-gloss polyester FDY.
A kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect, the sorting are selected from 14
~25% 50D~100D semi-gloss polyester FDY, the semi-gloss polyester DTY of 64~73%100~200D, 10~13% 100D~
200D cation terylene or color knit polyester DTY.
A kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect, the tool of the final finishing
Body step are as follows:
1. cuing open suede: being carried out on cuing open suede machine, control two sides villus length is consistent;2. setting: it is shaped with boarding machine, baking oven temperature
Degree is 100-160 DEG C;3. dyeing: semi-gloss terylene disperse dyes, the cationic terylene dye of positive ion, color are knitted terylene and are not needed
Dyeing;4. drying;5. hot light;6. plucking;7. carding;8. cropping.
The flange that a kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect is prepared
Velvet fabric.
The flannel fabric, the fabric finished product Gram Mass are 200~400g/m2。
Advantageous effects of the invention:
1) fabric hand feel of the present invention is plentiful, three-dimensional beautiful, bottom surface structure stretch.It is more to can be applied to home textile, clothes etc.
A field.Grammes per square metre is in 200-400g/m2Between.
2) present invention combs using the 3rd suede as under hair, and another two suede comb shapes solve conventional because of flower at the flower pattern of protrusion
Type demand sley bar sky is worn and the show-through problem that is formed, and has concave-convex sense plastic effect.The flower pattern of the fabric is more beautiful to be had
Characteristic, fabric is more three-dimensional plentiful, soft.
3) present invention, which does not need the final finishings such as etching, embossing, can form concave-convex flower pattern effect, reduce process flow,
Save the cost improves production efficiency.And the flower pattern persistence that jacquard weave is formed is good, is unlikely to deform.
Detailed description of the invention
Fig. 1 be each the tissue gauze pad motion diagram singly combed in the embodiment of the present invention 1.
Fig. 2 be each the tissue gauze pad motion diagram singly combed in the embodiment of the present invention 2.
Specific embodiment
The invention will be further described below in conjunction with the accompanying drawings.Following embodiment is only used for clearly illustrating the present invention
Technical solution, and not intended to limit the protection scope of the present invention.
Embodiment 1
A kind of jacquard double needle-bar flannel fabric of plastic effect, is made of following mass percent components: 75D/36f half
Light polyester FDY is that 24.8%, 120D/192f semi-gloss polyester DTY is that 64.3%, 120D/192f cation terylene or color knit terylene
It is 10.9%, which cooperatively forms the Argyle with three-dimensional sense plastic effect using height suede effect and flower pattern.
The preparation process of the fabric is: the detailed process of each technique is as follows: including single comb institutional framework apolegamy, beam worker
Sequence, warping, weaving, setting etc..
1, preparatory process
Select 50~100D semi-gloss polyester FDY, 120~200D semi-gloss polyester DTY, 120~200D cation terylene or color
Knit polyester DTY;
2, warping technology
The temperature and humidity at warping scene: 25 ± 1 DEG C of temperature, relative humidity 65 ± 5%, higher and stable temperature and humidity has
Help Polyester Yarns turn stabilization and soft surface, avoids Polyester Yarns from tangling each other, be conducive to Polyester Yarns warp knit product
Production.
Routinely warping operation process, polyester filament carry out warping.Suitably add white oil and antistatic agent during warping, disappears
The electrostatic generated during high-speed winding except chemical-fibres filaments.
3, weaving process
Machine parameter:
Type: double-needle bed raschel tricot machine RD7DPLM;
Machine number: 16~22 needles/25.4mm;
Door width: 77~130 inches.
Warp knitting fabrics structure: gauze pad motion diagram is shown in Fig. 1:
GB1 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear;
GB2 comb: 0-1-1-1/1-0-0-0//, completely wear;
GB3 comb: 0-1-0-1/1-0-1-0//, completely wear;
GB4 comb:
23-22-21-20/22-23-20-21/21-20-19-18/20-21-18-19/19-18-17-16/18-19-16-
17/17-16-15-14/16-17-14-15/15-14-13-12/14-15-12-13/13-12-11-10/12-13-10-11/
11-10-9-8/10-11-8-9/9-8-7-6/8-9-6-7/7-6-5-4/6-7-4-5/5-4-3-2/4-5-2-3/3-2-1-0/
2-3-0-1/3-2-1-0/2-3-0-1/3-2-5-4/2-3-4-5/5-4-7-6/4-5-6-7/7-6-9-8/6-7-8-9/9-8-
11-10/8-9-10-11/11-10-13-12/10-11-12-13/13-12-15-14/12-13-14-15/15-14-17-16/
14-15-16-17/17-16-19-18/16-17-18-19/19-18-21-20/18-19-20-21/21-20-23-22/20-
21-22-23/23-22-25-24/22-23-25-24/25-24-23-22/25-24-22-23//, 44 skies 4 are worn;
GB5 comb:
2-3-4-5/3-2-5-4/4-5-6-7/5-4-7-6/6-7-8-9/7-6-9-8/8-9-10-11/9-8-11-10/
10-11-12-13/11-10-13-12/12-13-14-15/13-12-15-14/14-15-16-17/15-14-17-16/16-
17-18-19/17-16-19-18/18-19-20-21/19-18-21-20/20-21-22-23/21-20-23-22/22-23-
24-25/23-22-25-24/22-23-24-25/23-22-25-24/22-23-20-21/23-22-21-20/20-21-18-
19/21-20-19-18/18-19-16-17/19-18-17-16/16-17-14-15/17-16-15-14/14-15-12-13/
15-14-13-12/12-13-10-11/13-12-11-10/10-11-8-9/11-10-9-8/8-9-6-7/9-8-7-6/6-7-
4-5/7-6-5-4/4-5-2-3/5-4-3-2/2-3-0-1/3-2-0-1/0-1-2-3/0-1- 3-2//, 4 wear 44 skies;
GB6 comb: 1-0-0-0/0-1-1-1//, completely wear;
GB7 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear.
Raw material and mode of entrying:
GB1 comb, GB2 comb, GB6 comb, GB7 comb: 50~100D semi-gloss polyester FDY;
GB3 comb: 100~200D semi-gloss polyester DTY;
GB4 comb and GB5 comb: 100~200D cation terylene or color knit polyester DTY.
The computer display screen of the input controls cabinets such as digital band yarn, warp run-in and drawing density will be organized, after preservation in load
Machine file can be switched on.
Weaving is completed to obtain blank cloth, weighs, pack, blank storage.
4, postfinishing process
1. cuing open suede: being carried out on suede machine in special cut open, control two sides villus length is consistent;2. setting: it is shaped with boarding machine,
Oven temperature is 100-160 DEG C, while controlling cloth requirement width and grammes per square metre;3. dyeing: semi-gloss terylene disperse dyes, sun from
The sub- terylene dye of positive ion, color knit terylene and do not need to dye;4. drying;5. hot light: remove impurity, improve flannelette feel and
Gloss;6. plucking;7. carding;8. cropping;9. then examining, weighing, packaging, warehousing finished products.
By process above, the jacquard double needle-bar face flannel with plastic effect style of the present embodiment can be obtained
Material.
Warp knitting technology list is shown in Table 1.
Table 1
GB1, GB2, GB6 and GB7 comb wear semi-gloss Polyester Yarns, and GB3 comb wears semi-gloss Polyester Yarns, and GB4 and GB5 are cation or color
Knit Polyester Yarns.GB1, GB2, GB6 and GB7 comb walk chaining, inlaid thread or double warp plain stitch, fabric bottom surface formed " hard bottom plate " or
" soft seat " effect;GB3 comb pillar stitch connects front and back needle bed, cuts open and forms under hair in flannelette after width;GB4 and GB5 comb use
Warp plain stitch's connection front and back needle bed is higher than after cuing open width in flannelette formation by cooperatively forming diamond shape and/or star-shaped flower pattern effect
The lint of under hair.Relief plastic effect and effect of decorative patterns are formed by the collocation of height lint.Lint face before non-plucking
As using front.
Embodiment 2
A kind of jacquard double needle-bar flannel fabric of plastic effect, is made of following mass percent components: 75D/36f half
Light polyester FDY is that 27.2%, 120D/192f semi-gloss polyester DTY is that 65.8%, 120D/192f cation terylene or color knit terylene
It is 7.0%, which cooperatively forms the etoile with three-dimensional sense plastic effect using height suede effect and flower pattern.
The preparation process of the fabric is: the detailed process of each technique is as follows: including single comb institutional framework apolegamy, beam worker
Sequence, warping, weaving, setting etc..
1, preparatory process
Select 50~100D semi-gloss polyester FDY, 120~200D semi-gloss polyester DTY, 120~200D cation terylene or color
Knit polyester DTY;
2, warping technology
The temperature and humidity at warping scene: 25 ± 1 DEG C of temperature, relative humidity 65 ± 5%, higher and stable temperature and humidity has
Help Polyester Yarns turn stabilization and soft surface, avoids Polyester Yarns from tangling each other, be conducive to Polyester Yarns warp knit product
Production.
Routinely warping operation process, polyester filament carry out warping.Suitably add white oil and antistatic agent during warping, disappears
The electrostatic generated during high-speed winding except chemical-fibres filaments.
3, weaving process
Machine parameter:
Type: double-needle bed raschel tricot machine RD7DPLM;
Machine number: 16~22 needles/25.4mm;
Door width: 77~130 inches.
Warp knitting fabrics structure: gauze pad motion diagram is shown in Fig. 2:
GB1 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear;
GB2 comb: 0-1-1-1/1-0-0-0//, completely wear;
GB3 comb: 0-1-0-1/1-0-1-0//, completely wear;
GB4 comb:
28-29-26-27/29-28-27-26/28-29-26-27/29-28-27-26/26-27-24-25/27-26-25-
24/26-27-24-25/27-26-25-24/26-27-24-25/27-26-25-24/24-25-22-23/25-24-23-22/
24-25-22-23/25-24-23-22/24-25-22-23/25-24-23-22/22-23-20-21/23-22-21-20/22-
23-20-21/23-22-21-20/22-23-20-21/23-22-21-20/20-21-18-19/21-20-19-18/20-21-
18-19/21-20-19-18/20-21-18-19/21-20-19-18/18-19-16-17/17-16-15-14/14-15-12-
13/13-12-11-10/10-11-8-9/9-8-7-6/6-7-4-5/5-4-3-2/2-3-0-1/5-4-3-2/6-7-4-5/9-8-
7-6/10-11-8-9/13-12-11-10/14-15-12-13/17-16-15-14/18-19-16-17/21-20-19-18/20-
21-18-19/21-20-19-18/20-21-18-19/21-20-19-18/20-21-18-19/23-22-21-20/22-23-
20-21/23-22-21-20/22-23-20-21/25-24-23-22/24-25-22-23/25-24-23-22/24-25-22-
23/25-24-23-22/24-25-22-23/27-26-25-24/26-27-24-25/27-26-25-24/26-27-24-25/
27-26-25-24/26-27-24-25/29-28-27-26/28-29-26-27/29-28-27-26/28-29-26-27/28-
28-28-28/28-28-28-28/28-28-28-28/28-28-28-28/28-28-28-28/28-28-28-28/28-28-
28-28/28-28-28-28/28-28-28-28,72 skies 4 are worn;
GB5 comb:
2-3-0-1/3-2-1-0/2-3-0-1/3-2-1-0/4-5-2-3/5-4-3-2/4-5-2-3/5-4-3-2/4-5-
2-3/5-4-3-2/6-7-4-5/7-6-5-4/6-7-4-5/7-6-5-4/6-7-4-5/7-6-5-4/8-9-6-7/9-8-7-6/
8-9-6-7/9-8-7-6/8-9-6-7/9-8-7-6/10-11-8-9/11-10-9-8/10-11-8-9/11-10-9-8/10-
11-8-9/11-10-9-8/12-13-10-11/15-14-13-12/16-17-14-15/19-18-17-16/20-21-18-19/
23-22-21-20/24-25-22-23/27-26-25-24/28-29-26-27/27-26-25-24/24-25-22-23/23-
22-21-20/20-21-18-19/19-18-19-18/16-17-14-15/15-14-13-12/12-13-10-11/11-10-9-
8/10-11-8-9/11-10-9-8/10-11-8-9/11-10-9-8/10-11-8-9/9-8-7-6/8-9-6-7/9-8-7-6/
8-9-6-7/7-6-5-4/6-7-4-5/7-6-5-4/6-7-4-5/7-6-5-4/6-7-4-5/5-4-3-2/4-5-2-3/5-4-
3-2/4-5-2-3/5-4-3-2/4-5-2-3/3-2-1-0/2-3-0-1/3-2-1-0/2-3-0-1/2-2-2-2/2-2-2-2/
2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2,72 skies 4 are worn;
GB6 comb: 1-0-0-0/0-1-1-1//, completely wear;
GB7 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear.
Raw material and mode of entrying:
GB1 comb, GB2 comb, GB6 comb, GB7 comb: 50~100D semi-gloss polyester FDY;
GB3 comb: 100~200D semi-gloss polyester DTY;
GB4 comb and GB5 comb: 100~200D cation terylene or color knit polyester DTY.
The computer display screen of the input controls cabinets such as digital band yarn, warp run-in and drawing density will be organized, after preservation in load
Machine file can be switched on.
Weaving is completed to obtain blank cloth, weighs, pack, blank storage.
4, postfinishing process
1. cuing open suede: being carried out on suede machine in special cut open, control two sides villus length is consistent;2. setting: it is shaped with boarding machine,
Oven temperature is 100-160 DEG C, while controlling cloth requirement width and grammes per square metre;3. dyeing: semi-gloss terylene disperse dyes, sun from
The sub- terylene dye of positive ion, color knit terylene and do not need to dye;4. drying;5. hot light: remove impurity, improve flannelette feel and
Gloss;6. plucking;7. carding;8. cropping;9. then examining, weighing, packaging, warehousing finished products.
By process above, the jacquard double needle-bar face flannel with plastic effect style of the present embodiment can be obtained
Material.
Warp knit production technology list is shown in Table 2.
Table 2
The above is only a preferred embodiment of the present invention, it is noted that for the semi-gloss technology people of the art
For member, without departing from the technical principles of the invention, several improvement and deformations can also be made, these improvement and deformations
Also it should be regarded as protection scope of the present invention.
Claims (8)
1. a kind of preparation process of the jacquard double needle-bar flannel fabric with plastic effect, which is characterized in that in the crosspointer of 7 combs
On bed raschel machine, wherein sley bar is worn semi-gloss Polyester Yarns by the 1st, 2,6 and 7, walks chaining, inlaid thread or double warp plain stitch, in
Between the 3rd sley bar, connect front and back needle bed with chaining, form under hair;4th, 5 wear cationic Polyester Yarns sley bar, are connected with through flat
Front and back needle bed is connect, the longer lint for being higher than the 3rd comb is formed.
2. a kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect according to claim 1,
It is characterized in that, specifically includes following steps:
1) sorting: selection semi-gloss polyester FDY, semi-gloss polyester DTY, cationic terylene or color knit polyester DTY;
2) warping: semi-gloss terylene, cationic terylene or color are knitted into terylene, carry out warping on computer copy warping machine;
3) it weaves: being weaved using 7 comb double-needle bed raschel tricot machines, blank cloth is obtained after weaving;
4) final finishing;
5) it detects, packaging.
3. a kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect according to claim 2,
It is characterized in that, single comb institutional framework apolegamy when warping and weaving and mode of entrying are as follows:
GB1 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear;
GB2 comb: 0-1-1-1/1-0-0-0//, completely wear;
GB3 comb: 0-1-0-1/1-0-1-0//, completely wear;
GB4 comb:
23-22-21-20/22-23-20-21/21-20-19-18/20-21-18-19/19-18-17-16/18-19-16-17/
17-16-15-14/16-17-14-15/15-14-13-12/14-15-12-13/13-12-11-10/12-13-10-11/11-
10-9-8/10-11-8-9/9-8-7-6/8-9-6-7/7-6-5-4/6-7-4-5/5-4-3-2/4-5-2-3/3-2-1-0/2-3-
0-1/3-2-1-0/2-3-0-1/3-2-5-4/2-3-4-5/5-4-7-6/4-5-6-7/7-6-9-8/6-7-8-9/9-8-11-
10/8-9-10-11/11-10-13-12/10-11-12-13/13-12-15-14/12-13-14-15/15-14-17-16/14-
15-16-17/17-16-19-18/16-17-18-19/19-18-21-20/18-19-20-21/21-20-23-22/20-21-
22-23/23-22-25-24/22-23-25-24/25-24-23-22/25-24-22-23//, 44 skies 4 are worn;
GB5 comb:
2-3-4-5/3-2-5-4/4-5-6-7/5-4-7-6/6-7-8-9/7-6-9-8/8-9-10-11/9-8-11-10/10-
11-12-13/11-10-13-12/12-13-14-15/13-12-15-14/14-15-16-17/15-14-17-16/16-17-
18-19/17-16-19-18/18-19-20-21/19-18-21-20/20-21-22-23/21-20-23-22/22-23-24-
25/23-22-25-24/22-23-24-25/23-22-25-24/22-23-20-21/23-22-21-20/20-21-18-19/
21-20-19-18/18-19-16-17/19-18-17-16/16-17-14-15/17-16-15-14/14-15-12-13/15-
14-13-12/12-13-10-11/13-12-11-10/10-11-8-9/11-10-9-8/8-9-6-7/9-8-7-6/6-7-4-5/
7-6-5-4/4-5-2-3/5-4-3-2/2-3-0-1/3-2-0-1/0-1-2-3/0-1-3-2//, 4 wear 44 skies;
GB6 comb: 1-0-0-0/0-1-1-1//, completely wear;
GB7 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear.
Or
GB1 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear;
GB2 comb: 0-1-1-1/1-0-0-0//, completely wear;
GB3 comb: 0-1-0-1/1-0-1-0//, completely wear;
GB4 comb:
28-29-26-27/29-28-27-26/28-29-26-27/29-28-27-26/26-27-24-25/27-26-25-24/
26-27-24-25/27-26-25-24/26-27-24-25/27-26-25-24/24-25-22-23/25-24-23-22/24-
25-22-23/25-24-23-22/24-25-22-23/25-24-23-22/22-23-20-21/23-22-21-20/22-23-
20-21/23-22-21-20/22-23-20-21/23-22-21-20/20-21-18-19/21-20-19-18/20-21-18-
19/21-20-19-18/20-21-18-19/21-20-19-18/18-19-16-17/17-16-15-14/14-15-12-13/
13-12-11-10/10-11-8-9/9-8-7-6/6-7-4-5/5-4-3-2/2-3-0-1/5-4-3-2/6-7-4-5/9-8-7-
6/10-11-8-9/13-12-11-10/14-15-12-13/17-16-15-14/18-19-16-17/21-20-19-18/20-
21-18-19/21-20-19-18/20-21-18-19/21-20-19-18/20-21-18-19/23-22-21-20/22-23-
20-21/23-22-21-20/22-23-20-21/25-24-23-22/24-25-22-23/25-24-23-22/24-25-22-
23/25-24-23-22/24-25-22-23/27-26-25-24/26-27-24-25/27-26-25-24/26-27-24-25/
27-26-25-24/26-27-24-25/29-28-27-26/28-29-26-27/29-28-27-26/28-29-26-27/28-
28-28-28/28-28-28-28/28-28-28-28/28-28-28-28/28-28-28-28/28-28-28-28/28-28-
28-28/28-28-28-28/28-28-28-28,72 skies 4 are worn;
GB5 comb:
2-3-0-1/3-2-1-0/2-3-0-1/3-2-1-0/4-5-2-3/5-4-3-2/4-5-2-3/5-4-3-2/4-5-2-3/
5-4-3-2/6-7-4-5/7-6-5-4/6-7-4-5/7-6-5-4/6-7-4-5/7-6-5-4/8-9-6-7/9-8-7-6/8-9-
6-7/9-8-7-6/8-9-6-7/9-8-7-6/10-11-8-9/11-10-9-8/10-11-8-9/11-10-9-8/10-11-8-
9/11-10-9-8/12-13-10-11/15-14-13-12/16-17-14-15/19-18-17-16/20-21-18-19/23-
22-21-20/24-25-22-23/27-26-25-24/28-29-26-27/27-26-25-24/24-25-22-23/23-22-
21-20/20-21-18-19/19-18-19-18/16-17-14-15/15-14-13-12/12-13-10-11/11-10-9-8/
10-11-8-9/11-10-9-8/10-11-8-9/11-10-9-8/10-11-8-9/9-8-7-6/8-9-6-7/9-8-7-6/8-
9-6-7/7-6-5-4/6-7-4-5/7-6-5-4/6-7-4-5/7-6-5-4/6-7-4-5/5-4-3-2/4-5-2-3/5-4-3-
2/4-5-2-3/5-4-3-2/4-5-2-3/3-2-1-0/2-3-0-1/3-2-1-0/2-3-0-1/2-2-2-2/2-2-2-2/2-
2-2-2/2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2/2-2-2-2,72 skies 4 are worn;
GB6 comb: 1-0-0-0/0-1-1-1//, completely wear;
GB7 comb: 5-5-5-5/0-0-0-0/4-4-4-4/0-0-0-0//, completely wear.
4. a kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect according to claim 3,
It is characterized in that, component and blend proportion used in single comb institutional framework are as follows:
GB1 comb: 50~100D semi-gloss polyester FDY;
GB2 comb: 50~100D semi-gloss polyester FDY;
GB3 comb: 100~200D semi-gloss polyester DTY;
GB4 comb: 100~200D cation terylene or color knit polyester DTY;
GB5 comb: 100~200D cation terylene or color knit polyester DTY;
GB6 comb: 50~100D semi-gloss polyester FDY;
GB7 comb: 50~100D semi-gloss polyester FDY.
5. a kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect according to claim 2,
It is characterized in that, the sorting is selected from 14~25% 50D~100D semi-gloss polyester FDY, the semi-gloss of 64~73%100~200D is washed
Synthetic fibre DTY, 10~13% 100D~200D cation terylene or color knit polyester DTY.
6. a kind of preparation process of jacquard double needle-bar flannel fabric with plastic effect according to claim 2,
It is characterized in that, the specific steps of the final finishing are as follows:
1. cuing open suede: being carried out on cuing open suede machine, control two sides villus length is consistent;2. setting: being shaped with boarding machine, oven temperature is
100-160℃;3. dyeing: semi-gloss terylene disperse dyes, the cationic terylene dye of positive ion, color knit terylene and do not need to contaminate
Color;4. drying;5. hot light;6. plucking;7. carding;8. cropping.
7. a kind of jacquard double needle-bar face flannel with plastic effect described in any claim in -6 according to claim 1
The flannel fabric that the preparation process of material is prepared.
8. flannel fabric according to claim 7, which is characterized in that the fabric finished product Gram Mass be 200~
400g/m2。