CN110273219A - A kind of llama fabric and its production method - Google Patents
A kind of llama fabric and its production method Download PDFInfo
- Publication number
- CN110273219A CN110273219A CN201910624266.6A CN201910624266A CN110273219A CN 110273219 A CN110273219 A CN 110273219A CN 201910624266 A CN201910624266 A CN 201910624266A CN 110273219 A CN110273219 A CN 110273219A
- Authority
- CN
- China
- Prior art keywords
- fabric
- llama
- parts
- production method
- fabric according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of llama fabrics, the fabric combines right tiltedly cord small jacquard tissue by warp thread and weft yarn, is woven into the super tight structure that aggregate scheduling is 110%, wherein, warp thread twists w/c50/50 27.8tex single thread using S, and weft yarn twists w/c50/50 41.6tex using Z.A kind of production method of llama fabric, warp thread weaving, perching together with weft yarn again after warping, sizing, denting.After such scheme, the sense of touch of the existing pure wool of the fabric is well-pressed and have micro-elasticity；Have again pure cotton exquisiteness, it is sliding it is glutinous, lines is clear, glossiness, color is splendid gorgeous after dyeing, wool-like effect is excellent.
Description
Technical field
The present invention relates to textile garment fabric field more particularly to a kind of llama fabric and its production methods.
Background technique
Even to this day we require dress higher and higher, and from keeping warm not only keeping warm but also good-looking, this centre to be paid
Out it is more than little by little, along with the improvement of people's living standards, present garment market industry highly competitive.In addition to clothes
Design wants unique, above all garment material will select correctly, the performance of fabric determines the design of duplication, according to recent fabric flow
From the point of view of row trend and market sales volume situation, tatting slubbing fashionable dress hair and knitting warp plush, weft-knitted plush, tricot knitting undercoat
Flannelette, weft-knitted undercoat suede and color are knitted the dynamic pin kind in wool spinning hair overall market and are locally increased, and exchange hand shakes uplink, par fabric
For amount compared with increased early period, trendy intention fabric conclusion of the business increment is big.
Based on this understanding, it would be desirable to a kind of sense of touch of existing pure wool, it is well-pressed and have micro-elasticity；There is the thin of pure cotton again
Greasy, sliding glutinous, lines is clearly, glossiness, color is splendid gorgeous after dyeing, the excellent fabric of wool-like effect.
Summary of the invention
It is well-pressed and have micro-elasticity the technical problem to be solved in the present invention is to provide a kind of sense of touch of existing pure wool；Have again pure
The exquisiteness of cotton, sliding glutinous, lines are clearly, glossiness, color is splendid gorgeous after dyeing, the excellent fabric of wool-like effect and its production
Method.
In order to solve the above technical problem, the present invention provides technical solution it is as follows:
A kind of llama fabric, which is characterized in that the fabric combines right tiltedly cord small jacquard group by warp thread and weft yarn
It knits, is woven into the super tight structure that aggregate scheduling is 110%, wherein warp thread twists w/c50/5027.8tex single thread using S, and weft yarn is adopted
W/c50/50 41.6tex is twisted with Z.
In addition: the close radial direction diameter is 665/10CM, and the close broadwise diameter is 275/10CM.
In addition: the ultimate strength of fabric: through to >=1460, broadwise >=520.
A kind of production method of llama fabric, it is characterised in that: warp thread after warping, sizing, denting again with weft yarn
Weaving, perching together.
In addition: in sizing operation, formula of size are as follows: PVA-177 25kg, converted starch 75kg, auxiliary agent 20kg, cured
3kg, after adding water, through mashing off, bored slurry time 15min, 115 DEG C of bored slurry temperature degree is tuned into solid content 12%, 7.2 ± 0.1 (3# of viscosity
Funnel), pH value 7, volume 850L slurries.
In addition: weaving process uses air-jet loom, using big Zhang Li, high speed operation, and the main burner peace of air-jet loom
Gas clamp device is filled, the chucking power that yarn passes through is increased, right side goes out shed open using 4 sections of variation waste selvage yarn threading methods.
In addition: using bull part, few warp beam, equal tension warping on Benniger high-speed warping machine in warping process.
In addition: further including processing of singing, the processing of singing, which is located between the weaving and the perching, to be carried out, specifically
To make cloth be at exceptionally straight state by tenslator, cloth is then bypassed into red-hot metal roller surface, is made
Fabric is contacted with metal roller, and wherein the front and back of fabric is successively contacted with the surface of metal roller, metal roller surface
Temperature be 100-130 DEG C, two metal roller burning-off surface villus, the surface of metal roller is needed simultaneously except Slag treatment, will
It is bonded in the fusing residue removal of the hair of metal roller surface.
In addition: it further include cleaning treatment, the cleaning treatment carries out after being located at the processing of singing, specifically by
Tenslator makes cloth be in exceptionally straight state, then by washing pool, water temperature is maintained between 30-50 DEG C, washing pool
Inside contain cleaning agent, vibrating roller is provided in pond, fabric bypasses vibrating roller, and is bonded with the surface of vibrating roller, vibrating roller
Vibration frequency is 300-500 times/seconds, after fabric comes out out of washing pool, handles using water flushing, is finally dried.
In addition: the parts by weight composition of the cleaning agent are as follows: 10-12 parts of stearic acid, 15-17 parts of anhydrous sodium sulfate,
1-3 parts of sodium carbonate, 5-8 parts of vegetable preservative, 3-6 parts of soap base, double 6-10 parts of the stearates of polyethylene glycol, dodecyl
12-15 parts of benzene sulfonic acid sodium salt, 30-50 parts of water.
It is well-pressed and have micro-elasticity the beneficial effects of the present invention are: the sense of touch of the existing pure wool of the fabric；There is the thin of pure cotton again
Greasy, sliding glutinous, lines is clearly, glossiness, color is splendid gorgeous after dyeing, and wool-like effect is excellent.
Detailed description of the invention
Present invention will be further explained below with reference to the attached drawings and specific embodiments:
Fig. 1 is the invention product organization chart.
Note: ×: it indicates that warp thread floats on weft yarn, blank: indicating fill yarns float on warp thread.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to the accompanying drawings and embodiments, right
The present invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, and
It is not used in the restriction present invention.
A kind of llama fabric, which is characterized in that the fabric combines right tiltedly cord small jacquard group by warp thread and weft yarn
It knits, is woven into the super tight structure that aggregate scheduling is 110%, wherein warp thread twists w/c50/5027.8tex single thread using S, and weft yarn is adopted
W/c50/50 41.6tex, warp thread weaving, perching together with weft yarn again after warping, sizing, denting are twisted with Z.
In sizing operation, formula of size are as follows: PVA-177 25kg, converted starch 75kg, auxiliary agent 20kg, cured 3kg add
After water, through mashing off, bored slurry time 15min, 115 DEG C of bored slurry temperature degree, be tuned into solid content 12%, viscosity 7.2 ± 0.1 (3# funnel),
The slurries of pH value 7, volume 850L.It being matched by compound size, further enhances slurries sizing performance, slurries impregnability is good,
Serous coat wearability is good, keeps the starching of script llama yarn difficult, it is easy to which the problem of light sizing is resolved.
In addition, sizing operation includes starching, control beam of a loom axis is wide: 156.1 centimetres, beam of a loom length: and 1800 meters, the rate of sizing:
13 ± 0.3%, elongation: 1.1%, regain: 6.5%, drying room temperature: 150 DEG C of wet area, dry 145 DEG C of area, sizing speed:
80m/min, each section of tension: unwinding: 650N, stock tank: 100N, drying chamber: 150N does to distinguish twisting: 2600N, winding: 3700N, pressure
Yarn: 4000N, a fast squeezing pressure: 12KN, two fast squeezing pressures: 27KN, slurry groove temperature: 93 DEG C.
Weaving process uses air-jet loom, and using big Zhang Li, the main burner installation gas of high speed operation, air-jet loom is clamped
It sets, increases the chucking power that yarn passes through, right side goes out shed open using 4 sections of variation waste selvage yarn threading methods, guarantees that yarn flies in reed slot
Steadily, meanwhile, weft yarn clamping is stronger, prevents looped weft problem completely.Control loom: speed: 630 revs/min, upper machine breadth: 156
Centimetre, warp tension: 380KG, Cropping Length: 170 meters/, relative humidity: 78%, heald level time: 280 °, beam of a loom diameter:
780mm, yield per minute: 0.21m, back beam height :+1, warp stop frame height: 0, comprehensive flat height: 1-8 pages: 139mm, 9-10 page:
144mm。
In addition, in warping process, using bull part, few warp beam, equal tension warping on Benniger high-speed warping machine, control
Speed processed: 950 ms/min, warping head part: 728*14, warped length: 20000 meters, tension rail is opened delay time: 3 seconds, tension
Yarn gripper, which is opened, to postpone: 2 seconds, tension rail position: 1.5mm, rolling density: 0.8kg/dm3。
In denting process, control reed width: 156.1 centimetres, every dent penetrates number: ground tissue: 4/reed, side texture 4/
Reed is gaited: ground tissue 12345678, side texture 9 10.
Obtain fabric: close radial diameter is 665/10CM, and close broadwise diameter is 275/10CM, the ultimate strength of fabric: diameter
Xiang Jingxiang >=1460, broadwise >=520.The sense of touch of the existing pure wool of the fabric, it is well-pressed and have micro-elasticity；There are exquisiteness, the cunning of pure cotton again
Glutinous, lines is clearly, glossiness, color is splendid gorgeous after dyeing, and wool-like effect is excellent.
According in " People's Republic of China's textile industry standard " FZ/T 13034-2016 combed cotton with wool blended
Painting cloth, the fabric need to meet this several breadth, density and ultimate strength performance detections, and specific detection method is as follows:
1, breadth detects: the fabric sample under relaxed state being placed in smooth flat under standard atmospheric conditions, is used
Steel ruler measures the length and breadth of fabric, and the measurement for fabric length, fabric length sectional measures when necessary, each segment length
The sum of be sample total length.
2, Density Detection: according to any one in the feature selecting following three method of fabric.
Method A: decomposing the fabric sample of predetermined size, counts yarn radical, converts to the yarn radical of 10cm length.
Method B: the yarn radical that measurement is seen in pouce glass window, conversion to yarn root contained in 10cm length
Number.
Method C: fabric radial direction is measured using mobile Density mirror or ties up the yarn radical into certain length, is converted
Yarn radical in 10cm length.
3, ultimate strength detects: the sample of predetermined size is stretched with constant elongation rate until disconnected de-, record ultimate strength
And extension at break, if it is desired, also can record disconnected de- strength and disconnected de- elongation.
Specific detection data is as follows:
In addition, further including other steps in production method, the following provide three embodiments:
Embodiment one:
It further include processing of singing in production method, processing of singing, which is located between weaving and perching, to be carried out, specifically by
Tenslator makes cloth be at exceptionally straight state, then by cloth bypass red-hot metal roller surface, make fabric with
The contact of metal roller, wherein the front and back of fabric is successively contacted with the surface of metal roller, the temperature of metal roller surface
It is 100 DEG C, two metal roller burning-off surface villus, the surface of metal roller needs that metal will be bonded in except Slag treatment simultaneously
The fusing residue of the hair of roller surface removes.By processing of singing, it can be effectively removed the villus of web surface, to make fabric
Feel more preferably, and it is more attractive.
In addition, further including cleaning treatment, cleaning treatment is located at processing of singing and carries out later, fills specifically by tension force
Setting makes cloth be in exceptionally straight state, and then by washing pool, water temperature is maintained between 30 DEG C, cleaning agent is contained in washing pool,
Vibrating roller is provided in pond, fabric bypasses vibrating roller, and is bonded with the surface of vibrating roller, and the vibration frequency of vibrating roller is 300
Secondary/second after fabric comes out out of washing pool, handles using water flushing, is finally dried.By cleaning treatment, can incite somebody to action
After processing of singing, the villus residue for being pasted onto the fusing of web surface is cleaned, simultaneously, moreover it is possible to which it is some right on fabric to remove
The unfavorable chemical substance of body, avoids human body when wearing fabric, and chemical substance volatilization causes harm to the human body, the height of vibrating roller
Frequency vibration can make fabric in a small range and water Fast Collision, so that chemical substance be accelerated to be detached from fabric.
The parts by weight of cleaning agent form are as follows: and 10 parts of stearic acid, 15 parts of anhydrous sodium sulfate, 1 part of sodium carbonate, vegetalitas anti-corrosion
5 parts of agent, 3 parts of soap base, double 6 parts of the stearates of polyethylene glycol, 12 parts of neopelex, 30 parts of water.
Embodiment two:
It further include processing of singing in production method, processing of singing, which is located between weaving and perching, to be carried out, specifically by
Tenslator makes cloth be at exceptionally straight state, then by cloth bypass red-hot metal roller surface, make fabric with
The contact of metal roller, wherein the front and back of fabric is successively contacted with the surface of metal roller, the temperature of metal roller surface
It is 120 DEG C, two metal roller burning-off surface villus, the surface of metal roller needs that metal will be bonded in except Slag treatment simultaneously
The fusing residue of the hair of roller surface removes.By processing of singing, it can be effectively removed the villus of web surface, to make fabric
Feel more preferably, and it is more attractive.
In addition, further including cleaning treatment, cleaning treatment is located at processing of singing and carries out later, fills specifically by tension force
Setting makes cloth be in exceptionally straight state, and then by washing pool, water temperature is maintained between 40 DEG C, cleaning agent is contained in washing pool,
Vibrating roller is provided in pond, fabric bypasses vibrating roller, and is bonded with the surface of vibrating roller, and the vibration frequency of vibrating roller is 400
Secondary/second after fabric comes out out of washing pool, handles using water flushing, is finally dried.By cleaning treatment, can incite somebody to action
After processing of singing, the villus residue for being pasted onto the fusing of web surface is cleaned, simultaneously, moreover it is possible to which it is some right on fabric to remove
The unfavorable chemical substance of body, avoids human body when wearing fabric, and chemical substance volatilization causes harm to the human body, the height of vibrating roller
Frequency vibration can make fabric in a small range and water Fast Collision, so that chemical substance be accelerated to be detached from fabric.
The parts by weight of cleaning agent form are as follows: and 11 parts of stearic acid, 16 parts of anhydrous sodium sulfate, 2 parts of sodium carbonate, vegetalitas anti-corrosion
7 parts of agent, 5 parts of soap base, double 8 parts of the stearates of polyethylene glycol, 14 parts of neopelex, 40 parts of water.
Embodiment three: further including processing of singing in production method, and processing of singing, which is located between weaving and perching, to be carried out,
So that cloth is at exceptionally straight state specifically by tenslator, cloth is then bypassed into red-hot metal roller table
Face contacts fabric with metal roller, and wherein the front and back of fabric is successively contacted with the surface of metal roller, metal roller
The temperature on surface is 130 DEG C, two metal roller burning-off surface villus, and the surface of metal roller is needed simultaneously except Slag treatment, will
It is bonded in the fusing residue removal of the hair of metal roller surface.By processing of singing, it can be effectively removed the villus of web surface,
To make the feel of fabric more preferably, and it is more attractive.
In addition, further including cleaning treatment, cleaning treatment is located at processing of singing and carries out later, fills specifically by tension force
Setting makes cloth be in exceptionally straight state, and then by washing pool, water temperature is maintained between 50 DEG C, cleaning agent is contained in washing pool,
Vibrating roller is provided in pond, fabric bypasses vibrating roller, and is bonded with the surface of vibrating roller, and the vibration frequency of vibrating roller is 500
Secondary/second after fabric comes out out of washing pool, handles using water flushing, is finally dried.By cleaning treatment, can incite somebody to action
After processing of singing, the villus residue for being pasted onto the fusing of web surface is cleaned, simultaneously, moreover it is possible to which it is some right on fabric to remove
The unfavorable chemical substance of body, avoids human body when wearing fabric, and chemical substance volatilization causes harm to the human body, the height of vibrating roller
Frequency vibration can make fabric in a small range and water Fast Collision, so that chemical substance be accelerated to be detached from fabric.
The parts by weight of cleaning agent form are as follows: and 12 parts of stearic acid, 17 parts of anhydrous sodium sulfate, 3 parts of sodium carbonate, vegetalitas anti-corrosion
8 parts of agent, 6 parts of soap base, double 10 parts of the stearates of polyethylene glycol, 15 parts of neopelex, 50 parts of water.
In addition, to compare the difference of the web surface villus between existing fabric and fabric of the present invention, for three
Embodiment has respectively carried out experiment test, specific detection method are as follows: with detecting instrument to the suede of 20 pieces of existing web surfaces
Approximate number amount is detected, and is obtained average value, while detecting to the villus quantity of 20 pieces of web surfaces of the present invention, is obtained
Average value out, the following are the data of Experimental comparison:
Embodiment one:
Embodiment two:
Embodiment three:
In addition, to compare the difference of the contained chemical substance being harmful to the human body between existing fabric and fabric of the present invention
It is different, experiment test, detection method are as follows: fabric in the market is individually positioned in closed appearance have respectively been carried out for three embodiments
It in device and heats, is in temperature in container between 40 DEG C -50 DEG C, then after heating 1 hour, after 2 hours and 3 hours
Afterwards, the content of harmful chemical in the air of closed container is detected with detecting instrument, this experiment is using 20 pieces on the market
Cloth repeats aforesaid operations respectively, finally obtains average value；Then it is repeated again with 20 pieces of fabrics of the present invention above-mentioned same
Step obtains average value, and the following are the data of Experimental comparison:
Embodiment one:
Embodiment two:
Embodiment three:
In short, the foregoing is merely illustrative of the preferred embodiments of the present invention, it is not intended to limit the invention, it is all in the present invention
Spirit and principle within made any modifications, equivalent replacements, and improvements etc., should be included in protection scope of the present invention it
It is interior.
Claims (10)
1. a kind of llama fabric, which is characterized in that the fabric combines right tiltedly cord small jacquard tissue by warp thread and weft yarn,
It is woven into the super tight structure that aggregate scheduling is 110%, wherein warp thread twists w/c50/50 27.8tex single thread using S, and weft yarn uses
Z twists w/c50/50 41.6tex.
2. llama fabric according to claim 1, it is characterised in that: the close radial direction diameter is 665/10CM, institute
It is 275/10CM that it is close, which to state broadwise diameter,.
3. llama fabric according to claim 2, it is characterised in that: the ultimate strength of fabric: through to >=1460, latitude
To >=520.
4. the production method of llama fabric according to claim 3, it is characterised in that: warp thread in warping, sizing, wear
Weaving, perching together with weft yarn again after reed.
5. the production method of llama fabric according to claim 4, it is characterised in that: in sizing operation, slurry is matched
Side are as follows: PVA-177 25kg, converted starch 75kg, auxiliary agent 20kg, cured 3kg, after adding water, through mashing off, bored slurry time 15min,
115 DEG C of bored slurry temperature degree is tuned into the slurries of solid content 12%, viscosity 7.2 ± 0.1 (3# funnel), pH value 7, volume 850L.
6. the production method of llama fabric according to claim 5, it is characterised in that: weaving process is knitted using jet
Machine, using big Zhang Li, high speed operation, the main burner of air-jet loom installs gas clamp device, increases the chucking power that yarn passes through, right
Side goes out shed open using 4 sections of variation waste selvage yarn threading methods.
7. the production method of llama fabric according to claim 6, it is characterised in that: use bull in warping process
Part, few warp beam, equal tension warping on Benniger high-speed warping machine.
8. the production method of the llama fabric according to any one of claim 4-7, it is characterised in that: further include burning
Hair processing, the processing of singing, which is located between the weaving and the perching, to be carried out, and makes cloth specifically by tenslator
Material is at exceptionally straight state, and cloth is then bypassed red-hot metal roller surface, contacts fabric with metal roller, wherein
The front and back of fabric is successively contacted with the surface of metal roller, and the temperature of metal roller surface is 100-130 DEG C, two gold
Belong to roller burning-off surface villus, the surface of metal roller needs that the hair of metal roller surface will be bonded in except Slag treatment simultaneously
Melt residue removal.
9. the production method of llama fabric according to claim 8, it is characterised in that: it further include cleaning treatment, institute
It states after cleaning treatment is located at the processing of singing and carries out, so that cloth is in exceptionally straight state specifically by tenslator,
Then by washing pool, water temperature is maintained between 30-50 DEG C, cleaning agent is contained in washing pool, is provided with vibrating roller in pond,
Fabric bypasses vibrating roller, and be bonded with the surface of vibrating roller, and the vibration frequency of vibrating roller is 300-500 times/seconds, and fabric is from water
After being come out in wash pool, handles using water flushing, be finally dried.
10. the production method of llama fabric according to claim 9, it is characterised in that: the weight of the cleaning agent
Number composition are as follows: 10-12 parts of stearic acid, 15-17 parts of anhydrous sodium sulfate, 1-3 parts of sodium carbonate, 5-8 parts of vegetable preservative,
3-6 parts of soap base, double 6-10 parts of the stearates of polyethylene glycol, 12-15 parts of neopelex, 30-50 parts of water.