CN110253109B - 一种CCSB钢+1Cr18NI9TI异种钢的焊接方法 - Google Patents

一种CCSB钢+1Cr18NI9TI异种钢的焊接方法 Download PDF

Info

Publication number
CN110253109B
CN110253109B CN201910631805.9A CN201910631805A CN110253109B CN 110253109 B CN110253109 B CN 110253109B CN 201910631805 A CN201910631805 A CN 201910631805A CN 110253109 B CN110253109 B CN 110253109B
Authority
CN
China
Prior art keywords
welding
steel
1cr18ni9ti
ccsb
dissimilar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201910631805.9A
Other languages
English (en)
Other versions
CN110253109A (zh
Inventor
熊宏权
徐仁
业秋娜
杨晗
甘超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cssc Guijiang Shipbuilding Co ltd
Original Assignee
Cssc Guijiang Shipbuilding Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cssc Guijiang Shipbuilding Co ltd filed Critical Cssc Guijiang Shipbuilding Co ltd
Priority to CN201910631805.9A priority Critical patent/CN110253109B/zh
Publication of CN110253109A publication Critical patent/CN110253109A/zh
Application granted granted Critical
Publication of CN110253109B publication Critical patent/CN110253109B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种CCSB钢+1Cr18NI9TI异种钢的焊接方法，将CCSB钢与1Cr18NI9TI异种钢的板缝对接采用无间隙安装，局部间隙值控制在0‑2mm，错边量控制在0‑1mm，然后在板缝背面进行定位焊，定位焊长度20mm；板缝采用机械加工的形式开坡口，1Cr18NI9TI异种钢侧不开坡口，CCSB钢侧开“K”型坡口,坡口角度65°±5°，然后打磨坡口及其两侧30mm范围，以及清除背面焊缝20mm范围内氧化膜及污物，直至露出金属光泽；本发明提供的CCSB钢+1Cr18NI9TI异种钢的焊接方法，焊缝无表面气孔、焊瘤及表面裂纹，磁导率能够满足使用要求。

Description

一种CCSB钢+1Cr18NI9TI异种钢的焊接方法
技术领域
本发明属于焊接技术领域，具体涉及一种CCSB钢+1Cr18NI9TI异种钢的焊接方法。
背景技术
对于CCSB钢+异种钢材料的焊接，以往都采用焊条进行多层多道焊，这种焊接方法存在诸多问题：1.由于材料本身的特性，磁偏吹现象严重，焊接操作困难，尤其立焊位置操作难度更大，焊工劳动强度大；2.因1Cr18NI9TI异种钢具有导热性差、线膨胀系数大的特点，故焊接过程中极易产生焊接变形，尤其是薄板焊接时会出现明显挠曲变形；由于材料的固有特性，CCSB钢+1Cr18NI9TI异种钢材料采用焊接时，磁导率难以保证。
发明内容
本发明的目的在于提供一种CCSB钢+1Cr18NI9TI异种钢的焊接方法，旨在解决现有技术中CCSB钢与异种钢焊接时容易出现焊接变形、磁导率难以保证的问题。
为实现上述技术目的，达到上述技术效果，本发明通过以下技术方案实现：
本发明提供了一种CCSB钢+1Cr18NI9TI异种钢的焊接方法，采用适合1Cr18NI9TI异种钢焊接的不锈钢焊条A307，焊接设备，按照相应的焊接参数，进行CCSB钢+1Cr18Ni9Ti异种钢的平对接的焊接，具体焊接方法如下：
1)、焊接条件选用
①焊接设备选用：选用AT320型直流电焊机；
②焊接材料选用：选用直径为3.2mm的不锈钢焊条A307；
③焊接参数：
Figure BDA0002128924730000021
2)、焊接程序
①将CCSB钢与1Cr18NI9TI异种钢的板缝对接采用无间隙安装，局部间隙值控制在0-2mm，错边量控制在0-1mm，然后在板缝背面进行定位焊，定位焊长度20mm；
②板缝采用机械加工的形式开坡口，1Cr18NI9TI异种钢侧不开坡口，CCSB钢侧开“K”型坡口,坡口角度65°±5°，然后打磨坡口及其两侧30mm范围，以及清除背面焊缝20mm范围内氧化膜及污物，直至露出金属光泽；
③CCSB钢与1Cr18NI9TI异种钢对接缝的焊接，采用多层多道焊，每层焊道的厚度不大于3mm，其工艺为：
A.多层焊施焊前，每层焊道间用不锈钢丝刷清理,避免弧坑裂纹的产生；
B.焊接时采用小电流、短电弧、快速焊，需要摆动时摆动宽度控制在2.5倍焊条直径范围内；
C.焊道层间温度小于100度；
D.正面施焊，反面进行碳弧气刨清根，清根后再用砂轮机打磨，直至露出金属光泽后再焊下一道焊道，且各焊道层焊接接头相互错开。
优选地，采用红外线测温仪检测焊缝层和焊道间的温度。
本发明的优点：
本发明提供的CCSB钢+1Cr18NI9TI异种钢的焊接方法，焊缝无表面气孔、焊瘤及表面裂纹，磁导率能够满足使用要求。
附图说明
图1为本发明所述的CCSB钢+1Cr18Ni9Ti异种钢平对接坡口的结构示意图；
图2为本发明所述的平对接坡口焊道层的结构示意图。
具体实施方式
为了使本发明的目的，技术方案及优点更加清楚明白，以下结合附图通过具体实施例对本发明进一步详细说明。应当理解，此处所描述的具体实施例仅用以解释本发明，并不用于限定本发明。
实施例1：CCSB钢+1Cr18Ni9Ti异种钢的平对接的焊接方法；
(1)焊接设备为：AT320型直流电焊机；
(2)焊丝为：直径为3.2mm的不锈钢焊条A307；
(3)焊接参数为：
Figure BDA0002128924730000031
焊接过程：由两名持证焊工配合，如图1所示，按65°K型坡口，焊接钢板厚度14mm，装配间隙0-2mm的要求组装CCSB钢+1Cr18Ni9Ti异种钢，并对CCSB钢+1Cr18Ni9Ti异种钢实施横向加强，以防焊后变形；CCSB钢+1Cr18Ni9Ti异种钢组装完成后，按照上述要求调节好设备及参数，在K型坡口处布置7个焊道层，如图2所示，焊接焊道层时进行左右对称施焊，K型坡口焊接一个面1-3焊道层之后(打底焊)焊接其余4-7焊道层(盖面焊)，施焊期间保持焊道层间温度小于100度，K型坡口面焊缝共分二层焊完，在坡口背面采用碳弧气刨清根，砂轮机打磨坡口直至露出金属光泽后，按焊接电流120-130A、焊接电压23-25V的工艺参数进行焊接。
以下是对上述实施例1的焊接效果进行外观检查、X射线拍片、力学性能测试。
1.外观检查(评定标准：GB/T3802-1997)：
Figure BDA0002128924730000041
2.X射线拍片(评定标准：GB/T3558-94)：
经X射线拍片，焊缝无夹渣、气孔、裂纹等缺陷，焊缝质量评定合格。
3.力学性能检测(评定标准：GJB64.1A-97)：
Figure BDA0002128924730000042
根据以上检测结果，焊接接头的外观及内部质量、力学性能均满足相关标准要求。

Claims (2)

1.一种CCSB钢+1Cr18NI9TI异种钢的焊接方法，其特征在于：采用适合1Cr18NI9TI异种钢焊接的不锈钢焊条A307，焊接设备，按照相应的焊接参数，进行CCSB钢+1Cr18Ni9Ti异种钢的平对接的焊接，具体焊接方法如下：
1)、焊接条件选用
①焊接设备选用：选用AT320型直流电焊机；
②焊接材料选用：选用直径为3.2mm的不锈钢焊条A307；
③焊接参数：
Figure FDA0002128924720000011
2)、焊接程序
①将CCSB钢与1Cr18NI9TI异种钢的板缝对接采用无间隙安装，局部间隙值控制在0-2mm，错边量控制在0-1mm，然后在板缝背面进行定位焊，定位焊长度20mm；
②板缝采用机械加工的形式开坡口，1Cr18NI9TI异种钢侧不开坡口，CCSB钢侧开“K”型坡口,坡口角度65°±5°，然后打磨坡口及其两侧30mm范围，以及清除背面焊缝20mm范围内氧化膜及污物，直至露出金属光泽；
③CCSB钢与1Cr18NI9TI异种钢对接缝的焊接，采用多层多道焊，每层焊道的厚度不大于3mm，其工艺为：
A.多层焊施焊前，每层焊道间用不锈钢丝刷清理,避免弧坑裂纹的产生；
B.焊接时采用小电流、短电弧、快速焊，需要摆动时摆动宽度控制在2.5倍焊条直径范围内；
C.焊道层间温度小于100度；
D.正面施焊，反面进行碳弧气刨清根，清根后再用砂轮机打磨，直至露出金属光泽后再焊下一道焊道，且各焊道层焊接接头相互错开。
2.如权利要求1所述的CCSB钢+1Cr18NI9TI异种钢的焊接方法，其特征在于：采用红外线测温仪检测焊缝层和焊道间的温度。
CN201910631805.9A 2019-07-12 2019-07-12 一种CCSB钢+1Cr18NI9TI异种钢的焊接方法 Active CN110253109B (zh)