CN110230208A - A kind of highly effective flame-retardant antibacterial and mouldproof release negative oxygen ion textile fabric - Google Patents
A kind of highly effective flame-retardant antibacterial and mouldproof release negative oxygen ion textile fabric Download PDFInfo
- Publication number
- CN110230208A CN110230208A CN201910581008.4A CN201910581008A CN110230208A CN 110230208 A CN110230208 A CN 110230208A CN 201910581008 A CN201910581008 A CN 201910581008A CN 110230208 A CN110230208 A CN 110230208A
- Authority
- CN
- China
- Prior art keywords
- fabric
- cloth
- antibacterial
- mouldproof
- highly effective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of highly effective flame-retardant antibacterial and mouldproofs to discharge negative oxygen ion textile fabric, belongs to textile fabric manufacturing technology field；A kind of highly effective flame-retardant antibacterial and mouldproof release negative oxygen ion textile fabric, comprising the following steps: spinning, yarn colouring pretreatment, braiding, the processing of base fabric fabric, perching, Cloth Cutting, whole boiling hot, reel factory；The present invention contaminates yarn processed by this method; the sodium chloride of addition can effectively play the role of fixation; and then the case where making fabric be not in colour fading; extend the service life of fabric; the textile fabric made of this method has the function of fire-retardant, antibacterial, mould proof; and then make the fabric when encountering fire; the personal safety of user is effectively protected; it can effectively prevent fabric from making moist by antibacterial and mouldproof layer simultaneously mould proof; and then a large amount of bacteriums will not be bred, it ensure that the health of human body of user.
Description
Technical field
The present invention relates to textile fabric manufacturing technology fields more particularly to a kind of highly effective flame-retardant antibacterial and mouldproof to discharge negative oxygen
Ion textile fabric.
Background technique
Textile fabric has two class of Weft knitted fabric and warp knitted fabric, Weft knitted fabric is normal by method for weaving point
With low-elasticity terylene fibre or special-shaped dacron thread, Polyamide Yarns, cotton yarn, wool yarn etc. for raw material, using plain stitch, change plain stitch,
Rib-loop plain stitch, double rib plain stitch, figured texture weave, pile stitch etc. weave on various weft machines.
The manufacturing process of textile fabric in the prior art mainly include spinning, braiding, perching, cutting, sewing, it is whole scald,
It examines；Textile fabric is widely used in apparel modeling design.
But the performance of textile fabric in the prior art is relatively simple, when encountering fire prevention situation, can not play isolation fire
The effect in source, and be possible to that the sprawling of fire source can be accelerated, it may threaten the personal safety of user, in wet environment, put
It after setting a period of time, may make moist mouldy, influence the normal use of user, and textile fabric in the prior art does not resist
Bacterium performance may carry a large amount of bacteriums in use, may will affect the health of human body of user, and then a kind of efficient
The mould proof release negative oxygen ion textile fabric of flame-proof antibiotic is particularly important.
Summary of the invention
The purpose of the present invention is to solve the problems of the prior art, and a kind of highly effective flame-retardant antibacterial and mouldproof proposed is applied
Put negative oxygen ion textile fabric.
To achieve the goals above, present invention employs following technical solutions:
A kind of highly effective flame-retardant antibacterial and mouldproof release negative oxygen ion textile fabric, specifically includes the following steps:
S1, spinning, by plant fiber spun yarn；
S2, yarn colouring pretreatment；
S3, braiding, will treated that yarn puts is woven into base fabric fabric on the textile machine；
S4, the processing of base fabric fabric: key step includes fitting fireprotection layer cloth, antibacterial and mouldproof layer cloth；
S5, perching；
S6, Cloth Cutting: by the Cloth Cutting completed the process at required size；
S7, it is whole scald: by after cutting cloth press；
S8, reel factory: by the cloth roll after ironing on fabric drum.
Preferably, in step s2 yarn colouring pretreatment the following steps are included:
A, 300-500g dyestuff is placed in dye bucket, 0.8-1L warm water is added and washes open, is stirred evenly using stirring rod；
B, 30-40L boiled water is added；
C, yarn is placed in dye bucket, and be stirred continuously；
D, yarn is taken out, it is cooling to place 20-40min；
E, the loose colour on yarn is rinsed using clear water；
F, temperature is placed to be 8-10 DEG C, dry under the ventilated environment that humidity is 40-60%RH.
Preferably, in step s4 base fabric fabric processing the following steps are included:
A, by treated, base fabric fabric is placed on uncoiling machine；
B, it glues: adhesive glue being applied to base fabric web surface using gluing coating head；
C, fireprotection layer cloth, the placement of antibacterial and mouldproof layer cloth are coated on the cloth of adhesive glue；
D, base fabric cloth, fireprotection layer cloth, antibacterial and mouldproof layer cloth are placed on to press on calender and are bonded；
E, it is sent into baking oven and dries；
F, the base fabric cloth of drying, fireprotection layer cloth, antibacterial and mouldproof layer cloth are placed on compounding machine and are bonded.
Preferably, it is additionally added sodium chloride 40-60g.
Preferably, fireprotection layer cloth is fireproof cloth made of fire-retardant pe material in step s4.
Preferably, the antibacterial and mouldproof cloth in step s4 is bamboo charcoal fiber cloth.
Preferably, the glue in step B is the polyurethane PU for mixing the crosslinking agent of butanone and 6%-10% of 20%-30%
Glue.
Preferably, oven temperature is 50-70 DEG C in step E, drying time 20-30min.
Preferably, the calender is four-roll calender.
Compared with prior art, the present invention provides a kind of highly effective flame-retardant antibacterial and mouldproofs to discharge negative oxygen ion textile face
Material, have it is following the utility model has the advantages that
1, the highly effective flame-retardant antibacterial and mouldproof discharges negative oxygen ion textile fabric and 400g dyestuff is placed on dye bucket before manufacture
In, 0.9L warm water is added, is stirred evenly using stirring rod, 35L boiled water is added, adds sodium chloride 50g, yarn is placed on and is matched
It sets in the dye bucket of good colourant, is stirred continuously using stirring rod, taken out after dyeing 30min, spread out, use after cooling placement 30min
Clear water washes away the loose colour on cloth, and the cloth after flushing is placed under the ventilated environment that temperature is 9 DEG C, humidity is 50%RH and is dried in the air
It shines 1 day, yarn processed is contaminated by this method, the sodium chloride of addition can effectively play the role of fixation, and then make fabric will not
The case where fading extends the service life of fabric.
2, the highly effective flame-retardant antibacterial and mouldproof discharges negative oxygen ion textile fabric, and the yarn after dyeing is put on the textile machine
It is woven into base fabric fabric, the base fabric fabric after processing is placed on uncoiling machine, adhesive glue is applied to base using gluing coating head
Fireprotection layer cloth, antibacterial and mouldproof layer cloth are placed two surface of basic fabric, by base fabric cloth, fireprotection layer by two surface of cloth fabric
Cloth, antibacterial and mouldproof layer cloth, which are placed on calender, presses bonding, and then it is made tentatively to be formed, and preliminary molding fabric is sent into
It is dried in baking oven, the base fabric cloth of drying, fireprotection layer cloth, antibacterial and mouldproof layer cloth is placed on compounding machine and is bonded, and then shape
At composite textile, the textile fabric made of this method has the function of fire-retardant, antibacterial, mould proof, and then makes the fabric
When encountering fire, the personal safety of user is effectively protected, while fabric can effectively be prevented by antibacterial and mouldproof layer
It makes moist mould proof, and then a large amount of bacteriums will not be bred, ensure that the health of human body of user.
3, the highly effective flame-retardant antibacterial and mouldproof discharges negative oxygen ion textile fabric, and the textile fabric after fitting will pass through
Inspection process is examined, and underproof cloth is filtered out, and using the qualified cloth of presses ironing, the cloth after ironing will pass through volume
Cloth machine is rolled up on fabric drum, and then is dispatched from the factory and sold.
Specific embodiment
Below in conjunction in the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
Embodiment:
A kind of highly effective flame-retardant antibacterial and mouldproof release negative oxygen ion textile fabric, specifically includes the following steps:
S1, spinning, by plant fiber spun yarn；
S2, yarn colouring pretreatment；
S3, braiding, will treated that yarn puts is woven into base fabric fabric on the textile machine；
S4, the processing of base fabric fabric: key step includes fitting fireprotection layer cloth, antibacterial and mouldproof layer cloth；
S5, perching；
S6, Cloth Cutting: by the Cloth Cutting completed the process at required size；
S7, it is whole scald: by after cutting cloth press；
S8, reel factory: by the cloth roll after ironing on fabric drum.
In step s2 yarn colouring pretreatment the following steps are included:
A, 400g dyestuff is placed in dye bucket, 0.9L warm water is added and washes open, is stirred evenly using stirring rod；
B, 35L boiled water is added；
C, yarn is placed in dye bucket, and be stirred continuously；
D, yarn is taken out, it is cooling to place 30min；
E, the loose colour on yarn is rinsed using clear water；
F, temperature is placed to be 9 DEG C, dry under the ventilated environment that humidity is 50%RH.
In step s4 base fabric fabric processing the following steps are included:
A, by treated, base fabric fabric is placed on uncoiling machine；
B, it glues: adhesive glue being applied to base fabric web surface using gluing coating head；
C, fireprotection layer cloth, the placement of antibacterial and mouldproof layer cloth are coated on the cloth of adhesive glue；
D, base fabric cloth, fireprotection layer cloth, antibacterial and mouldproof layer cloth are placed on to press on calender and are bonded；
E, it is sent into baking oven and dries；
F, the base fabric cloth of drying, fireprotection layer cloth, antibacterial and mouldproof layer cloth are placed on compounding machine and are bonded.
It is additionally added sodium chloride 50g.
Fireprotection layer cloth is fireproof cloth made of fire-retardant pe material in step s4.
Antibacterial and mouldproof cloth in step s4 is bamboo charcoal fiber cloth.
Glue in step B is the polyurethane PU glue for mixing 25% butanone and 8% crosslinking agent.
Oven temperature is 60 DEG C in step E, drying time 25min.
Calender is four-roll calender.
The highly effective flame-retardant antibacterial and mouldproof discharges negative oxygen ion textile fabric and 400g dyestuff is placed on dye before manufacture
In bucket, 0.9L warm water is added, is stirred evenly using stirring rod, 35L boiled water is added, adds sodium chloride 50g, yarn is placed on
It in the dye bucket for configuring good colourant, is stirred continuously using stirring rod, is taken out after dyeing 30min, spread out, make after cooling placement 30min
The loose colour on yarn is washed away with clear water, the yarn after flushing is placed under the ventilated environment that temperature is 9 DEG C, humidity is 50%RH
Sunning 1 day contaminates yarn processed by this method, and the sodium chloride of addition can effectively play the role of fixation, and then after making processing
Fabric the case where being not in colour fading, extend the service life of fabric.
Yarn after dyeing is put and is woven into base fabric fabric on the textile machine, the base fabric fabric after processing is placed in debatching
On machine, adhesive glue is applied to two surface of base fabric fabric using gluing coating head, fireprotection layer cloth, antibacterial and mouldproof layer cloth are placed
Base fabric cloth, fireprotection layer cloth, antibacterial and mouldproof layer cloth are placed on calender and press bonding, in turn by two surface of basic fabric
So that it is tentatively formed, preliminary molding fabric is sent into baking oven and is dried, by the base fabric cloth of drying, fireprotection layer cloth, antibacterial
Mould proof layer cloth, which is placed on compounding machine, to be bonded, and then forms composite textile, and the textile fabric made of this method has
Fire-retardant, antibacterial, mould proof function, and then make the fabric when encountering fire, the personal safety of user is effectively protected, simultaneously
It can effectively prevent fabric from making moist by antibacterial and mouldproof layer mould proof, and then a large amount of bacteriums will not be bred, ensure that user's
Health of human body.
Textile fabric after fitting will be examined by inspection process, underproof cloth be filtered out, using presses
Qualified cloth is pressed, the cloth after ironing will be rolled up on fabric drum by batcher, and then dispatch from the factory and sell.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (9)
1. a kind of highly effective flame-retardant antibacterial and mouldproof discharges negative oxygen ion textile fabric, which is characterized in that specifically includes the following steps:
S1, spinning, by plant fiber spun yarn；
S2, yarn colouring pretreatment；
S3, braiding, will treated that yarn puts is woven into base fabric fabric on the textile machine；
S4, the processing of base fabric fabric: key step includes fitting fireprotection layer cloth, antibacterial and mouldproof layer cloth；
S5, perching；
S6, Cloth Cutting: by the Cloth Cutting completed the process at required size；
S7, it is whole scald: by after cutting cloth press；
S8, reel factory: by the cloth roll after ironing on fabric drum.
2. a kind of highly effective flame-retardant antibacterial and mouldproof according to claim 1 discharges negative oxygen ion textile fabric, feature exists
In, in step s2 yarn colouring pretreatment the following steps are included:
300-500g dyestuff is placed in dye bucket, 0.8-1L warm water is added and washes open, is stirred evenly using stirring rod；
30-40L boiled water is added；
Yarn is placed in dye bucket, and is stirred continuously；
Yarn is taken out, it is cooling to place 20-40min；
The loose colour on yarn is rinsed using clear water；
F, temperature is placed to be 8-10 DEG C, dry under the ventilated environment that humidity is 40-60%RH.
3. a kind of highly effective flame-retardant antibacterial and mouldproof according to claim 2 discharges negative oxygen ion textile fabric, feature exists
In, in step s4 base fabric fabric processing the following steps are included:
A, by treated, base fabric fabric is placed on uncoiling machine；
B, it glues: adhesive glue being applied to base fabric web surface using gluing coating head；
C, fireprotection layer cloth, the placement of antibacterial and mouldproof layer cloth are coated on the cloth of adhesive glue；
D, base fabric cloth, fireprotection layer cloth, antibacterial and mouldproof layer cloth are placed on to press on calender and are bonded；
E, it is sent into baking oven and dries；
F, the base fabric cloth of drying, fireprotection layer cloth, antibacterial and mouldproof layer cloth are placed on compounding machine and are bonded.
4. a kind of highly effective flame-retardant antibacterial and mouldproof according to claim 2 discharges negative oxygen ion textile fabric, feature exists
In being additionally added sodium chloride 40-60g.
5. a kind of highly effective flame-retardant antibacterial and mouldproof according to claim 3 discharges negative oxygen ion textile fabric, feature exists
In fireprotection layer cloth is fireproof cloth made of fire-retardant pe material in step s4.
6. a kind of highly effective flame-retardant antibacterial and mouldproof according to claim 3 discharges negative oxygen ion textile fabric, feature exists
In the antibacterial and mouldproof cloth in step s4 is bamboo charcoal fiber cloth.
7. a kind of highly effective flame-retardant antibacterial and mouldproof according to claim 3 discharges negative oxygen ion textile fabric, feature exists
In the glue in step B is the polyurethane PU glue for mixing the crosslinking agent of butanone and 6%-10% of 20%-30%.
8. a kind of highly effective flame-retardant antibacterial and mouldproof according to claim 3 discharges negative oxygen ion textile fabric, feature exists
In oven temperature is 50-70 DEG C in step E, drying time 20-30min.
9. a kind of highly effective flame-retardant antibacterial and mouldproof according to claim 3 discharges negative oxygen ion textile fabric, feature exists
In the calender is four-roll calender.