CN103129082A - Processing method of antibiotic crease-resist fabrics - Google Patents
Processing method of antibiotic crease-resist fabrics Download PDFInfo
- Publication number
- CN103129082A CN103129082A CN201110382417.5A CN201110382417A CN103129082A CN 103129082 A CN103129082 A CN 103129082A CN 201110382417 A CN201110382417 A CN 201110382417A CN 103129082 A CN103129082 A CN 103129082A
- Authority
- CN
- China
- Prior art keywords
- antibiotic
- processing method
- fabrics
- fabric
- resist
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a processing method of antibiotic crease-resist fabrics. The processing method of the antibiotic crease-resist fabrics comprises the following steps: a) preparing an antibiotic fabric layer, b) preparing a crease-resist layer, c) fitting of a functional fabric layer, d) post-processing of fabrics. The invention discloses the processing method of the antibiotic crease-resist fabrics, the processing method of the antibiotic crease-resist fabrics is reasonable in process arrangement and moderate in preparing cost, the crease-resist effect of the prepared fabrics is remarkable, the air permeability is excellent, during the using process, the fabrics can return straight naturally along with the increasing of temperature, the good look performance of clothes is effectively ensured, and by means of the typical antibiotic and deodorizing effects of internal layer fabrics, the fabrics are enabled to be comprehensive in function and wide in application range.
Description
Technical field
The present invention relates to a kind of fabric, relate in particular to a kind of processing method with wrinkle resistant antibiotic facing material of memory function, belong to fabric class technical field.
Background technology
With the quickening pace of modern life, a lot of people have no time to arrange the clothing of oneself, and are if all take dry-cleaning away, not only consuming time but also increase living cost.Therefore, the people on work position of running often wear the shirt of fold, slack and undisciplined overcoat, and whole people seems to lack spirit, has affected to a certain extent individual overall image.Popular non-ironing shirt, wrinkle resistant overcoat on the market, mostly use some special process, for example: fabric is contaminated in special dip dyeing liquid for shell, make face liber have certain intensity and shape, re-use steam shaping, make fabric still can keep straight elevator later in washing, but the fabric durability of this PROCESS FOR TREATMENT is mostly all lower, after washing repeatedly, fabric has distortion in various degree, and clothing is lower service life; Have again, some technique is to smear the viscose glues such as PU, PVC on the fabric top layer, form wrinkle resistant coating, the wrinkle resistant performance of fabric is increased substantially, durability also satisfies people's instructions for use, but it is unsatisfactory to process in this way the performance of later fabric aspect gas permeability and absorption of perspiration, the long-time fabric of this material of wearing, for some skins than more sensitive crowd, tend to occur the phenomenons such as allergy, decortication, to the healthy hidden danger that caused of people, the application of fabric is restricted.
Summary of the invention
For the demand, the invention provides a kind of processing method of antibiotic Anti-wrinkle fabric, this fabric processing method science, reasonable, the top layer fabric has the excellent in shape memory function, can keep straight elevator after the washing Exposure to Sunlight, and the fabric permeability is good, has antibiotic, health-care efficacy, human body is had no adverse effects, and the clothing that makes degree comfortable and easy to wear is high.
The present invention is a kind of processing method of antibiotic Anti-wrinkle fabric, and this processing method comprises the steps: a) preparation antibiotic facing material layer, b) the anti-rennet of preparation, the c) applying of the functional surfaces bed of material, d) fabric post processing.
In a preferred embodiment of the present invention, in described step a), in the antibiotic facing material layer, each composition and percentage composition are: nanometer bamboo carbon fiber 20-30%, natural cotton 25-35%, terylene 40-55%; Preparation process is: 1) preparation anti-bacterial blended yarn lines, 2) preparation natural cotton strand bar, 3) woven one-tenth antibiotic facing material on the woven machine of longitude and latitude.
In a preferred embodiment of the present invention, in described longitude and latitude weaving, warp, parallel number of share of stock ratio are 2:3, the woven density 210*220 of longitude and latitude, and the antibiotic facing material layer thickness that makes is 0.3-0.45mm.
In a preferred embodiment of the present invention, in described step b), the primary raw material of anti-rennet is polyurethane, and add appropriate dispersant, sting mixture and extrusion aid, by mixing, compacting, be extruded into the operations such as rod, compressing tablet, biaxial tension, film forming, make polyurethane film.
In a preferred embodiment of the present invention, the thickness of described polyurethane film is about 0.1mm, and its film-forming temperature is controlled at 70 ℃-75 ℃.
In a preferred embodiment of the present invention, in described step c), evenly be coated with heat curing-type viscose glue TPU between two-layer functional fabric, coat thickness is 0.02mm; Polyurethane film to the antibiotic facing material layer, forms anti-rennet by the pressure roller compoiste adhering
In a preferred embodiment of the present invention, after fitting, described functional fabric also needs to heat pressurized treatments on hot press, and its heating and temperature control is at 60 ℃, and pressure is 3-4MPa.
In a preferred embodiment of the present invention, in described step d), the fabric aftertreatment technology comprises destarch, dyeing, washing, dries, singes, wide cut typing etc.
The present invention has disclosed a kind of processing method of antibiotic Anti-wrinkle fabric, this fabric processing method procedure arrangement is reasonable, preparation cost is moderate, the wrinkle resistant effect of the fabric that makes is remarkable, and permeability is good, and fabric in use can recover straight elevator naturally along with the rising of temperature, effectively guarantee the appearance property that clothing is good, and the distinctive antibacterial and deodouring effect of internal layer fabric makes the function of this fabric more comprehensive, has wide range of applications.
Description of drawings
The present invention is further detailed explanation below in conjunction with the drawings and specific embodiments:
Fig. 1 is the processing method process figure of a kind of antibiotic Anti-wrinkle fabric of the embodiment of the present invention.
The specific embodiment
In order to make those skilled in the art person understand better technical scheme of the present invention, and above-mentioned purpose of the present invention, feature and advantage can be become apparent more, the present invention is further detailed explanation below in conjunction with embodiment and embodiment accompanying drawing.
As shown in Figure 1, be the processing method process figure of a kind of antibiotic Anti-wrinkle fabric of the embodiment of the present invention; This processing method comprises the steps: a) preparation antibiotic facing material layer, b) the anti-rennet of preparation, the c) applying of the functional surfaces bed of material, d) fabric post processing.
Embodiment 1
Concrete preparation process is as follows:
A) preparation antibiotic facing material layer, in the antibiotic facing material layer, each composition and percentage composition are: nanometer bamboo carbon fiber 25%, natural cotton 30%, terylene 45%;
Preparation process is as follows:
1) at first, nanometer bamboo carbon fiber and terylene are made the mixed yarn lines by blowing, opener, drafting, rove, spun yarn, winding procedure, yarn bar diameter is 0.25mm;
2) then, natural cotton is made natural cotton strand bar by blowing, opener, drafting, rove, spun yarn, winder, twisting operation, strand bar diameter is 0.14mm;
3) last, as warp, natural cotton strand bar is made antibiotic facing material as parallel by the longitude and latitude weaving with the scribbled bar of preparation; In above-mentioned longitude and latitude weaving, warp, parallel number of share of stock ratio are 2:3, the woven density 210*220 of longitude and latitude, and the antibiotic facing material layer thickness that makes is 0.35-0.4mm;
B) the anti-rennet of preparation, the primary raw material of this anti-rennet is polyurethane, and add appropriate dispersant, sting mixture and extrusion aid, by mixing, compacting, be extruded into the operations such as rod, compressing tablet, biaxial tension, film forming, make polyurethane film; The thickness of this polyurethane film is about 0.1mm, and its film-forming temperature is controlled at 70 ℃-75 ℃;
C) at first the applying of the functional surfaces bed of material, evenly applies heat curing-type viscose glue TPU on the antibiotic facing material layer, coat thickness is 0.02mm, forms adhesive layer; Then, the polyurethane film that makes is passed through the pressure roller compoiste adhering to adhesive layer, form anti-rennet; At last, implement the heating pressing technology on hot press, make two shell fabric compositions bonding, its heating and temperature control is at 60 ℃, and pressure is 4MPa;
D) fabric post processing, aftertreatment technology comprise destarch, dyeing, washing, dry, singe, wide cut typing etc., and the bake out temperature of fabric is controlled at below 55 ℃, and the time is 30-40 minute.
Embodiment 2
The concrete preparation process of fabric is as follows:
A) preparation antibiotic facing material layer, in the antibiotic facing material layer, each composition and percentage composition are: nanometer bamboo carbon fiber 20%, natural cotton 30%, terylene 50%;
Preparation process is as follows:
1) at first, nanometer bamboo carbon fiber and terylene are made the mixed yarn lines by blowing, opener, drafting, rove, spun yarn, winding procedure, yarn bar diameter is 0.22mm;
2) then, natural cotton is made natural cotton strand bar by blowing, opener, drafting, rove, spun yarn, winder, twisting operation, strand bar diameter is 0.14mm;
3) last, as warp, natural cotton strand bar is made antibiotic facing material as parallel by the longitude and latitude weaving with the scribbled bar of preparation; In above-mentioned longitude and latitude weaving, warp, parallel number of share of stock ratio are 2:3, the woven density 210*220 of longitude and latitude, and the antibiotic facing material layer thickness that makes is 0.35-0.38mm;
B) the anti-rennet of preparation, the primary raw material of this anti-rennet is polyurethane, and add appropriate dispersant, sting mixture and extrusion aid, by mixing, compacting, be extruded into the operations such as rod, compressing tablet, biaxial tension, film forming, make polyurethane film; The thickness of this polyurethane film is about 0.1mm, and its film-forming temperature is controlled at 70 ℃-75 ℃;
C) at first the applying of the functional surfaces bed of material, evenly applies heat curing-type viscose glue TPU on the antibiotic facing material layer, coat thickness is 0.02mm, forms adhesive layer; Then, the polyurethane film that makes is passed through the pressure roller compoiste adhering to adhesive layer, form anti-rennet; At last, implement the heating pressing technology on hot press, make two shell fabric compositions bonding, its heating and temperature control is at 60 ℃, and pressure is 3.5MPa;
D) fabric post processing, aftertreatment technology comprise destarch, dyeing, washing, dry, singe, wide cut typing etc., and the bake out temperature of fabric is controlled at below 55 ℃, and the time is 30-35 minute.
The recovering of folds temperature range of the antibiotic Anti-wrinkle fabric that makes by above-mentioned technique is 10 ℃-55 ℃, gap in anti-rennet between the thin polyurethane membrane molecule can change along with the variation of temperature, temperature raises, and the vigor between material molecule strengthens, mutual active force grow, it is large that gap between molecule becomes, 2 ℃ of every risings, the gap increases 1.2-1.6%, makes this fabric just can naturally unfold under solar radiation, eliminate fold, keep the good appearance property of clothing.
The present invention has disclosed a kind of processing method of antibiotic Anti-wrinkle fabric, be characterized in: this fabric processing method procedure arrangement is reasonable, preparation cost is moderate, the wrinkle resistant effect of the fabric that makes is remarkable, and permeability is good, and fabric in use can recover straight elevator naturally along with the rising of temperature, effectively guarantee the appearance property that clothing is good, and the distinctive antibacterial and deodouring effect of internal layer fabric makes the function of this fabric more comprehensive, has wide range of applications.
Protection scope of the present invention is not limited to this, anyly is familiar with those skilled in the art in the technical scope that the present invention discloses, and the variation that can expect easily or replacement are within all should being encompassed in protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claim was defined.
Claims (7)
1. the processing method of an antibiotic Anti-wrinkle fabric, is characterized in that, this processing method comprises the steps: a) preparation antibiotic facing material layer, b) the anti-rennet of preparation, the c) applying of the functional surfaces bed of material, d) fabric post processing.
2. the processing method of antibiotic Anti-wrinkle fabric according to claim 1, is characterized in that, in described step a), in the antibiotic facing material layer, each composition and percentage composition are: nanometer bamboo carbon fiber 20-30%, natural cotton 25-35%, terylene 40-55%; Preparation process is: 1) preparation anti-bacterial blended yarn lines, 2) preparation natural cotton strand bar, 3) woven one-tenth antibiotic facing material on the woven machine of longitude and latitude.
3. the processing method of antibiotic Anti-wrinkle fabric according to claim 2, is characterized in that, in described longitude and latitude weaving, warp, parallel number of share of stock ratio are 2:3, the woven density 210*220 of longitude and latitude, and the antibiotic facing material layer thickness that makes is 0.3-0.45mm.
4. the processing method of antibiotic Anti-wrinkle fabric according to claim 1, it is characterized in that, in described step b), the primary raw material of anti-rennet is polyurethane, and add appropriate dispersant, sting mixture and extrusion aid, by mixing, compacting, be extruded into the operations such as rod, compressing tablet, biaxial tension, film forming, make polyurethane film.
5. the processing method of antibiotic Anti-wrinkle fabric according to claim 4, is characterized in that, the thickness of described polyurethane film is about 0.1mm, and its film-forming temperature is controlled at 70 ℃-75 ℃.
According to claim 1 to 5 described antibiotic Anti-wrinkle fabric processing method, it is characterized in that, in described step c), evenly be coated with heat curing-type viscose glue TPU between two-layer functional fabric, coat thickness is 0.02mm; Polyurethane film to the antibiotic facing material layer, forms anti-rennet by the pressure roller compoiste adhering
The processing method of antibiotic Anti-wrinkle fabric according to claim 6 is characterized in that, also needs after described functional fabric is fitted to heat pressurized treatments on hot press, and its heating and temperature control is at 60 ℃, and pressure is 3-4MPa.
7. the processing method of antibiotic Anti-wrinkle fabric according to claim 1, is characterized in that, in described step d), the fabric aftertreatment technology comprises destarch, dyeing, washing, dries, singes, wide cut typing etc.