CN103462262A - Processing method for novel crease-resistant suit - Google Patents

Processing method for novel crease-resistant suit Download PDF

Info

Publication number
CN103462262A
CN103462262A CN 201310436738 CN201310436738A CN103462262A CN 103462262 A CN103462262 A CN 103462262A CN 201310436738 CN201310436738 CN 201310436738 CN 201310436738 A CN201310436738 A CN 201310436738A CN 103462262 A CN103462262 A CN 103462262A
Authority
CN
China
Prior art keywords
layer
fabric
processing
cloth
uniforms
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201310436738
Other languages
Chinese (zh)
Inventor
黄惠琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KUNSHAN ZHOUSHI HUIHONG GARMENT FACTORY
Original Assignee
KUNSHAN ZHOUSHI HUIHONG GARMENT FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KUNSHAN ZHOUSHI HUIHONG GARMENT FACTORY filed Critical KUNSHAN ZHOUSHI HUIHONG GARMENT FACTORY
Priority to CN 201310436738 priority Critical patent/CN103462262A/en
Publication of CN103462262A publication Critical patent/CN103462262A/en
Pending legal-status Critical Current

Abstract

The invention discloses a processing method for a novel crease-resistant suit. The processing method comprises the following steps of (a) preparing a surface layer; (b) preparing a middle layer; (c) preparing a lining layer; (d) adhering fabric layers; (e) after-treating fabric cloth; (f) cutting and sewing a suit. The processing method for the novel crease-resistant suit, disclosed by the invention, has reasonable working procedures and a simple preparation process and is moderate in cost; the fabric cloth of the processed suit is high in interlayer bonding strength; the fabric of the middle layer is good in strength and toughness, the straightness of the fabric of the surface layer of the suit can be ensured, and the ironing frequency of the suit is effectively reduced; meanwhile, the fabric cloth of the suit is high in air permeability, and the good wearing comfort of the suit can be ensured.

Description

A kind of processing method of novel crease-shedding uniforms
Technical field
The present invention relates to a kind of processing method of western-style clothes, relate in particular to the processing method of the exsertile western-style clothes of a kind of wrinkle resistance, belong to the garment technology field.
Background technology
A western-style clothes great variety of models, fabric texture is soft, deeply is subject to youthfully to like.Along with scientific and technological fast development, new material, new technology and new technology are widely applied on the fabric of western-style clothes, thereby the panoramic functional western-style clothes such as antibiotic, uvioresistant, waterproof, antistatic occurred.
With the quickening pace of modern life, a lot of people have no time to arrange the clothing of oneself, if take dry-cleaning away, not only consuming time but also increase living cost.Popular non-ironing suiting on the market, some special preparation techniques have mostly been applied, as: fabric is contaminated in special dip dyeing liquid for shell, make face liber there is certain intensity and shape, re-use steam shaping, make fabric still can keep straight elevator later in washing, but the fabric durability of this PROCESS FOR TREATMENT is mostly all lower, after washing repeatedly, fabric has distortion in various degree, and clothing is lower service life; Have again, some technique is on the fabric top layer or nexine applies PU or PVC, form wrinkle resistant composite material, the wrinkle resistant performance of fabric is increased substantially, and durability also meets people's instructions for use, but it is unsatisfactory to process in this way the performance of later fabric aspect gas permeability and absorption of perspiration, the long-time fabric of this material of wearing, human body there will be discomfort, to people are healthy, causes a hidden trouble, and there is defect in the practicality aspect.
  
Summary of the invention
For the demand, the invention provides a kind of processing method of novel crease-shedding uniforms, this processing method procedure arrangement is reasonable, the western-style clothes interfacial bonding strength made is high, its intermediate fabric layer has good intensity and toughness, can guarantee the straight and upright of western-style clothes top layer fabric, effectively reduce the flatiron number of times of western-style clothes, for people's life is provided convenience.
The present invention is a kind of processing method of novel crease-shedding uniforms, and this processing method comprises the steps: a) to prepare top layer, b) prepares intermediate layer, c) prepares nexine, and d) precoat is bonding, e) fabric cloth post processing, f) cutting of western-style clothes and making.
In a preferred embodiment of the present invention, in described step a), the primary raw material on top layer is the animal woollen, the quantitative polyster fibre of blending in it, and terylene content is no more than 20%; Top layer is prepared on Computerized flat knitting machine, knit fabric cloth be the fine needle wool fabric, its fabric width is 144cm, grammes per square metre is about 240-260g/m*m; After the preparation of top layer, also need the processing of being dyeed, wash, singe, drying.
In a preferred embodiment of the present invention, in described step b), intermediate layer is the high density polyester fiber cloth, and the specification of selected polyster fibre bar is 75D/30F; The woven moulding on the woven machine of longitude and latitude of intermediate fabric layer cloth, warp, tram number of share of stock ratio are about 3:2, and the woven density of fabric cloth is about 168*196.
In a preferred embodiment of the present invention, in described step c), the blend fabric that nexine is natural cotton and spandex, its warp, tram number of share of stock ratio are about 1:2, and the woven density of fabric cloth is about 96*64.
In a preferred embodiment of the present invention, in described step d), the selected adhesive of the adhesive surface bed of material is the polyurethane viscose glue, the adhesion process of precoat comprises the bonding of the bonding and intermediate layer of intermediate layer and nexine and top layer, adhesion process is as follows: at first, adhesive is coated on one side, intermediate layer in the mode of setting; Then, fitted and exert pressure in the side of coating adhesive mixture and nexine fabric, pressure is controlled at 1.5-2MPa, and the time is 20-25 minute; Then, coating adhesive mixture on the another side, intermediate layer, and the top layer fabric is fitted on it, in like manner to exert pressure, pressure is controlled at 2-2.5MPa, and the time is 30-35 minute; Finally, the fabric cloth after bonding is carried out to drying and processing, temperature is controlled at 40 ℃ of left and right, and the time is 1.5-2 hour.
The present invention has disclosed a kind of processing method of novel crease-shedding uniforms, this processing method procedure arrangement is reasonable, preparation technology is easy, cost is moderate, the interfacial bonding strength of the suiting cloth made is high, its intermediate fabric layer has good intensity and toughness, can guarantee the straight and upright of western-style clothes top layer fabric, has effectively reduced the flatiron number of times of western-style clothes; Simultaneously, the permeability of suiting cloth is good, can guarantee the degree comfortable and easy to wear that western-style clothes is good.
The accompanying drawing explanation
Below in conjunction with the drawings and specific embodiments, the present invention is further detailed explanation:
Fig. 1 is the process figure of the processing method of the novel crease-shedding uniforms of the embodiment of the present invention.
The specific embodiment
Below in conjunction with accompanying drawing, preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made to more explicit defining.
Fig. 1 is the process figure of the processing method of the novel crease-shedding uniforms of the embodiment of the present invention; This processing method comprises the steps: a) to prepare top layer, b) prepares intermediate layer, c) prepares nexine, and d) precoat is bonding, e) fabric cloth post processing, f) cutting of western-style clothes and making.
Embodiment 1
The specific implementation process of the processing method of the novel crease-shedding uniforms that the present invention mentions is as follows:
A) prepare top layer, the top layer raw material choose rabbit hair, the quantitative polyster fibre of blending in woollen, terylene content is about 20%; Top layer is prepared on Computerized flat knitting machine, knit fabric cloth be the fine needle wool fabric, its fabric width is 144cm, grammes per square metre is about 240g/m*m, thickness is about 0.3mm; After the preparation of top layer, also need the processing of being dyeed, wash, singe, drying;
B) prepare intermediate layer, intermediate layer is the high density polyester fiber cloth, and the specification of selected polyster fibre bar is 75D/30F; The woven moulding on the woven machine of longitude and latitude of intermediate fabric layer cloth, warp, tram number of share of stock ratio are about 3:2, and the woven density of fabric cloth is about 168*196, and woven thickness is about 0.15-0.2mm;
C) prepare nexine, the blend fabric that nexine is natural cotton and spandex, blending rate is about 95%:5%, and warp, tram number of share of stock ratio are about 1:2, and the woven density of fabric cloth is about 96*64, and woven thickness is about 0.2-0.25mm;
D) precoat is bonding, and the selected adhesive of the adhesive surface bed of material is the polyurethane viscose glue, and viscose glue is applied with list structure, and its width is about 1cm, and thickness is about 0.1mm, and the distance between adjacent viscose top is about 5mm; The adhesion process of precoat comprises the bonding of the bonding and intermediate layer of intermediate layer and nexine and top layer, and adhesion process is as follows: at first, adhesive is coated on one side, intermediate layer in the mode of setting; Then, fitted and exert pressure in the side of coating adhesive mixture and nexine fabric, pressure is controlled at the 1.5MPa left and right, and the time is 25 minutes; Then, coating adhesive mixture on the another side, intermediate layer, and the top layer fabric is fitted on it, in like manner to exert pressure, pressure is controlled at the 2MPa left and right, and the time is 35 minutes; Finally, the fabric cloth after bonding is carried out to drying and processing, temperature is controlled at 40 ℃ of left and right, and the time is 1.5 hours, and purpose is to remove moisture unnecessary in adhesive, with the fixed effect of guaranteeing that fabric cloth is good;
E) fabric cloth post processing, the fabric post processing comprises the techniques such as destarch, washing, oven dry, thermal finalization, cutting edge;
F) cutting of western-style clothes and making.
Embodiment 2
The specific implementation process of the processing method of the novel crease-shedding uniforms that the present invention mentions is as follows:
A) prepare top layer, top layer raw material choose sheep's wool, the quantitative polyster fibre of blending in woollen, terylene content is about 15%; Top layer is prepared on Computerized flat knitting machine, knit fabric cloth be the fine needle wool fabric, its fabric width is 144cm, grammes per square metre is about 260g/m*m, thickness is about 0.35mm; After the preparation of top layer, also need the processing of being dyeed, wash, singe, drying;
B) prepare intermediate layer, intermediate layer is the high density polyester fiber cloth, and the specification of selected polyster fibre bar is 75D/30F; The woven moulding on the woven machine of longitude and latitude of intermediate fabric layer cloth, warp, tram number of share of stock ratio are about 3:2, and the woven density of fabric cloth is about 168*196, and woven thickness is about 0.15-0.2mm;
C) prepare nexine, the blend fabric that nexine is natural cotton and spandex, blending rate is about 95%:5%, and warp, tram number of share of stock ratio are about 1:2, and the woven density of fabric cloth is about 96*64, and woven thickness is about 0.2-0.25mm;
D) precoat is bonding, and the selected adhesive of the adhesive surface bed of material is the polyurethane viscose glue, and viscose glue is applied with list structure, and its width is about 1cm, and thickness is about 0.12mm, and the distance between adjacent viscose top is about 5mm; The adhesion process of precoat comprises the bonding of the bonding and intermediate layer of intermediate layer and nexine and top layer, and adhesion process is as follows: at first, adhesive is coated on one side, intermediate layer in the mode of setting; Then, fitted and exert pressure in the side of coating adhesive mixture and nexine fabric, pressure is controlled at the 2MPa left and right, and the time is 20 minutes; Then, coating adhesive mixture on the another side, intermediate layer, and the top layer fabric is fitted on it, in like manner to exert pressure, pressure is controlled at the 2.5MPa left and right, and the time is 30 minutes; Finally, the fabric cloth after bonding is carried out to drying and processing, temperature is controlled at 40 ℃ of left and right, and the time is 1.5-2 hour, and purpose is to remove moisture unnecessary in adhesive, with the fixed effect of guaranteeing that fabric cloth is good;
E) fabric cloth post processing, the fabric post processing comprises the techniques such as destarch, washing, oven dry, thermal finalization, cutting edge;
F) cutting of western-style clothes and making.
The present invention has disclosed a kind of processing method of novel crease-shedding uniforms, be characterized in: this processing method procedure arrangement is reasonable, preparation technology is easy, cost is moderate, the interfacial bonding strength of the suiting cloth made is high, its intermediate fabric layer has good intensity and toughness, can guarantee the straight and upright of western-style clothes top layer fabric, has effectively reduced the flatiron number of times of western-style clothes; Simultaneously, the permeability of suiting cloth is good, can guarantee the degree comfortable and easy to wear that western-style clothes is good.
The above; it is only the specific embodiment of the present invention; but protection scope of the present invention is not limited to this; any those of ordinary skill in the art are in the disclosed technical scope of the present invention; the variation that can expect without creative work or replacement, within all should being encompassed in protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.

Claims (5)

1. the processing method of a novel crease-shedding uniforms, is characterized in that, this processing method comprises the steps: a) to prepare top layer, b) prepares intermediate layer, c) prepares nexine, and d) precoat is bonding, e) fabric cloth post processing, f) cutting of western-style clothes and making.
2. the processing method of novel crease-shedding uniforms according to claim 1, is characterized in that, in described step a), the primary raw material on top layer is the animal woollen, the quantitative polyster fibre of blending in it, and terylene content is no more than 20%; Top layer is prepared on Computerized flat knitting machine, knit fabric cloth be the fine needle wool fabric, its fabric width is 144cm, grammes per square metre is about 240-260g/m*m; After the preparation of top layer, also need the processing of being dyeed, wash, singe, drying.
3. the processing method of novel crease-shedding uniforms according to claim 1, is characterized in that, in described step b), intermediate layer is the high density polyester fiber cloth, and the specification of selected polyster fibre bar is 75D/30F; The woven moulding on the woven machine of longitude and latitude of intermediate fabric layer cloth, warp, tram number of share of stock ratio are about 3:2, and the woven density of fabric cloth is about 168*196.
4. the processing method of novel crease-shedding uniforms according to claim 1, is characterized in that, in described step c), and the blend fabric that nexine is natural cotton and spandex, its warp, tram number of share of stock ratio are about 1:2, and the woven density of fabric cloth is about 96*64.
5. the processing method of novel crease-shedding uniforms according to claim 1, it is characterized in that, in described step d), the selected adhesive of the adhesive surface bed of material is the polyurethane viscose glue, the adhesion process of precoat comprises the bonding of the bonding and intermediate layer of intermediate layer and nexine and top layer, adhesion process is as follows: at first, adhesive is coated on one side, intermediate layer in the mode of setting; Then, fitted and exert pressure in the side of coating adhesive mixture and nexine fabric, pressure is controlled at 1.5-2MPa, and the time is 20-25 minute; Then, coating adhesive mixture on the another side, intermediate layer, and the top layer fabric is fitted on it, in like manner to exert pressure, pressure is controlled at 2-2.5MPa, and the time is 30-35 minute; Finally, the fabric cloth after bonding is carried out to drying and processing, temperature is controlled at 40 ℃ of left and right, and the time is 1.5-2 hour.
CN 201310436738 2013-09-24 2013-09-24 Processing method for novel crease-resistant suit Pending CN103462262A (en)