CN110219085A - For improving the Yarn spinning method and fabric of fabric moisture water vapour permeability - Google Patents
For improving the Yarn spinning method and fabric of fabric moisture water vapour permeability Download PDFInfo
- Publication number
- CN110219085A CN110219085A CN201910551754.9A CN201910551754A CN110219085A CN 110219085 A CN110219085 A CN 110219085A CN 201910551754 A CN201910551754 A CN 201910551754A CN 110219085 A CN110219085 A CN 110219085A
- Authority
- CN
- China
- Prior art keywords
- fabric
- section
- odd
- yarn
- shaped cross
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of for improving the Yarn spinning method and fabric of fabric moisture water vapour permeability.This method includes carrying out air vortex spinning by the terylene short fiber of odd-shaped cross section of section, obtains odd-shaped cross section Polyester Yarns；The odd-shaped cross section Polyester Yarns is subjected to starching processing；Fabric blank is made according to preset condition in odd-shaped cross section Polyester Yarns after starching；By the fabric blank desizing and drying and shaping, article is made.Not only process is simple and the fabric moisture penetrability produced is good for the Yarn spinning method.
Description
Technical field
The present invention relates to the technical fields of fabric, more particularly to a kind of for improving the spinning of fabric moisture water vapour permeability
Method and the fabric as made from the Yarn spinning method.
Background technique
With economic rapid development, requirement of the people for comfortable features of clothing is increasingly improved, the comfort of clothes itself
Hot wet migration, contact comfort and visual adaptability can be divided into.Wherein, hot wet migration is evaluate comfortable features of clothing one
Item important indicator.Hot wet migration refers to that human body is maintained and adjusted between human body and the heat-moisture transfer of environment to be stablized, and is human normal
Physiological function creates good condition, feels so that human body be made to keep comfortable.
Traditional ring spinning processes have multiple working procedure, and spinning line is complex, resultant yarn rate is slow.In common spinning
In yarn method, the section of the terylene short fiber used is mostly regular circle, and spinning is formed by fabric and is unfavorable for perspiring moisture-inhibiting.
Therefore, for the moisture absorption water vapour permeability for the fabric that the process of Yarn spinning method in the prior art is excessively complicated and is woven
Bad technical problem, it is necessary to which a kind of spinning that can simplify spinning line and be conducive to improve fabric moisture water vapour permeability is provided
Yarn method, and the fabric as made from the Yarn spinning method.
Summary of the invention
It is bad for the process excessively moisture absorption water vapour permeability of complexity and the fabric woven of Yarn spinning method in the prior art
The technical issues of, the embodiment of the present invention, which provides one kind, can simplify spinning line and be conducive to improve fabric moisture water vapour permeability
Yarn spinning method.This is used to improve the Yarn spinning method of fabric moisture water vapour permeability using air vortex spinning method, relative to ring spinning
The process that method reduces rove, so that spinning line is brief, resultant yarn rate is high.Further, this is used to improve fabric moisture
The Yarn spinning method of water vapour permeability uses the terylene short fiber of odd-shaped cross section, so that the fabric of spinning is more conducive to moisture absorption moisture-inhibiting.
To achieve the goals above, the technical solution that one embodiment of the invention provides is as follows: one kind is for improving fabric suction
The Yarn spinning method of drenched wet performance, including step S1: carrying out air vortex spinning by the terylene short fiber of odd-shaped cross section of section, obtain different
Tee section Polyester Yarns；Step S2: the odd-shaped cross section Polyester Yarns is subjected to starching processing；Step S3: the abnormity after starching is cut
Fabric blank is made according to preset condition in face Polyester Yarns；Step S4: by the fabric blank desizing and drying and shaping, fabric is made
Finished product.
As a further improvement of the present invention, the odd-shaped cross section is cross section.
As a further improvement of the present invention, the step of air vortex spinning includes: that the terylene of the odd-shaped cross section is short
Fibre carries out blowing on combined opening and scutching machine；Terylene short fiber after blowing is subjected to cotton carding on carding machine, obtains the carded sliver；By the carded sliver
After three draftings, ripe bar is obtained；Ripe bar feeding vortex flow spinner is spun into odd-shaped cross section Polyester Yarns.
As a further improvement of the present invention, in the air vortex spinning the step of, spinning speed is 300~600m/
Min, feeding than be 0.9~0.95, batch angle be 12 °~15 °, spinning tension be 100~150, yarn linear density be 20~
60S。
As a further improvement of the present invention, the slurry in step S2 is PVA, and the concentration of slurry is 10%~20%.
As a further improvement of the present invention, the preset condition in step S3 includes close through density, weft density, fabric covering
Degree, configuration tissue.
As a further improvement of the present invention, the range through density is 200~240/10cm, the range of weft density
For 200~240/10cm, the range of fabric coverage density is 73%~76%, and the range for configuring tissue is 2~8 pieces.
As a further improvement of the present invention, the desizing boiling time in step S4 is 30~60 minutes, washing times 2
~3 times, drying temperature is 60 DEG C~80 DEG C, and drying time is 40~60 minutes.
The embodiment of the present invention also provides a kind of fabric.The fabric is made using any of the above-described kind of Yarn spinning method.
The invention has the following advantages that
A kind of Yarn spinning method for improving fabric moisture water vapour permeability provided by the embodiment of the present invention uses vortex spinning
Yarn process reduces the process of rove compared with traditional ring spinning process, and spinning line is brief, resultant yarn rate is high.Into one
Step ground, a kind of Yarn spinning method for improving fabric moisture water vapour permeability provided by the embodiment of the present invention is using odd-shaped cross section
Terylene short fiber is based on capillarity since the gap between the fiber and yarn of odd-shaped cross section is more, surface area is big, and fabric has more
Good ventilative, moisture-inhibiting and hygroscopicity.
Detailed description of the invention
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below
There is attached drawing needed in technical description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this
The some embodiments recorded in invention, for those of ordinary skill in the art, without creative efforts,
It is also possible to obtain other drawings based on these drawings.
Fig. 1 is that a kind of process for improving the Yarn spinning method of fabric moisture water vapour permeability provided in an embodiment of the present invention is shown
It is intended to；
Fig. 2 is the scanning electron microscope schematic diagram in odd-shaped cross section spun polyester thread section of the invention.
Specific embodiment
Technical solution in order to enable those skilled in the art to better understand the present invention, below in conjunction with of the invention real
The attached drawing in example is applied, technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work, all should belong to protection of the present invention
Range.
Join shown in Fig. 1, it is provided in an embodiment of the present invention a kind of for improving the Yarn spinning method of fabric moisture water vapour permeability
Flow diagram.In this embodiment, Yarn spinning method includes four steps.
Step S1: air vortex spinning is carried out by the terylene short fiber of odd-shaped cross section of section, obtains odd-shaped cross section Polyester Yarns.At this
In embodiment, the step of air vortex spinning includes: that the terylene short fiber of the odd-shaped cross section is carried out blowing on combined opening and scutching machine；It will
Terylene short fiber after blowing carries out cotton carding on carding machine, obtains the carded sliver；After three drafting of the carded sliver, ripe bar is obtained；By ripe bar
Vortex is spun into odd-shaped cross section Polyester Yarns.In the air vortex spinning the step of, spinning speed is 300~600m/min, feeds ratio
It is 0.9~0.95, batching angle is 12 °~15 °, and spinning tension is 100~150, and yarn linear density is 20~60S.
A kind of Yarn spinning method for improving fabric moisture water vapour permeability provided by the embodiment of the present invention uses vortex spinning
Yarn process reduces the process of rove compared with traditional ring spinning process, and spinning line is brief, resultant yarn rate is high.
As shown in Fig. 2, in this embodiment, the specific shape of odd-shaped cross section is cross section.The abnormity of cross section is fine
Dimension has four grooves, and groove has capillarity, can rapid wetness guiding perspiration discharging.
Step S2: the odd-shaped cross section Polyester Yarns is subjected to starching processing.In this embodiment, the slurry in sizing process
For PVA, the concentration of slurry is 10%~20%.
Step S3: fabric blank is made according to preset condition in the odd-shaped cross section Polyester Yarns after starching.Preset condition includes
Through density, weft density, fabric coverage density, configuration tissue.Range through density is 200~240/10cm, the model of weft density
It encloses for 200~240/10cm, the range of fabric coverage density is 73%~76%, and the range for configuring tissue is 2~8 pieces.
Step S4: by the fabric blank desizing and drying and shaping, article is made.In this embodiment, desizing water
Boiling the time is 30~60 minutes, and washing times are 2~3 times, and drying temperature is 60 DEG C~80 DEG C, and drying time is 40~60 points
Clock.
Further, the embodiment of the present invention also provides a kind of fabric.The fabric is made using any of the above-described kind of Yarn spinning method.
A kind of Yarn spinning method for improving fabric moisture water vapour permeability provided by the embodiment of the present invention uses the terylene of odd-shaped cross section
Short fibre can make fabric have preferably ventilative, moisture-inhibiting since the gap between the fiber and yarn of odd-shaped cross section is more, surface area is big
And hygroscopicity.
In order to verify the moisture absorption water vapour permeability of fabric made by the embodiment of the present invention, hereafter respectively with circular cross-section vortex spinning
Three kinds of yarn, odd-shaped cross section vortex spinning yarn and circular cross-section ring spinning line yarns carry out test and compare their mechanical properties
And the hot wet migration energy of fabric.
Test 1
This test carries out blowing using cross section terylene short fiber yarn first on combined opening and scutching machine, in carding machine after blowing
Upper progress cotton carding obtains the carded sliver, and ripe bar will be obtained after three drafting of the carded sliver with spinning speed 360m/min, ratio 0.95 is fed, batches
15 ° of angle, spinning tension 120, line density 30S is vortexed and is spun into odd-shaped cross section Polyester Yarns.
Yarn 10%PVA starching on GA392 type single-yarn sizing equipment that vortex is spun into, the yarn of first-class slurry is through close
220/10cm, 220/10cm of filling density, No. 11 reeds of 8 brown frames, every reed two penetrates, configures plain weave, weave into grey cloth.
By the fabric at 100 DEG C boiling 30min, dry 40min at 80 DEG C after cleaning, obtain having heat wet comfortable
The odd-shaped cross section terylene vortex-spun fabric of function.
Test 2
This test carries out blowing using circular-section terylene spun yarn first on combined opening and scutching machine, in carding machine after blowing
Upper progress cotton carding obtains the carded sliver, will obtain ripe bar after three drafting of the carded sliver, by ripe bar with spinning speed 360m/min, feeds ratio
0.95,15 ° of angle are batched, spinning tension 120, line density 30S is vortexed and is spun into circular-section terylene yarn.
Yarn 10%PVA starching on GA392 type single-yarn sizing equipment that vortex is spun into, the yarn of first-class slurry is through close
220/10cm, 220/10cm of filling density, No. 11 reeds of 8 brown frames, every reed two penetrates, configures plain weave, weave into grey cloth.
By the fabric at 100 DEG C boiling 30min, dry 40min at 80 DEG C after cleaning, obtain having heat wet comfortable
The circular-section terylene vortex-spun fabric of function.
Test 3
This test carries out blowing using circular-section terylene spun yarn first on combined opening and scutching machine, in carding machine after blowing
Upper progress cotton carding obtains the carded sliver, ripe bar will be obtained after three drafting of the carded sliver, by ripe bar with flier revolving speed 250r/min, roving twist
6T/10cm, regular roving feeding 10.00g/10cm are spun into rove, after by rove with spindle revolving speed 3000r/min, back area draft is than 1.2
Times, line density 30S, RING SPINNING is at circular-section terylene yarn.
Yarn 10%PVA starching on GA392 type single-yarn sizing equipment that vortex is spun into, the yarn of first-class slurry is through close
220/10cm, 220/10cm of filling density, No. 11 reeds of 8 brown frames, every reed two penetrates, configures plain weave, weave into grey cloth.
By the fabric at 100 DEG C boiling 30min, dry 40min at 80 DEG C after cleaning, obtain having heat wet comfortable
The circular-section terylene vortex-spun fabric of function.
Following all measure wicking height test datas are surveyed according to " FZ/T 01071-2008 textile capillary effect test method "
Test-object is quasi-；Water absorption rate test data are according to " the evaluation part 1 individual event of GB/T 21655.1-2008 textile absorbing fast-drying
Composite test method " testing standard.
Table 1 is the average value comparing result of the test result of the measure wicking height obtained when testing 1,2,3 configuration plain weave.
Table 1
It is known from Table 1 that the wicking rate of vortex spinning and tee section yarn woven fabric is higher than vortex spinning terylene circular cross-section fabric and ring
Ingot spins circular cross-section fabric, and wherein odd-shaped cross section vortex spinning Polyester Yarns fabric measure wicking height is knitted slightly larger than vortex spinning circular cross-section yarn
Object.
Table 2 is the average value comparing result of the water absorption rate test result obtained when testing 1,2,3 configuration plain weave.
Table 2
The embodiment of the present invention has the advantages that the embodiment of the present invention uses it can be seen from the contrast table tested
Raw material be that terylene is vortexed spun core-spun yarn, materials from a wealth of sources are simple, and promotion textile can be realized with common weaving process
Hot wet migration；Compared with common RING SPINNING, the processing step of rove is omitted in vortex spinning, and preparation flow is short, resultant yarn rate is high, drop
Low spinning cost；Using the special cross-section form of profiled filament, soft, the good fabric of moisture absorbing and sweat releasing property is woven.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (9)
1. a kind of for improving the Yarn spinning method of fabric moisture water vapour permeability, which is characterized in that the described method includes:
Step S1: air vortex spinning is carried out by the terylene short fiber of odd-shaped cross section of section, obtains odd-shaped cross section Polyester Yarns；
Step S2: the odd-shaped cross section Polyester Yarns is subjected to starching processing；
Step S3: fabric blank is made according to preset condition in the odd-shaped cross section Polyester Yarns after starching；
Step S4: by the fabric blank desizing and drying and shaping, article is made.
2. according to claim 1 a kind of for improving the Yarn spinning method of fabric moisture water vapour permeability, which is characterized in that institute
Stating odd-shaped cross section is cross section.
3. according to claim 1 a kind of for improving the Yarn spinning method of fabric moisture water vapour permeability, which is characterized in that institute
The step of stating air vortex spinning includes: that the terylene short fiber of the odd-shaped cross section is carried out blowing on combined opening and scutching machine；After blowing
Terylene short fiber carry out cotton carding on carding machine, obtain the carded sliver；After three drafting of the carded sliver, ripe bar is obtained；By ripe bar through being vortexed
Spinning machine is spun into odd-shaped cross section Polyester Yarns.
4. according to claim 3 a kind of for improving the Yarn spinning method of fabric moisture water vapour permeability, which is characterized in that
In the step of air vortex spinning, spinning speed is 300~600m/min, and than being 0.9~0.95, batching angle is 12 ° for feeding
~15 °, spinning tension is 100~150, and yarn linear density is 20~60s.
5. according to claim 1 a kind of for improving the Yarn spinning method of fabric moisture water vapour permeability, which is characterized in that step
Slurry in rapid S2 is PVA, and the concentration of slurry is 10%~20%.
6. according to claim 1 a kind of for improving the Yarn spinning method of fabric moisture water vapour permeability, which is characterized in that step
Preset condition in rapid S3 includes through density, weft density, fabric coverage density, configuration tissue.
7. according to claim 6 a kind of for improving the Yarn spinning method of fabric moisture water vapour permeability, which is characterized in that institute
Stating the range through density is 200~240/10cm, and the range of weft density is 200~240/10cm, fabric coverage density
Range is 73%~76%, and the range for configuring tissue is 2~8 pieces.
8. according to claim 1 a kind of for improving the Yarn spinning method of fabric moisture water vapour permeability, which is characterized in that step
The desizing boiling time in rapid S4 is 30~60 minutes, and washing times are 2~3 times, and drying temperature is 60 DEG C~80 DEG C, when drying
Between be 40~60 minutes.
9. a kind of fabric, which is characterized in that the fabric is using spinning described in any one of claims 1 to 8 claim
Method is made.