CN110201208A - 一种止血、杀菌的敷料及其制备方法 - Google Patents

一种止血、杀菌的敷料及其制备方法 Download PDF

Info

Publication number
CN110201208A
CN110201208A CN201910524438.2A CN201910524438A CN110201208A CN 110201208 A CN110201208 A CN 110201208A CN 201910524438 A CN201910524438 A CN 201910524438A CN 110201208 A CN110201208 A CN 110201208A
Authority
CN
China
Prior art keywords
dressing
parts
mixture
preparation
stirring
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910524438.2A
Other languages
English (en)
Inventor
梁铭涛
蔡仕国
张声斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHUHAI DAOTIAN MEDICAL TECHNOLOGY Co Ltd
Original Assignee
ZHUHAI DAOTIAN MEDICAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHUHAI DAOTIAN MEDICAL TECHNOLOGY Co Ltd filed Critical ZHUHAI DAOTIAN MEDICAL TECHNOLOGY Co Ltd
Priority to CN201910524438.2A priority Critical patent/CN110201208A/zh
Publication of CN110201208A publication Critical patent/CN110201208A/zh
Pending legal-status Critical Current

Abstract

本发明属于医用材料领域，特别公开了一种止血、杀菌的敷料，按重量份数计，包括以下组分：壳聚糖20‑40份，姜黄素5‑10份，牛磺酸1‑3份，透明质酸钠0.5‑1份，薄荷脑0.5‑3份，纳米银0.5‑3份，磷酸二氢铵1‑3份。另外，还提供了一种所述敷料的制备方法。相对于现有技术，本发明所述敷料止血速度快，针对较大面积的皮肤流血伤口具有很好的止血作用；本发明所述敷料杀菌效果好，特别是对化脓性球菌，具体的例如葡萄球菌、链球菌具有很好的杀菌效果，从而防止伤口化脓溃烂或感染。

Description

一种止血、杀菌的敷料及其制备方法
技术领域
本发明属于医用材料领域，特别涉及一种止血、杀菌的敷料及其制备方法。
背景技术
现有技术中的用于止血、杀菌的敷料种类繁多，但往往止血速度较慢，对大面积的皮肤流血创伤的止血效果不佳，影响实际对患者救助的效果。另外，现有技术中的医药敷料杀菌效果也较为单一，杀菌效果不理想，因此特别容易导致伤口化脓，引起进一步的感染。
壳聚糖具有止血恢复损伤皮肤的作用，经常应用于医用敷料中，但是单独使用壳聚糖起止血速度慢，现有技术中也添加一些辅助试剂来改善止血功能，但往往效果不佳。
因此，需要提供一种同时具有止血，且杀菌效果好，特别是针对化脓性的细菌要有很好的杀菌效果的敷料十分有必要。
发明内容
针对现有技术的不足，本发明提供一种止血、杀菌的敷料及其制备方法。所述一种止血、杀菌的敷料具有止血的功能，且杀菌效果好，特别是对化脓性球菌，具体的例如葡萄球菌、链球菌。
一种止血、杀菌的敷料，按重量份数计，包括以下组分：
优选的，一种止血、杀菌的敷料，按重量份数计，包括以下组分：
进一步优选的，一种止血、杀菌的敷料，按重量份数计，包括以下组分：
优选的，所述敷料，按重量份数计，还包括0.5-2份的氧化锌。
优选的，所述纳米银的尺寸为20-80nm；进一步优选的，所述纳米银的尺寸为40-60nm。
所述敷料还含有3-30份的水。
一种止血、杀菌的敷料的其制备方法，包括以下步骤：
(1)按配方量称取各组分，将壳聚糖、姜黄素、透明质酸钠、薄荷脑加入水中，搅拌，制得混合物A，备用；
(2)将牛磺酸和纳米银、磷酸二氢铵加入水中，搅拌，制得混合物B，备用；
(3)将混合物A和混合物B混合，搅拌，制得混合物C，然后将纱布浸入混合物C中，
然后取出纱布，烘干，制得所述敷料。
具体的，一种止血、杀菌的敷料的其制备方法，包括以下步骤：
(1)按配方量称取各组分，将壳聚糖、姜黄素、透明质酸钠、薄荷脑溶解于50-100份的水中，混合搅拌，制得混合物A，备用；
(2)将牛磺酸和纳米银、磷酸二氢铵加入到10-20份的水中搅拌，制得混合物B，备用；
(3)将混合物A和混合物B混合，搅拌，制得混合物C，然后将医药纱布浸入混合物C
中在20-40℃下浸泡12-24小时，取出纱布，烘干，即制得所述止血、杀菌的敷料。
优选的，步骤(1)中的搅拌的速度为200-400转/分钟，搅拌的时间为30-50分钟。
优选的，步骤(2)中所述的水的温度为50-70℃。
优选的，步骤(3)中的搅拌的速度为100-300转/分钟，搅拌的时间为1-2小时。
优选的，步骤(3)中的烘干是在65-75℃下烘干30-50分钟。
优选的，步骤(3)中的纱布的厚度为0.5-2mm。
本发明所述的壳聚糖、姜黄素、透明质酸钠、牛磺酸一同使用具有止血的功能，相对于单独使用壳聚糖，止血速度明显提升。所述纳米银、磷酸二氢铵、姜黄素和薄荷脑的协同使用，可提高敷料的杀菌效果，特别是对葡萄球菌、链球菌的杀菌效果。
相对于现有技术，本发明的有益效果如下：
(1)本发明所述敷料止血速度快，针对较大面积的皮肤流血伤口具有很好的止血作用；
(2)本发明所述敷料杀菌效果好，特别是对化脓性球菌，具体的例如葡萄球菌、链球菌具有很好的杀菌效果，从而防止伤口化脓溃烂或感染。
具体实施方式
为了让本领域技术人员更加清楚明白本发明所述技术方案，现列举以下实施例进行说明。需要指出的是，以下实施例对本发明要求的保护范围不构成限制作用。
实施例1
一种止血、杀菌的敷料，按重量份数计，包括以下组分：
所述纳米银的尺寸为20-40nm。
一种止血、杀菌的敷料的其制备方法，包括以下步骤：
(1)按配方量称取各组分，将壳聚糖、姜黄素、透明质酸钠、薄荷脑溶解于50份的水中，混合搅拌，制得混合物A，备用；
(2)将牛磺酸和纳米银、磷酸二氢铵加入到10份的水中搅拌，制得混合物B，备用；
(3)将混合物A和混合物B混合，搅拌，制得混合物C，然后将医药纱布浸入混合物C
中在25℃下浸泡24小时，取出纱布，烘干，即制得所述止血、杀菌的敷料。
步骤(1)中的搅拌的速度为400转/分钟，搅拌的时间为30分钟。
步骤(2)中所述的水的温度为50℃。
步骤(3)中的搅拌的速度为300转/分钟，搅拌的时间为1小时。
步骤(3)中的烘干是在65℃下烘干50分钟。
步骤(3)中的纱布的厚度为0.5-1mm。
实施例2
一种止血、杀菌的敷料，按重量份数计，包括以下组分：
所述敷料，按重量份数计，还包括1份的氧化锌。
所述纳米银的尺寸为40-60nm。
一种止血、杀菌的敷料的其制备方法，包括以下步骤：
(1)按配方量称取各组分，将壳聚糖、姜黄素、透明质酸钠、薄荷脑溶解于80份的水中，混合搅拌，制得混合物A，备用；
(2)将牛磺酸和纳米银、磷酸二氢铵、氧化锌加入到15份的水中搅拌，制得混合物B，
备用；
(3)将混合物A和混合物B混合，搅拌，制得混合物C，然后将医药纱布浸入混合物C
中在30℃下浸泡18小时，取出纱布，烘干，即制得所述止血、杀菌的敷料。
步骤(1)中的搅拌的速度为300转/分钟，搅拌的时间为35分钟。
步骤(2)中所述的水的温度为65℃。
步骤(3)中的搅拌的速度为250转/分钟，搅拌的时间为1.5小时。
步骤(3)中的烘干是在70℃下烘干50分钟。
步骤(3)中的纱布的厚度为1-2mm。
实施例3
一种止血、杀菌的敷料，按重量份数计，包括以下组分：
一种止血、杀菌的敷料的其制备方法，包括以下步骤：
(1)按配方量称取各组分，将壳聚糖、姜黄素、透明质酸钠、薄荷脑溶解于100份的水中，混合搅拌，制得混合物A，备用；
(2)将牛磺酸和纳米银、磷酸二氢铵加入到20份的水中搅拌，制得混合物B，备用；
(3)将混合物A和混合物B混合，搅拌，制得混合物C，然后将医药纱布浸入混合物C
中在40℃下浸泡12小时，取出纱布，烘干，即制得所述止血、杀菌的敷料。
步骤(1)中的搅拌的速度为200转/分钟，搅拌的时间为50分钟。
步骤(2)中所述的水的温度为70℃。
步骤(3)中的搅拌的速度为100转/分钟，搅拌的时间为2小时。
步骤(3)中的烘干是在65℃下烘干50分钟。
步骤(3)中的纱布的厚度为1.5-2mm。
对比例1
与实施例2相比，对比例1中所述敷料不含有姜黄素，其余组分与制备过程与实施例2相同。
对比例2
与实施例2相比，对比例2中所述敷料不含磷酸二氢铵和薄荷脑，其余组分与制备过程与实施例2相同。
对比例3
与实施例3相比，对比例3中所述敷料组分直接用100份的水混合，制得混合物C，其余后续步骤与实施例3相同。
产品效果测试
将实施例1-3、对比例1-3制备的敷料(所述敷料含有纱布，将敷料粉碎成100-200目)，分别等量加入到含有相同葡萄球菌菌落数的生理盐水中，另外还设置以对照组生理盐水(对照组中也加入等量的粉碎后的纱布，但纱布没有浸泡混合物C)，杀菌10分钟后，分别抽取1毫升置于培养基平皿中培养24小时，统计葡萄球菌菌落数量，对照组中葡萄球菌菌落数为a，实施例1-3和对比例1-3的敷料组中葡萄球菌菌落数为b，用(a-b)/a*100％(即杀菌率)来衡量敷料的杀葡萄球菌的效果，结果如表1所示。
表1：
实施例1 实施例2 实施例3 对比例1 对比例2 对比例3
杀菌率 98.9％ 99.5％ 98.2％ 85.5％ 76.6％ 70.2％
从表1可以看出，实施例1-3制备的敷料的杀葡萄球菌的效果明显优于对比例1-3制备的敷料的杀葡萄球菌的效果。
另外，用上述同样的方法来检测敷料对链球菌的杀菌效果，结果如表2所示。
表2：
实施例1 实施例2 实施例3 对比例1 对比例2 对比例3
杀菌率 99.1％ 99.6％ 98.9％ 82.5％ 73.6％ 71.2％
从表2可以看出，实施例1-3制备的敷料的杀链球菌的效果明显优于对比例1-3制备的敷料的杀链球菌的效果。
以同一只小白兔为实验对象，在小白兔的前腿的左右腿上刀划出宽2cm，长4cm的伤口，然后将实施例2制备的敷料和市售的同类型敷料(不同时含有姜黄素、透明质酸钠、牛磺酸)分别包覆3层于左右腿受伤处，结果使用实施例2制备的敷料包覆的伤口处无血液渗出，而市售的同类型敷料有血液渗出。可见，实施例2制备的敷料的止血效果更好。

Claims (10)

1.一种止血、杀菌的敷料，其特征在于，按重量份数计，包括以下组分：
2.根据权利要求1所述的敷料，其特征在于，所述敷料还含有3-30份的水。
3.根据权利要求1或2所述的敷料，其特征在于，按重量份数计，还包括0.5-2份的氧化锌。
4.根据权利要求1或2所述的敷料，其特征在于，所述纳米银的尺寸为20-80nm。
5.一种根据权利要求1-2中任一项所述的敷料的制备方法，其特征在于，包括以下步骤：
(1)按配方量称取各组分，将壳聚糖、姜黄素、透明质酸钠、薄荷脑加入水中，搅拌，制得混合物A，备用；
(2)将牛磺酸和纳米银、磷酸二氢铵加入水中，搅拌，制得混合物B，备用；
(3)将混合物A和混合物B混合，搅拌，制得混合物C，然后将纱布浸入混合物C中，
然后取出纱布，烘干，制得所述敷料。
6.根据权利要求5所述的制备方法，其特征在于，步骤(1)中的搅拌的速度为200-400转/分钟，搅拌的时间为30-50分钟；步骤(3)中的搅拌的速度为100-300转/分钟，搅拌的时间为1-2小时。
7.根据权利要求5所述的制备方法，其特征在于，步骤(2)中所述的水的温度为50-70℃。
8.根据权利要求5所述的制备方法，其特征在于，步骤(3)中的烘干是在65-75℃下保持30-50分钟。
9.根据权利要求5所述的制备方法，其特征在于，步骤(3)中的纱布的厚度为0.5-2mm。
10.根据权利要求5所述的制备方法，其特征在于，步骤(3)中将纱布浸入混合物C中在20-40℃下浸泡12-24小时。
CN201910524438.2A 2019-06-18 2019-06-18 一种止血、杀菌的敷料及其制备方法 Pending CN110201208A (zh)