CN110194935A - 一种导电无纺布胶带及其制备方法 - Google Patents
一种导电无纺布胶带及其制备方法 Download PDFInfo
- Publication number
- CN110194935A CN110194935A CN201910599098.XA CN201910599098A CN110194935A CN 110194935 A CN110194935 A CN 110194935A CN 201910599098 A CN201910599098 A CN 201910599098A CN 110194935 A CN110194935 A CN 110194935A
- Authority
- CN
- China
- Prior art keywords
- conductive
- woven fabrics
- weight
- parts
- acrylic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种导电无纺布胶带，由依次接触的单面离型膜、导电丙烯酸胶层、导电无纺布层和导电油墨层组成。本发明通过选取一种超薄的导电无纺布，导电无纺布表面涂覆一层特殊的导电丙烯酸胶层，导电无纺布背面涂覆一层导电油墨层，三层超高的导电性能叠加和协同作用，使得本发明制备得到的胶带优异的导电、屏蔽效果，同时由于导电油墨的加入还具有良好的耐腐蚀性能。
Description
技术领域
本申请涉及胶带技术领域，尤其涉及一种导电无纺布胶带及其制备方法。
背景技术
目前手机使用频率越来越高，人们对手机的要求也越来越高。随着手机系统升级，手机运行速度越来越快，手机性能的要求越来越高，产生了对胶带导电和屏蔽的需求。尤其是针对特别材质，还有可能对于胶带的可塑性、贴合性、包裹性和折叠性有特殊要求。
但现有技术公开的胶带导电、屏蔽和散热效果不佳，因此，一种导电、屏蔽和散热效果好的导电无纺布胶带是非常必要的。
发明内容
有鉴于此，本申请的目的在于提供一种导电无纺布胶带，本发明提供的胶带导电、屏蔽和散热效果好。
本发明提供了一种导电无纺布胶带，由依次接触的单面离型膜、导电丙烯酸胶层、导电无纺布层和导电油墨层组成。
优选的，所述单面离型膜的厚度为25～100μm；所述导电丙烯酸胶层的厚度为5～150μm；所述导电无纺布层的厚度为2～100μm；所述导电油墨层的厚度为1～50μm。
优选的，所述单面离型膜的厚度为25～75μm；所述导电丙烯酸胶层的厚度为5～100μm；所述导电无纺布层的厚度为2～50μm；所述导电油墨层的厚度为1～30μm。
优选的，所述单面离型膜包括聚对苯二甲酸乙二醇酯和硅油。
优选的，所述导电丙烯酸胶层包括以下组分：
丙烯酸胶粘剂80～120重量份，异氰酸酯固化剂0.1～0.3重量份、导电粒子0.5～1.5重量份、增粘树脂0.5～1.5重量份和乙酸乙酯30～50重量份；
优选的，所述异氰酸酯类固化剂选自甲苯二异氰酸酯、1,6-己二异氰酸酯、四甲基亚二甲苯基二异氰酸酯、六亚甲基二异氰酸酯和异佛尔酮二异氰酸酯中的一种或多种。
所述导电粒子选自镍粉、银粉、铜粉和石墨烯中的一种或几种；
所述增粘树脂包括丙烯酸树脂。
优选的，所述导电油墨层包括：
炭黑5～20重量份、聚氨酯树脂50～80重量份、导电粒子5～20重量份、异氰酸酯固化剂1～5重量份和调墨油5～10重量份。
优选的，所述异氰酸酯类固化剂选自甲苯二异氰酸酯、1,6-己二异氰酸酯、四甲基亚二甲苯基二异氰酸酯、六亚甲基二异氰酸酯和异佛尔酮二异氰酸酯中的一种或多种。
聚氨酯树脂为型号大日精化A-601的聚氨酯树脂和/或宏达HD-3268聚氨酯树脂。
所述导电粒子选自所述导电粒子选自镍粉、银粉、铜粉和石墨烯中的一种或几种。
本发明提供了一种导电无纺布胶带的制备方法，包括：
在所述单面离型膜上涂覆导电丙烯酸胶料，得到导电丙烯酸胶层；
在所述导电丙烯酸胶层上复合导电无纺布，得到导电无纺布层；
在所述导电无纺布层上涂覆导电油墨，得到导电无纺布胶带。
优选的，所述导电丙烯酸胶料包括以下组分：
丙烯酸胶粘剂80～120重量份，异氰酸酯固化剂0.1～0.3重量份、导电粒子0.5～1.5重量份、增粘树脂0.5～1.5重量份和乙酸乙酯30～50重量份。
与现有技术相比，本发明提供了一种导电无纺布胶带，由依次接触的单面离型膜、导电丙烯酸胶层、导电无纺布层和导电油墨层组成。本发明通过选取一种超薄的导电无纺布，导电无纺布表面涂覆一层特殊的导电丙烯酸胶层，导电无纺布背面涂覆一层导电油墨层，三层超高的导电性能叠加和协同作用，使得本发明制备得到的胶带优异的导电、屏蔽效果，同时由于导电油墨的加入还具有良好的耐腐蚀性能。
附图说明
图1为本发明提供的导电无纺布胶带的结构示意图。
具体实施方式
本发明提供了一种导电无纺布胶带及其制备方法，本领域技术人员可以借鉴本文内容，适当改进工艺参数实现。特别需要指出的是，所有类似的替换和改动对本领域技术人员来说是显而易见的，它们都属于本发明保护的范围。本发明的方法及应用已经通过较佳实施例进行了描述，相关人员明显能在不脱离本发明内容、精神和范围内对本文的方法和应用进行改动或适当变更与组合，来实现和应用本发明技术。
本发明提供了一种导电无纺布胶带，由依次接触的单面离型膜、导电丙烯酸胶层、导电无纺布层和导电油墨层组成。
参见图1，图1为本发明提供的导电无纺布胶带的结构示意图，其中，1为单面离型膜，2为导电丙烯酸胶层，3为导电无纺布层，4为导电油墨层。
本发明提供的导电无纺布胶带包括单面离型膜1。本发明对于所述单面离型膜的组成不进行限定，市售即可；优选包括聚对苯二甲酸乙二醇酯和硅油。
本发明所述单面离型膜的厚度优选为25～100μm；更优选为25～75μm。
本发明提供的导电无纺布胶带包括导电丙烯酸胶层2；本发明所述导电丙烯酸胶层的厚度优选为5～150μm；更优选为5～100μm。
按照本发明，所述导电丙烯酸胶层优选包括以下组分：
丙烯酸胶粘剂80～120重量份，异氰酸酯固化剂0.1～0.3重量份、导电粒子0.5～1.5重量份、增粘树脂0.5～1.5重量份和乙酸乙酯30～50重量份；
本发明所述导电丙烯酸胶层包括80～120重量份的丙烯酸胶粘剂；优选包括90～110重量份的丙烯酸胶粘剂；更优选包括100重量份的丙烯酸胶粘剂。
本发明对于所述丙烯酸胶粘剂不进行限定，本领域随机数人员熟知的市售即可。
按照本发明，所述导电丙烯酸胶层的导电率为103-105S/M。
本发明所述导电丙烯酸胶层包括0.1～0.3重量份异氰酸酯固化剂；优选包括0.15～0.25重量份异氰酸酯固化剂；更优选包括0.2重量份异氰酸酯固化剂。
其中，本发明所述异氰酸酯类固化剂优选选自甲苯二异氰酸酯、1,6-己二异氰酸酯、四甲基亚二甲苯基二异氰酸酯、六亚甲基二异氰酸酯和异佛尔酮二异氰酸酯中的一种或多种。本发明对其来源不进行限定，市售即可。
本发明所述导电丙烯酸胶层包括0.5～1.5重量份的导电粒子；优选包括0.8～1.2重量份的导电粒子，更优选包括1重量份的导电粒子。
本发明所述导电粒子优选选自镍粉、银粉、铜粉和石墨烯中的一种或几种；更优选为镍粉和石墨烯中的一种或几种；最优选为镍粉。
本发明提供的导电丙烯酸胶层包括0.5～1.5重量份的增粘树脂；优选包括0.8～1.2重量份的增粘树脂，更优选包括1重量份的增粘树脂。
本发明所述增粘树脂包括丙烯酸树脂。
本发明提供的导电丙烯酸胶层包括30～50重量份的乙酸乙酯；更优选包括35～45重量份的乙酸乙酯；最优选包括40重量份的乙酸乙酯。
本发明通过增粘树脂、导电粒子、丙烯酸胶粘剂和异氰酸酯固化剂等配合作用，制备的导电丙烯酸胶层导电性、屏蔽性能好。
本发明提供的导电无纺布胶带包括导电无纺布层。
本发明所述导电无纺布层的厚度优选为2～100μm；更优选为2～50μm。
本发明所述导电无纺布层为导电无纺布；本发明对其不进行特殊限定，本领域技术人员熟知的即可。
本发明提供的导电无纺布胶带包括导电油墨层。所述导电油墨层的导电率为104-105S/M。
按照本发明，所述导电油墨层的厚度优选为1～50μm；更优选为1～30μm。
其中，所述导电油墨层包括：
炭黑5～20重量份、聚氨酯树脂50～80重量份、导电粒子5～20重量份、异氰酸酯固化剂1～5重量份和调墨油5～10重量份。
本发明所述导电油墨层包括5～20重量份的炭黑；更优选为8～18重量份的炭黑；最优选包括10～15重量份的炭黑。
本发明所述导电油墨层包括50～80重量份的聚氨酯树脂；优选包括55～75重量份的聚氨酯树脂；更优选包括60～70重量份的聚氨酯树脂。
本发明聚氨酯树脂为型号大日精化A-601的聚氨酯树脂和/或宏达HD-3268聚氨酯树脂。
本发明所述导电油墨层包括5～20重量份的导电粒子；更优选包括8～18重量份的导电粒子；最优选包括10～15重量份的导电粒子。
本发明所述导电粒子优选选自镍粉、银粉、铜粉和石墨烯中的一种或几种；更优选为镍粉和石墨烯中的一种或几种；最优选为镍粉。
本发明所述导电油墨层优选包括1～5重量份异氰酸酯固化剂；更优选包括2～4重量份异氰酸酯固化剂。
本发明所述异氰酸酯类固化剂优选选自甲苯二异氰酸酯、1,6-己二异氰酸酯、四甲基亚二甲苯基二异氰酸酯、六亚甲基二异氰酸酯和异佛尔酮二异氰酸酯中的一种或多种。
本发明所述导电油墨层包括5～10重量份调墨油；更优选包括6～9重量份调墨油；本发明对于所述调墨油的具体组成不进行限定，本领域技术人员熟知的即可。
本发明通过选取一种超薄的导电无纺布，导电无纺布表面涂覆一层特殊的导电丙烯酸胶层，导电无纺布背面涂覆一层导电油墨层，三层超高的导电性能叠加和协同作用，使得本发明制备得到的胶带优异的导电、屏蔽效果，同时由于导电油墨的加入还具有良好的耐腐蚀性能。
本发明所述导电无纺布胶带尤其适用于于背光模组的包边工艺,EMI/RFI屏蔽和密封连接。
本发明提供了一种导电无纺布胶带的制备方法，包括：
在所述单面离型膜上涂覆导电丙烯酸胶料，得到导电丙烯酸胶层；
在所述导电丙烯酸胶层上复合导电无纺布，得到导电无纺布层；
在所述导电无纺布层上涂覆导电油墨，得到导电无纺布胶带。
本发明提供的导电无纺布胶带的制备方法首先在所述单面离型膜上涂覆导电丙烯酸胶料，得到导电丙烯酸胶层；
本发明对于所述具体的涂覆方式不进行限定，本领域技术人员熟知的即可，保证上述组成和厚度即可。
本发明所述导电丙烯酸胶料包括以下组分：
丙烯酸胶粘剂80～120重量份，异氰酸酯固化剂0.1～0.3重量份、导电粒子0.5～1.5重量份、增粘树脂0.5～1.5重量份和乙酸乙酯30～50重量份。
对于上述导电丙烯酸胶料的组成和配比上述已经有了清楚的描述，在此不再赘述。
在所述导电丙烯酸胶层上复合导电无纺布，得到导电无纺布层。
本发明对于所述导电无纺布不进行限定，本领域技术人员熟知满足上述厚度的即可。
在所述导电无纺布层上涂覆导电油墨，得到导电无纺布胶带。
本发明对于所述导电油墨层的具体组分上述有了清楚的描述，直接混合即可，本领域技术人员熟知具体操作方式即可，保证上述组成和厚度即可。
本发明提供了一种导电无纺布胶带，由依次接触的单面离型膜、导电丙烯酸胶层、导电无纺布层和导电油墨层组成。本发明通过选取一种超薄的导电无纺布，导电无纺布表面涂覆一层特殊的导电丙烯酸胶层，导电无纺布背面涂覆一层导电油墨层，三层超高的导电性能叠加和协同作用，使得本发明制备得到的胶带优异的导电、屏蔽效果，同时由于导电油墨的加入还具有良好的耐腐蚀性能。同时通过上述层结构以及具体组分的协同作用使得本发明制备得到的导电无纺布胶带还具有良好的散热性，良好的贴合性以及包裹性。
为了进一步说明本申请，下面结合实施例对本申请提供的具有电磁屏蔽功能的无基材胶带进行详细地描述，但不能将它们理解为对本申请保护范围的限定。
实施例1
将80重量份的丙烯酸胶粘剂，0.1重量份的甲苯二异氰酸酯、0.5重量份的导电粒子镍粉、0.5重量份丙烯酸树脂和30重量份乙酸乙酯混合，得到导电丙烯酸胶料。
将5重量份炭黑、50重量份A-601的聚氨酯树脂、5重量份镍粉、1重量份1,6-己二异氰酸酯和5重量份调墨油混合，得到导电油墨料。
在厚度为10μm导电无纺布层的一面涂覆50μm上述制备的导电丙烯酸胶料，得到导电丙烯酸胶层；
在所述导电无纺布层的另一面涂覆上述制备的20μm导电油墨，得到导电油墨层；
在所述导电丙烯酸胶层上覆30μm单面离型膜，得到导电无纺布胶带。
本发明对实施例1制备的导电无纺布胶带进行印刷性能测试，测试结果表明：实施例1制备的导电无纺布胶带的电阻值为0.1-0.5,屏蔽性能优异，用普通胶带和导电无纺布胶带分别包裹手机后，同时拨打两个手机，普通胶带可正常接通，而本实施例的无纺布胶带则，提示号码无法接通。
实施例2
将100重量份的丙烯酸胶粘剂，0.2重量份的四甲基亚二甲苯基二异氰酸酯、1重量份的导电粒子镍粉、1重量份丙烯酸树脂和40重量份乙酸乙酯混合，得到导电丙烯酸胶料。
将10重量份炭黑、60重量份A-601的聚氨酯树脂、10重量份镍粉、3重量份六亚甲基二异氰酸酯和7重量份调墨油混合，得到导电油墨料。
在厚度为30μm导电无纺布层的一面涂覆30μm上述制备的导电丙烯酸胶料，得到导电丙烯酸胶层；
在所述导电无纺布层的另一面涂覆上述制备的10μm导电油墨，得到导电油墨层；
在所述导电丙烯酸胶层上覆50μm单面离型膜，得到导电无纺布胶带。
本发明对实施例1制备的导电无纺布胶带进行印刷性能测试，测试结果表明：实施例2制备的导电无纺布胶带的电阻值为0.1-0.6；屏蔽性能优异，用普通胶带和导电无纺布胶带分别包裹手机后，同时拨打两个手机，普通胶带可正常接通，而本实施例的的无纺布胶带则，提示号码无法接通。
实施例3
将120重量份的丙烯酸胶粘剂，0.3重量份的异佛尔酮二异氰酸酯、1.5重量份的导电粒子镍粉、1.5重量份丙烯酸树脂和50重量份乙酸乙酯混合，得到导电丙烯酸胶料。
将20重量份炭黑、80重量份A-601的聚氨酯树脂、20重量份镍粉、1～5重量份1,6-己二异氰酸酯和10重量份调墨油混合，得到导电油墨料。
在厚度为50μm导电无纺布层的一面涂覆80μm上述制备的导电丙烯酸胶料，得到导电丙烯酸胶层；
在所述导电无纺布层的另一面涂覆上述制备的30μm导电油墨，得到导电油墨层；
在所述导电丙烯酸胶层上覆70μm单面离型膜，得到导电无纺布胶带。
本发明对实施例1制备的导电无纺布胶带进行印刷性能测试，测试结果表明：实施例3制备的导电无纺布胶带的电阻值为0.1-0.5；屏蔽性能优异，用普通胶带和导电无纺布胶带分别包裹手机后，同时拨打两个手机，普通胶带可正常接通，而本实施例的无纺布胶带则，提示号码无法接通。
以上所述仅是本申请的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本申请原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本申请的保护范围。
Claims (10)
1.一种超薄哑黑导电无纺布胶带，由依次接触的单面离型膜、导电丙烯酸胶层、导电无纺布层和导电油墨层组成。
2.根据权利要求1所述的导电无纺布胶带，其特征在于，所述单面离型膜的厚度为25～100μm；所述导电丙烯酸胶层的厚度为5～150μm；所述导电无纺布层的厚度为2～100μm；所述导电油墨层的厚度为1～50μm。
3.根据权利要求1所述的导电无纺布胶带，其特征在于，所述单面离型膜的厚度为25～75μm；所述导电丙烯酸胶层的厚度为5～100μm；所述导电无纺布层的厚度为2～50μm；所述导电油墨层的厚度为1～30μm。
4.根据权利要求1所述的导电无纺布胶带，其特征在于，所述单面离型膜包括聚对苯二甲酸乙二醇酯和硅油。
5.根据权利要求1所述的导电无纺布胶带，其特征在于，所述导电丙烯酸胶层包括以下组分：
丙烯酸胶粘剂80～120重量份，异氰酸酯固化剂0.1～0.3重量份、导电粒子0.5～1.5重量份、增粘树脂0.5～1.5重量份和乙酸乙酯30～50重量份。
6.根据权利要求5所述的导电无纺布胶带，其特征在于，
所述异氰酸酯类固化剂选自甲苯二异氰酸酯、1,6-己二异氰酸酯、四甲基亚二甲苯基二异氰酸酯、六亚甲基二异氰酸酯和异佛尔酮二异氰酸酯中的一种或多种；
所述导电粒子选自镍粉、银粉、铜粉和石墨烯中的一种或几种；
所述增粘树脂包括丙烯酸树脂。
7.根据权利要求1所述的导电无纺布胶带，其特征在于，所述导电油墨层包括：
炭黑5～20重量份、聚氨酯树脂50～80重量份、导电粒子5～20重量份、异氰酸酯固化剂1～5重量份和调墨油5～10重量份。
8.根据权利要求7所述的导电无纺布胶带，其特征在于，所述异氰酸酯类固化剂选自甲苯二异氰酸酯、1,6-己二异氰酸酯、四甲基亚二甲苯基二异氰酸酯、六亚甲基二异氰酸酯和异佛尔酮二异氰酸酯中的一种或多种；
聚氨酯树脂为型号大日精化A-601的聚氨酯树脂和/或宏达HD-3268聚氨酯树脂；
所述导电粒子选自所述导电粒子选自镍粉、银粉、铜粉和石墨烯中的一种或几种。
9.一种导电无纺布胶带的制备方法，其特征在于，包括：
在所述单面离型膜上涂覆导电丙烯酸胶料，得到导电丙烯酸胶层；
在所述导电丙烯酸胶层上复合导电无纺布，得到导电无纺布层；
在所述导电无纺布层上涂覆导电油墨，得到导电无纺布胶带。
10.根据权利要求9所述的制备方法，其特征在于，所述导电丙烯酸胶料包括以下组分：
丙烯酸胶粘剂80～120重量份，异氰酸酯固化剂0.1～0.3重量份、导电粒子0.5～1.5重量份、增粘树脂0.5～1.5重量份和乙酸乙酯30～50重量份。