CN110054951A - 一种仿花岗岩效果的地坪涂料体系及其使用方法 - Google Patents
一种仿花岗岩效果的地坪涂料体系及其使用方法 Download PDFInfo
- Publication number
- CN110054951A CN110054951A CN201910290084.XA CN201910290084A CN110054951A CN 110054951 A CN110054951 A CN 110054951A CN 201910290084 A CN201910290084 A CN 201910290084A CN 110054951 A CN110054951 A CN 110054951A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- agent
- coating
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种水性仿花岗岩石材效果的地坪漆涂料体系，包括：一层以上的底漆涂层，一层以上的水性多彩涂料涂层和一层以上的水性环氧丙烯酸杂化地坪漆涂层。本发明改变传统地坪材料单一颜色的表现效果，水性多彩漆、水性环氧丙烯酸杂化的地坪漆的搭配具有突出的耐候性、耐酸、耐碱、耐盐雾等特性，也为解决水性环氧地坪漆的耐候性差提出了新的方案，使地坪漆颜色单一的印象，过度到色彩丰富的花岗岩石材效果，相对于昂贵价格的花岗岩石材装饰地面，具有很高的使用价值。
Description
技术领域
本发明涉及一种仿花岗岩石材效果的地坪涂料体系及其使用方法，具体涉及一种水性多彩漆与水性环氧丙烯酸杂化地坪漆的涂料体系及其使用方法。
背景技术
一般地面的装饰材料，有地坪漆和花岗岩或大理石石材等，地坪漆给印象是颜色单调、单一色，如：绿色、灰色、黄色等，随着人们生活水平的提高，除对地坪漆的功能性要求之外，又对地坪漆的装饰性要求越来越高，单一色的地坪漆越来越难以满足人们要求。而花岗岩、大理石以其庄重的质感、耐久的品质、多样的色彩受到大家的青睐，但花岗岩、大理石的缺点也显而易见，价格昂贵、施工复杂、能源消耗大、破坏自然环境。与我国经济发展提出节约能源、节能减排、生态环保、低碳循环经济基本模式不相符，使很多用户望而却步。因此，开发具有花岗岩石材效果的地坪漆，既能有效弥补上述材料的不足，又环保、节能，实用价值高。
发明内容
本发明的目的是提供一种水性仿花岗岩石材效果的地坪涂料体系及其使用方法，以满足市场的多方面需求。
本发明的第一个目的是提供一种水性多彩涂料的制备方法，其特征在于，包括以下步骤：依据所选花岗岩的色点颜色将水性多彩基础漆进行调色，然后将300～400份调色水性多彩基础漆加入到300份隔离剂溶液中，用真空抽滤机抽滤出和所选花岗岩色点大小一致的色点，然后再加入300～400份的合成乳液，混合均匀并调整粘度，即可得到水性多彩涂料。
所述的水性多彩基础漆为：按总重量份为1000份计，取300～430份水、7～14份羟乙基纤维素、0.5～1.5份PH值调节剂、3～5份分散剂、1～3份杀菌剂、8～10份防冻剂、50～100份高岭土、0～100份钛白粉、350～400份弹性丙烯酸乳液、10～15份成膜助剂、1～3份渗透型润湿剂、80～120份隔离剂、1～3份聚氨酯增稠剂、3～5份碱溶涨增稠剂和3～5份消泡剂；将上述原料高速搅拌下依次混合并分散均匀即可。
所述的羟乙基纤维素增稠剂的分子量为3～10万；所述的分散剂为聚羧酸铵盐分散剂，例如阿克苏诺贝尔公司生产的Dispersant 747产品；所述的高岭土为煅烧型高岭土，例如山西恒源高岭土有限公司的HY-T-80产品；所述的钛白粉为金红石型钛白粉，例如四川龙蟒集团的R-996产品；所述的弹性丙烯酸乳液为纯丙烯酸酯聚合乳液，例如巴德富(常熟)科技有限公司的RS6733产品；所述的成膜助剂为十二碳醇酯或脂肪族羧酸二酯；所述的渗透型润湿剂为亲水性润湿剂，例如美国陶氏公司的BD405；所述的隔离剂为有机改性的蒙脱土，例如BYK助剂有限公司的S482或RDS；所述的聚氨酯增稠剂为非离子型聚氨酯流变改性剂，例如美国陶氏公司的SCT-275；所述的碱溶胀增稠剂为疏水改性碱溶胀缔合型增稠剂，例如美国陶氏公司的TT-935产品；
所述的隔离剂溶液为：按总重量份为1000份计，将920～950份的水加入到分散缸中，边搅拌边向分散缸中加入1～5份黄原胶，搅拌至均匀，再依次向分散缸中加入1～3份杀菌剂、1～3份消泡剂和3～5份PH值调节剂，然后缓慢加入40～60份隔离剂分散至无颗粒且半透明的溶液。
所述的黄原胶为酸性胞外杂多糖类高分子化合物，例如上海裕竹实业有限公司的HM-200产品。
所述的合成乳液为：按总重量份为1000份计，取750～800份硅丙乳液、50～70份成膜助剂、0.5～1.5份PH值调节剂、1～3份杀菌剂、20～40份防冻剂、1～3份消泡剂、80～150份水、3～5份碱溶涨增稠剂，在高速搅拌下将上述原料依次混合并分散均匀，得到合成乳液。
所述的硅丙乳液为改性硅丙乳液，例如巴德富(常熟)科技有限公司的RS3788产品；所述的成膜助剂为十二碳醇酯或脂肪族羧酸二酯，例如美国伊斯曼公司的Texanol产品；所述的碱溶胀增稠剂为疏水改性碱溶胀缔合型增稠剂，例如美国陶氏公司的TT-935产品。
进一步地，所述的水的电导率≤2US/CM；所述的PH值调节剂为2-氨基-2-甲基-1-丙醇；所述的杀菌剂为2-甲基-4-异噻唑啉-3-酮与1，2-苯并异噻唑啉-3-酮的复配溶液，例如托尔专用化学品(上海)有限公司的MBS产品；所述的防冻剂为1,2-丙二醇；所述的消泡剂为星型聚合物消泡剂，例如德国巴斯夫公司生产的FOAMSTAR A10产品。
本发明的第二个目的是提供一种水性环氧丙烯酸杂化地坪漆，其特征在于，包括甲组份和乙组份；将甲组份与乙组份按1.5～2.5：1的比例混合，搅拌均匀即得到水性环氧丙烯酸杂化地坪漆；
其中：所述的甲组份为：按总重量份为100份计，将80～85份水性环氧丙烯酸杂化树脂、5～12份活性稀释剂、0.5～1.5份流平剂、1～2份消泡剂按顺序加入至搅拌釜中，在速率为800～1500r/min的条件下搅拌20～60min即可得到；所述的乙组份为改性胺水性固化剂，为市售产品，例如美国空气化工公司的Anquamine 721水性环氧固化剂。
所述的环氧树脂为水性环氧丙烯酸杂化树脂，例如：陶氏AEH-20水性环氧丙烯酸杂化树脂；所述的活性稀释剂为碳原子数12～14的醇缩水甘油醚，例如：江苏三木化工股份有限公司的SM-90稀释剂；所述的流平剂为聚醚改性聚二甲基硅氧烷，例如：德国毕克化学的BYK333流平剂；所述的消泡剂为星型聚合物消泡剂，例如德国巴斯夫公司生产的FOAMSTAR A10产品。
本发明的第三个目的是提供一种水性仿花岗岩石材效果的地坪涂料体系，其特征在于，包括：一层以上的底漆涂层，一层以上的水性多彩涂料涂层和一层以上的水性环氧丙烯酸杂化的地坪漆涂层。
所述的底漆可以是市场上所售的任何地坪底漆，优选为以丙烯酸为成膜物质的高遮盖底漆或以丙烯酸为成膜物质的含砂高遮盖底漆，在使用时可根据需要进行调色。
为了实现上述目的，本发明的一种水性仿花岗岩石材效果的地坪漆涂料的施工方法，其特征在于：包括以下步骤：(1)清理需要涂装的基层表面；(2)对基层表面辊涂或喷涂底漆涂层，干燥24～48小时后或者待完全干透；(3)在底漆涂层的上表面喷涂水性多彩涂料涂层，干燥48～72小时后或者待完全干透；(4)在水性多彩涂料涂层的上表面辊涂或喷涂水性环氧丙烯酸杂化地坪漆涂层，干燥48～72小时后或者完全干透即可。
进一步地，所述的步骤(1)中，基层表面应结实平整、无浮灰、无裂缝、PH值≤10、含水率≤10％；
进一步地，本发明的一种水性仿花岗岩石材效果的地坪漆的施工方法，施工的环境温度可为5～35℃、空气相对湿度小于85％。
本发明改变传统地坪材料单一颜色的表现效果，不同质感的水性多彩基础漆与水性环氧丙烯酸杂化的地坪漆搭配，具有突出的耐候性、耐酸、耐碱、耐盐雾等特性，为解决水性环氧地坪漆的耐候性差提出了新的方案，可以获得色彩丰富且具有逼真的平面或毛面的花岗岩石的效果，改变了地坪漆颜色单一的印象，相对于昂贵价格的花岗岩石材装饰地面，具有很高的使用价值。
具体实施方式
以下将结合实施例对本发明的构思及产生的技术效果作进一步说明，以充分地了解本发明的目的、特征和效果，本实施例的内容不能作为限制本发明技术所要保护的范围。
本实施例和对比例中的原材料均为市售产品。原材料牌号和生产厂家：
实施例1
(1)水性多彩基础漆：按总重量份为1000份计，取316.5份水、12份羟乙基纤维素Natrosol 250HBR、1.5份PH值调节剂AMP-95、5份分散剂747、2份杀菌剂MBS、10份防冻剂1,2-丙二醇、100份高岭土HY-T-80、10份钛白粉R996、400份弹性丙烯酸乳液RS-6733、10份成膜助剂Texanol、3份渗透型润湿剂BD405、120份隔离剂溶液、2份聚氨酯增稠剂SCT-275、3份碱溶涨增稠剂TT-935和5份消泡剂A10；将上述原料高速搅拌下依次混合并分散均匀即可。
(2)隔离剂溶液：按总重量份为1000份计，将926份水加入到分散缸中，边搅拌边向分散缸中加入5份黄原胶HM-200，搅拌至均匀，再依次向分散缸中加入3份杀菌剂MBS、3份消泡剂A10和3份PH值调节剂AMP-95，然后缓慢加入60份隔离剂分散至无颗粒且半透明的溶液。
(3)合成乳液：按总重量份为1000份计，取800份硅丙乳液、50份成膜助剂Texanol、1.5份PH值调节剂AMP-45、3份杀菌剂MBS、20份防冻剂1,2-丙二醇、3份消泡剂A10、119.5份水、3份碱溶涨增稠剂TT-935，在高速搅拌下将上述原料依次混合并分散均匀，得到合成乳液。
(4)水包水多彩漆的制备：依据所选花岗岩的色点颜色将水性多彩基础漆进行调色，调出所需的各彩点颜色，然后将300份调色水性多彩基础漆加入到300份隔离剂溶液中，使用真空抽滤机时，注意选择合适目数的滤网抽滤出和所选花岗岩色点大小一致的色点(注：此实施例彩点为小点)，然后再加入400份的合成乳液，低速混合均匀即可得到水性多彩涂料。
(5)水性环氧丙烯酸杂化地坪漆的制备过程：甲组份为：按总重量份为100份计，将85份水性环氧丙烯酸杂化树脂AEH-20、10份活性稀释剂SM-90、1.5份流平剂BYK333、3.5份消泡剂A10按顺序加入至搅拌釜中，在速率为900～1200r/min的条件下搅拌30～40min即可得到；乙组分为Anquamine 721水性环氧固化剂；将甲组份与乙组份按2：1的比例混合，搅拌均匀即得到水性环氧丙烯酸杂化地坪漆。
施工过程：清理需要涂装的基层表面；对基层表面辊涂或喷涂底漆涂层50微米，干燥48小时后完全干透；在底漆涂层上表面喷涂水性多彩涂料涂层300微米，干燥48小时后或者待完全干透；在水性多彩涂料涂层上表面辊涂或喷涂水性环氧丙烯酸杂化的地坪漆涂层60微米，干燥72小时后或者待完全干透即可。
进一步地，所述的步骤(3)中，在步骤(1)上并对比所仿的花岗岩石材效果，可一次喷涂也可多次喷涂，为防止一次喷涂不能准确达到效果，优选为分两次喷涂，待完全干透；所述的步骤(4)中，在步骤(3)上辊涂或喷涂水性环氧丙烯酸杂化地坪漆2道；若两道施工，间隔时间48小时以上；待完全干透即完成。
实施例2
(1)水性多彩基础漆：按总重量份为1000份计，取379.5份水、12份羟乙基纤维素Natrosol 250HBR、1.5份PH值调节剂AMP-95、5份分散剂747、3份杀菌剂MBS、10份防冻剂1,2-丙二醇、50份高岭土HY-T-80、10份钛白粉R996、400份弹性丙烯酸乳液RS-6733、15份成膜助剂Texanol、3份渗透型润湿剂BD405、100份隔离剂溶液、3份聚氨酯增稠剂SCT-275、5份碱溶涨增稠剂TT-935和3份消泡剂A10；将上述原料高速搅拌下依次混合并分散均匀即可。
(2)隔离剂溶液：按总重量份为1000份计，将924份水加入到分散缸中，边搅拌边向分散缸中加入5份黄原胶HM-200，搅拌至均匀，再依次向分散缸中加入3份杀菌剂MBS、3份消泡剂A10和5份PH值调节剂AMP-95，然后缓慢加入60份隔离剂分散至无颗粒且半透明的溶液。
(3)合成乳液：按总重量份为1000份计，取800份硅丙乳液、50份成膜助剂Texanol、1.5份PH值调节剂AMP-95、3份杀菌剂MBS、20份防冻剂1,2-丙二醇、3份消泡剂A10、119.5份水、3份碱溶涨增稠剂TT-935，在高速搅拌下将上述原料依次混合并分散均匀，得到合成乳液。
(4)水包水多彩漆的制备：依据所选花岗岩的色点颜色将水性多彩基础漆进行调色，调出所需的各彩点颜色，然后将400份调色水性多彩基础漆加入到300份隔离剂溶液中，使用真空抽滤机时，注意选择不同目数的滤网，抽滤出和所选花岗岩色点大小一致的色点(注：此实施例彩点为大点)，然后再加入300份的合成乳液，低速混合均匀，调整粘度，即可得到水性多彩涂料。
(5)水性环氧丙烯酸杂化地坪漆的制备过程：
甲组份为：按总重量份为100份计，将85份水性环氧丙烯酸杂化树脂AEH-20、10份活性稀释剂SM-90、1.5份流平剂BYK333、3.5份消泡剂A10按顺序加入至搅拌釜中，在速率为900～1200r/min的条件下搅拌30～40min即可得到；乙组分为Anquamine 721水性环氧固化剂；将甲组份与乙组份按1.9：1的比例混合，搅拌均匀即得到水性环氧丙烯酸杂化地坪漆。
施工过程：清理需要涂装的基层表面；对基层表面辊涂或喷涂底漆涂层50微米，干燥24～48小时后完全干透；在底漆涂层上表面喷涂水性多彩涂料涂层500微米，干燥48～72小时后或者待完全干透；在水性多彩涂料涂层上表面辊涂或喷涂水性环氧丙烯酸杂化的地坪漆涂层60微米，干燥48～72小时后或者待完全干透即可。
Claims (15)
1.一种水性多彩涂料的制备方法，其特征在于，包括以下步骤：依据所选花岗岩的色点颜色将水性多彩基础漆进行调色，然后将300～400份调色水性多彩基础漆加入到300份隔离剂溶液中，用真空抽滤机抽滤出和所选花岗岩色点大小一致的色点，然后再加入300～400份的合成乳液，混合均匀并调整粘度，即可得到水性多彩涂料。
2.根据权利要求1所述的水性多彩涂料的制备方法，其特征在于，所述的水性多彩基础漆为：按总重量份为1000份计，取300～430份水、7～14份羟乙基纤维素、0.5～1.5份PH值调节剂、3～5份分散剂、1～3份杀菌剂、8～10份防冻剂、50～100份高岭土、0～100份钛白粉、350～400份弹性丙烯酸乳液、10～15份成膜助剂、1～3份渗透型润湿剂、80～120份隔离剂、1～3份聚氨酯增稠剂、3～5份碱溶涨增稠剂和3～5份消泡剂；将上述原料高速搅拌下依次混合并分散均匀即可。
3.根据权利要求2所述的水性多彩涂料的制备方法，其特征在于，所述的羟乙基纤维素增稠剂的分子量为3～10万；所述的分散剂为聚羧酸铵盐分散剂；所述的高岭土为煅烧型高岭土；所述的钛白粉为金红石型钛白粉；所述的弹性丙烯酸乳液为纯丙烯酸酯聚合乳液；所述的成膜助剂为十二碳醇酯或脂肪族羧酸二酯；所述的渗透型润湿剂为亲水性润湿剂；所述的隔离剂为有机改性的蒙脱土；所述的聚氨酯增稠剂为非离子型聚氨酯流变改性剂；所述的碱溶胀增稠剂为疏水改性碱溶胀缔合型增稠剂。
4.根据权利要求1所述的水性多彩涂料的制备方法，其特征在于，所述的隔离剂溶液为：按总重量份为1000份计，将920～950份的水加入到分散缸中，边搅拌边向分散缸中加入1～5份黄原胶，搅拌至均匀，再依次向分散缸中加入1～3份杀菌剂、1～3份消泡剂和3～5份PH值调节剂，然后缓慢加入40～60份隔离剂分散至无颗粒且半透明的溶液。
5.根据权利要求4所述的水性多彩涂料的制备方法，其特征在于，所述的黄原胶为酸性胞外杂多糖类高分子化合物。
6.根据权利要求1所述的水性多彩涂料的制备方法，其特征在于，所述的合成乳液为：按总重量份为1000份计，取750～800份硅丙乳液、50～70份成膜助剂、0.5～1.5份PH值调节剂、1～3份杀菌剂、20～40份防冻剂、1～3份消泡剂、80～150份水、3～5份碱溶涨增稠剂，在高速搅拌下将上述原料依次混合并分散均匀，得到合成乳液。
7.根据权利要求6所述的水性多彩涂料的制备方法，其特征在于，所述的成膜助剂为十二碳醇酯或脂肪族羧酸二酯；所述的碱溶胀增稠剂为疏水改性碱溶胀缔合型增稠剂。
8.根据权利要求2、4或6任一所述的水性多彩涂料的制备方法，其特征在于，所述的水的电导率≤2 US/CM；所述的PH值调节剂为2-氨基-2-甲基-1-丙醇；所述的杀菌剂为2-甲基-4-异噻唑啉-3-酮与1，2-苯并异噻唑啉-3-酮的复配溶液；所述的防冻剂为1,2-丙二醇；所述的消泡剂为星型聚合物消泡剂。
9.一种水性环氧丙烯酸杂化地坪漆，其特征在于，包括甲组份和乙组份；将甲组份与乙组份按1.5～2.5：1的比例混合，搅拌均匀即得到水性环氧丙烯酸杂化地坪漆；
其中：所述的甲组份为：按总重量份为100份计，将80～85份水性环氧丙烯酸杂化树脂、5～12份活性稀释剂、0.5～1.5份流平剂、1～2份消泡剂按顺序加入至搅拌釜中，在速率为800～1500r/min的条件下搅拌20～60min即可得到；所述的乙组份为改性胺水性固化剂。
10.根据权利要求9所述的水性环氧丙烯酸杂化地坪漆，其特征在于，所述的环氧树脂为水性环氧丙烯酸杂化树脂；所述的活性稀释剂为碳原子数12～14的醇缩水甘油醚；所述的流平剂为聚醚改性聚二甲基硅氧烷；所述的消泡剂为星型聚合物消泡剂。
11.一种水性仿花岗岩石材效果的地坪涂料体系，其特征在于，包括：一层以上的底漆涂层，一层以上的水性多彩涂料涂层和一层以上的水性环氧丙烯酸杂化地坪漆涂层。
12.根据权利要求11所述的水性仿花岗岩石材效果的地坪涂料体系，其特征在于，所述的底漆涂层为以丙烯酸为成膜物质的高遮盖底漆或以丙烯酸为成膜物质的含砂高遮盖底漆。
13.根据权利要求11所述的水性仿花岗岩石材效果的地坪涂料体系的施工方法，其特征在于，包括以下步骤：（1）清理需要涂装的基层表面；（2）对基层表面辊涂或喷涂底漆涂层，干燥24～48小时后或者待完全干透；（3）在底漆涂层的上表面喷涂水性多彩涂料涂层，干燥48～72小时后或者待完全干透；（4）在水性多彩涂料涂层的上表面辊涂或喷涂水性环氧丙烯酸杂化地坪漆涂层，干燥48～72小时后或者完全干透即可。
14.根据权利要求13所述的水性仿花岗岩石材效果的地坪涂料体系的施工方法，其特征在于，所述的步骤（1）中，基层表面应结实平整、无浮灰、无空鼓、无裂缝、PH值≤10、含水率≤10%。
15.根据权利要求13所述的水性仿花岗岩石材效果的地坪涂料体系的施工方法，其特征在于，施工的环境温度可为5～35℃、空气相对湿度小于85%。