CN109880257A - 一种医用高强度pvc膜及其制备方法 - Google Patents
一种医用高强度pvc膜及其制备方法 Download PDFInfo
- Publication number
- CN109880257A CN109880257A CN201910204532.XA CN201910204532A CN109880257A CN 109880257 A CN109880257 A CN 109880257A CN 201910204532 A CN201910204532 A CN 201910204532A CN 109880257 A CN109880257 A CN 109880257A
- Authority
- CN
- China
- Prior art keywords
- parts
- cooling
- pvc film
- food
- medical high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种医用高强度PVC膜，由以下重量份的原料配制而成：PVC树脂粉100份，食品级增塑剂0.8‑1.1份，食品级稳定剂3.0‑3.5份，加工助剂1.5‑1.7份，增强剂6‑7份，润滑剂0.8‑1份，色料群青0.06‑0.07份。本发明提供一种医用高强度PVC膜，寿命长，强度高，耐磨性好，防水性高，同时提供制备方法可以大规模生产。
Description
技术领域
本发明属于医用器材技术领域，具体涉及一种医用高强度PVC膜及其制备方法。
背景技术
医护工作者是直接与细菌、病毒对话的人群，对于与一些战地医护工作者或户外医护工作者，常规的医用药包不能满足其日常的需求，由于现有的医用药包采用布料缝制而成，其强度差，防水性差，而且随着现有的新材料的性能不断完善，是很多新材料不断地在新的领域中进行应用，如果采用PVC膜制备医疗包，如何将PVC膜制备成兼具抗菌、耐腐蚀、高强度，以及如何大规模的生产是个难题。
发明内容
发明目的：本发明的目的是为了弥补现有技术的不足，提供一种医用高强度PVC膜，其可以有效解决3D打印纸寿命短，强度不足，耐磨性差，而且不适合大规模的生产问题。
技术方案：一种医用高强度PVC膜，由以下重量份的原料配制而成：PVC树脂粉100份，食品级增塑剂0.8-1.1份，食品级稳定剂 3.0-3.5份，加工助剂1.5-1.7份，增强剂6-7份，润滑剂0.8-1份，色料群青0.06-0.07份。
优选的，医用高强度PVC膜由以下重量比的原料配制而成：由以下重量份的原料配制而成：PVC树脂粉100份，食品级增塑剂1份，食品级稳定剂 3.3份，加工助剂1.65份，增强剂6.5份，润滑剂0.9份，色料群青0.065份。
优选的，所述PVC树脂粉使用聚合度800。
一种制备权利要求1中医用高强度PVC膜的制备方法，包括如下步骤：
a、混合、按照质量份将原料投入高速混合机进行混合搅拌，混合时间260~320秒，温度为80~90℃；
b、冷拌、将步骤a混合后的组分输送到低速冷拌机内，进行搅拌冷却，控制冷拌温度≤55℃；
c、挤出、将冷拌后的混合物送入行星挤出机内进行挤出，控制挤出温度为145~165℃，出料光亮且呈麻花状熟料；
d、过滤、将挤出机出来的胶料送入三层过滤网进行过滤，接挤出机过来的胶料后，在经过80目60目80目三层过滤网后成圆柱状熟料输送向扎轮机，温度145℃~165℃范围内；
e、扎轮、经过滤机后的胶料进一步塑化后，成直线片状料直接输送主机，温度控制在160℃-165℃；
f、成型、将直线片状胶料送入五辊机进行成型，辊的速比在1.1-1.3倍调节，成型后的胶膜通过牵引轮牵至冷却轮；
g、冷却定型、冷却轮内通冷却水或冷冻水，使成型产品冷却定型；
h、卷取包装、冷却定型后的产品经过卷取机卷成桶状后，经质检人员检验合格，计量包装待发货。
优选的，所述步骤f中五辊机的五个辊温度依次为193-196°C、190-195°C、186-190°C、183-186°C、180-182°C。
有益效果：本发明所揭示的一种医用高强度PVC膜，通过在配方制作出来的打印纸，抗菌性能高、耐腐蚀性能高、强度高、防水性能高，通过其生产方法可以大规模的生产医用高强度PVC膜，提高生产效率；
成形时采取五辊压延，通过调节五辊之间的温度差，使压花后的PVC薄膜温度降低，从而使薄膜表面出现轻微收缩，表面结构更加紧密和光滑，提高了3D打印纸的强度和耐磨性能。
具体实施方式
下面结合具体实施例对本发明作进一步说明：
本发明所揭示的一种医用高强度PVC膜，由以下重量份的原料配制而成：PVC树脂粉100份，食品级增塑剂0.8-1.1份，食品级稳定剂 3.0-3.5份，加工助剂1.5-1.7份，增强剂6-7份，润滑剂0.8-1份，色料群青0.06-0.07份。
其中，所述PVC树脂粉使用聚合度800。
一种制备权利要求1中医用高强度PVC膜的制备方法，包括如下步骤：
a、混合、按照质量份将原料投入高速混合机进行混合搅拌，混合时间260~320秒，温度为80~90℃；
b、冷拌、将步骤a混合后的组分输送到低速冷拌机内，进行搅拌冷却，控制冷拌温度≤55℃；
c、挤出、将冷拌后的混合物送入行星挤出机内进行挤出，控制挤出温度为145~165℃，出料光亮且呈麻花状熟料；
d、过滤、将挤出机出来的胶料送入三层过滤网进行过滤，接挤出机过来的胶料后，在经过80目60目80目三层过滤网后成圆柱状熟料输送向扎轮机，温度145℃~165℃范围内；
e、扎轮、经过滤机后的胶料进一步塑化后，成直线片状料直接输送主机，温度控制在160℃-165℃；
f、成型、将直线片状胶料送入五辊机进行成型，五辊机的五个辊温度依次为193-196°C、190-195°C、186-190°C、183-186°C、180-182°C，辊的速比在1.1-1.3倍调节，成型后的胶膜通过牵引轮牵至冷却轮；
g、冷却定型、冷却轮内通冷却水或冷冻水，使成型产品冷却定型；
h、卷取包装、冷却定型后的产品经过卷取机卷成桶状后，经质检人员检验合格，计量包装待发货。
实施例一
一种医用高强度PVC膜，由以下重量份的原料配制而成：PVC树脂粉100份，食品级增塑剂0.8份，食品级稳定剂 3.0份，加工助剂1.5份，增强剂6份，润滑剂0.8份，色料群青0.06份。
实施例二
一种医用高强度PVC膜，由以下重量比的原料配制而成：由以下重量份的原料配制而成：PVC树脂粉100份，食品级增塑剂1份，食品级稳定剂 3.3份，加工助剂1.65份，增强剂6.5份，润滑剂0.9份，色料群青0.065份。
实施例三
一种医用高强度PVC膜，由以下重量份的原料配制而成：PVC树脂粉100份，食品级增塑剂1.1份，食品级稳定剂 3.5份，加工助剂1.7份，增强剂7份，润滑剂1份，色料群青0.07份。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (5)
1.一种医用高强度PVC膜，其特征在于：由以下重量份的原料配制而成：PVC树脂粉100份，食品级增塑剂0.8-1.1份，食品级稳定剂 3.0-3.5份，加工助剂1.5-1.7份，增强剂6-7份，润滑剂0.8-1份，色料群青0.06-0.07份。
2.根据权利要求1所述的一种医用高强度PVC膜，其特征在于：由以下重量比的原料配制而成：由以下重量份的原料配制而成：PVC树脂粉100份，食品级增塑剂1份，食品级稳定剂3.3份，加工助剂1.65份，增强剂6.5份，润滑剂0.9份，色料群青0.065份。
3.根据权利要求1或2所述的一种医用高强度PVC膜，其特征在于：所述PVC树脂粉使用聚合度800。
4.一种制备权利要求1中医用高强度PVC膜的制备方法，其特征在于包括如下步骤：
a、混合、按照质量份将原料投入高速混合机进行混合搅拌，混合时间260~320秒，温度为80~90℃；
b、冷拌、将步骤a混合后的组分输送到低速冷拌机内，进行搅拌冷却，控制冷拌温度≤55℃；
c、挤出、将冷拌后的混合物送入行星挤出机内进行挤出，控制挤出温度为145~165℃，出料光亮且呈麻花状熟料；
d、过滤、将挤出机出来的胶料送入三层过滤网进行过滤，接挤出机过来的胶料后，在经过80目60目80目三层过滤网后成圆柱状熟料输送向扎轮机，温度145℃~165℃范围内；
e、扎轮、经过滤机后的胶料进一步塑化后，成直线片状料直接输送主机，温度控制在160℃-165℃；
f、成型、将直线片状胶料送入五辊机进行成型，辊的速比在1.1-1.3倍调节，成型后的胶膜通过牵引轮牵至冷却轮；
g、冷却定型、冷却轮内通冷却水或冷冻水，使成型产品冷却定型；
h、卷取包装、冷却定型后的产品经过卷取机卷成桶状后，经质检人员检验合格，计量包装待发货。
5.根据权利要求4所述的一种医用高强度PVC膜的制备方法，其特征在于：所述步骤f中五辊机的五个辊温度依次为193-196°C、190-195°C、186-190°C、183-186°C、180-182°C。