CN109868547A - The high-elastic high reply of one kind is with the elastic plain weave fabric of idea weft knitting - Google Patents
The high-elastic high reply of one kind is with the elastic plain weave fabric of idea weft knitting Download PDFInfo
- Publication number
- CN109868547A CN109868547A CN201910147469.0A CN201910147469A CN109868547A CN 109868547 A CN109868547 A CN 109868547A CN 201910147469 A CN201910147469 A CN 201910147469A CN 109868547 A CN109868547 A CN 109868547A
- Authority
- CN
- China
- Prior art keywords
- elastic
- yarn
- idea
- weft
- plain weave
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high-elastic high replies with the elastic plain weave fabric of idea weft knitting, weft-knitted single knitting machine is first passed through using latitude plain stitch by inelastic yarn and elastomeric polyurethane fiber yarn, it then is 190 DEG C~200 DEG C in temperature, under conditions of machine speed is 20~24m/min, setting treatment is done on forming machine then at the high-elastic high reply with the elastic plain weave fabric of idea weft knitting.Fabric of the present invention is using weft-knitted single knitting machine by non-elastic yarn and spandex, it is formed using latitude plain stitch, make spandex be sticked together to form firm spandex network by high temperature pre-setting, it can be replied rapidly after stretching, good recovery is also able to maintain after multi-drawing, no matter thataway cuts out all no flash, not scattered side, not crimping, therefore the present invention has the characteristics that extraordinary high-elastic, Gao Huifu, with idea, it is upper in the design and use of the products such as underwear, the comfort property of personal clothes can be greatly improved.
Description
Technical field
The present invention relates to a kind of novel high-elastic high replies with the elastic plain weave fabric of idea weft knitting.
Background technique
Currently, weft-knitted elastic fabric is widely used as underwear, leggings, brassiere cup etc..Modern female dress is got over
More focus on fashion, individual character and perfect stature, is pierced by that intention is unlimited, the design inspiration of actual experience designer.And it underpants, beats
Underpants, brassiere cup are indispensable clothes in women wardrobe, frivolous, soft, personal, feel is fabulous, sufficiently performance female
Property leg lines, while ventilative good, dress is repeatedly indeformable, can arbitrarily cut to any direction without crimping, not decoherence, yarn
Adhesion is close between line.So good underpants, leggings, brassiere cup fabric need high-elastic, Gao Huifu, with idea effect,
Fabric only in this way could perfect the characteristics of realizing underpants, leggings, brassiere cup.This is right for good feel, gas permeability
It is very easy to realize for knitting fabric, but high-elastic, Gao Huifu, is difficult to the elastic plain weave fabric of weft knitting of idea
, because weft knitting elasticity plain weave fabric is because of institutional framework problem, easily crimping, high elongation necessarily has high reply
Rate, it is extremely difficult.After multiple ultimate elongation, general fabric coil displacement is serious, at this time needs the strong of spandex
Power retraction, but it is serious in coil displacements same after multi-drawing using common spandex, it is difficult to be replied in time in place, then preparing
It is a kind of to be able to achieve high-elastic high reply with the fabric of idea with regard to particularly important.
Summary of the invention
The present invention provides high-elastic high reply with the elastic plain weave fabric of idea weft knitting, and this fabric has high-elastic, high time
The features such as multiple, with idea.
The invention is realized by the following technical scheme:
The high-elastic high reply of one kind is first led to the elastic plain weave fabric of idea weft knitting by inelastic yarn and elastomeric polyurethane fiber yarn
Weft-knitted single knitting machine is crossed using latitude plain stitch, is then 190 DEG C~200 DEG C in temperature, machine speed is the item of 20~24m/min
Under part, setting treatment is done on forming machine then at the high-elastic high reply with the elastic plain weave fabric of idea weft knitting；
The non-elastic yarn is chemical-fibres filaments, and line density is 5~30 daniers；
The elastomeric polyurethane fiber yarn is that energy adhesion is good at 190 DEG C~200 DEG C and elastic force loses lesser spandex, its line
Density is 15~70 daniers；
The knitting needle density of the weft-knitted single knitting machine used is per inch 40~100.
A length of 160~the 210mm/100G of yarn of the chemical fibre non-elastic yarn.The chemical fibre non-elastic yarn use is longer
The long braiding of yarn, allows fabric to reach comfortable elasticity and rebound, such as 40G38 inch equipment, 20D chemical fibre non-elastic yarn makees this fabric, yarn
A length of 160~210mm/100G.
Preferably, the fineness of non-elastic yarn is less than or equal to the fineness of elastomeric polyurethane fiber yarn.
The prior art before relatively, the invention has the following advantages: fabric of the present invention utilizes weft-knitted single knitting machine
By non-elastic yarn and spandex, formed using latitude plain stitch, by high temperature pre-setting make spandex be sticked together to be formed it is firm
Spandex network, can be replied rapidly after stretching, good recovery is also able to maintain after multi-drawing, no matter thataway is cut
All no flash, not scattered side, not crimping are cut out, therefore the present invention has the characteristics that extraordinary high-elastic, Gao Huifu, with idea, inside
The design of the products such as clothing and use are upper, can greatly improve the comfort property of personal clothes.
Detailed description of the invention
Attached drawing 1 is the circuit diagram of fabric non-elastic yarn and specific spandex yarn of the present invention.
Specific embodiment
For the ease of the understanding of those skilled in the art, the invention will be further described with reference to the accompanying drawing.
Embodiment 1
The high-elastic high reply of one kind is first led to the elastic plain weave fabric of idea weft knitting by inelastic yarn and elastomeric polyurethane fiber yarn
Weft-knitted single knitting machine is crossed using latitude plain stitch, is then 190 DEG C~200 DEG C in temperature, machine speed is the item of 20~24m/min
Under part, setting treatment is done on forming machine then at the high-elastic high reply with the elastic plain weave fabric of idea weft knitting；In temperature
Degree is that 190 DEG C~200 DEG C spandexs will do it bonding, forms reticular structure；
The non-elastic yarn is chemical-fibres filaments, and line density is 5~30 daniers；
The elastomeric polyurethane fiber yarn is that energy adhesion is good at 190 DEG C~200 DEG C and elastic force loses lesser spandex, its line
Density is 15~70 daniers；
The knitting needle density of the weft-knitted single knitting machine used is per inch 40~100.
A length of 160~the 210mm/100G of yarn of the chemical fibre non-elastic yarn.The chemical fibre non-elastic yarn use is longer
The long braiding of yarn, allows fabric to reach comfortable elasticity and rebound, such as 40G38 inch equipment, 20D chemical fibre non-elastic yarn makees this fabric, yarn
Length is generally in 160~210mm/100G.
Preferably, the fineness of non-elastic yarn is less than or equal to the fineness of elastomeric polyurethane fiber yarn.
In specific braiding, in the following way:
The weaving machine model that the present embodiment uses when weaving: Santoni single knit or the weft knitting of other producers are single
Face large circle machine.Machine range: 24G-60G.Weave is that non-elastic yarn uses every piece of mode of latitude plain together with specific spandex
Lopping on needle.For example, showing the circuit diagram of the fabric in fig. 1.
The forming machine of the present embodiment is: vertical letter Monforts steam heat-shaping equipment, machine sizing bellows are 8-10 section, double
Padding machine stock tank.Sizing mode is that steam is heated to after 190 DEG C -200 DEG C, and fabric crosses the high temperature antioxygen of huntsman in stock tank
Agent NY:10g/l does high-temperature shaping processing, achievees the effect that spandex is viscous glutinous.The high-temperature anti-oxidant NY of Huntsman can be prevented
There are yellowing problems in high-temperature shaping in polyamide fibre yarn.
Dyeing and finishing: washing → predetermined → overflow dye → dehydration → rear whole.
Article No.: JS0532MN-1
The present embodiment uses raw material: triumphant nation PA6 20D/34F SD DTY (non-elastic yarn)；Asahi Chemical Industry's SF 40D (spandex
Elastomeric yarn).
Breadth: 148CM
Grammes per square metre: 125GSM
Spandex content: 45%
Physical testing parameter (method D4964,20 pounds of pulling force)
Longitudinal aperture: 261.4%
Broadwise aperture: 266%
Longitudinal modulus (when 30% aperture): 0.32 pound
Longitudinal modulus (when 50% aperture): 0.74 pound
Longitudinal modulus (when 70% aperture): 1.13 pounds
Longitudinal modulus (when 90% aperture): 1.48 pounds
Broadwise modulus (when 30% aperture): 0.36 pound
Broadwise modulus (when 50% aperture): 0.80 pound
Broadwise modulus (when 70% aperture): 1.21 pounds
Broadwise modulus (when 90% aperture): 1.61 pounds
The Length recovery 94.3% of the present embodiment.
The Width recovery 95.5% of the present embodiment.
Arbitrarily cut out all no flash, not scattered side, not crimping.
It should be noted that described above is not the restriction to technical solution of the present invention, wound of the invention is not being departed from
Under the premise of making design, it is any obviously replace it is within the scope of the present invention.
Claims (3)
1. a kind of high-elastic high reply is with the elastic plain weave fabric of idea weft knitting, it is characterised in that: by inelastic yarn and spandex
Elastomeric yarn first passes through weft-knitted single knitting machine using latitude plain stitch, is then 190 DEG C~200 DEG C in temperature, and machine speed is 20~
Under conditions of 24m/min, setting treatment is done on forming machine then at the high-elastic high reply with the elastic plain weave group of idea weft knitting
Woven fabric；
The non-elastic yarn is chemical-fibres filaments, and line density is 5~30 daniers；
The elastomeric polyurethane fiber yarn is that energy adhesion is good at 190 DEG C~200 DEG C and elastic force loses lesser spandex, its line density
For 15~70 daniers；
The knitting needle density of the weft-knitted single knitting machine used is per inch 40~100.
2. the high-elastic high reply of one kind according to claim 1 is with the elastic plain weave fabric of idea weft knitting, it is characterised in that:
A length of 160~the 210mm/100G of yarn of the chemical fibre non-elastic yarn.
3. the high-elastic high reply of one kind according to claim 1 is with the elastic plain weave fabric of idea weft knitting, it is characterised in that:
The fineness of non-elastic yarn is less than or equal to the fineness of elastomeric polyurethane fiber yarn.