CN109836729A - 一种改性塑料的配方 - Google Patents
一种改性塑料的配方 Download PDFInfo
- Publication number
- CN109836729A CN109836729A CN201711231470.9A CN201711231470A CN109836729A CN 109836729 A CN109836729 A CN 109836729A CN 201711231470 A CN201711231470 A CN 201711231470A CN 109836729 A CN109836729 A CN 109836729A
- Authority
- CN
- China
- Prior art keywords
- parts
- formula
- calcium carbonate
- modified plastics
- plastics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种改性塑料的配方，它由以下质量份数的组分制成：聚氨乙烯树脂30‑50份、丙烯酸树脂30‑40份、铝粉5‑10份、铁粉5‑10份、碱木质素3‑5份、碳酸钙2‑4份、分散剂2‑6份、热稳定剂1‑4份、增塑剂0.5‑3份、助剂4‑8份。本发明通过采用特殊方法对碳酸钙进行改性处理，提高了塑料的力学性能，尤其是塑料的拉伸强度和弯曲强度，稳定性极好。
Description
技术领域
本发明涉及塑料技术领域，尤其涉及一种改性塑料的配方。
背景技术
改性塑料属于石油化工产业链中的中间产品，主要由五大通用塑料和五大工程塑料为塑料基质加工丽成，具有阻燃、抗冲、高韧性、易加工性等特点。我国的改性塑料行业目前总体的发展水平较低，行业内企业的生产规模普遍偏小，产品的市场状况也呈现出初级产品多，中级产品质量不稳定，高级产品缺乏的特点，远不能满足我国21 世纪经济发展的需要。因此，改性塑料作为化工新材料领域中的一个重要组成部分，也己被国家列为重点发展的科技领域之一。
目前，现有的一般聚氯乙烯塑料，相对密度1.4左右，玻璃化温度77-90℃,170℃左右开始分解，对光和热的稳定性差，在100℃以上或经长时间阳光曝晒，就会分解而产生氯化氢，并进一步自动催化分解，引起变色，物理机械性能也迅速下降。
发明内容
为了克服现有技术中存在上述的不足，本发明提供一种具备抗拉性、抗弯性和稳定性好的改性塑料的配方。
本发明解决其技术问题的技术方案是：一种改性塑料的配方，它由以下质量份数的组分制成：聚氨乙烯树脂30-50份、丙烯酸树脂30-40份、铝粉5-10份、铁粉5-10份、碱木质素3-5份、碳酸钙2-4份、分散剂2-6份、热稳定剂1-4份、增塑剂0.5-3份、助剂4-8份。
作为优选，所述热稳定剂为二盐基亚磷酸铅。
作为优选，所述碳酸钙采用1-2%浓度甲基丙烯酸溶液浸泡1小时后，过滤，用去离子水清洗，然后再用1-2%聚丁基丙烯酸溶液浸泡，加热至80-90℃，保持2小时后，冷却至室温，过滤，用去离子水清洗，干燥，粉碎至80-100目粉末。
本发明的有益效果在于：本发明通过采用特殊方法对碳酸钙进行改性处理，提高了塑料的力学性能，尤其是塑料的拉伸强度和弯曲强度，稳定性极好。
具体实施方式
下面结合具体实施方式对本发明作进一步详细说明。
一种改性塑料的配方，它由以下质量份数的组分制成：聚氨乙烯树脂30-50份、丙烯酸树脂30-40份、铝粉5-10份、铁粉5-10份、碱木质素3-5份、碳酸钙2-4份、分散剂2-6份、热稳定剂1-4份、增塑剂0.5-3份、助剂4-8份。
本发明在制备时，将上述原料按如下顺序依次投入搅拌机中混合，先投入聚氨乙烯树脂主料，然后投入丙烯酸树脂辅料，接着投入分散剂、热稳定剂、增塑剂和助剂，然后投入铝粉和铁粉，最后投入碳酸钙和碱木质素，当原料全部投入搅拌机中时设置搅拌时间30-80min，形成混料，将混料加入双螺杆挤出机中，加工温度为180-260℃主机的转速为500rpm，挤出后冷却、风干切粒，即可制备出所述改性塑料。
作为优选，所述热稳定剂为二盐基亚磷酸铅。
作为优选，所述碳酸钙采用1-2%浓度甲基丙烯酸溶液浸泡1小时后，过滤，用去离子水清洗，然后再用1-2%聚丁基丙烯酸溶液浸泡，加热至80-90℃，保持2小时后，冷却至室温，过滤，用去离子水清洗，干燥，粉碎至80-100目粉末。
本发明通过采用特殊方法对碳酸钙进行改性处理，提高了塑料的力学性能，尤其是塑料的拉伸强度和弯曲强度，稳定性极好。
Claims (3)
1.一种改性塑料的配方，其特征在于，它由以下质量份数的组分制成：聚氨乙烯树脂30-50份、丙烯酸树脂30-40份、铝粉5-10份、铁粉5-10份、碱木质素3-5份、碳酸钙2-4份、分散剂2-6份、热稳定剂1-4份、增塑剂0.5-3份、助剂4-8份。
2.根据权利要求1所述的改性塑料的配方，其特征在于：所述热稳定剂为二盐基亚磷酸铅。
3.根据权利要求1所述的改性塑料的配方，其特征在于：所述碳酸钙采用1-2%浓度甲基丙烯酸溶液浸泡1小时后，过滤，用去离子水清洗，然后再用1-2%聚丁基丙烯酸溶液浸泡，加热至80-90℃，保持2小时后，冷却至室温，过滤，用去离子水清洗，干燥，粉碎至80-100目粉末。