CN109833852A - 空气净化用材料的制备方法 - Google Patents
空气净化用材料的制备方法 Download PDFInfo
- Publication number
- CN109833852A CN109833852A CN201711188976.6A CN201711188976A CN109833852A CN 109833852 A CN109833852 A CN 109833852A CN 201711188976 A CN201711188976 A CN 201711188976A CN 109833852 A CN109833852 A CN 109833852A
- Authority
- CN
- China
- Prior art keywords
- weight
- added
- parts
- carbon dust
- taking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种空气净化用材料的制备方法，包括以下步骤：(1)取1.6‑2重量份的过氧化二苯甲酰，加入到其重量30‑40倍的去离子水中，搅拌均匀；(2)取2‑3重量份的三乙胺，加入到其重量5‑7倍的无水乙醇中，搅拌溶解；(3)取47‑50重量份的碳粉，加入到其重量3‑4倍的硫酸溶液中，得活化碳粉溶液；(4)加入去离子水80‑100重量份，充分混合搅拌；(5)取20‑30重量份的甲基丙烯酸甲酯，送入到反应釜中，通入氮气，常温干燥，得活化碳粉沉积聚合物；(6)在碳粉沉积聚合物内加入发泡剂，干燥1‑3小时后即得空气净化材料。本发明增强了成品的空气净化能力，还具有一定消毒效果，增强空气净化能力。
Description
技术领域
本发明属于空气净化技术领域，具体涉及一种空气净化用材料的制备方法。
背景技术
空气净化是指针对室内的各种环境问题提供杀菌消毒、降尘除霾、祛除有害装修残留以及异味等的整体解决方案，这样能有效改善生活、办公条件，增进身心健康。室内环境污染物和污染来源主要包括放射性气体、霉菌、颗粒物、装修残留、二手烟等。当今室内由于用到了多种人造材料的装修，因而存在着甲醛、甲苯等污染和有害气体的广泛存在，这对人们的健康产生了严重的危害。目前空气净化材料主要是通过物理吸附、化学方法、催化等技术来除去有害物，常用的物理吸附材料主要有活性炭，活性炭因具有大的比表面积，很容易吸收空气中的有害气体，因此在日常生活中被广泛用于室内空气净化，而活性炭只能吸附有害气体而不能过滤较大的空气污染物。
发明内容
本发明所要解决的技术问题便是针对上述现有技术的不足，提供一种空气净化用材料的制备方法。
本发明所采用的技术方案是：一种空气净化用材料的制备方法，包括以下步骤：
(1)取1.6-2重量份的过氧化二苯甲酰，加入到其重量30-40倍的去离子水中，搅拌均匀；
(2)取2-3重量份的三乙胺，加入到其重量5-7倍的无水乙醇中，搅拌溶解；
(3)取47-50重量份的碳粉，加入到其重量3-4倍的硫酸溶液中，升高温度为50-60℃，超声1-2小时，过滤，将沉淀水洗，真空100-110℃下干燥完全，冷却至常温，加入到上述三乙胺的乙醇溶液中，在65-70℃下保温搅拌30-40分钟，得活化碳粉溶液；
(4)加入去离子水80-100重量份，充分混合搅拌；
(5)取20-30重量份的甲基丙烯酸甲酯，送入到反应釜中，通入氮气，升高温度为60-70℃，滴加上述过硫酸铵的水溶液，滴加完毕后保温搅拌2-3小时，加入上述活化碳粉溶液，升高温度为75-80℃，保温搅拌30-40分钟，出料，过滤，将沉淀水洗，常温干燥，得活化碳粉沉积聚合物；
(6)在碳粉沉积聚合物内加入发泡剂，干燥1-3小时后即得空气净化材料。
作为优选，所述步骤(3)中取碳粉50份。
本发明的有益效果在于：本发明通过将聚合物消除的方式，提高了碳粉对较大的空气污染物吸附效果，增强了成品的空气净化能力，将聚苯乙烯发泡进一步提高了成品的吸附能力，二氯异氰尿酸钠、三氯异氰尿酸还具有一定消毒效果，增强空气净化能力。
具体实施方式
下面将结合具体实施例对本发明作进一步详细说明。
一种空气净化用材料的制备方法，包括以下步骤：
(1)取1.6-2重量份的过氧化二苯甲酰，加入到其重量30-40倍的去离子水中，搅拌均匀；
(2)取2-3重量份的三乙胺，加入到其重量5-7倍的无水乙醇中，搅拌溶解；
(3)取47-50重量份的碳粉，加入到其重量3-4倍的硫酸溶液中，升高温度为50-60℃，超声1-2小时，过滤，将沉淀水洗，真空100-110℃下干燥完全，冷却至常温，加入到上述三乙胺的乙醇溶液中，在65-70℃下保温搅拌30-40分钟，得活化碳粉溶液；
(4)加入去离子水80-100重量份，充分混合搅拌；
(5)取20-30重量份的甲基丙烯酸甲酯，送入到反应釜中，通入氮气，升高温度为60-70℃，滴加上述过硫酸铵的水溶液，滴加完毕后保温搅拌2-3小时，加入上述活化碳粉溶液，升高温度为75-80℃，保温搅拌30-40分钟，出料，过滤，将沉淀水洗，常温干燥，得活化碳粉沉积聚合物；
(6)在碳粉沉积聚合物内加入发泡剂，干燥1-3小时后即得空气净化材料。作为优选，所述步骤(3)中取碳粉50份。
本发明通过将聚合物消除的方式，提高了碳粉对较大的空气污染物吸附效果，增强了成品的空气净化能力，将聚苯乙烯发泡进一步提高了成品的吸附能力，二氯异氰尿酸钠、三氯异氰尿酸还具有一定消毒效果，增强空气净化能力。
Claims (2)
1.一种空气净化用材料的制备方法，其特征在于：包括以下步骤：
(1)取1.6-2重量份的过氧化二苯甲酰，加入到其重量30-40倍的去离子水中，搅拌均匀；
(2)取2-3重量份的三乙胺，加入到其重量5-7倍的无水乙醇中，搅拌溶解；
(3)取47-50重量份的碳粉，加入到其重量3-4倍的硫酸溶液中，升高温度为50-60℃，超声1-2小时，过滤，将沉淀水洗，真空100-110℃下干燥完全，冷却至常温，加入到上述三乙胺的乙醇溶液中，在65-70℃下保温搅拌30-40分钟，得活化碳粉溶液；
(4)加入去离子水80-100重量份，充分混合搅拌；
(5)取20-30重量份的甲基丙烯酸甲酯，送入到反应釜中，通入氮气，升高温度为60-70℃，滴加上述过硫酸铵的水溶液，滴加完毕后保温搅拌2-3小时，加入上述活化碳粉溶液，升高温度为75-80℃，保温搅拌30-40分钟，出料，过滤，将沉淀水洗，常温干燥，得活化碳粉沉积聚合物；
(6)在碳粉沉积聚合物内加入发泡剂，干燥1-3小时后即得空气净化材料。
2.根据权利要求1所述的空气净化用材料的制备方法，其特征在于：所述步骤(3)中取碳粉50份。