CN109810238A - 用于扬声器上的聚氨酯高分子材料的配方 - Google Patents
用于扬声器上的聚氨酯高分子材料的配方 Download PDFInfo
- Publication number
- CN109810238A CN109810238A CN201910031242.XA CN201910031242A CN109810238A CN 109810238 A CN109810238 A CN 109810238A CN 201910031242 A CN201910031242 A CN 201910031242A CN 109810238 A CN109810238 A CN 109810238A
- Authority
- CN
- China
- Prior art keywords
- loudspeaker
- high molecule
- polyurethane high
- formula
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种用于扬声器上的聚氨酯高分子材料的配方,该配方包括A料和B料,其中A料包括以下质量百分配比的组成:多元醇:80%‑95%;催化剂:0.5%‑7%;色膏:0.5%‑2%;水:0.2%‑0.5%,B料为异氰酸酯,所述A料和B料的比例为100:40~60,所述各组分的百分配比之和为100%,所述多元醇为聚酯多元醇和聚醚多元醇中的一种。本发明研发的聚氨酯高分子材料生产的喇叭垫,在颜色上能够根据市场需要进行灵活的变化,能够根据扬声器安装的实际安装场所装配相应硬度的喇叭垫,因此实现不同硬度的喇叭垫合理装配,而且本发明采用的配方均为环保材料,生产出的喇叭垫耐热、耐油、抗腐蚀和抗老化性能优异,因此大大延长了喇叭垫的使用寿命。
Description
技术领域
本发明涉及用于扬声器上的聚氨酯高分子材料的配方,属于橡胶材料与硅胶材料技术领域的创新。
背景技术
扬声器又称“喇叭”,是一种把电信号转变为声信号的换能器件,扬声器的性能优劣对音质的影响很大,扬声器在音响设备中是一个最薄弱的器件,而对于音响效果而言,它又是一个最重要的部件,扬声器的种类繁多,而且价格相差很大,音频电能通过电磁,压电或静电效应,使其纸盆或膜片振动并与周围的空气产生共振(共鸣)而发出声音。喇叭发声振动的时候就会振动,这种振动就会跟声音产生抵消,特别是对于中低频,所以音响加装喇叭垫圈的主要目的是:降低共振,使喇叭安装更结实,喇叭垫一般分为两种,一种是木垫圈,另一种是塑料垫圈,目前市场上传统喇叭垫材质主要是橡胶,其在环保问题、硬度和颜色多样性化要求、使用寿命等方面受到了很大的局限性。传统橡胶喇叭垫需要经过五个环节才能制成成品,即生胶塑炼,配合,混炼,半成品制备以及硫化处理成型,气味重,且只能做一种黑色颜色及硬度60-80度的硬度,使用寿命最多8年,而且易发霉老化。
发明内容
本发明针对现有技术存在的不足,提供用于扬声器上的聚氨酯高分子材料的配方,具有可以实现硬度和颜色多样化、环保且使用寿命可达15年的优点,以解决上述背景技术所提到的问题。
本发明解决上述技术问题的技术方案如下:用于扬声器上的聚氨酯高分子材料的配方,该配方包括A料和B料,其中A料包括以下质量百分配比的组成:多元醇:80% - 95%;催化剂:0.5% - 7%;色膏:0.5% - 2%;水:0.2% - 0.5%,B料为异氰酸酯,所述A料和B料的比例为100:40-60,所述各组分的百分配比之和为100%。
进一步,所述多元醇为聚酯多元醇和聚醚多元醇中的一种,所述聚醚多元醇采用聚氧化丙烯二醇、聚氧化丙烯三醇和聚四氢呋喃二醇中的一种。
进一步,所述异氰酸酯采用甲苯二异氰酸酯(TDI)、异佛尔酮二异氰酸酯(IPDI)、二苯基甲烷二异氰酸酯(MDI)、二环己基甲烷二异氰酸酯(HMDI)、六亚甲基二异氰酸酯(HDI)和赖氨酸二异氰酸酯(LDI)中的一种。
进一步,包括多元醇:85% - 90%;催化剂:1% - 3%;色膏:0.8% - 1.8%;水:0.3% -0.4%,B料为异氰酸酯,所述A料和B料的比例为100:40-60,所述各组分的百分配比之和为100%。
进一步,所述色膏的颜色包括黄色、红色、灰色和橙色。
进一步,所述A料中采用的水为发泡剂。
综上所述,本发明具有以下有益效果:
(1)本发明研发的聚氨酯高分子材料生产的喇叭垫,在颜色上能够根据市场需要进行灵活的变化,能够根据扬声器安装的实际安装场所装配相应硬度的喇叭垫,因此实现不同硬度的喇叭垫合理装配,而且本发明采用的配方均为环保材料,生产出的喇叭垫耐热、耐油、抗腐蚀和抗老化性能优异,因此大大延长了喇叭垫的使用寿命。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例一:
本实施例提供用于扬声器上的聚氨酯高分子材料的配方,该配方包括A料和B料,其中A料包括以下组分:聚氧化丙烯二醇:915千克;催化剂:65千克;红色色膏:17千克;水:3千克,B料为甲苯二异氰酸酯:450千克。
实施例二:本实施例与实施例一的区别特征在于:本实施例提供用于扬声器上的聚氨酯高分子材料的配方,该配方包括A料和B料,其中A料包括以下组分:聚氧化丙烯三醇:910千克;催化剂:68千克;橙色色膏:19千克;水:3千克,B料为甲苯二异氰酸酯:460千克。
实施例三:本实施例与实施例一和实施例二的区别特征在于:本实施例提供用于扬声器上的聚氨酯高分子材料的配方,该配方包括A料和B料,其中A料包括以下组分:聚四氢呋喃二醇:923千克;催化剂:60千克;黄色色膏:14千克;水:3千克,B料为二苯基甲烷二异氰酸酯(MDI):480千克。
实施例四:本实施例与实施例一、实施例二和实施例三的区别特征在于:
本实施例提供用于扬声器上的聚氨酯高分子材料的配方,该配方包括A料和B料,其中A料包括以下组分:聚氧化丙烯三醇:913千克;催化剂:63千克;灰色色膏:20千克;水:4千克,B料为赖氨酸二异氰酸酯:580千克。
利用本发明的用于扬声器上的聚氨酯高分子材料的配方,生产出的聚氨酯高分子材料,能够用于替换现有的用于扬声器上的橡胶材料与硅胶材料。
通过上述实验,本发明的聚氨酯高分子材料配方制成的喇叭垫,与现有技术对比,在颜色上能够根据市场需要进行灵活的变化,能够根据扬声器安装的实际安装场所装配相应硬度的喇叭垫,因此实现不同硬度的喇叭垫合理装配,而且本发明采用的配方均为环保材料,生产出的喇叭垫耐热、耐油、抗腐蚀和抗老化性能优异,因此大大延长了喇叭垫的使用寿命,使用寿命可由原先的八年增加到十五年之久。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (6)
1.一种用于扬声器上的聚氨酯高分子材料的配方,其特征在于:该配方包括A料和B料,其中A料包括以下质量百分配比的组成:多元醇:80% - 95%;催化剂:0.5% - 7%;色膏:0.5%- 2%;水:0.2% - 0.5%,B料为异氰酸酯,所述A料和B料的比例为100:40-60,所述各组分的百分配比之和为100%。
2.根据权利要求1所述的用于扬声器上的聚氨酯高分子材料的配方,其特征在于:所述多元醇为聚酯多元醇和聚醚多元醇中的一种,所述聚醚多元醇采用聚氧化丙烯二醇、聚氧化丙烯三醇和聚四氢呋喃二醇中的一种。
3.根据权利要求1所述的用于扬声器上的聚氨酯高分子材料的配方,其特征在于:所述异氰酸酯采用甲苯二异氰酸酯(TDI)、异佛尔酮二异氰酸酯(IPDI)、二苯基甲烷二异氰酸酯(MDI)、二环己基甲烷二异氰酸酯(HMDI)、六亚甲基二异氰酸酯(HDI)和赖氨酸二异氰酸酯(LDI)中的一种。
4.根据权利要求1所述的用于扬声器上的聚氨酯高分子材料的配方,其特征在于:包括多元醇:85% - 90%;催化剂:1% - 3%;色膏:0.8% - 1.8%;水:0.3% - 0.4%,B料为异氰酸酯,所述A料和B料的比例为100:40-60,所述各组分的百分配比之和为100%。
5.根据权利要求1所述的用于扬声器上的聚氨酯高分子材料的配方,其特征在于:所述色膏的颜色包括黄色、红色、灰色和橙色。
6.根据权利要求1所述的用于扬声器上的聚氨酯高分子材料的配方,其特征在于:所述A料中采用的水为发泡剂。