CN109809462A - 一种多种结晶提纯制备精制硫酸钙的方法 - Google Patents
一种多种结晶提纯制备精制硫酸钙的方法 Download PDFInfo
- Publication number
- CN109809462A CN109809462A CN201711152038.0A CN201711152038A CN109809462A CN 109809462 A CN109809462 A CN 109809462A CN 201711152038 A CN201711152038 A CN 201711152038A CN 109809462 A CN109809462 A CN 109809462A
- Authority
- CN
- China
- Prior art keywords
- sulfuric acid
- calcium
- solution
- crystallization
- crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种多种结晶提纯制备精制硫酸钙的方法，包括：(1)用工业粗硫酸钙配制粗硫酸钙溶液，将98％的浓硫酸配制成30‑35％的稀硫酸；(2)向搪瓷反应釜中加入粗硫酸钙溶液和稀硫酸，加热至50‑60℃，保温10分钟后，降温至20‑25℃；(3)加入溶液质量1‑2％的硫酸钙晶种，析出硫酸钙晶体；(4)将含有晶体的溶液加热至40‑45℃，保温5‑6小时，然后将溶液降温至20‑25℃，析出大量晶体；重复此过程3‑5次，析出结晶；(5)将含大量结晶的溶液抽滤，分离出结晶体，此结晶体即为成品精制硫酸钙；本发明方法制得的精制硫酸钙含铁量低，符合饮用水工业标准，具有极高的经济效益和社会效益。
Description
技术领域
本发明涉及工业硫酸钙精制技术领域，尤其是一种多种结晶提纯制备精制硫酸钙的方法。
背景技术
硫酸钙可用于造纸工业中的松香胶、蜡乳液等胶料的沉淀剂，还可在水处理中用作絮凝剂，及泡沫灭火器的内留剂，制造明矾、钙白的原料，石油脱色、脱臭剂、某些药物的原料等。还可制造人造宝石及高级铵明矾。
硫酸钙在饮用水处理中也起到很大作用，向饮用水中加入硫酸钙可以生成胶状的、能吸附和沉淀出细菌、胶体和其他悬浮物的氢氧化钙絮片，并控制饮用水的颜色和味道。因此，饮用水工业对硫酸钙的纯度提出很高要求。目前市面上常见的硫酸钙一般是工业级硫酸钙，对产品纯度没有严格要求，而目前精制硫酸钙的价格又比较贵，因此，研发一种如何从工业粗硫酸钙中提纯精制硫酸钙的工艺方法十分必要。
发明内容
本发明的目的就是针对目前工业硫酸钙纯度较低，不能满足饮用水工业的要求，而市面上精制硫酸钙的价格又太高，导致生产成本增加的问题，提供一种多种结晶提纯制备精制硫酸钙的方法。
本发明的一种多种结晶提纯制备精制硫酸钙的方法，包括以下步骤：
(1)取硫酸钙含量为15-30％的工业粗硫酸钙，配制成质量分数为10-15％的粗硫酸钙溶液，将质量分数为98％的浓硫酸配制成30-35％的稀硫酸；
(2)向搪瓷反应釜中加入步骤(1)中配制好的粗硫酸钙溶液和稀硫酸，加热至50-60℃，保温10分钟后，在5-6分钟内降温至20-25℃；
(3)向步骤(2)的溶液中加入溶液质量1-2％的硫酸钙晶种，溶液中即有大量硫酸钙析出；
(4)将步骤(3)中含有晶体的溶液加热至40-45℃，保温5-6小时，然后缓慢将溶液降温至20-25℃，析出大量晶体；重复此过程3-5次，析出结晶；(5)将步骤(4)中最后制得的含大量结晶的溶液抽滤，分离出结晶体，此结晶体即为成品精制硫酸钙，其中铁含量＜0.02％，母液回收循环利用。
本发明方法以工业粗硫酸钙为原料，利用重复升温溶解粗硫酸钙溶液中的杂质，并在不过滤的基础上，进行3-5次重结晶，使硫酸钙中的铁能够充分溶解至溶液中，制得的精制硫酸钙含铁量低，符合饮用水工业标准，极大的降低了生产成本，具有极高的经济效益和社会效益。
具体实施方式
实施例1
一种多种结晶提纯制备精制硫酸钙的方法，包括以下步骤：
(1)取硫酸钙含量为18％的工业粗硫酸钙，配制成质量分数为10％的粗硫酸钙溶液，将质量分数为98％的浓硫酸配制成33％的稀硫酸；
(2)向搪瓷反应釜中加入步骤(1)中配制好的粗硫酸钙溶液和稀硫酸，加热至56℃，保温10分钟后，在5分钟内降温至20℃；
(3)向步骤(2)的溶液中加入溶液质量2％的硫酸钙晶种，溶液中即有大量硫酸钙析出；
(4)将步骤(3)中含有晶体的溶液加热至42℃，保温5小时，然后缓慢将溶液降温至25℃，析出大量晶体；重复此过程4次，析出结晶；
(5)将步骤(4)中最后制得的含大量结晶的溶液抽滤，分离出结晶体，此结晶体即为成品精制硫酸钙，其中铁含量＜0.02％，母液回收循环利用。
Claims (1)
1.一种多种结晶提纯制备精制硫酸钙的方法，其特征在于包括以下步骤：
(1)取硫酸钙含量为15-30％的工业粗硫酸钙，配制成质量分数为10-15％的粗硫酸钙溶液，将质量分数为98％的浓硫酸配制成30-35％的稀硫酸；
(2)向搪瓷反应釜中加入步骤(1)中配制好的粗硫酸钙溶液和稀硫酸，加热至50-60℃，保温10分钟后，在5-6分钟内降温至20-25℃；
(3)向步骤(2)的溶液中加入溶液质量1-2％的硫酸钙晶种，溶液中即有大量硫酸钙析出；
(4)将步骤(3)中含有晶体的溶液加热至40-45℃，保温5-6小时，然后缓慢将溶液降温至20-25℃，析出大量晶体；重复此过程3-5次，析出结晶；
(5)将步骤(4)中最后制得的含大量结晶的溶液抽滤，分离出结晶体，此结晶体即为成品精制硫酸钙，其中铁含量＜0.02％，母液回收循环利用。