CN109762124A - 纳基聚酯隔热膏及其制备方法 - Google Patents

纳基聚酯隔热膏及其制备方法 Download PDF

Info

Publication number
CN109762124A
CN109762124A CN201811554497.6A CN201811554497A CN109762124A CN 109762124 A CN109762124 A CN 109762124A CN 201811554497 A CN201811554497 A CN 201811554497A CN 109762124 A CN109762124 A CN 109762124A
Authority
CN
China
Prior art keywords
component
glass bead
base polyester
superinsulation
cream
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811554497.6A
Other languages
English (en)
Inventor
吕德欣
闫严
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201811554497.6A priority Critical patent/CN109762124A/zh
Publication of CN109762124A publication Critical patent/CN109762124A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种纳基聚酯隔热膏及其制备方法，原料包括等比例的组分A和组分B，其中：组分A为纳米级的玻化微珠与组合聚醚按比例混合，组合聚醚：玻化微珠=100:10‑14；组分B为纳米级的玻化微珠和异氰酸酯按比例混合，异氰酸酯：纳米材料=100:10‑14。本发明的有益效果为：本发明的纳基聚酯超级隔热膏，适用温度：‑100—200℃，防火等级B1级，施工时无污染，导热系数小于等于0.027 w/m·k，可做到工业任何异形结构保温。

Description

纳基聚酯隔热膏及其制备方法
技术领域
本发明涉及一种保温材料，具体是一种纳基聚酯超级隔热膏及其制备方法。
背景技术
现有保温材料（-100—200℃）主要使用为橡塑材料，纤维类材料，聚氨酯材料，橡塑材料缺点：不防火，适用范围-20—80℃，燃烧后有大量有害气体，纤维类材料缺点：保温效果差，导热系数高，施工时有大量粉尘产生，对人体有害。聚氨酯材料缺点：使用温度-50—100℃，防火等级b2，强度低，易损坏，无法做到工业异性保温。
发明内容
为了克服上述缺陷，本发明提供了一种纳基聚酯超级隔热膏及其制备方法，适用温度范围广，防火等级B1级，施工时无污染，导热系数小于等于0.027 w/m·k，可做到工业任何异形结构保温。
本发明为实现上述目的所采用的技术方案是：纳基聚酯超级隔热膏，原料包括等比例的组分A和组分B，其中：
组分A为纳米级的玻化微珠与组合聚醚按比例混合，组合聚醚：玻化微珠=100:10-14；
组分B为纳米级的玻化微珠和异氰酸酯按比例混合，异氰酸酯：纳米材料=100:10-14。
进一步地，所述玻化微珠粒径为50-100nm。
进一步地，组合聚醚：玻化微珠=100: 13。
进一步地，异氰酸酯：纳米材料=100:11。
另外，本发明还提供了纳基聚酯超级隔热膏的制备方法，将纳米级玻化微珠按照所述比例掺入至组合聚醚中，经过低速搅拌机均匀搅拌制成组分A；另将玻化微珠按所述比例掺入至异氰酸酯中，经过低速搅拌机均匀搅拌制成组分B，组分A和组分B按照1:1比例混合搅拌进行催化反应。
进一步地，催化反应时，环境温度控制在15-20℃。
进一步地，催化反应时，搅拌机转速控制在400r/m,搅拌时间≥12min。
本发明的有益效果为：本发明的纳基聚酯超级隔热膏，适用温度：-100—200℃，防火等级B1级，施工时无污染，导热系数小于等于0.027 w/m·k，可做到工业任何异形结构保温。
具体实施方式
下面具体实施例对本发明作进一步解释说明。
实施例1
纳基聚酯超级隔热膏，原料包括等比例的组分A和组分B，其中：
组分A为纳米级的玻化微珠与组合聚醚按比例混合，组合聚醚：玻化微珠=100:13；
组分B为纳米级的玻化微珠和异氰酸酯按比例混合，异氰酸酯：纳米材料=100:11。
所述玻化微珠粒径平均粒径在60nm。
将纳米级玻化微珠按照所述比例掺入至组合聚醚中，经过低速搅拌机均匀搅拌制成组分A；另将玻化微珠按所述比例掺入至异氰酸酯中，经过低速搅拌机均匀搅拌制成组分B，组分A和组分B按照1:1比例混合搅拌进行催化反应。催化反应时，环境温度控制在15-20℃，搅拌机转速控制在400r/m,搅拌时间≥12min。
实施例2
纳基聚酯超级隔热膏，原料包括等比例的组分A和组分B，其中：
组分A为纳米级的玻化微珠与组合聚醚按比例混合，组合聚醚：玻化微珠=100:14；
组分B为纳米级的玻化微珠和异氰酸酯按比例混合，异氰酸酯：纳米材料=100:11。
所述玻化微珠粒径平均粒径在70nm。
将纳米级玻化微珠按照所述比例掺入至组合聚醚中，经过低速搅拌机均匀搅拌制成组分A；另将玻化微珠按所述比例掺入至异氰酸酯中，经过低速搅拌机均匀搅拌制成组分B，组分A和组分B按照1:1比例混合搅拌进行催化反应。催化反应时，环境温度控制在15-20℃，搅拌机转速控制在400r/m,搅拌时间≥12min。
实施例3
纳基聚酯超级隔热膏，原料包括等比例的组分A和组分B，其中：
组分A为纳米级的玻化微珠与组合聚醚按比例混合，组合聚醚：玻化微珠=100:11；
组分B为纳米级的玻化微珠和异氰酸酯按比例混合，异氰酸酯：纳米材料=100:12。
所述玻化微珠粒径平均粒径在65nm。
将纳米级玻化微珠按照所述比例掺入至组合聚醚中，经过低速搅拌机均匀搅拌制成组分A；另将玻化微珠按所述比例掺入至异氰酸酯中，经过低速搅拌机均匀搅拌制成组分B，组分A和组分B按照1:1比例混合搅拌进行催化反应。催化反应时，环境温度控制在15-20℃，搅拌机转速控制在400r/m,搅拌时间≥12min。
实施例4
纳基聚酯超级隔热膏，原料包括等比例的组分A和组分B，其中：
组分A为纳米级的玻化微珠与组合聚醚按比例混合，组合聚醚：玻化微珠=100:14；
组分B为纳米级的玻化微珠和异氰酸酯按比例混合，异氰酸酯：纳米材料=100:14。
所述玻化微珠粒径平均粒径在80nm。
将纳米级玻化微珠按照所述比例掺入至组合聚醚中，经过低速搅拌机均匀搅拌制成组分A；另将玻化微珠按所述比例掺入至异氰酸酯中，经过低速搅拌机均匀搅拌制成组分B，组分A和组分B按照1:1比例混合搅拌进行催化反应。催化反应时，环境温度控制在15-20℃，搅拌机转速控制在400r/m,搅拌时间≥12min。

Claims (7)

1.纳基聚酯超级隔热膏，其特征在于，原料包括等比例的组分A和组分B，其中：
组分A为纳米级的玻化微珠与组合聚醚按比例混合，组合聚醚：玻化微珠=100:10-14；
组分B为纳米级的玻化微珠和异氰酸酯按比例混合，异氰酸酯 ：纳米材料=100:10-14。
2.根据权利要求1所述的纳基聚酯超级隔热膏，其特征在于，所述玻化微珠粒径为50-100nm。
3.根据权利要求1所述的纳基聚酯超级隔热膏，其特征在于，组合聚醚：玻化微珠=100:13。
4.根据权利要求1或3所述的纳基聚酯超级隔热膏，其特征在于，异氰酸酯 ：纳米材料=100:11。
5.如权利要求1-4任一项所述的纳基聚酯超级隔热膏的制备方法，其特征在于，将纳米级玻化微珠按照所述比例掺入至组合聚醚中，经过低速搅拌机均匀搅拌制成组分A；另将玻化微珠按所述比例掺入至异氰酸酯中，经过低速搅拌机均匀搅拌制成组分B，组分A和组分B按照1:1比例混合搅拌进行催化反应。
6.根据权利要求5所述的纳基聚酯超级隔热膏的制备方法，其特征在于，催化反应时，环境温度控制在15-20℃。
7.根据权利要求5所述的纳基聚酯超级隔热膏的制备方法，其特征在于，催化反应时，搅拌机转速控制在400r/m,搅拌时间≥12min。
CN201811554497.6A 2018-12-19 2018-12-19 纳基聚酯隔热膏及其制备方法 Pending CN109762124A (zh)